ACOUSTIC EMISSION CHARACTERISTICS OF STRESS CORROSION CRACKS IN A TYPE 304 STAINLESS STEEL TUBE  

HWANG, WOONGGI (School of Aerospace and Mechanical Engineering, Korea Aerospace University)
BAE, SEUNGGI (School of Aerospace and Mechanical Engineering, Korea Aerospace University)
KIM, JAESEONG (Center for Robot Technology and Manufacturing, Institute for Advanced Engineering)
KANG, SUNGSIK (Department of Nuclear Safety Research)
KWAG, NOGWON (Ultrasonic Division)
LEE, BOYOUNG (School of Aerospace and Mechanical Engineering, Korea Aerospace University)
Publication Information
Nuclear Engineering and Technology / v.47, no.4, 2015 , pp. 454-460 More about this Journal
Abstract
Acoustic emission (AE) is one of the promising methods for detecting the formation of stress corrosion cracks (SCCs) in laboratory tests. This method has the advantage of online inspection. Some studies have been conducted to investigate the characteristics of AE parameters during SCC propagation. However, it is difficult to classify the distinct features of SCC behavior. Because the previous studies were performed on slow strain rate test or compact tension specimens, it is difficult to make certain correlations between AE signals and actual SCC behavior in real tube-type specimens. In this study, the specimen was a AISI 304 stainless steel tube widely applied in the nuclear industry, and an accelerated test was conducted at high temperature and pressure with a corrosive environmental condition. The study result indicated that intense AE signals were mainly detected in the elastic deformation region, and a good correlation was observed between AE activity and crack growth. By contrast, the behavior of accumulated counts was divided into four regions. According to the waveform analysis, a specific waveform pattern was observed during SCC development. It is suggested that AE can be used to detect and monitor SCC initiation and propagation in actual tubes.
Keywords
Acoustic emission; Signal; Stainless steel; Stress corrosion crack; Waveform;
Citations & Related Records
Times Cited By KSCI : 1  (Citation Analysis)
연도 인용수 순위
1 H. Mazille, R. Rothea, C. Tronel, An acoustic emission technique for monitoring pitting corrosion of austenitic stainless steels, Corros. Sci 37 (1995) 1365-1375.   DOI
2 J.K. Lim, D.S. Chung, S.H. Chung, Evaluation of SCC susceptibility of weld HAZ in structural steel (I)-material properties and strain rate, J. Korean Weld. Soc 11 (1993) 48-60.
3 H. Leinonen, T. Schildt, H. Hanninen, Stress corrosion cracking-crevice interaction in austenitic stainless steels characterized by acoustic emission, Metall. Mater. Trans. A 42 (2011) 424-433.
4 H. Chang, E. Han, J.Q. Wang, W. Ke, Acoustic emission study of corrosion fatigue crack propagation mechanism for LY12CZ and 7075-T6 aluminum alloys, J. Mater. Sci 40 (2005) 5669-5674.   DOI
5 J. Kovac, C. Alaux, T. James Marrow, E. Govekar, A. Legat, Correlations of electrochemical noise, acoustic emission and complementary monitoring techniques during intergranular stress-corrosion cracking of austenitic stainless steel, Corros. Sci 52 (2010) 2015-2025.   DOI
6 M.G. Alvarez, P. Lapitz, J. Ruzzante, AE response of type 304 stainless steel during stress corrosion crack propagation, Corros. Sci 50 (2008) 3382-3388.   DOI
7 M. Fregonese, H. Idrissi, H. Mazille, L. Renaud, Y. Cetre, Monitoring pitting corrosion of AISI 316L austenitic stainless steel by acoustic emission technique: choice of representative acoustic parameters, J. Mater. Sci 36 (2001) 557-563.   DOI
8 J. Xu, X. Wu, E.-H. Han, Acoustic emission during pitting corrosion of 304 stainless steel, Corros. Sci 53 (2011) 1537-1546.   DOI
9 G. Du, J. Li, W.K. Wang, C. Jiang, S.Z. Song, Detection and characterization of stress-corrosion cracking on 304 stainless steel by electrochemical noise and acoustic emission techniques, Corros. Sci 53 (2011) 2918-2926.   DOI
10 H. Shaikh, R. Amirthalingam, T. Anita, N. Sivaibharasi, T. Jaykumar, P. Manohar, H.S. Khatak, Evaluation of stress corrosion cracking phenomenon in an AISI type 316LN stainless steel using acoustic emission technique, Corros. Sci 49 (2007) 740-765.   DOI
11 M. Perrin, L. Gaillet, C. Tessier, H. Idrissi, Assessment of stress corrosion cracking in prestressing strands using AE technique, J. Acoust. Emiss 26 (2008) 32-39.
12 Y.K. Woo, Study on the Prediction of the Stress Corrosion Crack Occurrence in the Tube and Control the Crack Depth Using Acoustic Emission Method (Master's thesis), Korea Aerospace University, Goyang-si, Gyeonggi-do, South Korea, 2013.
13 K.I. Kim, I.C. Kang, A study on stress corrosion cracking of weld zone in 304-stainless steel, J. Korean Weld. Soc 5 (1987) 35-43.
14 H.S. Yu, E.G. Na, S.H. Chung, A study on the stress corrosion cracking behaviors for weld joint of steel with various pH values in synthetic sea water, J. Korean Weld. Soc 13 (1995) 510-520.
15 H.S. You, J.K. Lim, S.H. Chung, A study on the stress corrosion cracking evaluation for weld joint of steel by using miniaturized small specimen, J. Korean Weld. Soc 12 (1994) 411-423.
16 A.J. Russell, D. Tromans, A fracture mechanics study of stress corrosion cracking of type-316 austenitic steel, Metall. Trans. A 10 (1979) 1229-1238.   DOI
17 J.H. Kim, J.S. Kim, J. Lee, N.G. Kwag, B.Y. Lee, The basic study on the method of acoustic emission signal processing for the failure detection in the NPP structures, J. Korean Soc. Nondestruct. Test 29 (2009) 485-492.
18 K.Y. Sung, I.S. Kim, Y.K. Yoon, Characteristics of acoustic emission during stress corrosion cracking of Inconel 600 alloy, Scr. Mater 37 (1997) 1255-1262.   DOI