• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.4
• /
• pp.143-149
• /
• 2020

Calcium phosphates recognized as important bio-materials have been successfully synthesized by simple precipitation using waste abalone shells, which are rich mineral sources of calcium. Calcium hydroxide (Ca(OH)₂) originated from abalone shells was used as calcium source (precursor) for the preparation. Synthesis of calcium phosphates was performed by reacting calcium hydroxide with phosphoric acid (H₃PO₄) in aqueous solution. The initial precursor Ca/P ratios were adjusted to 1.50, 1.59 and 1.67, and the effect of the composition and the heat treatment on the synthesized powders and sintered bodies was investigated. The phases of the sintered ceramics prepared at 1150℃ were hydroxyapatite (HAp), β-tricalcium phosphate (β-TCP), and biphasic phosphate (HAp with β-TCP)), which were determined by the initial precursor Ca/P ratios. The results demonstrate the possibility for the synthesis of high value-added calcium phosphates from economical starting materials with low cost and high availability.

• Journal of Ceramic Processing Research
• /
• v.20 no.6
• /
• pp.655-659
• /
• 2019

Calcium phosphates such as HA (hydroxyapatite), β-TCP (tricalcium phosphate) and biphasic HA/β-TCP, were synthesized by wet chemical precipitation in aqueous solution combined with ball milling process. Nanosize powders of the calcium phosphates were synthesized using Ca(OH)2 and H3PO4. The effects of initial precursor Ca/P ratio (1.30, 1.50 and 1.67), ball milling process and post heat-treatment on the phase evolution behavior of the powders were investigated. The phase of resulting powder was controllable by adjusting the initial Ca/P ratio. HA was the only phase for as-prepared powders in both cases of Ca/P ratios of 1.50 and 1.67. The single HA phase without any noticeable second phase was obtained for the initial Ca/P ratio of 1.67 in the overall heat-treatment range. Pure β-TCP and biphasic calcium phosphate (HA/β-TCP) were synthesized from precursor solutions having Ca/P molar ratios of 1.30 and 1.50, respectively, after having been heat-treated above 700 ℃. The β-TCP phase has appeared on the pre-existing DCPD (dicalcium phosphate dihydrate) and/or HA phase. Dense ceramics having translucency were obtained at a considerably lower sintering temperature. The modified process offered a fast, convenient and economical route for the synthesis of calcium phosphates.

• Journal of Sericultural and Entomological Science
• /
• v.36 no.1
• /
• pp.37-43
• /
• 1994

The effects of some sodium phosphates as auxiliary agents were studied on the blockade of hardness for silk degumming. In this work, four kinds of sodium phosphates were tested and the results were obtained through masking effects of metallic ions, difference of pH value and boil-off ratio. The degumming of calcium ingredient was analyzed by means of atomic absorption spectrophotometer and degumming test of cocoon shell was performed in the presence of calcium ingredient and sodium phosphates added to soap solution. In the view of the effects of sodium phosphates on calcium hardness, tetrasodium pyrophosphate(TSPP) and sodium phosphate dibasic(SPD) masked calcium ions more than sodium phosphate monobasic(SPM) and sodium hexametaphosphate(SHP). SHP and TSPP have excellent abilities of masking ferrous ions. The pH values of TSPP solution is higher than others, but lower than soap solution. The pH values were differently measured one another among the sodium phosphates but the boil-off ratio was increased in case of sodium phosphate with high pH value.

• Journal of Industrial and Engineering Chemistry
• /
• v.68
• /
• pp.220-228
• /
• 2018

In this study, we found a simple surface biofunctionalization of biphasic calcium phosphate (BCP) based on the high affinity between alendronate and the calcium ions of BCP, and the strong interaction between heparin and bone morphogenic protein-2 (BMP-2). The biofunctionalized BCP did not be precipitated well and display a remarkable enhancement of osteogenic activity of human adipose-derived stem cells by showing increased alkaline phosphatase (ALP), calcium deposition and osteogenic-related genes (i.e., Runx-2, ALP, osteocalcin, and osteopontin), and bone regeneration in the calvarial defect model. Therefore, this simple surface technique can be used to easily functionalize various calcium phosphates.

