• Journal of the Korea Concrete Institute
• /
• v.16 no.6 s.84
• /
• pp.805-811
• /
• 2004

In this paper, effects of mixture proportion and material condition on both fundamental properties, drying and autogenous shrinkage of high performance concrete are discussed. According to the results, for the effect of mixture proportion on the fundamental properties, decrease in W/B and unit water content results in reduction of fluidity, while air content has no variation. Compressive strength exhibits an decreasing tendency with an increase in W/B and unit water content do not remarkable affect the compressive strength. For the effect of materials on the fluidity, the fluidity of low heat portland cement(LPC) is smaller than that of ordinary portland cement(OPC). The use of Polycarbonic acid based superplasticizer(PS) has more favorable effect on enhancing fluidity than Naphtalene based superplasticlzer(NS) and Melamine based superplasticizer(MS). Air content of concrete using LPC is larger than that using OPC. The effects of superplasticizer type on the air content is larger in order of MS, PS and NS. The use of LPC exhibited lower strength development at early age than OPC, whereas after 91days, similar level of compressive strength is achieved regardless of cement type. Compressive strength of concrete is not affected by SP type. For the effect of mixture proportion and materials on drying and autogenous shrinkage, an increase in W/B results in reduction of drying shrinkage and an decrease in water content leads to reduce drying shrinkage. Autogenous shrinkage is not observed until 49 days with the concrete mixture with $35\%$ of W/B and $145 kg/m^3$ of water content. This is due to the combination effects of expansion admixture and shrinkage reducing admixture, which causes an offset of autogenous shrinkage. The use of LPC results in a reduction in autogenous shrinkage compared with OPC. SP type has little influence on the autogenous shrinkage. It is found from the results that mixture proportioning of high performance concrete incorporating fly ash, silica fume, expansion admixture and shrinkage reducing admixture is need to focus on the increase in W/B and the reduction in water content and the use of LPC and MS is also required to use to secure the stability against shrinkage properties.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.6
• /
• pp.114-122
• /
• 2014

Currently, global warming has become a serious problem arising from the usage of fossil fuels such as coal and petroleum. Moreover, due to the global warming, heat wave, heavy snow, heavy rain, super typhoon are frequently occurring all over the world. Due to these serious natural disasters, concrete structures and infrastructures are seriously damaged or collapsed. In order to handle these problems, climate change oriented construction technology and codes are necessary at this time. Therefore, in this study, the validity of the present concrete mixture proportions are evaluated considering temperature and humidity change. The specimens cured at various temperature and humidity conditions were tested to obtain their compressive and split tensile strengths at various curing ages. Moreover, performance based evaluation (PBE) method was used to analyze the satisfaction percentage of the concrete cured at various condition. From the probabilistic method of performance evaluation of concrete performance, feasibility and usability can be determined for future concrete mix design.

• Journal of the Korea Institute of Building Construction
• /
• v.21 no.3
• /
• pp.195-202
• /
• 2021

Concrete quality is mainly managed through the reliable prediction and control of compressive strength. Although related industries have established a relevant datasets based on the mixture proportions and compressive strength gain, whereas they have not been shared due to various reasons including technology leakage. Consequently, the costs and efforts for quality control have been wasted excessively. This study aimed to develop a web-based numerical model, which would present diverse optimal values including concrete strength prediction to the user, and to establish a sustainable database (DB) collection system by inducing the data entered by the user to be collected for the DB. The system handles the overall technology related to the concrete. Particularly, it predicts compressive strength at a mean accuracy of 89.2% by applying the artificial neural network method, modeled based on extensive DBs.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.16 no.6
• /
• pp.163-170
• /
• 2012

With the advantage of a rapid exothermic reaction property, jet set concrete may be used as a cold weather concrete because it can reach the required strength before being damaged by cold weathers. And it can be hardened more quickly if the field temperature is properly compensated by heating. Because ordinary concrete cannot be hardened well under sub-zero temperatures, anti-freeze agents are typically added to prevent the frost damage and to ensure the proper hardening of concrete. While the addition of a large amount of anti-freeze agent is effective to prevent concrete from freezing and accelerates cement hydration resulting in shortening the setting time and enhancing the initial strength, it induces problems in long-term strength growth. Also, it is not economically feasible because most anti-freeze agents are mainly composed of chlorides. Recent studies reported that magnesia-phosphate composites can be hardened very quickly and hydrated even in low temperatures, which can be used as an alternative of cold weather concrete for cold weathers and very cold places. As a preliminary study, to obtain the material properties, mortar specimens with different mixture proportions of magnesia-phosphate composites were manufactured and series of experiments were conducted varying the curing temperature. From the experimental results, an appropriate mixture design for cold weathers and very cold places is suggested.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.29 no.1A
• /
• pp.101-108
• /
• 2009

The performance of high-early strength pavement concrete for large areas is influenced by the physical and chemical environment during service life. Generally, penetration, diffusion, and absorption of harmful materials that exist outside the concrete cause damage to its structure. Thus, we have to use a mixture for durability to keep the required quality for the planned service life. Moreover, in using high-early-strength cement and accelerators, a high heat of hydration to create the initial strength can cause cracks. Based on evaluations from optimal mix proportions of high-early-strength pavement concrete for large areas, we conducted water permeability, abrasion resistance, freeze-thaw, plastic, drying, and autogenous shrinkage tests. Test result showed that a mix of accelerator and PVA fibers showed excellent performance.

