• Proceedings of the KIEE Conference
• /
• 1988.07a
• /
• pp.324-327
• /
• 1988

The photovoltaic performances of a-si : H$n^{+}-p-p^{+}$ solar cells have been investigated. The optimum substrate temperature for the deposition of a-Si : H $n^{+}-p-p^{+}$ cell decreases with increasing doping concentration of the p-layer, and is less than 200$^{\circ}C$ when the gas phase doping concentration is higher than 10 ppm. The results can be explained as the dependences of substrate temperature for the relaxation of silicon atoms and for the bonded hydrogen concentration in the p-layer.

• Korean Journal of Materials Research
• /
• v.29 no.5
• /
• pp.322-327
• /
• 2019

Hole carrier selective MoOx film is obtained by atomic layer deposition(ALD) using molybdenum hexacarbonyl[$Mo(CO)_6$] as precursor and ozone($O_3$) oxidant. The growth rate is about 0.036 nm/cycle at 200 g/Nm of ozone concentration and the thickness of interfacial oxide is about 2 nm. The measured band gap and work function of the MoOx film grown by ALD are 3.25 eV and 8 eV, respectively. X-ray photoelectron spectroscopy(XPS) result shows that the $Mo^{6+}$ state is dominant in the MoOx thin film. In the case of ALD-MoOx grown on Si wafer, the ozone concentration does not affect the passivation performance in the as-deposited state. But, the implied open-circuit voltage increases from $576^{\circ}C$ to $620^{\circ}C$ at 250 g/Nm after post-deposition annealing at $350^{\circ}C$ in a forming gas ambient. Instead of using a p-type amorphous silicon layer, high work function MoOx films as hole selective contact are applied for heterojunction silicon solar cells and the best efficiency yet recorded (21 %) is obtained.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.11a
• /
• pp.58.2-58.2
• /
• 2010

본 연구에서는 n-type wafer에 비정질 실리콘을 증착한 이종접합 태양전지를 열처리 방법을 이용하여 열처리의 효과를 분석함으로써 이종접합 태양전지에 효율적인 열처리 효과에 대하여 연구하였다. P, N-layer는 PECVD(Plasma-enhanced chemical vapor deposition) I-layer는 HWCVD(Hot wire chemical vapor deposition), ITO는 RF 마그네트론 스퍼터링법으로 동일한 조건에서 제작하였고 rapid thermal process를 이용하여 진공 중에서 $150^{\circ}C$, $200^{\circ}C$, $220^{\circ}C$, $250^{\circ}C$까지 열처리를 하였다. 열처리 전과 후 QSSPC로 minority carrier life time, 자외 가시선 분광분석 장치로 투과 반사도를, Ellipsometer로 흡수 계수 등의 변화를 조사하였다. 열처리 후 Minority carrier life time, Voc 및 광변환 효율이 증가하였다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.4 no.3
• /
• pp.238-244
• /
• 1994

We investigated solution growth of silicon on borosilicate and quartz glass substrates in the temperature range of $800^{\circ}C~520^{\circ}C$. A thin Al-Si layer evaporated onto the substrate serves to improve the wetting between the substrate and the Al/Ga solvent. Nucleation takes place by a reaction of Al with $SiO_2$ from the substrate. We obtained silicon deposits with a grain size up to a few 100 $\mu\textrm{m}$. There was a perferential (111) orientation for the case of quartz glass substrates while there is a strong contribution of other orientations for the deposition of Si on borosilicate glass substrates.

• Journal of the Korean Vacuum Society
• /
• v.22 no.4
• /
• pp.218-224
• /
• 2013

We measure solar currents transformed from quantum efficiency as a function of incident angles of solar lights. According to conventional models for solar cells, solar currents can be induced when electrons are separated into electrons and holes in the presence of incident solar lights. On the contrary, solar currents can be possible at the time when pinned charge density waves go beyond the pinning potential barrier under the influence of incident solar beams suggested by some authors. In this experiment, measured solar currents and our theory are in good correspondence to confirm the angle dependence of solar lights.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.388-388
• /
• 2016