• Journal of the Korea Institute of Building Construction
• /
• v.14 no.1
• /
• pp.68-75
• /
• 2014

In order to increase the integrity of the wellbore which is used to prevent the leakage of supercritical $CO_2$, it is necessary to develop a concrete that is strongly resistant to carbonation. In an environment where the concentration of $CO_2$ is exceptionally high, $Ca^{2+}$ ion concentration in pore solution of Portland cement concrete will drop significantly due to the rapid consumption of calcium hydroxide, which decreases the stability of the calcium silicate hydrate. In this research, calcium phosphates were used to modify Portland cement system in order to produce hydroxyapatite, a hydration product that is strongly resistant to carbonation under such an environment. According to the experimental results, calcium phosphates reacted with Portland cement to form hydroxyapatite. The formation of hydroxyapatite was verified using X-ray diffraction analyses with selective extraction techniques. When using dicalcium phosphate dihydrate and tricalcium phosphate, the 28-day compressive strength was lower than that of plain cement paste. However, the specimen with monocalcium phosphate monohydrate showed equivalent strength to that of plain cement paste.

• Journal of Life Science
• /
• v.16 no.4
• /
• pp.676-682
• /
• 2006

To develop high efficiency biofertilizer solubilizing insoluble phosphates, lactate dehydrogenase (ldh) gene was isolated from Staphylococcus sp. LJ2. Genetic constructions were carried out using the pGEM-T-easy vector and pHSG398. Recombinant DNA plasmids containing the ldh gene were transferred to Klebsiella sp. DA71-1 by electroporation. The selected transformant was named as a DA71-1/pLYJ. The insoluble phosphates solubilization activity of DA71-1/pLYJ was higher than that of DA71-1 at various culture conditions. Glucose was the best carbon source for insoluble phosphates solubilization among the used carbon sources. Maximal insoluble phosphates solubilizing was found in sucrose minimal (SM) medium containing 3% glucose. The solubilizing activity of DA71-1/pLYJ against three types of insoluble phosphates, such as tri-calcium phosphate, hydroxyapatite, aluminium phosphate, were quantitatively determined. The optimal temperature and initial pH to solubilize insoluble phosphates in the SM medium was $37^{\circ}C$ and pH 5.0, respectively.

• Journal of the Korean Dietetic Association
• /
• v.6 no.2
• /
• pp.108-116
• /
• 2000

The purpose of this study was to investigate the relationship among calcium intake, blood parameters related with bone metabolism, and serum lipids in healthy adults on self-selected diet. Subjects were consisted of 40 female college students residing in Chungnam. Anthropometric measurements, dietary intake measurements and blood collection were conducted. Serum concentrations of total protein, albumin, alkaline phosphates, leucine amino peptidase, BUN, calcium, inorganic phosphorus, and lipids were measured by biochemical analyzer and ICP spectrometer. The results were as follows. The mean age of subjects was 22.34 years and weight, height and BMI were 52.89kg, 161.29cm and 20.34, respectively. The daily mean energy and calcium intakes were 81.75% and 64.38% of RDA. The mean animal 1:2. The mean serum concentrations were 6.54g/dl(total protein), 4.12g/dl(albumin), 123.24U/(alkaline phosphates), 36.59U/l(leucine amino peptidase), 8.26mg/dl(calcium), 3.29mg/dl(inorganic phosphorus), 60.73mg/dl(triglyceride), 138.49mg/dl(total cholesterol), 65.95mg/dl(HDL-cholesterol), and 60.39mg/dl(LDL-cholesterol). There were no significant differences among calcium intake, bone metabolism parameters, and serum lipids when analyzed by Pearson's correlation coefficient. More systematic studies are required to investigate the roles of calcium in healthy persons on self-selected diets containing different levels of calcium.

