• Journal of the Korea Concrete Institute
• /
• v.24 no.2
• /
• pp.111-120
• /
• 2012

This paper is a report about lap splice performance of rebar embedded in the strain-hardening cement-based composites (SHCCs) under monotonic and repeated tension loading. Ten mix proportions of cement-based composites such as SHCCs and normal concrete were investigated. The study parameters are comprised of (1) types of reinforcing fibers (polyethylene and steel fiber), (2) replacement levels of expansive admixture (EXA, 0% and 10%), and (3) compressive strength (30 and 100 MPa) of cement-based composites. Lap splice lengths (ld) of rebars in SHCC materials and normal concrete were 60% and 100% of splice length calculated by code requirements for structural concrete, respectively. Test results indicated that SHCCs materials can lead to enhancements in the lap splice performance of embedded rebar. All of the fiber reinforcement conditions (PE-SHCC and PESF-SHCC) considered in this study produced considerable improvements in the tensile strength, cracking behavior, and bond strength of lap-spliced rebar. Furthermore, adding EXA to SHCC matrix improved the tensile lap splice performance of rebar in SHCC materials. However, for controlling crack behavior, the performance of PE-SHCC was better than that of PESF-SHCC due to its mechanical properties. This study demonstrated an effective approach for reducing required development length of lap spliced rebar by using SHCC materials.

• Journal of the Korea Concrete Institute
• /
• v.23 no.1
• /
• pp.49-55
• /
• 2011

The distresses of alkali-silica reaction (ASR) was recently reported at highway cement concrete pavement in Korea, which showed typical cracking and spalling patterns of ARS. Korea is was no longer safe zone against ASR, needding to find a control methodology against ASR. The purpose of this research was to provide a control methodology against ASR using mineral admixtures through a series of laboratory test program. Laboratory works included the accelerated mortar bar test (AMBT) by ASTM C 1260 regulation with five types of aggregate and three types of mineral admixtures (fly ash, ground granulated blast-furnace slag and silica fume). The result of ASTM C 1260 test for five types of aggregates without mineral admixtures showed that Siltstone and Mudstone were found to be "reactive." Tuff and Andesite-1 were found to be "possiblely reactive." In case of concrete mixed with 10, 20, and 30% fly ash, all specimens except Mudstone mixed with 10% FA were found to be "non-reactive". In cases of concrete mixed with 30, 40, and 50% ground granulated blast-furnace slag and 5, 7.5, and 10% silica fume, all specimens were found to be "non-reactive." These results could be selectively applied in constructions in Korea.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.12
• /
• pp.694-701
• /
• 2018

Larger crack widths can be observed more in FRP-reinforced concrete members than in steel-reinforced concrete members as a result of the lower elastic modulus and bond strength of FRP reinforcement. The ACI 440.1R-15 design guide provides equations derived as the maximum bar spacing to control the crack widths indirectly. On the other hand, it is not concerned with long-term effects on the crack control design provisions. This study provides suggestions for how to incorporate time-dependent effects into the crack width equation. The work presented herein includes the results from 8 beams composed of four rectangular and T-shaped FRP-reinforced concrete beams tested for one year under four-point bending. Over a one year period, the crack widths increased as much as 2.6~3.0 times in GFRP and AFRP-reinforced specimens and 1.1~1.4 times in the CFRP-reinforced specimens compared to steel-reinforced specimens. In addition, the average multiple for crack width at one year relative to the instantaneous crack width upon the application of the sustained load was 2.4 in the specimens with a rectangular section and 3.1 in the specimens with a T-shaped section. As a result, it is recommended conservatively that the time-dependent coefficient be taken as 2.5 for the rectangular beams and 3.5 for T-beams.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.29 no.4A
• /
• pp.281-290
• /
• 2009

