• 한국수소및신에너지학회논문집
• /
• 제26권4호
• /
• pp.339-346
• /
• 2015

The synthesis of Fischer-Tropsch (FT) oil is the catalytic hydrogenation of CO to give a range of products, which can be used for the production of high-quality diesel fuel, gasoline and linear chemicals. This studied catalyst was prepared Cobalt-supported alumina and silica by the incipient wet impregnation of the nitrates of cobalt, promoter and organic solvent with supports. Cobalt catalysts were calcined at $350^{\circ}C$ before being loaded into the FT reactors. After the reduction of catalyst has been carried out under $450^{\circ}C$ for 24h, FT reaction of the catalyst has been carried out at GHSV of 4,000/hr under $200^{\circ}C$ and 20atm. From these experimental results, we have obtained the results as following; In case of $SiO_2$ catalysts, the activity of 12wt% $Cobalt-SiO_2$ synthesized by organic solvent was about 2 or 3 times higher than the activity of 12wt% $Cobalt-SiO_2$ catalyst synthesized without organic solvent. In particular, the activity of the $Cobalt-SiO_2$ catalyst prepared in the presence of an organic solvent P was two to three times higher than that of the $Cobalt-SiO_2$ catalyst prepared without the organic solvent. Effect of Cr and Cu metal as a promoter was found little. 200 h long-term activity test was performed with a $Co/SiO_2$ catalyst prepared in the presence of an organic solvent of Glyoxal solution.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2010년도 추계학술대회 초록집
• /
• pp.133.2-133.2
• /
• 2010

Fischer-Tropsch synthesis (FTS) was carried out in heat-exchanger typed reactor with cobalt metallic foam catalyst. Considering the heat and mass transfer limitations in the cobalt catalyst, a Co-foam catalyst with an inner metallic foam frame and an outer cobalt catalyst was developed. The Co-foam catalyst was highly selective toward liquid hydrocarbon production and the liquid hydrocarbon productivity at $203^{\circ}C$ reached to $52.5ml/(kg_{cat}{\cdot}h)$, which was higher than that obtained by the Co-pellet. Furthermore, the heat-exchanger typed reactor was developed to efficiently control the highly exothermic reaction heat. The reaction heat generated in the FTS reaction on the cobalt active site was easily transferred to reactor wall by the metallic foam in the catalyst and the transferred reaction heat was directly removed by the hot oil which circulated the wall side of the heat-exchanger typed reactor.

• 공업화학
• /
• 제26권6호
• /
• pp.743-745
• /
• 2015

본 연구에서는 실온에서 간단히 염기의 양을 조절함으로서 세 가지 종류의 서로 다른 형태의 비결정질의 cobalt phosphate를 합성하였다. 합성된 샘플의 결정성과 형태를 X-Ray Diffraction (XRD)과, Scanning Electron Microscopy (SEM)를 통하여 확인하였으며, sodium borohydride의 수소발생 불균일 촉매로서 적용하였다. 촉매들 중에서 실온에서 합성한 비결정질의 cobalt phosphate 중에서 염기의 양이 가장 적은 10 nm 이하의 얇은 판상 형태의 촉매가 표면적이 넓어 가장 좋은 수소 발생 촉매활성을 보였다.

• International Journal of Safety
• /
• 제1권1호
• /
• pp.58-61
• /
• 2002

A preparation method of cobalt supported alumina catalyst for a emergency escape mask cartridge has been studied. Catalysts were prepared by incipient wetness impregnation method using pre-shaped $\gamma$=alumina powders of 70-100 mesh. The catalyst was tested in a continuous-flow reactor system and characterized by elemental analysis, BET and TGA-DTA techniques. Cobalt shows higher activity than platinum or nickel for carbon monoxide oxidation at room temperature. Optimum loading amount of cobalt was 10 wt.% for CO oxidation and the reaction activity increases gradually with the increase of calcination temperature up to $450^{\circ}C.

• 대한화학회지
• /
• 제68권2호
• /
• pp.87-92
• /
• 2024

The commercialization of rechargeable metal-air batteries is extremely desirable but designing stable oxygen reduction reaction (ORR) catalysts with non-noble metal still has faced challenges to replace platinum-based catalysts. The nonnoble metal catalysts for ORR were prepared to improve the catalytic performance and stability by the thermal decomposition of ZIF-8 with optimum cobalt loading. The porous carbon was obtained by the calcination of ZIF-8 and different loading amounts of Co nanoparticles were anchored onto porous carbon forming a Co/PC catalyst. Co/PC composite shows a significant increase in the ORR value of current and stability (500 h) due to the good electronic conductive PCN support and optimum cobalt metal loading. The significantly improved catalytic performance is ascribed to the chemical structure, synergistic effects, porous carbon networks, and rich active sites. This method develops a new pathway for a highly active and advantageous catalyst for electrochemical devices.

