• Fire Science and Engineering
• /
• v.25 no.2
• /
• pp.95-100
• /
• 2011

The ultimate purpose of this study is to improve the irrational system related to flame retardant coating performance test of field flame retardant coating articles and to secure the reliability of flame retardant coating through rational flame retardant coating test. To achieve this, the analysis was conducted on the interior finishing materials used in the interior fields and the trends of recent field flame retardant coating, based on the results of flame retardant coating performance test of field flame retardant coating articles which the first-line fire stations have recently conducted. And I attempted to present the methods of field flame retardant coating performance test suitable to current realities and the ways of improvement for securing reliability by analyzing the problems with the methods and procedures of field flame retardant coating articles and the registration system of flame retardant coating business.

• Proceedings of the Korea Institute of Fire Science and Engineering Conference
• /
• 2008.04a
• /
• pp.65-68
• /
• 2008

Intumescent coating system for fire resistance has undesirable weaknesses that fire resistance performance of steel members is being deteriorated due to cracks and falling-offs of the coverings as time goes after completion of the coverings to the members. This study is designed to understand changes in durability of intumescent coating system through follow-up tests on bond strength and thickness for the domestic intumescent coating system.

• Journal of Power System Engineering
• /
• v.2 no.3
• /
• pp.49-54
• /
• 1998

This paper is investigated of hardness and adhesiveness of plasma sprayed coating steels by AE(Acoustic Emission) testing when loading a tensile. AE Parameters used are Event, Count, Energy and Amplitude. Test specimens are carbon steel(S45C) with sprayed coating layers of Ni-4.5wt.%Al(bond coating) and $TiO_2$(top coating), and carry out heat treatment at $800^{\circ}C\;and\;1000^{\circ}C$, respectively. The micro-hardness of the heat treatment specimen have been improved more than that of non-heat treatment. On the tensile test, the process and occurence of the exfoliation of the sprayed coating layer can be estimated by AE Characteristics of AE parameters, such as event, count, amplitude and energy, on the layer exfoliation are shown the similar aspects. The exfoliation of bond coating occure at about 20% of strain and top coating is about 5% of strain.

• Fire Science and Engineering
• /
• v.23 no.1
• /
• pp.40-47
• /
• 2009

Applying fire resistive coating to steel members is one of the general methods to secure fire resistance performance of steel members. And intumescent coating system is currently one of methods giving fire resistance to steel members. Intumescent coating system for fire resistance, however, has undesirable weaknesses that fire resistance performance of steel members is being deteriorated due to cracks and falling-offs of the coverings as time goes after completion of the coverings to the members. So it is necessary to understand changes of the durability and the fire resistance performance of intumescent coating system over a time elapse and to reflect such change properly into the building design and construction. This research is performed to present the test method of durability and the maintenance of intumescent coating system through theoretical investigation of the test method of durability and the guide of maintenance & management of intumescent coating system of several countries, including the Britain, United States, Japan.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2006.04a
• /
• pp.124-131
• /
• 2006

It is well known that smoother surface in substrate for coating or converting can obtain better results. Generally paper substrate is taking machine calendar process in papermaking system to give more uniformity and to get better coating runnability. This paper was prepared to find better idea for obtaining smoother surface after precalendering precoated paper as a substrate of double coating system. It was shown precalendering had effect on roughness improvement for precoating layer but was difficult to say it was effected to supercalendering results for double coating. The porosity and ink evaluation with precalendered double coated paper is needed to identify more essential clue for precalendering effect.

• Journal of Aerospace System Engineering
• /
• v.2 no.2
• /
• pp.42-45
• /
• 2008

Under the non-operating exposure condition in the hot area, the T-50 cockpit temperature is expected over the requirement according to T-50 environmental criteria. So it is necessary to protect the cockpit from the high temperature condition during the non-operating exposure because the high temperature of the cockpit may result in the cockpit equipment malfunction. In this study, the transparency coating is selected as the method for protecting the cockpit from the high temperature exposure and analyzed the effect on the cockpit heat load attenuation. Some kinds of cockpit coating were reviewed and selected and the analysis was performed about the effect before and after coating application under 1% hot day condition based on the T-50 FSD hot soaking test data. The result of analysis show transparency coating is so effective to attenuate the heat load of T-50 cockpit.

