• Transactions of Materials Processing
• /
• v.28 no.4
• /
• pp.219-225
• /
• 2019

This study deals with the effect of austempering temperature and time on the microstructures and mechanical properties of high-carbon nano-bainite steels. Although all the austempered specimens are mainly composed of bainite, martensite, and retained austenite, the specimens which are austempered at lower temperatures contain finer packets of bainite. As the duration for austempering increases, bainite packets are clearly seen due to larger amount of carbon atoms being redistributes into bainite and retained austenite during bainite transformation. As the austempering time increases, the hardness of the specimens gradually decreases as a result of lower martensite volume fraction, and later increases again due to the formation of nano-bainite structure. The Charpy impact test results indicate that the impact toughness of the austempered specimens can be improved if the formation of nano-bainite structure and the transformation induced plasticity effect of retained austenite are optimized at higher austempering temperature.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.21 no.3
• /
• pp.307-312
• /
• 2001

Ultrasonic signals from Charpy impact test specimen have been analyzed in order to evaluate the integrity of reactor pressure vessel. Base and weld metal that were extracted from reactor vessel doting plant outages according to the schedule of the surveillance test required by the related regulations have been used and the ultrasonic test parameters including velocity, attenuation, etc. showed a close correlations with the amount of neutron irradiation for base metal, relatively homogeneous materials. This result showed certain possibility where a nondestructive method could be used to predict the fluence of the Irradiation due to neutron in nuclear reactor vessel materials.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.08a
• /
• pp.172-179
• /
• 1999

As the martensite structure cause fracture failure during drawing from 5.5mm rod to 3.05mm dia. wire without additional heat treatment, the optium cooling condition to inhibit the occurrence of martensite was investigated. In order to get SAE9254+V quality, the effects of alloying element, vanadium on the mechanical properties were investigated. Based upon CCT and TTT curves and the results form cooling test in mill, optimun cooling was found in the condition of the laying head temp of 780$^{\circ}C$ and of the conveyor speed at 0.15m/sec with the whole cover closed. The wire rods produced under the condition showed the best mechanical properties of 120kg/$\textrm{mm}^2$ in TS and 50% in RA, having an excellent drawability. In vanadium added steels, tensile strength was improved without degrading elongation and charpy impact value. That means the strengthening by vanadium is mainly due to the grain refinement by the fine precipitates during tempering process.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.29 no.3
• /
• pp.219-223
• /
• 2009

This paper prescribed the structural integrity of the API 5L X65 pipeline subjected to tensile pre-strain. The effects of pre-strain on the mechanical properties of API 5L X65 pipe were substantially investigated through a variety of the experimental procedures. Axial tensile pre-strain of 1.5, 5 and 10% was applied to plate-type tensile specimens cut from the pipe body prior to mechanical testing. Tensile test revealed that yield strength and tensile strength were increased with increasing tensile pre-strain. The increasing rate of the yield strength owing to the pre-strain is greater than that of the tensile strength. However, the pre-strain up to 5% had a little effect on the decreasing of the fracture toughness. The structural integrity of the API 5L X65 pipeline subjected to large plastic deformation was evaluated through the fitness-for service code.

• Journal of Mechanical Science and Technology
• /
• v.15 no.10
• /
• pp.1417-1422
• /
• 2001

Since fracture surface presents clear evidence to describe the circumstances of material failure event, analysis of fracture surface should provide plenty of useful information for failure prevention. Thus if we extract proper information from the fracture surface, the safety evaluation, for plant component could be more accurate. In general, the chaotic morphology of fracture surface is determined by the degree of material degradation as well as by other factors such as type of load, geometry of specimen, notch condition, microstructure of material and environment. In this research, we developed a fractal analysis technology for the fracture surface of aged turbine rotor steel based on the slit-island technique using an image analyzer. Moreover the correlation between the fractal dimension and the aging time was studied.