Chemical mist deposition (CMD) of poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) was investigated with cavitation frequency f, solvent, flow rate of nitrogen, substrate temperature $T_s$, and substrate dc bias $V_s$ as variables for efficient PEDOT:PSS/crystalline (c-)Si heterojunction solar cells (Fig. 1). The high-speed camera and differential mobility analysis characterizations revealed that average size and flux of PEDOT:PSS mist depend on f, solvent, and $V_s$. The size distribution of mist particles including EG/DI water cosolvent is also shown at three different $V_s$ of 0, 1.5, and 5 kV for a f of 3 MHz (Fig. 2). The size distribution of EG/DI water mist without PEDOT:PSS is also shown at the bottom. A peak maximum shifted from 300-350 to 20-30 nm with a narrow band width of ~150 nm for PEDOT:PSS solution, whose maximum number density increased significantly up to 8000/cc with increasing $V_s$. On the other hand, for EG/water cosolvent mist alone, the peak maximum was observed at a 72.3 nm with a number density of ~700/cc and a band width of ~160 nm and it decreased markedly with increasing $V_s$. These findings were not observed for PEDOT:PSS/EG/DI water mist. In addition, the Mie scattering image of PEDOT:PSS mist under white bias light was not observed at $V_s$ above 5 kV, because the average size of mist became smaller. These results imply that most of solvent is solvated in PEDOT:PSS molecule and/or solvent is vaporized. Thus, higher f and $V_s$ generate preferentially fine mist particle with a narrower band width. Film deposition occurred when $V_s$ was impressed on positive to a c-Si substrate at a Ts of $30-40^{\circ}C$, whereas no deposition of films occurred on negative, implying that negatively charged mist mainly provide the film deposition. The uniform deposition of PEDOT:PSS films occurred on textured c-Si(100) substrate by adjusting $T_s$ and $V_s$. The adhesion of CMD PEDOT:PSS to c-Si enhanced by $V_s$ conspicuously compared to that of spin-coated film. The CMD PEDOT:PSS/c-Si solar cell devices on textured c-Si(100) exhibited a ${\eta}$ of 11.0% with the better uniformity of the solar cell parameters. Furthermore, ${\eta}$ increased to 12.5% with a $J_{sc}$ of $35.6mA/cm^2$, a $V_{oc}$ of 0.53 V, and a FF of 0.67 with an antireflection (AR) coating layer of 20-nm-thick CMD molybdenum oxide $MoO_x$ (n= 2.1) using negatively charged mist of 0.1 wt% 12 Molybdo (VI) phosphoric acid n-Hydrate) $H_3(PMo_{12}O_40){\cdot}nH_2O$ in methanol. CMD. These findings suggest that the CMD with negatively charged mist has a great potential for the uniform deposition of organic and inorganic on textured c-Si substrate by adjusting $T_s$ and $V_s$.

• Current Photovoltaic Research
• /
• v.4 no.1
• /
• pp.12-15
• /
• 2016

Screen printing technique followed by firing has commonly been used as metallization for both laboratory and industrial based solar cells. In the solar cell industry, the firing process is usually conducted in a belt furnace and needs to be optimized for fabricating high efficiency solar cells. The printed-Al layer on the silicon is rapidly heated at over $800^{\circ}C$ which forms a layer of back surface field (BSF) between Si-Al interfaces. The BSF layer forms $p-p^+$ structure on the rear side of cells and lower rear surface recombination velocity (SRV). To have low SRV, deep $p^+$ layer and uniform junction formation are required. In this experiment, firing process was carried out by using conventional tube furnace with $N_2$ gas atmosphere to optimize $V_{oc}$ of laboratory cells. To measure the thickness of BSF layer, selective etching was conducted by using a solution composed of hydrogen fluoride, nitric acid and acetic acid. The $V_{oc}$ and pseudo efficiency were measured by Suns-$V_{oc}$ to compare cell properties with varied firing condition.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.31-31
• /
• 2009

