• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.12
• /
• pp.813-820
• /
• 2015

We have studied commercialization and process optimization of protective film on transparent conductive coated substrate, nano silver on flexible PET (poly ethylene terephthalate), by means of roll-to-roll micro-gravure coater. Nanosilver on flexible PET substrate is potential materials to replace ITO (indium tin oxide). Protective film is most important to maintain unique silver pattern on top of transparent PET. PSA pressure sensitive adhesives) was developed solely for nano silver on PET and protective film was successfully laminated. We have optimized all process conditions such as coating thickness, line speed and aging time & temperature via experimental design. Transparent conductive film and its protective film developed in this research are commercially available at this moment.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.1
• /
• pp.52-59
• /
• 2000

In order to develop the transparent anti-static film with higher than 80% transparency to visible light, organic conductive compounds, N-methyl phenazinium 7,7,8,8-tetracyanoquinonedimethane (TCNQ) com-plex salts was synthesized and bar-coated on the polythylene terephthalate (PET) film using polymer binders. The best surface properties were obtained when acrylic binder was used. A single layer of TCNQ made of a acrylic binder showed a surface resistance of 10\ulcorner $\Omega$/ , a conductivity of 10\ulcorner S/cm, and a transparency of 75%. An optical microscopic examination revealed that the binder was first solidi-fied on the surface of PET film over which the needle-shaped TCNQ crystals were grown. An acrylic polyol coating over the TCNQ layer improved the transparency to 87%, becuase the acrylic polyol covers the surface of TCNQ crystals to reduce the surface roughness. This conductive material has thermal stability at room temperature and 4$0^{\circ}C$ over 4,000 h.

• Journal of the Korean Society for Precision Engineering
• /
• v.31 no.11
• /
• pp.993-998
• /
• 2014

Silver (Ag) grid patterned PET substrates were manufactured by thermal roll-imprinting methods. We coated highly conductive layer (HCL) as a supply electrode on the Ag grid patterned PET in the three kinds of conditions. One was no-HCL without conductive PEDOT:PSS on the Ag grid patterned PET substrate, another was thin-HCL coated with ~50 nm thickness of conductive PEDOT:PSS on the Ag grid PET, and the other was thick-HCL coated with ~95 nm thickness of conductive PEDOT:PSS. These three HCLs in order showed 73.8%, 71.9%, and 64.7% each in transmittance, while indicating $3.84{\Omega}/{\Box}$, $3.29{\Omega}/{\Box}$, and $2.65{\Omega}/{\Box}$ each in sheet resistance. Fabrication of organic solar cells (OSCs) with HCL Ag grid patterned PET substrates showed high power conversion efficiency (PCE) on the thin-HCL device. The thick-HCL device decreased efficiency due to low open circuit voltage ($V_{OC}$). And the Ag grid pattern device without HCL had the lowest energy efficiency caused by quite low short current density ($J_{SC}$).

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.33 no.6
• /
• pp.500-504
• /
• 2020

Heating films were prepared with composites of poly (methyl methacrylate) and conductive graphite. The as-prepared composite was deposited on a PET film and then fabricated using a bar coater to produce a film with uniform thickness. Copper electrodes were attached to both ends of the as-prepared film, and the heating characteristics of the film were analyzed while applying a DC voltage. The electrical conductivity and heating temperature of the heating films depended on the size, structure, content, and the dispersion characteristics of the graphite in the composite. The thermal energy was adjusted by controlling the electrical energy, based on the Joule heating theory. The electrical resistance of the film was altered in proportion to Ohm's law, and the heating temperature was changed according to the structure of the film (interelectrode spacing or electrode length) and the conductive graphite content. When the content of conductive graphite in the film increases, the electrical resistance decreases, and the heating temperature increases; however, there is no significant change above a certain content (50%).

• Applied Chemistry for Engineering
• /
• v.33 no.4
• /
• pp.381-385
• /
• 2022

It is very important to secure the adhesion durability between the base film and the conductive paste for the development of a sensor for detecting hazardous chemicals. In this study, an ester binder was used to improve the adhesive properties which can be a problem when applying the sensor to the cross cut 0B or 1B grade. This problem was found while evaluating the adhesive properties by coating the polyaniline/graphene nano plate (GNP) paste on the polyethylene terephthalate (PET) film. When 10 wt% or more of the ester-based binder was added, the cross cut grade to which the sensor can be applied was 3B or higher. It was confirmed that the excessive addition of the binder may affect the electrical properties of the conductive paste and actually decrease the reactivity to sulfuric acid. To improve the electrical property, a carbon black (CB) content was varied resulting in the optimum electrical property observed at 2 wt% of CB.

