Unpredictable failures can occur due to the DHC (delayed hydride cracking) or the degradation of fracture toughness by hydride embrittlement in CANDU pressure tube which can result from the absorption of hydrogen or deuterium in the high temperature coolant. To investigate the hydride embrittlement of CANDU Zr-2.5Nb pressure tube, the transverse tensile test and the fracture toughness test were performed from room temperature to $300^{\circ}C$ using three different specimens which have an AR (As Received), 100, and 200 ppm hydrogen. As the amount of absorbed hydrogen was increased, the transverse yield strength and the ultimate tensile strength were also increased. In addition, as the test temperature became higher they were decreased linearly. While, at room temperature, the hydrogenbsorbed specimens represented the embrittlement which resulted in sudden decreasing of fracture toughness, the fracture characteristics became ductile such as AR specimen at high temperatures. Through the observation of fracture surface using SEM, it was found that the stress state of mixed mode could be related to the fissure which was believed to decrease the global fracture toughness.

• Structural Engineering and Mechanics
• /
• 제59권5호
• /
• pp.867-883
• /
• 2016

In this paper, the effects of steel-fiber and rebar reinforcements on the ultimate bearing strength of the local anchorage zone were investigated based on experiments and comparisons between test results and design-equation predictions (AASHTO 2012, NCHRP 1994). Eighteen specimens were fabricated using the same anchorage device, which is one of the conventional anchorage devices, and two transverse ribs were used to secure an additional bearing area for a compact anchorage-zone design. Eight of the specimens were reinforced with only steel fiber and are of two concrete strengths, while six were reinforced with only rebars for two concrete strengths. The other four specimens were reinforced with both rebars and steel fiber for one concrete strength. The test and the comparisons between the design-equation predictions and the test results showed that the ultimate bearing strength and the section efficiency are highly affected by the reinforcement details and the concrete strength; moreover, the NCHRP equation can be conservatively applied to various local anchorage zones for the prediction of the ultimate bearing strength, whereby conditions such as the consideration of the rib area and the calibration factor are changed.

• 대한기계학회논문집
• /
• 제9권2호
• /
• pp.135-139
• /
• 1985

본 논문에서는 이러한 점을 감안하여 SCM4(KS규격)재에 대해서 Unloading Co- mpliance법 및 초음파법에 의한 크랙개시점검출을 시도한 결과로부터 파괴인성시험에 있어서 초음파법의 유요성을 밝히고저 한다.

• Nuclear Engineering and Technology
• /
• 제47권4호
• /
• pp.454-460
• /
• 2015

Acoustic emission (AE) is one of the promising methods for detecting the formation of stress corrosion cracks (SCCs) in laboratory tests. This method has the advantage of online inspection. Some studies have been conducted to investigate the characteristics of AE parameters during SCC propagation. However, it is difficult to classify the distinct features of SCC behavior. Because the previous studies were performed on slow strain rate test or compact tension specimens, it is difficult to make certain correlations between AE signals and actual SCC behavior in real tube-type specimens. In this study, the specimen was a AISI 304 stainless steel tube widely applied in the nuclear industry, and an accelerated test was conducted at high temperature and pressure with a corrosive environmental condition. The study result indicated that intense AE signals were mainly detected in the elastic deformation region, and a good correlation was observed between AE activity and crack growth. By contrast, the behavior of accumulated counts was divided into four regions. According to the waveform analysis, a specific waveform pattern was observed during SCC development. It is suggested that AE can be used to detect and monitor SCC initiation and propagation in actual tubes.

• 열처리공학회지
• /
• 제14권4호
• /
• pp.212-219
• /
• 2001

The fatigue test was carried out to evaluate the fatigue characteristics of fire resistance steel for frame structure and heat affected zone (HAZ) by the one side Gas Metal Arc Welding (GMAW). In this paper, the fatigue crack growth behavior was investigated with the compact tension specimen of base metal and the HAZ according to chemical composition and rolling end temperature, respectively. And the acoustic emission signals obtained from the fatigue test were analyzed by the time-frequency analysis method as a nondestructive evaluation. Main results obtained are summarized as follows; The hardness was appeared softening phenomenon that weld metal and HAZ are lower than that of base metal. Fatigue life of welded specimen was longer than that of base metal. m was 3~4.5 in base metal and 3.8~5.8 in HAZ. The main frequency range of acoustic emission signal analyzed from time-frequency method is different with the range by noise and crack. Also, it could be classified that it was also generated by fracture mechanics of dimple, inclusion etc.

• Nuclear Engineering and Technology
• /
• 제35권3호
• /
• pp.206-213
• /
• 2003

This study focuses on an understanding of the environmental effect on delayed hydride cracking velocity (DHCV) of CANDU Zr-2.5Nb tubes. To simulate DHC susceptibility of the Zr-2.5Nb tubes in reactor operating conditions, DHC tests were successfully carried out in pressurized water at 180 and $250^{\circ}C$ using a self-designed autoclave for the first time. Using 17 mm compact tension specimens electorlytically charged to 34 and 60 ppm H, 3 to 7 DHCV data were determined in water at both temperatures and compared to those determined in air that were already confirmed to be valid through a round robin test on DHCV of Zr-2.5Nb tubes sponsored by a IAEA coordinated research program. The pressurized water environment has little effect on DHCV of Zr-2.5Nb tube in water at both temperatures even though DHCV is slightly lower in water than that in air. The lower DHCV of the Zr-2.5Nb tube during short-term tests is discussed in viewpoint of the cooling rate from the peak temperature to the test temperature.

