• Korean Journal of Metals and Materials
• /
• v.47 no.2
• /
• pp.99-106
• /
• 2009

The high temperature corrosion properties of heat resistant steels were investigated in oxidation atmosphere including sulfur dioxide. The heat resistant steels of T22, T92, T122, T347HFG and T304H were evaluated at 620, $670^{\circ}C$ for 400 hours. The corrosion rates showed a decreasing tendency while chrome contents of those steels increased from 2 mass.% to 19 mass.%. The in crease in temperature increasement has an more effect on the corrosion rates of low chrome steels than high chrome steels. The weight gains of T22, T92, T304H at $670^{\circ}C$ were 3.7, 1.65, 1.23 times compared with those at $620^{\circ}C$. The external scale formed on T22 was composed of hematite, magnetite and Fe-Cr spinel and internal layer including iron oxide mixed with sulfide. The scales formed on T92, T122, T304H consisted of an outer layer of hematite and inner layer of chrome oxide and hematite. The proportion of chrome oxide at inner layer was increased when the chrome contents in heat resistant steels were increased.

• Journal of the Korean Ceramic Society
• /
• v.12 no.1
• /
• pp.29-36
• /
• 1975

This study was conducted to research the formation, color development and application for colored glazes of the spinel solid solutions of the green pigment. On specimens prepared by calcining the oxide and basic carbonate mixture at 1250℃ for 1.5 hour, the x-ray analysis, measurement of reflectance and the test of their stabiality as a glaze pigment were carried out. The results are summarized as follows 1) Each sample is composed of single spinel and not of mixture of spinel. 2) Formation of continuous soild solution, except for a few instances, pertaining to Vegard's law was confirmed by means of the x-ray analysis. 3) The more difference between absorption and reflectance lies, the lighter colors are. When the absorption occurs at the high-reflectance, the excitation purity becomes low. On the contrary when the absorption takes place at the low-reflectance, the excitation purity becomes low. On the contrary when the absorption takes place at the low-reflectance, the excitation purity is higher. 4) Colors obtained in the CdO-MgO-Cr2O3-Al2O3 system, as the amounts of Al3+ increased, change from green through brown to pink, and the absorption peak shifts towards violet region. 5) An increase in Co2+ in the CoO-MgO-Cr2O3-Al2O3 system, changes the color from blue green to dark blue. The excitation purity is higher, and the absorption peak shifts toward regions. 6) Colors are green in the NiO-MgO-Cr2O3 and CdO-MgO-Cr2O3 systems in general, but in the ZnO-MgO-Cr2O3 system brillant hue is not obtained. 70 According to the results of the colored glaze test, the spinels turn outto be stable as brilliant glaze pigment in the calcium-magnesia glaze.

• Journal of the Korean earth science society
• /
• v.44 no.2
• /
• pp.161-168
• /
• 2023

While numerous previous studies investigated the provenance and tectonic history of the Gyeongsang Supergroup, less are known about other Cretaceous strata in South Korea. This study presents preliminary results from petrographic analysis of the Cretaceous Icheonri Formation distributed in Gijang-gun, Busan. Based on the immature texture and composition of the Icheonri sediments, we interpret that they were derived from weakly denudated Cretaceous arc volcanoes developed along the eastern margin of the Asian continent, with limited weathering and transport. Additionally, the presence of chrome spinel grains in the sediments suggests the existence of ultramafic bodies exposed in their provenance. Further studies will advance our understanding of the tectonic developments in the southeastern Gyeongsang Basin, and facilitate a comprehensive correlation between the Icheonri Formation and the Gyeongsang Supergroup.

• Journal of the Korean Ceramic Society
• /
• v.51 no.5
• /
• pp.505-510
• /
• 2014

The properties of black ceramic pigments including thermal and glaze stability were systematically investigated so that these pigments could be used to decorate porcelain products. Various compositions of $(Ni,Mn)(Fe,Cr,Mn)_2O_4$ and $Co(Fe,Cr)_2O_4$ powders were synthesised using a solid state reaction method. The obtained $Co(Fe,Cr)_2O_4$ and $(Ni,Mn)(Fe,Cr,Mn)_2O_4$ powders showed single phases of spinel structure after calcination processes at $1000^{\circ}C$ and $1200^{\circ}C$, respectively. CIE $L^*a^*b^*$ colourimetric parameters of glazed $Co(Fe,Cr)_2O_4$ and $(Ni,Mn)(Fe,Cr,Mn)_2O_4$ pigments were analyzed according to the different amounts of Cr substitution. In addition, the amount of $Cr^{+6}$ remaining in the $Co(Fe,Cr)_2O_4$ and $(Ni,Mn)(Fe,Cr,Mn)_2O_4$ pigments was also measured.