• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.629-634
• /
• 2001

Recently, to consider financial and constructive aspect, usage of Admixture, like Blast-Furnace Slag and Fly-Ash, are increased. Also the use of cold-weather-concrete is increased. Blast-furnace Slag, a by-product of steel industry, have many advantage, to reduce the heat of hydration, increase in ultimate strength and etc. But it also reduces early-age strength, so it is prevented from using of Blast-Furnace Slag at cold-weather-concrete. In this study, for the purpose of increasing usage of Blast-Furnace Slag at cold-weather-concrete, it is investigated the strength properties of concrete subjected to frost damage for the cause of early age curing. According to this study, if early curing is carried out before having frost damage, the strength of concrete, subjected to frost damage, is recovered. And that properties is not connected with the frost cause.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.04a
• /
• pp.361-366
• /
• 1999

The purpose of this study is to evaluate the structural performance of Reinforced steel fiber concrete structures using early age concrete. Reinforced concrete structures using early age concrete are result in the degradation of structural performance due to crack, overload, unexpected vibration and impact load. Specimens, designed by the over 0.75% of steel fiber incorporated, were showed the ductile behavior and failed slowly with flexure and flexure-shear. Increasing the percent of steel fiber incorporated(0.25~2.0%), the ultimate shear stress of each specimen were increased 12~40% than that of specimen SSS.

• Journal of Environmental Science International
• /
• v.19 no.1
• /
• pp.105-114
• /
• 2010

The objective of the paper is to experimentally investigate the compressive strength of the concrete incorporating fly ash. Ordinary Portland cement(OPC). Water to binder ratio(W/B) ranging from 30% to 60% and curing temperature ranging from $-10^{\circ}{\sim}65^{\circ}C$ were also adopted for experimental parameters. Fly ash was replaced by 30% of cement contents. According to the results, strength development of concrete contained with fly ash is lower than that of plain concrete in low temperature at early age and maturity. In high curing temperature, the concrete with fly ash has higher strength development than that of low temperature regardless of the elapse of age and maturity. Fly ash can have much effect on the strength development of concrete at the condition of mass concrete, hot weather concreting and the concrete products for the steam curing.

• The Research Journal of the Costume Culture
• /
• v.8 no.5
• /
• pp.754-770
• /
• 2000

The definite objects of this study are as follows ; 1. The study presents concrete objects of the shape of adult women's neck and shoulder after comparing and analyzing the features of five age groups ; the former young age, the latter young age, the former middle age, the latter middle age, the latter middle age and the old age. 2. The study presents concrete objects of adult women's neck and shoulder by the body types ; bend-forward type, straight type and lean-back type in order to be examined the body types. The results of this study are as follows ; 1. The shape of neck and shoulder needs the several concrete objects of each types because of the variable factors in size and body types. But the concrete objects of the types referred in five age groups contain all the important factors and enable to design the body suitable clothes. 2. This study shows that generally bend-forward type contains rising shoulder and lean-back type contains drooping shoulder, and straight type contains average value of neck and shoulder. The results of this study developed the body-suitable clothes of bend-forward type, straight type and lean-back type.

• Nuclear Engineering and Technology
• /
• v.45 no.3
• /
• pp.393-400
• /
• 2013

Concrete undergoing early frost damage in cold weather will experience significant loss of not only strength, but also of permeability and durability. Accordingly, concrete codes like ACI-306R prescribe a minimum compressive strength and duration of curing to prevent frost damage at an early age and secure the quality of concrete. Such minimum compressive strength and duration of curing are mostly defined based on the strength development of concrete. However, concrete subjected to frost damage at early age may not show a consistent relationship between its strength and durability. Especially, since durability of concrete is of utmost importance in nuclear power plant structures, this relationship should be imperatively clarified. Therefore, this study verifies the feasibility of the minimum compressive strength specified in the codes like ACI-306R by evaluating the strength development and the durability preventing the frost damage of early age concrete for nuclear power plant. The results indicate that the value of 5 MPa specified by the concrete standards like ACI-306R as the minimum compressive strength to prevent the early frost damage is reasonable in terms of the strength development, but seems to be inappropriate in the viewpoint of the resistance to chloride ion penetration and freeze-thaw. Consequently, it is recommended to propose a minimum compressive strength preventing early frost damage in terms of not only the strength development, but also in terms of the durability to secure the quality of concrete for nuclear power plants in cold climates.

