• Journal of the Korea Concrete Institute
• /
• v.17 no.3 s.87
• /
• pp.329-334
• /
• 2005

The use of Polymer Concrete (PC) is growing very rapidly in many structural and construction applications such as box culverts, hazardous waste containers, trench lines, floor drains and the repair and overlay of damaged cement concrete surfaces in pavements, bridges, etc. However, PC has a defect economically because resin which be used for binder is expensive. Therefore the latest research is being progressed to replace existing resin with new resin which can reduce the high cost. Here, Polymer concrete using the recycled PET(polyethylene terephthalate) has some merits such as decrease of environmental destruction, decrease of environmental pollution and development of new construction materials. The variables of this study are amount of resin, curing condition and maximum size of coarse aggregate to find out mechanic properties of this. Stress-strain curve was obtained using MTS equipment by strain control. The results indicated that modulus of elasticity was increased gradually in an ascending branch of curve, as an increase of resin content. Compressive strength was the highest for resin content of $13\%$. And Compressive strength was increased as maximum size of coarse aggregate increases. The strain at maximum stress increases with an increase of resin content and size of coarse aggregate. For the descending branch of stress-strain curve the brittle fracture was decreased when it was cured at the room temperature compared to high temperature.

• Journal of the Korea Concrete Institute
• /
• v.23 no.1
• /
• pp.77-86
• /
• 2011

The concrete creep deformation of a hybrid composite section can cause additional deformation of the composite section and the stress relaxation of pre-compressive stress on the concrete section due to partial restraint of the deformation. In this study, the stress relaxation coefficient method (SRCM) is derived for simple analysis of complicate hybrid or composite sections for engineering purpose. Also, an equation of the stress relaxation coefficient (SRC) required for the SRCM is proposed. The SRCM is derived with the parameters of a creep coefficient, section and loading properties using the same method as the constant-creep step-by-step method (CC-SSM). The errors of the SRCM is improved by using the proposed SRC equation than the average SRC's which were estimated from the CC-SSM. The root mean square error (RMSE) of the SRCM with the proposed SRC equation for concrete with creep coefficient less than 3 was less than 1.2% to the creep deformation at the free condition and was 3.3% for the 99% reliability. The proposed SRC equation reflects the internal restraint of composite sections, and the effective modulus of elasticity computed with the proposed SRC can be used effectively to estimate the rigidity of a composite section in a numerical analysis which can be applied in analysis of the external restrain effect of boundary conditions.

• Earthquakes and Structures
• /
• v.8 no.1
• /
• pp.275-304
• /
• 2015

The objective of this paper is to investigate the validity of transmitting boundaries in dynamic analysis of soil-structure interaction problems. As a case study, the proposed Baghdad metro line is considered. The information about the dimensions and the material properties of the concrete tunnel and surrounding soil were obtained from a previous study. A parametric study is carried out to investigate the effect of several parameters including the peak value of the horizontal component of earthquake displacement records and the frequency of the dynamic load. The computer program (Mod-MIXDYN) is used for the analysis. The numerical results are analyzed for three conditions; finite boundaries (traditional boundaries), infinite boundaries modelled by infinite elements (5-node mapped infinite element) presented by Selvadurai and Karpurapu, 1988), and infinite boundaries modelled by dashpot elements (viscous boundaries). It was found that the transmitting boundary absorbs most of the incident energy. The distinct reflections observed for the "fixed boundaries" disappear by using "transmitted boundaries". This is true for both cases of using viscous boundaries or mapped infinite elements. The type and location of the dynamic load represent two controlling factors in deciding the importance of using infinite boundaries. It was found that the results present significant differences when earthquake is applied as a base motion or a pressure load is applied at the surface ground. The peak value of the vertical displacement at nodes A, B, E and F (located at the tunnel's crown and side walls, and at the surface above the tunnel and at the surface 6.5 m away from tunnel's centre respectively) increases with the frequency of the surface pressure load for both cases 1 and 2 (traditional boundaries and mapped infinite elements respectively) while it decreases for case 3 (viscous boundaries). The modular ratio Ec/Es (modulus of elasticity of the concrete lining to that of the surrounding soil) has a considerable effect on the peak value of the horizontal displacement at node B (on the side wall of the tunnel lining) increase about (17.5) times, for the three cases (1, 2, and 3).