• Applied Chemistry for Engineering
• /
• v.29 no.2
• /
• pp.162-167
• /
• 2018

The effect of the average particle size and shape of silver nanoparticles for the transparent conductive film (TCF) was studied. Optical and electrical properties of silver conductive lines coated on the polyethylene terephthalate (PET) film was also measured. Silver nanoparticles produced by Ag-CM, Ag-ME, Ag-EE methods showed an excellent conductivity compared to those produced by Ag-EB, Ag-CR and Ag-PL methods, but a little difference in the transparency. In the case of the former three silver nanoparticles, the average particle size was about 80 nm or less and the size was uniform. For the latter case, the severe agglomeration phenomena of particles was observed and the average particle size was 100 nm or more. This result was consistent with the result of the uniformity of the pattern shape and thickness on conductive line patterns observed by SEM. Therefore, it was confirmed that the electrical characteristics could be obtained when the average particle size of silver nanoparticles is smaller and the uniformity of the particles is maintained.

• Clean Technology
• /
• v.13 no.3
• /
• pp.180-187
• /
• 2007

The indium tin oxide(ITO) film on PET was prepared by a wet coating method to obtain the transparent film with a high conductance. ITO nano-particles was synthesized by a SAS method at 15 MPa and $50^{\circ}C$, where optimized rate of In/Sn was 65. Average diameter and resistivity of ITO obtained from SAS are $15{\pm}2\;nm$ and $4{\times}10^4\;{\Omega}{\cdot}cm$. Coating solution was prepared at pH 10. The ITO film was obtained by solution including 0.1 0.5, 1, and 2 ITO wt% on PET. Roughness(Ra) of ITO film with 0.1, 0.5, 1. and 2 ITO wt% is 4, 10, 12, and 16 nm. Resistivity with an increasing ITO concentration is $3.7{\times}10^6,\;2.4{\times}10^6,\;8{\times}10^5,\;and\;2{\times}10^5\;{\Omega}{\cdot}cm$. Transmissivity of ITO film decreased as 89, 88, 86, and 82% with an increasing ITO concentration as 0.1, 0.5, 1, and 2 wt%.

• Applied Chemistry for Engineering
• /
• v.19 no.1
• /
• pp.37-44
• /
• 2008

The multi-layer PET film of ITO/ATO was prepared by a wet coating method to obtain the transparent film with a high conductance at low cost. ITO nano-particles were synthesized by a SAS method at 15 MPa and $50^{\circ}C$, where optimized rate of In/Sn was 65. Average diameter and resistivity of ITO obtained from SAS are $15{\pm}2nm$ and $4{\times}10^4{\Omega}{\cdot}cm$. Coating solution was prepared at pH 10. Roughness (Ra), resistivity, and transmissivity of ATO film on PET are 9 nm, $5.5{\times}10^6{\Omega}{\cdot}cm$, and 91%. The multi-layered film of ITO/ATO was obtained by solution including 0.1, 0.5, 1.0, and 2.0 ITO wt% on ATO layer. Roughness (Ra) of multi-layered film with 0.1, 0.5, 1.0, and 2.0 ITO wt% is 4, 10, 12, and 16 nm, respectively. Corresponding resistivity with an increasing ITO concentration is $3.7{\times}10^6$, $2.4{\times}10^6$, $8{\times}10^5$, and $2{\times}10^5{\Omega}{\cdot}cm$. Transmissivity of ITO/ATO film decreases as 89, 88, 86, and 82% with an increasing ITO concentration as 0.1, 0.5, 1.0, and 2.0 wt%.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.36 no.5
• /
• pp.517-521
• /
• 2012

Carbon nanotubes (CNTs) have been regarded as a promising material for the fabrication of flexible conductors such as transparent electrodes, flexible heaters, and transparent speakers. In this study, a multiwalled carbon nanotube (MWCNT) film was deposited on a polyethylene terephthalate (PET) substrate using a spraying technique. MWCNTs were dispersed in water using sodium dodecyl sulfate (SDS). To evaluate the effect of the weight ratio between SDS and MWCNTs on the electromechanical properties of the film, direct tensile tests and optical strain measurement were conducted. It was found that the CNT film hardly affected the mechanical behavior of CNT/PET composite films, while the electrical behavior of the CNT film was strongly affected by the SDS concentration in the CNT film. The electrical resistance of CNT/PET films gradually increased with the strain applied to the PET substrate, even up to a large strain that ruptured the substrate.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.205-206
• /
• 2008

The transparent conductive film was prepared by bar coating method of poly (3, 4-ethylenedioxythiophene) (PEDOT) and poly (sodium 4-stylenesulfonate) grafted multi-walled carbon nanotubes (MWNT-PSS) nanocomposites solution on the polyethylene terephthalate (PET) film. In this case, multi-wall carbon nanotubes was treated by chemical methods to obtain water soluble MWNT-PSS and then blending with PEDOT. The non-covalent bonding of polymer to the MWNT surface was confirmed by Fourier transform infrared (FT-IR), thermal gravimetric analysis (TGA) and Transmission electro microscope (TEM) investigation also showed a polymer-wrapped MWNT structure. Furthermore, the electrical, transmission properties of the transparent conductive film were investigated and compared with control samples are raw PEDOT films.