• Journal of the Korean Society of Safety
• /
• v.18 no.2
• /
• pp.16-21
• /
• 2003

The object of this research is to prevent the industrial accidents which frequently occurred in breaking the coating in cement silo. Research was conducted to identify the cause of the coating formation, and the model experiment of aeration system was done to investigate the effect of moisture air on the coating formation. The results show that dehumidification of supply air in aeration system is the most important factor to suppress the coating formation, and the refrigerated low pressure air dryer applicable to the aeration system of cement silo was newly designed and developed. When this air dryer is applied to the cement silo, 88% of the moisture component of supply air can be reduced. Therefore the cleaning cycle extends over twice, and it contributes to the decrease of industrial accidents and cleaning cost.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.05a
• /
• pp.248-254
• /
• 2002

The most controversial topics in plasma sprayed ceramic coating system are recently mechanical properties such as bond strength, cohesive strength, toughness and so on. Determination of bond strength of coatings is one of the most important problems. In the industry, the bond strength of coating system has been estimated by Pull-off test(ASTM standard C633-79). But, without a fixed jig and specimen, it is impossible to obtain the bond strength. Therefore, it is necessary to study the critical fracture load on interface of the coating by indentation test. Because the critical fracture load plays an important role in evaluating the bond strength for plasma sprayed ceramic coating system. So, we have estimated critical fracture load in plasma sprayed ceramic coating system, and it was shown that inverse relationship between the cross-section hardness of coating and the critical fracture load(Pc). In case of the high load(1kgf, 2kgf) in $Al_{2}O_{3}+13%TiO_{2}$, it was found that the critical point(Pco), which the coating was broken on.

• Tribology and Lubricants
• /
• v.32 no.4
• /
• pp.125-131
• /
• 2016

In recent years, thick ta-C coating has attracted considerable interest owing to its existing and potential commercial importance in applications such as automobile accessories, drills, and gears. The thickness of the ta-C coating is an important parameter in these applications. However, the biggest problems are achieving efficient coating and uniformity over a large area with high-speed deposition. Feasibility is confirmed for the ta-C coating thickness of up to 9.0 µm (coating speed: 3.0 µm/h, fixed substrate) using a single FCVA cathode. The thickness was determined using multiple coating cycles that were controlled using substrate temperature and residual stresses. In the present research, we have designed a coating system using FCVA plasma and produced enhanced thick ta-C coating. The system uses a specialized magnetic field configuration with stabilized DC arc plasma discharge during deposition. To achieve quality that is acceptable for use in automobile accessories, the magnetic field, T-type filters, and 10 pieces of a multi-cathode are used to demonstrate the deposition of the thick ta-C coating. The results of coating performance indicate that uniformity is ±7.6 , deposited area is 400 mm, and the thickness of the ta-C coating is up to 5.0 µm (coating speed: 0.3 µm/h, revolution and rotation). The hardness of the coating ranges from 30 to 59 GPa, and the adhesion strength level (HF1) ranges from 20 to 60 N, depending on the ta-C coating.

• Elastomers and Composites
• /
• v.48 no.4
• /
• pp.282-287
• /
• 2013

Slot coating has been widely spread in photo resist coating on glass for flat display monitor. High quality of coating is required as high quality of image in display is needed. Coating quality in the slot coating is divided into nozzle direction quality and machine direction quality. Nozzle direction quality is related to flow uniformity inside the die whereas machine direction quality is related to die lip design and operational conditions. In this study coating uniformity in the machine direction of slot coating has been investigated through computer simulation. Die lip angle and die lip length were considered as outside die geometry and coating speed was considered as operational condition. Coating behavior has been analyzed and coating quality has been evaluated through computer simulation. Coating thickness decreased and coating uniformity increased as coating speed increased. However, the stability of meniscus formation was reduced and subsequently coating stability was reduced as coating speed increased. Coating thickness deviation decreased as die lip angle increased in down stream die. Coating thickness decreased and time to reaching steady state increased as increased die lip length in down stream die.