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.13 no.1
• /
• pp.147-158
• /
• 2000

For the large scale reinforced concrete cooling tower shells, the shape imperfection can be introduced due not only to mistakes in the process of construction but also to the long term behavior of concrete. The shape imperfection evokes the additional responses such as displacements and stresses in addition to the design values. In this study, the statistical behavior of the RC cooling tower shell due to the shape imperfection is investigated using the Monte Carlo simulation. The radius of cooling tower and the shell thickness are adopted as the parameters which cause the shape imperfection. The shape imperfection is modeled as a stochastic field rather than the local one of axisymmetric or bulge type of imperfection. The randomness in the radius is shown to be more affecting the structural responses than the randomness in the shell thickness. In addition to the geometrical randomness, the effect of randomness in the modulus of elasticity on the structural response is also investigated and compared with that of the geometrical ones.

• Journal of the Korea Concrete Institute
• /
• v.19 no.6
• /
• pp.701-706
• /
• 2007

This study evaluated the durability of high-performance shotcrete mixed in the proper proportions using alkali-free and cement mineral accelerators as a permanent support that maintains its strength for the long term. Durability tests were performed the chloride permeability, repeated freezing and thawing, accelerated carbonation, and the effects of salt environments. Test results showed that all the shotcrete mixes included silica fume had low permeability. In addition, after 300 freeze/thaw cycles, the shotcrete mix had excellent freeze/thaw resistance more than the 85% relative dynamic modulus of elasticity. The accelerated carbonation test results were no effect of accelerator type but, the depth of carbonation was greater in the shotcrete mix containing silica fume. No damage was seen in a salt environments. Therefore, the high performance shotcrete mix proportions used in this study showed excellent durability.

• Proceedings of the Korean Society of Agricultural Engineers Conference
• /
• 2003.10a
• /
• pp.403-406
• /
• 2003

This study is performed to evaluate the strength and nan-fracture test of the ready mixed concrete(RMC) using polypropylene. The slump is reached in $8{\pm}2cm$ of each RMC using polypropylene or without polypropylene, air content is reached in $4.5{\pm}1.5%$, the chloride content is below $0.3kg/m^3$. The compressive strength of RMC not using polypropylene is appeared over $210kgf/cm^2$ at the curing age 7 days and $239kgf/cm^2$ at the curing age 28 days. The compressive strength of RMC using polypropylene is appeared over $188kgf/cm^2$ at the curing age 7 days and $238kgf/cm^2$ at the curing age 28 days. The dynamic modulus of elasticity of RMC not using polypropylene is appeared over $298{\times}10^3kgf/cm^2$ at the curing age 7 days and $342{\times}10^3kgf/cm^2$ at the curing age 28 days. The RMC using polypropylene is appeared over $284{\times}10^3kgf/cm^2$ at the curing age 7 days and $238{\times}10^3kgf/cm^2$ at the curing age 28 days. The pulse velocity of RMC not using polypropylene is appeared over 4,198m/s at the curing age 7 days and 4,382m/s at the curing age 28 days. The RMC using polypropylene is appeared over 4,182m/s at the curing age 7 days and 4,342m/s at the curing age 28 days.

• Korean Journal of Agricultural Science
• /
• v.24 no.2
• /
• pp.194-206
• /
• 1997

This paper was performed to evaluate the properties of no-coarse lightweight concrete using perlite and expanded polystyrene bead on fine aggregate. The results were shown that w/c and unit weight was affected by absorption ratio and unit weight of using aggregate itself. The compressive strength of no-coarse lightweight concrete was showed $187kgf/cm^2$ by using natural sand, $170kgf/cm^2$ by using perlite. Tensile and bending strength were showed the same tendency of compressive strength, but when expanded polystyrene bead concrete dose not have strength nearly. The pulse velocity and static modulus of elasticity of no-coarse lightweight concrete were smaller than that of normal cement concrete. And stress-strain curves were shown that was increased with increase of stress, and when the stress-strain curve using expanded polystyrene bead was repeated at short intervals increase and decrease irregularly.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.2
• /
• pp.107-115
• /
• 2019