• Nutrition Research and Practice
• /
• v.5 no.5
• /
• pp.396-403
• /
• 2011

Ceramides (Cer) comprise the major constituent of sphingolipids in the epidermis and are known to play diverse roles in the outermost layers of the skin including water retention and provision of a physical barrier. In addition, they can be hydrolyzed into free sphingoid bases such as $C_{18}$ sphingosine (SO) and $C_{18}$ sphinganine (SA) or can be further metabolized to $C_{18}$ So-1-phosphate (S1P) and $C_{18}$ Sa-1-phosphate (Sa1P) in keratinocytes. The significance of ceramide metabolites emerged from studies reporting altered levels of SO and SA in skin disorders and the role of S1P and Sa1P as signaling lipids. However, the overall metabolism of sphingoid bases and their phosphates during keratinocyte differentiation remains not fully understood. Therefore, in this study, we analyzed these Cer metabolites in the process of keratinocyte differentiation. Three distinct keratinocyte differentiation stages were prepared using 0.07 mM calcium (Ca$^{2+}$) (proliferation stage), 1.2 mM Ca$^{2+}$ (early differentiation stage) in serum-free medium, or serum-containing medium with vitamin C (50 ${\mu}L$/mL) (late differentiation stage). Serum-containing medium was also used to determine whether vitamin C increases the concentrations of sphingoid bases and their phosphates. The production of sphingoid bases and their phosphates after hydrolysis by alkaline phosphatase was determined using high-performance liquid chromatography. Compared to cells treated with 0.07 mM Ca$^{2+}$, levels of SO, SA, S1P, and SA1P were not altered after treatment with 1.2 mM Ca$^{2+}$. However, in keratinocytes cultured in serum-containing medium with vitamin C, levels of SO, SA, S1P, and SA1P were dramatically higher than those in 0.07- and l.2-mM Ca$^{2+}$-treated cells; however, compared to serum-containing medium alone, vitamin C did not significantly enhance their production. Taken together, we demonstrate that late differentiation induced by vitamin C and serum was accompanied by dramatic increases in the concentration of sphingoid bases and their phosphates, although vitamin C alone had no effect on their production.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.3
• /
• pp.253-260
• /
• 2017

As global warming became a worldwide issue, a significant effort has been made on the development of technology related to $CO_2$ capture and storage. Geologic sequestration of $CO_2$ is one of those technologies for safe disposal of $CO_2$. Geologic sequestration stores $CO_2$ in the form of supercritical fluid into the underground site surrounded by solid rock, and concrete is used for prevention of $CO_2$ leakage into the atmosphere. In such case, concrete may experience severe damage by attack of supercritical $CO_2$, and especially in contact with underground water, very aggressive form of carbonation can occur. In this work, to prevent such deterioration in concrete, calcium phosphates were added to the portland cement to produce hydroxyapatite, one of the most stable mineral in the world. Temperature rise, viscosity, set and stiffening, and strength development of cement paste incorporating three different types of calcium phosphates were investigated. According to the results, it was found that the addition of calcium phosphate increased apparent viscosity, but decreased maximum temperature rise and 28 day compressive strength. It was found that monocalcium phosphate was found to be inappropriate for portland cement based material. Applicability of dicalcium and tricalcium phosphates for portland cement needs to be evaluated with further investigation, including the long term compressive strength development.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.29 no.5
• /
• pp.203-207
• /
• 2019

Calcium phosphates such as hydroxyapatite (HAp), tricalcium phosphate (${\beta}$-TCP), and biphasic calcium phosphate (BCP, HAp/${\beta}$-TCP) have been prepared via hydrothermal treatment. The synthesis was conducted by reacting ($Ca(OH)_2$) aqueous solution with phosphoric acid ($H_3PO_4$) under different hydrothermal synthesis conditions (temperatures up to $150^{\circ}C$ and pH lower than 12). The effects of initial precursor Ca/P ratio (1.30, 1.50 and 1.67) and post heat treatment on the phase evolution behavior of the powders and sintered ceramics were investigated. The phases of resulting powders and sintered ceramics were controllable by adjusting the initial Ca/P ratio. A single HAp phase without any noticeable second phase was obtained for the initial Ca/P ratio of 1.67 in the overall heat treatment range. Pure ${\beta}$-TCP and biphasic calcium phosphate (HAp/${\beta}$-TCP) were synthesized from precursor solutions having Ca/P molar ratios of 1.30 and 1.50, respectively, after having been heat treated at $900^{\circ}C$ or higher. Dense ceramics with translucency were obtained at considerably lower sintering temperatures.