• 대한화학회지
• /
• 제39권9호
• /
• pp.698-704
• /
• 1995

33중량%의 PVC와 66중량%의 o-NPOE 가소제에 1중량%의 중성 전극물질인 4'-benzothiazolyl-benzo-15-crown-5를 사용하여 성형한 막전극은 다른 15-크라운-5난 18-크라운-6 유토체들에 비하여 나트륨에 대하여 보다 낮은 선택성을 갖는 칼륨선택성을 나타내었다. 이 막전극의 전기화학적 성질들(감응기울기, 선택성, 섬출한계 및 수명)을 잘 알려져 있는 칼륨선택성 전극물질인 발리노마이신, benzo-15-crown-5, 4'-aminobenzo-15-15-crown-5, benzo-18-crown-6, dibenzo-18-crown-6 및 bis[(benzo-15-crown-5)-4'-ylnethuyl]pimelate를 사용한 전극막들의 것과 동일한 실험 조건하에서 비교하였다. 이러한 비교연구를 통하여 벤조티아졸기가 치환된 벤조크라운에테르 화합물이 증가된 칼륨이온 선택성을 나타내게되는 이유를 치환기의 효과와 이온의 분배계수효과로 설명하였다.

• 전기의세계
• /
• 제28권4호
• /
• pp.53-63
• /
• 1979

Interface recombination velocity in $Al_{x}$G $a_{1-x}$ As-GaAs and $Al_{0.85}$, G $a_{0.15}$ As-GaA $s_{1-y}$S $b_{y}$ heterojunction systems is studied as a function of lattice mismatch. The results are applied to the design of highly efficient III-V heterojunction solar cells. A horizontal liquid-phase epitaxial growth system was used to prepare p-p-p and p-p-n $Al_{x}$G $a_{1-x}$ As-GaA $s_{1-y}$S $b_{y}$-A $l_{x}$G $a_{1-x}$ As double heterojunction test samples with specified values of x and y. Samples were grown at each composition, with different GaAs and GaAs Sb layer thicknesses. A method was developed to obtain the lattice mismatch and lattice constants in mixed single crystals grown on (100) and (111)B oriented GaAs substrates. In the AlGaAs system, elastic lattice deformation with effective Poisson ratios .mu.$_{eff}$ (100=0.312 and .mu.$_{eff}$ (111B) =0.190 was observed. The lattice constant $a_{0}$ (A $l_{x}$G $a_{1-x}$ As)=5.6532+0.0084x.angs. was obtained at 300K which is in good Agreement with Vegard's law. In the GaAsSb system, although elastic lattice deformation was observed in (111) B-oriented crystals, misfit dislocations reduced the Poisson ratio to zero in (100)-oriented samples. When $a_{0}$ (GaSb)=6.0959 .angs. was assumed at 300K, both (100) and (111)B oriented GaAsSb layers deviated only slightly from Vegard's law. Both (100) and (111)B zero-mismatch $Al_{0.85}$ G $a_{0.15}$As-GaA $s_{1-y}$S $b_{y}$ layers were grown from melts with a weight ratio of $W_{sb}$ / $W_{Ga}$ =0.13 and a growth temperature of 840 to 820 .deg.C. The corresponding Sb compositions were y=0.015 and 0.024 on (100) and (111)B orientations, respectively. This occurs because of a fortuitous in the Sb distribution coefficient with orientation. Interface recombination velocity was estimated from the dependence of the effective minority carrier lifetime on double-heterojunction spacing, using either optical phase-shift or electroluminescence timedecay techniques. The recombination velocity at a (100) interface was reduced from (2 to 3)*10$^{4}$ for y=0 to (6 to 7)*10$^{3}$ cm/sec for lattice-matched $Al_{0.85}$G $a_{0.15}$As-GaA $s_{0.985}$S $b_{0.015}$ Although this reduction is slightly less than that expected from the exponential relationship between interface recombination velocity and lattice mismatch as found in the AlGaAs-GaAs system, solar cells constructed from such a combination of materials should have an excellent spectral response to photons with energies over the full range from 1.4 to 2.6 eV. Similar measurements on a (111) B oriented lattice-matched heterojunction produced some-what larger interface recombination velocities.ities.ities.s.

• 마이크로전자및패키징학회지
• /
• 제28권4호
• /
• pp.85-89
• /
• 2021

AlGaN 기반 UV-C 발광다이오드(LEDs)에 전기화학적 전위차 활성화(EPA)에 의한 p-형 활성화를 진행하였다. 높은 저항과 낮은 전도도를 유발하는 중성 Mg-H의 복합체의 수소원자를 EPA를 이용하여 제거하여 p-형 활성화 효율을 높였다. 중성 Mg-H 복합체는 주요 매개 변수인 용액, 전압, 시간에 의해 Mg^-과 H⁺로 분해되며, 2차 이온질량 분광법(SIMS) 분석을 통하여 개선된 정공 캐리어의 농도를 확인할 수 있었다. 이 메커니즘은 결국 내부 양자효율(IQE)의 증가, 광 추출 효율 향상, 역 전류 영역의 누설전류 값 개선, 접합 온도 개선 등을 이루어 결과적으로 UV-C LED의 수명을 향상시켰다. 체계적인 분석을 위해 SIMS, Etamax IQE 시스템, 적분구, 전류-전압(I-V) 측정 등을 사용하였으며, 그 결과를 기존의 N₂-열 처리 방법과 비교 평가하였다.