• Korean Journal of Agricultural Science
• /
• v.18 no.2
• /
• pp.140-147
• /
• 1991

This paper was performed to obtain the data applied to use of synthetic lightweight aggregate concrete affected by alkali silica reaction. The results obtained were summarized as follows : 1. The expansion of each type concrete was increased with increase of curing age, respectively. Also, at the curing age 90 days, the rate of expansion of type A, B, C and D concrete was increased 0.173%, 0.575%, 0.230% and 0.680%, respectively. Specially, the rate of expansion of type D concrete was shown 3.93 times higher than the type A concrete. The cracks width were increased with increase of expansion and at the 0.680% expansion, the maximum width was shown 0.5 mm. 2. The dynamic modulus of elasticity of each type concrete was increased with increase of curing age, respectively. At the curing age 30 days, the highest dynamic modulus of elasticity was showed at each type concrete, respectively. But, it was gradually decreased with increase of curing age at those concrete, respectively. Also, at the curing age A, B, C and D concrete was increased 24.3%, 33.7%, 28.1% and 37.0%, respectively. The rate of loss in type D concrete was shown 1.52 times higher than the type A concrete. 3. The ultrasonic pulse velocity of each type concrete was increased with increase of curing age, respectively. At the curing age 30 days, the highest ultrasonic pulse velocity was showed at each type concrete, respectively. But, it was gradually decreased with increase of curing age at those concrete, respectively. Also, at the curing age 90 days, the percentage loss of ultrasonic pulse velocity of type A, B, C and D concrete was increased 6.4%, 8.7%, 8.5% and 14.2%, respectively. The rate of loss in type D concrete was shown 2.21 times higher than the type A concrete. 4. The relation between dynamic modulus of elasticity and ultrasonic pulse velocity was highly significant. The dynamic modulus of elasticity was increased with increase and decreased with decrease of ultrasonic pulse velocity. Also, the decreasing rate of the dynamic modulus of elasticity was shown 2-7 times higher than the ultrasonic pulse velocity at each age, respectively. 5. The dynamic modulus of elasticity and ultrasonic pulse velocity were decreased with increase of expansion, and the decreasing rates were increased with increase of curing age. The increasing rate of expansion was shown higher than the decreasing rate of dynamic modulus and ultrasonic pulse velocity.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.24 no.4
• /
• pp.391-398
• /
• 2011

After a concrete is poured, reinforced concrete structures were distressed by physical and chemical factor over time. It is in need to define important variables related to structural behavior for effectively conducting seismic analysis of structures with age-related degradation. In this study, a sensibility analysis using the first-order second moment method was performed to analyze an important variables for the reinforced concrete shear wall with age-related degradation. Because the seismic capacity of aging structures without a concrete hardening effect can be underestimated, the sensibility of analysis variables was analyzed according to the concrete hardening. Important variables for RC shear wall with age-related degradation was presented by using the tornado diagram.

• Magazine of the Korea Concrete Institute
• /
• v.7 no.5
• /
• pp.164-171
• /
• 1995

Drying shrinkage and hydration heat are important factors on the initiation of the crack in con crete at early age. Therefore, the stress caused by hydration heat and drying shrinkage should be .analyzed to predict whether the crack occurrs or not. And, mechanical properties of early age concrete is also required for the predicting crack formation In this study, non-destructive test method of resonance frequency was used to find the relation between dynamic modulus and mechanical properties of concrete in early age. Test results were compared with existing equations, and a new equation based on test. results in this study and other data was also proposed

• Structural Engineering and Mechanics
• /
• v.67 no.2
• /
• pp.155-163
• /
• 2018

The Early-age construction loading and changing properties of concrete, especially in the multi-story structures can affect the slab deflection, significantly. Based on previously conducted experiment on eight simply-supported one-way slabs this paper investigates the effect of concrete type, fiber type and content, loading value, cracking moment, ultimate moment and applied moment on the instantaneous deflection of Self-Compacting Concrete (SCC) slabs. Two distinct loading levels equal to 30% and 40% of the ultimate capacity of the slab section were applied on the slabs at the age of 14 days. A wide range of the existing models of the effective moment of inertia which are mainly developed for conventional concrete elements, were investigated. Comparison of the experimental deflection values with predictions of the existing models shows considerable differences between the recorded and estimated instantaneous deflection of SCC slabs. Calculated elastic deflection of slabs at the ages of 14 and 28 days were also compared with the experimental deflection of slabs. Based on sensitivity analysis of the effective parameters, a new model is proposed and verified to predict the effective moment of inertia in SCC slabs with and without fiber reinforcing under two different loading levels at the age of 14 days.

• Structural Engineering and Mechanics
• /
• v.37 no.5
• /
• pp.459-473
• /
• 2011

The study of the early age concrete properties is becoming more important, as the thermal effects and the shrinkage, even in the first hours, could generate cracks, increasing the permeability of the structure and being able to induce problems of durability and functionality in the same ones. The detailed study of the stresses development during the construction process can be decisive to keep low the cracking levels. In this work a computational model, based on the finite element method, was implemented to simulate the early age concrete behavior and, specially, the evaluation of the cracking risk. The finite element analysis encloses the computational modeling of the following phenomena: chemical, thermal, moisture diffusion and mechanical which occur at the first days after the concrete cast. The developed software results were compared with experimental values found in the literature, demonstrating an excellent approach for all the implemented analysis.