In this study, an analysis technique of hybrid girder considering nonlinearity of steel-concrete contact surface is presented. Steel-concrete hybrid girder shows partial-interaction behavior due to the deformation of shear connectors, slip and detachment at the interface, and cracks under the applied loads. Therefore, the partial-interaction approach becomes more reasonable. Contact surface is modeled by interface element and analyzed nonlinearly because of cost of time and effort to detailed model and analysis. Steel and Concrete are modeled considering non-linearity of materials. Material property of contact surface is obtained from push-out test and input to interface element. For the constitutive models, Drucker-Prager and smeared cracking model are used for concrete in compression and tension, respectively, and a von-Mises model is used for steel. This analysis technique is verified by comparing it with test results. Using verified analysis technique, various analyses are performed with different parameters such as nonlinear material property of interface element and prestress. The results are compared with linear analysis result and analysis result with the assumption of full-interaction.

• Journal of the Korea Concrete Institute
• /
• v.18 no.3 s.93
• /
• pp.331-338
• /
• 2006

This paper presents the experimental results on volumetric changes in ordinary portland cement concrete made with various water-to-cement ratios(W/C's) ranging from 0.32 to 0.50 and cured in low different conditions. Curing regimes employed in this work were designed to exhibit autogenous and drying shrinkage as well as swelling of concrete. The concrete avoided any moist evaporation(Regime f showed only autogenous shrinkage and the lower the W/C, the feater the autogenous shrinkage. The concrete exposed to air drying conditions at $20{\pm}1^{\circ}C$ and $60{\pm}3%$ RH after 6-day water curing at $20{\pm}1^{\circ}C$(Regime II) swelled and then started to shrink. The maximum swelling value of concrete developed in water curing was between 15 and $40{\pm}10^{-6}$, and the greatest total shrinkage(autogenous+drying shrinkage) was obtained for the mixture made with W/C of 0.32. The concrete let to air drying conditions(Regime III) showed greater total shrinkage compared to the concrete cured in Regime II. The concrete exposed to air drying condition after 6-day sealed curing(Regime IV) exhibited slightly smaller total shrinkage than that of the concrete cured in Regime III. Net drying shrinkage that can be derived from the results of Regime I, III, and IV increased as the W/C increased despite of similar total shrinkage. This result indicated that drying shrinkage governs total shrinkage of high-W/C concretes. In other words, a portion of autogenous shrinkage in total shrinkage increased in low-W/C concretes. Therefore, it should be controlled in terms of cracking potential. Finally, total shrinkage of high-strength and high-performance concrete made with low W/C can be effectively reduced by appropriate early moisture curing.

• Structural Engineering and Mechanics
• /
• v.73 no.6
• /
• pp.613-620
• /
• 2020

The research study is focuses on a form of all-bolted joint with the external ring stiffening plate in the prefabricated steel structure. The components are bolted at site after being fabricated in the factory. Six specimens were tested under cyclic loading, and the effects of column axial compression ratio, concrete-filled column, beam flange sub plate, beam web angle cleats, and spliced column on the failure mode, hysteretic behavior and ductility of the joints were analyzed. The results shown that the proposed all-bolted joint with external ring stiffening plate performed high bearing capability, stable inflexibility degradation, high ductility and plump hysteretic curve. The primary failure modes were bucking at beam end, cracking at the variable section of the external ring stiffening plate, and finally welds fracturing between external ring stiffening plate and column wall. The bearing capability of the joints reduced with the axial compression ratio increased. The use of concrete-filled steel tube column can increase the bearing capability of joints. The existence of the beam flange sub plate, and beam web angle cleat improves the energy dissipation, ductility, bearing capacity and original rigidity of the joint, but also increase the stress concentration at the variable section of the external reinforcing ring plate. The proposed joints with spliced column also performed desirable integrity, large bearing capacity, initial stiffness and energy dissipation capacity for engineering application by reasonable design.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.20 no.6
• /
• pp.46-55
• /
• 2016