• 한국강구조학회 논문집
• /
• 제16권6호통권73호
• /
• pp.781-792
• /
• 2004

스티프너가 없는 얇은 강판을 사용한 골조강판벽 시스템에 대한 실험연구를 실시하였다. 1경간 3층의 골조강판벽에 주기횡하중을 재하하였으며, 주요한 실험 변수는 강판의 두께, 기둥의 강도이다. 실험결과를 이용하여 강판벽의 강도, 변형능력, 에너지 소산능력을 연구하였으며, 이를 토대로 골조강판벽의 파괴메카니즘을 분석하였다. 실험결과, 얇은 강판을 사용하는 골조강판벽은, 높은 강도, 낮은 연성능력, 캔틸레버거동특성을 나타내는 일반적인 가새골조나 스티프너 보강된 강판벽과는 여러 면에서 다른 거동특성을 나타낸다. 골조강판벽에서는 강판의 조기국부좌굴과 인장응력장 작용이 발생하면서, 전 층에 고르게 항복변형이 분포된다. 이로 인하여 변형형태는 휨변형과 전단변형의 복합형태를 나타내며, 우수한 강도 및 에너지 소산능력과 연성모멘트 골조에 버금가는 변형능력을 나타내었다. 그러나 일반적인 가새골조와는 달리 보, 기둥 등의 골조부재는 강판의 인장응력장을 지지할 수 있도록 설계되어야 하며, 따라서 기둥의 강도가 작고 콤팩트 단면을 사용하지 않은 경우에는 약층현상이 발생하며 강도가 급격히 저하되었다. 얇은 강판을 사용하는 골조강판벽은 일반적인 가새골조나 스티프너 보강 강판벽과는 차별되는 우수한 변형능력을 갖고 있으므로 연성내진구조시스템으로 활용할 수 있다.

• 한국안전학회지
• /
• 제9권1호
• /
• pp.9-18
• /
• 1994

In this study, we conducted experimental tests to evaluate fracture behaviors of fresh-butt welded metal by Acoustic Emission technique. We selected similar welding and dissimilar welding process, the one welded for SM45C, SS41 and SUS304 of each material, the other for SM45C and SS41, SM45C and SUS304 and SS41 and SUS304. The fracturing processes of weld metal were estimatied through the fracture toughness test with compact tension specimens and fractography analysis. In ASTM test method E-399, type I curves for materials of this study were obtained by load-cod diagram of fracture toughness test. and 5% offset load( $P_{5}$) was estimated as the estimated crack initial load( $P_{Q}$), The estimated crack initial load( $P_{Q}$) of similar welding materials generally lower than base matal, and then SM45C appeared greatly in decreasing rate of PB, SS41 and SUS304 appeared in order. $P_{Q}$ of dissimilar welding materials were lower than the similar welding materials. $P_{Q}$ of welding of SM45C and SS41 appeared in small, SUS304 and SS41 appeared greatly in dissimilar welding materials. In fracture toughness test, AE counts increased before the inflection point of the slope, decreased after that. It was found that increasing of AE counts were due to the microcrack formation at the crack tip near the $P_{5}$ point through AE data. For welding materials in this study, both low and high AE amplitude appeared simulataneously. It was confirmed that the low AE amplotude was due to formation of micro void, micro crack or micro dimple, the high AE amplitude was caused by microvoid coalescence and quasi-cleavage fracture through analyses of fractograpy.apy.apy.apy.

• 동력기계공학회지
• /
• 제7권4호
• /
• pp.55-60
• /
• 2003

This paper is to investigate the fatigue crack growth of plasma-sprayed coating steels according to heat treatments. The experimental materials are carbon steels(substrate: S45C) with plasma-sprayed coating layers of Ni-4.5%Al and $TiO_2$. The fatigue test is conducted on compact tension specimen by a servo-hydraulic fatigue testing machine. The specimens are heat-treated at $400^{\circ}C\;and\;800^{\circ}C$, respectively. Loading condition is a constant amplitude sinusoidal wave with a frequency of 10Hz and a load ratio of 0.1. The fatigue crack growth length is automatically measured by a compliance method. In the case of non-heat treated specimens, the fatigue crack growth rates of both substrate and coating specimen are almost same. The crack growth rates of substrates and coating steels by heat treatment are larger than those of the non-heat treated one, because the ductile property increase by heat treatment. In ${\Delta}K<18MPa{\cdot}m^{1/2}$, the crack growth rates of the heat-treated specimens are slightly taster than non-heat treated one. But the both heated and non-heated one are almost same in ${\Delta}K>18MPa{\cdot}m^{1/2}$.

• 대한기계학회논문집
• /
• 제14권1호
• /
• pp.79-86
• /
• 1990

본 연구에서는 균열 길이의 별도 측정없이, 하중변위 곡선에서 직접 $J_{IC}$를 결정하는 방법을 제안하고 그 타당성을 조사한다. 또한 키이 곡선(key curve)을 이용하여 $J_{IC}$를 좀더 간단하게 구하는 방법에 대해서도 알아본다. 위의 방법으 로 결정된 $J_{IC}$의 값은 ASTM에 의해 제안된 R-곡선 방법으로 고한 $J_{IC}$의 값 과 비교된다. 본 연구의 타당성을 조사하기 위하여 기계 구조용합금강인 SCM4를 사 용한 파괴 실험을 수행한다.