• Steel and Composite Structures
• /
• v.51 no.3
• /
• pp.271-288
• /
• 2024

The primary objective of this study is to investigate the production and performance characteristics of structural concrete incorporating varying proportions (0%, 25%, and 50% by volume) of pumice stone, as well as aluminum lathe as an additive at 0%, 1%, 2%, and 3%, under fire conditions. The experiment will be conducted over a period of up to 1 hour, at temperatures ranging from 24℃, 200℃, 400℃ and 600℃. For the purpose of this, a total of twelve test samples were manufactured, and then tests of compressive strength (CS), splitting tensile strength (STS), and flexural strength (FS) were performed on these samples.Next, a comparison was made between the obtained values and the influence of temperature. To achieve this objective, the manufactured samples were placed at temperatures of 200℃, 400℃, and 600℃ for a duration of 1 hour, and were subjected to the influence of temperature.These values at 24 ℃ were then contrasted with the CS results obtained from test samples that were subjected to the temperature effect for an hour at 200 ℃, 400 ℃, and 600 ℃. A comprehensive analysis of the test outcomes reveals that the incorporation of aluminum lathe wastes into a mixture results in a significant reduction in the compressive strength of the concrete. As a result of this adjustment, the CS values dropped by 32.93%, 45.70%, and 52.07%, respectively. Furthermore, It was shown that testing the ratios of pumice stone alone resulted in a decrease in CS outcomes. Additionally, it was found that the presence of higher temperatures is clearly the primary factor contributing to the decrease in the strength of concrete. Due to elevated temperatures, the CS values decreased by 19.88%, 28.27%, and 38.61% respectively.After this investigation, an equation that explains the connection between CS and STS was provided through the utilization of the data of the experiments that were carried out.

• Journal of the Korea Concrete Institute
• /
• v.26 no.2
• /
• pp.201-210
• /
• 2014

The present study proposes a phased model to assess the lifecycle $CO_2$ amount of concrete structures. The considered system boundary is from cradle to recycling, which includes constituent material, transportation, batching and mixing in ready-mixed concrete plant, use and demolition of structure, and crushing and recycling of demolished concrete. The $CO_2$ uptake of concrete by carbonation during lifetime (40 years) of a structure and the recycling life (20 years) after demolition is estimated using a simple approach generalized to predict the carbonation depth from the surfaces of concrete element and recycled aggregates. Based on the proposed phased model, a performance evaluation table is realized to straightforwardly examine the lifecycle $CO_2$ amount of concrete structures. The proposed model demonstrates that the contribution of ordinary portland cement (OPC) to lifecycle $CO_2$ emission of the concrete structure occupies approximately 85%. Furthermore, the $CO_2$ uptake is estimated to be approximately 15~18% of the lifecycle $CO_2$ emissions of concrete structures, which corresponds to be 19~22% of the emissions from OPC production. Overall, the proposed $CO_2$ performance table is expected to be practically useful as a guideline to determine the $CO_2$ emission or uptake at each phase of concrete structures.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.28 no.3
• /
• pp.37-46
• /
• 2024

This study investigates the evolution of concrete damage due to chloride-induced steel corrosion through Impact-echo (IE) testing. Three reinforced concrete specimens, each measuring 1500 mm in length, 400 mm in width, and 200 mm in thickness, were fabricated using three concrete mixture proportions of blended cement types: ordinary Portland cement, ground granulated blast-furnace slag and fly ash. Steel corrosion in the concrete was accelerated by impressing a 0.5 A current following a 35-day cycle of wet-and-dry saturation in a 3% NaCl solution. Initial IE data collected during the saturation phase showed no significant changes, indicating that moisture had a minimal impact on IE signals and highlighting the slow progress of corrosion under natural conditions. Post-application of current, however, there was a noticeable decline in both IE peak frequency and the P-wave velocity in the concrete as the duration of the impressed current increased. Remarkably, progressive monitoring of IE proves highly effective in capturing the critical features of steel-corrosion induced concrete deterioration, such as the onset of internal damages and the rate of damage propagation. These results demonstrate the potential of progressive IE data monitoring to enhance the reliability of diagnosing and prognosticating the evolution of concrete damage in marine environment.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.3
• /
• pp.452-459
• /
• 2017

In recent years, to reduce self-weight of structural elements, the use of SCP (Steel Concrete Plate) instead of prestressed concrete is increasing. Because SCP has a complicated sectional shape and includes a large number of studs, the use of high-fluidity concrete is required. Therefore, in this study, to prevent the restrained shrinkage behavior by the stud, the effects of using an expansive agent (EA) and shrinkage reducing agent (SRA) were investigated, and the optimal mixture proportions to maximize the filling capacity were determined based on the fine aggregate ratio. The test results indicated that the combined use of EA and SRA exhibited the smallest shrinkage. The ratio of the crushed sand and washed sea sand was determined to be 5:5, and the proper fine aggregate ratio was found to be 55.6%, because when the ratio was too high, a decrease in strength and an increase in shrinkage strain were expected. The high-fluidity concrete effectively filled the large-sized SCP module.

• Journal of the Korea Concrete Institute
• /
• v.26 no.6
• /
• pp.751-759
• /
• 2014

Currently, due to global warming, occurrences of extreme climate phenomena such as heat wave, heavy snow, heavy rain, super typhoon are continuously increasing all over the world. Due to these extreme climate phenomena, concrete structures and infrastructures are exposed to serious deterioration and damage. However, researches on construction technologies and standards to confront the climate change generated problems are needed presently. In order to better handle these problems, the validity of the present concrete mixture proportions are evaluated considering wind speed and sunlight exposure time based on climate change record in Seoul, Korea. The specimens cured at various wind speed and sunlight exposure time conditions were tested to obtain their compressive and split tensile strengths at various curing ages. Moreover, performance based evaluation (PBE) method was used to analyze the target strength satisfaction percentage of the concrete cured for the curing conditions. From the probabilistic method of performance evaluation of concrete performance, feasibility and usability of current concrete mix design practice for climate change conditions can be evaluated.