PECVD를 이용하여 제조된 미세결정질 p-i-n 실리콘 박막 태양전지에서, p 층은 태양전지의 윈도우 역할 및 그 위에 증착될 i ${\mu}c-Si:H$ 층의 'seed'층 역할을 수행하기 때문에, p층의 구조적 및 전기적, 광학적 특성은 태양전지의 전체 성능에 큰 영향을 미칠 수 있다. 본 연구에서는 $SiH_4$ 농도를 변화시켜 각기 다른 결정 특성을 갖는 p ${\mu}c-Si:H$층을 제조하고 그 위에 i ${\mu}c-Si:H$ 층을 증착하여 p층의 결정 특성변화와 그에 따른 i ${\mu}c-Si:H$ 층 및 'superstrate' p-i-n 미세결정질 실리콘 박막 태양전지의 특성 변화를 조사하였다. P층의 경우, $SiH_4$ 농도가 증가함에 따라 결정분율 (Xc)이 감소하여 비정질화되었으며 그에 따라 dark conductivity가 감소하는 경향을 나타내었다. 각기 다른 결정분율을 가지는 p 'seed' 층 위에 증착된 태양전지는, p 'seed' 층의 결정분율이 증가함에 따라 개방전압, 곡선인자, 변환효율이 경향적으로 감소하였다. 이는 p 층 결정분율 변화에 따른 p/i 계면특성 저하 및 그 위에 증착되는 i ${\mu}c-Si:H$ 층의 결함밀도 증가 등에 따른 태양전지 특성 감소 때문인 것으로 판단되며, 이를 분석하기 위하여 i ${\mu}c-Si:H$ 층의 전기적, 구조적 특성 분석 및 태양전지의 dark I-V 특성 등을 분석하고자 한다.

• Korean Journal of Materials Research
• /
• v.26 no.8
• /
• pp.401-405
• /
• 2016

The cobalt silicides were investigated for employment as a catalytic layer for a DSSC. Using an E-gun evaporation process, we prepared a sample of 100 nm-thick cobalt on a p-type Si (100) wafer. To form cobalt silicides, the samples were annealed at temperatures of $300^{\circ}C$, $500^{\circ}C$, and $700^{\circ}C$ for 30 minutes in a vacuum. Four-point probe, XRD, FE-SEM, and CV analyses were used to determine the sheet resistance, phase, microstructure, and catalytic activity of the cobalt silicides. To confirm the corrosion stability, we also checked the microstructure change of the cobalt silicides after dipping into iodide electrolyte. Through the sheet resistance and XRD results, we determined that $Co_2Si$, CoSi, and $CoSi_2$ were formed successfully by annealing at $300^{\circ}C$, $500^{\circ}C$, and $700^{\circ}C$, respectively. The microstructure analysis results showed that all the cobalt silicides were formed uniformly, and CoSi and $CoSi_2$ layers were very stable even after dipping in the iodide electrolyte. The CV result showed that CoSi and $CoSi_2$ exhibit catalytic activities 67 % and 54 % that of Pt. Our results for $Co_2Si$, CoSi, and $CoSi_2$ revealed that CoSi and $CoSi_2$ could be employed as catalyst for a DSSC.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.190-190
• /
• 2003

여러원소 (Sb, F 등)를 도핑한 SnO$_2$ 투명전도막은 여러 가지 훌륭한 특성으로 Solar cell, heat mirrors, gas sensors, liquid crystal displays, thick film resistor 등과 같이 넓은 범위에서 응용되고 있다. 본 연구에서는 Sb 도핑된 Tin Oxide films이 Sol-gel dip coating법에 의해 준비되었다. SnO$_2$:Sb 용액은 SnC1$_2$ 와 SbC1$_3$ Power를 알코올에 용해하여 Ethylene glycol 와 Citric acid를 첨가하여 합성하였다. 막의 상형성은 XRD와 SEM(Scanning electron microscope)에 의해서 분석되었으며, 특성분석은 투과율(UV/VIS Spectrophotometer)과 표면전기저항(four point probe)으로 분석되었다. SiO$_2$ barrier이 SnO$_2$:Sb 막의 특성에 미치는 영향을 확인하기 위하여 XPS(X-ray photoelectron spectroscopy) 분석이 적용되었다.