• 한국수소및신에너지학회논문집
• /
• 제25권3호
• /
• pp.247-254
• /
• 2014

The synthesis of Fischer-Tropsch oil is the catalytic hydrogenation of CO to give a range of products, which can be used for the production of high-quality diesel fuel, gasoline and linear chemicals. Our cobalt based catalyst was prepared Co/alumina, silica and titania by the incipient wet impregnation of the nitrates of cobalt and promoter with supports. Cobalt catalysts was calcined at $350^{\circ}C$ before being loaded into the FT reactors. After the reduction of catalyst has been carried out under $450^{\circ}C$ for 24hrs, FT reaction of the catalyst has been carried out at GHSV of 4,000/hr under $200^{\circ}C$ and 20atm. From these test results, we have obtained the results as following ; in case of 12wt% Co-supported $Al_2O_3$, $SiO_2$ and $TiO_2$ catalysts, maximum activities of the catalysts were appeared at the promoters of Mn, Mo and Ce respectively. The activity of 12wt% $Co/Al_2O_3$ added a Mn promoter was about 3 times as high as that of 12wt% $Co/Al_2O_3$ catalyst without promoters. When it has been the experiment at the range of reaction temperature of $200{\sim}220^{\circ}C$ and GHSV of 1,546~5,000/hr, the results have shown generally increasing the activities with the increase of reaction temperature and GHSV.

• Bulletin of the Korean Chemical Society
• /
• 제27권9호
• /
• pp.1381-1385
• /
• 2006

Cobalt (cyclam) complex has been successfully immobilized onto SBA-15, and proven to be an active catalyst for the epoxidation of styrene with tert-butyl hydroperoxide as a terminal oxidant. The selectivity for styrene oxide was observed to be up to 66% with 40% styrene conversion after 12h reaction time. The reversible redox cycle between Co(III) and Co(II) couple which was supposed to play key role during the epoxidation reaction was supported by a cyclic voltametry analysis. The textural properties of the catalyst was characterized by XRD, N2 adsorption-desorption, and TEM analysis.

• 한국수소및신에너지학회논문집
• /
• 제25권2호
• /
• pp.114-121
• /
• 2014

The synthesis of Fischer-Tropsch oil is the catalytic hydrogenation of CO to give a range of products, which can be used for the production of high-quality diesel fuel, gasoline and linear chemicals. Our cobalt catalyst was prepared Co/alumina, Co/silica and Co/titania by the incipient wetness impregnation of the nitrates of cobalt with supports. Co-based catalysts was calcined at $400^{\circ}C$ before being loaded into the FT reactors. After the reduction of catalyst has carried out under $450^{\circ}C$, FT reaction of the catalyst has carried out at GHSV of 4,000 under $200^{\circ}C$ and 20atm. From test results, the order of increasing activity for the catalyst was Co/alumina > Co/silica > Co/titania. When the content of Co metal such as 5, 12, 20 and 30wt% was changed, an CO conversion increased as the content of Co metal increased. The activity of catalyst has obtained the best value at 12wt% Co content.

• 자원리싸이클링
• /
• 제14권4호
• /
• pp.17-21
• /
• 2005

망간단괴 용융환원 시 철과 니켈을 주로 함유하고 있는 Ni-Cd 폐전지와 코발트 등을 함유한 석유화학 폐촉매를 대상으로 첨가 원료로서의 사용 가능성을 검토하였다. Ni-Cd 폐전지의 경우 망간단괴와의 첨가비에 관계없이 $5\%$ 코크스 첨가 시, 주회수 대상 금속인 니켈을 전량 합금상으로 회수할 수 있었다. 한편 폐촉매의 경우 폐촉매의 첨가비가 증가할수록 많은 환원제가 필요한데 이는 폐촉매 중의 코발트가 산화물 형태로 존재하여 이를 환원하기 위한 환원제가 필요하기 때문이다. 본 방법은 금속계 폐자원을 처리하고 동시에 유가금속을 회수할 수 있는 방법으로 향후 망간단괴 개발의 상용화 시 경제성을 증대시키고 폐자원의 재활용에 기여 할 것이다.

• 한국재료학회지
• /
• 제26권8호
• /
• pp.401-405
• /
• 2016

The cobalt silicides were investigated for employment as a catalytic layer for a DSSC. Using an E-gun evaporation process, we prepared a sample of 100 nm-thick cobalt on a p-type Si (100) wafer. To form cobalt silicides, the samples were annealed at temperatures of $300^{\circ}C$, $500^{\circ}C$, and $700^{\circ}C$ for 30 minutes in a vacuum. Four-point probe, XRD, FE-SEM, and CV analyses were used to determine the sheet resistance, phase, microstructure, and catalytic activity of the cobalt silicides. To confirm the corrosion stability, we also checked the microstructure change of the cobalt silicides after dipping into iodide electrolyte. Through the sheet resistance and XRD results, we determined that $Co_2Si$, CoSi, and $CoSi_2$ were formed successfully by annealing at $300^{\circ}C$, $500^{\circ}C$, and $700^{\circ}C$, respectively. The microstructure analysis results showed that all the cobalt silicides were formed uniformly, and CoSi and $CoSi_2$ layers were very stable even after dipping in the iodide electrolyte. The CV result showed that CoSi and $CoSi_2$ exhibit catalytic activities 67 % and 54 % that of Pt. Our results for $Co_2Si$, CoSi, and $CoSi_2$ revealed that CoSi and $CoSi_2$ could be employed as catalyst for a DSSC.