Three small scale hollow circular reinforced concrete columns(4.5 aspect ratio) were tested under cyclic lateral load with constant axial load. Diameter of section is 400 mm, hollow diameter is 200 mm. The selected test variable are transverse steel ratio. Volumetric ratio of spirals of all the columns is 0.302~0.604% in the plastic hinge region. It corresponds to 45.9~91.8% of the minimum requirement of confining steel by Korean Bridge Design Specifications, which represent existing columns not designed by the current seismic design specifications or designed by seismic concept. The final objectives of this study are to provide quantitative reference data and tendency for performance or damage assessment based on the performance levels such as cracking, yielding, steel fracture, etc. In this paper, describes mainly failure behavior, strength degradation behaviour, displacement ductility of circular reinforced concrete bridge columns with respect to test variables.

• International Journal of Highway Engineering
• /
• v.11 no.2
• /
• pp.37-44
• /
• 2009

Currently the reasonability of threshold values for rutting and cracking does not clearly defined at the Pavement Rehabilitation Decision Tree on national highway PMS(Pavement Management System). The goal of this study is to provide the reasonable threshold values for the national highway asphalt concrete pavement rehabilitation. To achieve this goal, test section that represents typical asphalt concrete pavement of national highway was selected and pavement export were participated. Pavement condition survey has been conducted and pavement performance data at the selected roadway section were analyzed. From this study, reasonable threshold values of Pavement Rehabilitation Decision Tree were suggested based on the pavement expert's engineering judgement. In terms of crack repairs, the application of overlay after cutting is required to deteriorated area where existing crack ratio is over 35% and just overlay is required to where crack ratio is over 20%. On rutting, rut depth over 13mm is required to overlay after cutting and rut depth over 10mm is just needed to overlay.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.3
• /
• pp.279-288
• /
• 2016

The fundamental performance of any construction material should cover at least two phases: safety and serviceability. Safety commonly represents adequate strength, while serviceability encompasses the control of cracking and deflections at service loads. With respect to rapid hydraulic binders as a construction material, the above two phases should also be considered. Recent research on rapid cooling ladle furnace slag (RC-LFS) has drawn much attention, particularly given that it shows remarkable rapid hydraulic ability to pulverize to a fineness of $6,300cm^2/g$. This industrial byproduct could contribute to developing the sustainability of the rapidly hardening cementitious material system. This paper aims to expand upon the applicability of an RC-LFS-based binder that is composed of two parts. It also seeks to illustrate the engineering performance of an RC-LFS-based hybrid fiber-reinforced composite and to increase the strength of the RC-LFS-based composite. Each step of this experiment followed ASTM standards. The engineering performance, in both fresh state and hardening state, was tested and discussed in this paper. According to the experimental results for fresh concrete, the air content increased following the addition of polypropylene fiber. For hardened concrete, the toughness and strength improved following the addition of a hybrid fiber. The hybrid fiber mixture, which contains 0.75% of steel fiber and 0.25% of polypropylene fiber, shows even better engineering performance than other mixtures.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.2 no.3 s.6
• /
• pp.101-108
• /
• 2002

There exist many construction joints in segmentally constructed bridge girders. It is required coupling of tendons or overlapping of tendons to introduce continuous prestress through several spans of bridges. Even though tendon coupling method is easier to use in practice, some cracking problems around construction joints have been reported and complicated stress states around construction joints in PSC girders is not clearly investigated. The purpose of this paper is to investigate in detail the complicated longitudinal stress distributions around the construction joints in prestressed concrete girders with tendon couplers. To this end, a comprehensive experimental program has been set up and a series of specimens have been tested to identify the effects of tendon coupling and segmental construction of bridge sections. The present study indicates that the longitudinal stress distributions of PSC girders with tendon couplers are quite different from those of PSC girders without tendon couplers. The longitudinal compressive stresses introduced by prestressing are greatly reduced around coupled joints according to tendon coupling ratios.