The many countries are facing the shortage of natural resources, and the supply of aggregates are being exhausted. To consider this situation a variety of studies were performed for the development of alternative resources. In particular, high density filler material was used for shielding radioactive waste, large amount of natural aggregates are required in order to produce filler material. Also, in order to improve the shielding performance of filler material, it is required to increase the density of the filler material. Therefore, in this study was carried out to provide basic data for expanding the feasibility of high density industrial waste resource as aggregate in heavyweight concrete. From the test results, OPC case, concrete strength decreased by using heavyweight waste glass as fine aggregate, however, it is improved by using mineral admixture as binder. Therefore, when the heavyweight waste glass and steel slag are applied to heavyweight concrete, it is desirable to use mineral admixture, especially to use BFS than FA. Meanwhile, when the steel slag was replaced as coarse aggregate of heavyweight concrete, elasticity of modulus and radiation shielding performance can be improved owing to high density of steel slag.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.14 no.8
• /
• pp.4033-4038
• /
• 2013

Sedimentary rocks from construction waste are discarded through open storage and landfilling, which causes an increase in construction cost and inefficient of execution of works. Some sandstone are selected and utilized as aggregates, but shale is buried as industrial waste. Therefore, in this research, we evaluated weathering properties of shale aggregate that is widely distributed throughout Daegu-Kyeongbuk region and freeze-thaw characteristics of concrete according to the replacement ratio of shale aggregate, in an effort to stabilize aggregate supply-demand in Daegu-Kyeongbuk region and develop alternative aggregates. We used red shale and black shale in the experiment, which were exported from a construction site in Deagu. We verified the usage of shale as a concrete aggregate by comparing andesite, which is broadly used as a thick aggregate for concrete, to hornfels, which is a metamorphic sedimentary rock. As a result of the experiment, we observed no degradation phenomenon for andesite and hornfels. However, a part of country rock containing black shale was found to be exfoliated. Red shale started having cracks in the direction of stratification after 1.5 months of direct exposure, and it broke into smaller pieces after approximately 4 months. After 300 cycles of freeze-thaw process on the concrete manufactured according to the replacement ratio of shale aggregate, the modulus of elasticity was 97% for plain and 95% for hornfels. In the case of RS_100, it was 57% after 210 cycles, and for BS_100, it was 54% after 240 cycles. Therefore, we established that, as the number of repetition increases, the freeze-thaw resistance decreases dramatically.

• Computers and Concrete
• /
• v.14 no.5
• /
• pp.599-612
• /
• 2014

This paper presents the effects of the construction stages using time dependent material properties on the structural behaviour of concrete arch dams. For this purpose, a double curvature Type-5 arch dam suggested in "Arch Dams" symposium in England in 1968 is selected as a numerical example. Finite element models of Type-5 arch dam are modelled using SAP2000 program. Geometric nonlinearity is taken into consideration in the construction stage analysis using P-Delta plus large displacement criterion. In addition, the time dependent material strength variations and geometric variations are included in the analysis. Elasticity modulus, creep and shrinkage are computed for different stages of the construction process. In the construction stage analyses, a total of 64 construction stages are included. Each stage has generally $6000m^3$ concrete volume. Total duration is taken into account as 1280 days. Maximum total step and maximum iteration for each step are selected as 200 and 50, respectively. The structural behaviour of the arch dam at different construction stages has been examined. Two different finite element analyses cases are performed. In the first case, construction stages using time dependent material properties are considered. In the second case, only linear static analysis (not considered construction stages) is taken into account. Variation of the displacements and stresses are obtained from the both analyses. It is highlighted that construction stage analysis using time dependent material strength variations and geometric variations has an important effect on the structural behaviour of arch dams. The maximum longitudinal, transverse and vertical displacements obtained from construction stages and static analyses are 1.35 mm and 0 mm; -8.44 and 6.68 mm; -4.00 and -9.90 mm, respectively. In addition, vertical displacements increase from the base to crest of the dam for both analyses. The maximum S11, S22 and S33 stresses are obtained as 1.60MPa and 2.84MPa; 1.39MPa and 2.43MPa; 0.60MPa and 0.50MPa, respectively. The differences between maximum longitudinal, transverse, and vertical stresses obtained from construction stage and static analyses are 78%, 75%, and %17, respectively. On the other hand, there is averagely 12% difference between minimum stresses for all three directions.