• Journal of Advanced Marine Engineering and Technology
• /
• v.40 no.9
• /
• pp.774-779
• /
• 2016

This study was performed to study the possibility of TMCP's application for side shell plating curved structures through mechanical property testing to understand if the rules and regulations of DNV and the quality standard of IACS after line heating for TMCP steel and normalizing DH32 material steel could be satisfied. Experimental results showed that TMCP's strength was measured to YS = 385 MPa, 18% higher than the required 315 MPa and TS = 525 MPa, complying with the required range of between 440 and 570 MPa. The minus 20 degree impact test for the Charpy V-Notch complied with the required standard and in addition the hardness test satisfied the requirement of 'Hv10 = 130 ~ 320' by reaching an average of T : 216 and L : 275 respectively.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.8
• /
• pp.1421-1428
• /
• 1992

It has been increasingly recognized that the safety analysis considering fracture mechanics is required of the pressure vessels made of 2 1/4 Cr-1Mo steel for safe operation due to temper-embrittlement during long term service. In this study, the fracture toughnesses of degraded and recovered 2 1/4 Cr-1Mo steels have been studied with J$_{IC}$ test specimens at room temperature and the results will be compared with the data obtained from the Charpy impact test. The fracture toughness data from above experiments will be applied to life prediction based on the surface crack growth for degraded and recovered Cr-Mo pressure vessels.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2002.05a
• /
• pp.29-34
• /
• 2002

[ $Nb/MoSi_2-ZrO_2$ ] laminate composites have been successfully fabricated by alternately stacking $MoSi_2-ZrO_2$ powder layer and Nb sheet, followed by hot pressing in a graphite mould. The fabricating parameters were selected as hot press temperatures. The instrumented Charpy impact test was carried out at the room temperature in order to investigate the relationship between impact properties and fabricating temperatures. The interfacial shear strength between $MoSi_2-ZrO_2$ and Nb, which is associated with the fabricating temperature and the growth of interfacial reaction layer, is also discussed. The plastic deformation of Nb sheet and the interfacial delamination were macroscopically observed. The $Nb/MoSi_2-ZrO_2$ laminate composites had the maximum impact value when fabricated at 1623K, accompanying the increase of fracture displacement and crack propagation energy. The interfacial shear strength of $Nb/MoSi_2-ZrO_2$ laminate composites increased with the growth of interfacial reaction layer, which resulted from the increase of fabricating temperature. there is an appropriate interfacial shear strength for the enhancement of impact value of $Nb/MoSi_2-ZrO_2$ laminate composites. A large increase of interfacial shear strength restrains the plastic deformation of Nb sheet.

• Journal of Korea Foundry Society
• /
• v.21 no.3
• /
• pp.179-186
• /
• 2001

Melt super-heating which promotes shape modification of ${\beta}$ intermetallic compounds was conducted to improve mechanical properties of recycled AC2B aluminum alloy. Modification of needle-shape ${\beta}$ intermetallic compounds was effective for the specimens of AC2B aluminum alloys containing 0.85wt.% Fe by melt super-heating, in which the melts had been held at $850^{\circ}C$ or $950^{\circ}C$ for 30 minutes respectively. Owing to the modification of needle-shape of ${\beta}$ intermetallic compounds by melt superheating of the alloy with containing 0.85wt.% Fe to $950^{\circ}C$, increases in elongation and tensile strength were prominent to be more than double and 55% respectively in comparison with the melt heated to $740^{\circ}C$. Moreover, modification of needle-shape ${\beta}$ intermetallic compounds in the alloy containing O.85wt.% Fe by $950^{\circ}C$ melt super-heating led to 48% improvement of the value of impact absorbed energy as compared with the melt heated to $740^{\circ}C$.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.12
• /
• pp.2109-2115
• /
• 2001

Miniaturized specimen technology is useful to characterize the mechanical behavior when it is difficult to sample the material enough for the test. In this study, two kinds of miniaturized Charpy impact specimens(i.e., miniaturized specimen with side groove and without side groove) of aged 1Cr- lMo-0.25V steel were prepared and tested. The relationship between the extent of degradation in terms of ductile brittle transition temperature(DBTT) and the fracture stress of 1Cr-1Mo-0.25V steel was established. The fracture stress obtained from miniaturized specimen without side groove turned out to be linearly related with the DBTT of standard specimen. Therefore the fracture toughness of aged turbine rotor steel might be evaluated by the fracture stress. In addition, the correlation between DBTT of standard specimen and that of miniaturized specimen was investigated. As the results of normalizing DBTT by maximum elastic tensile stress, the normalized DBTT of miniaturized specimen without side groove allows one to estimate that of standard specimen.