• 한국세라믹학회지
• /
• 제28권6호
• /
• pp.465-470
• /
• 1991

AlN powder was synthesized by carbothermal reduction and nitridation of aluminum hydroxides precipitated in 5∼11 pH range from Al2(SO4)3$.$18H2O aqueous solution. Nitridation reactivity of hydroxide, which depends on precipitation pH, reaction temperature and time, was examined by XRD analysis at 1200∼1350$^{\circ}C$ and compared with that of commercial ${\alpha}$-Al2O3. Hydroxides obtained at higher pH could be more easily nitridated and, considering DTA/TG and BET results, the reason seems to be specific surface area difference of reactants depending on the content of decomposed structural water and the transition rate from transition-Al2O3 to ${\alpha}$-Al2O3.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.119-120
• /
• 2013

공구, 다이몰드 등에 널리 쓰이는 TiC, TiN, CrN, TiCrN, TiAlN 코팅의 산화특성을 비교하기 위하여 $600^{\circ}C-900^{\circ}C$에서 대기중 산화시험을 실시하였다. 내산화성은 (TiC, TiN), TiAlN, TiCrN, CrN 코팅의 순서로 증가하였다. 코팅원소중 Ti는 $TiO_2$로, Cr은 $Cr_2O_3$로, Al은 $Al_2O_3$로 산화되었다.

• 한국세라믹학회지
• /
• 제33권2호
• /
• pp.235-241
• /
• 1996

Self-Propagating high temperature synthesis(SHS) technique was used to synthesize the spinel phase of MgAl2O from MgO and Al powder. Processing factors such as mixing time preheating temperature and ignition catalyst were varied to determine the optimum condition to form MgAl2O4 phase. The reaction products were heat treated at the temperature range of 120$0^{\circ}C$ and 150$0^{\circ}C$. to observe phase transformation of unreacted materials. Processing factors such as 48 hrs-mixing 80$0^{\circ}C$-preheating and 20wt% KNO3-ignition catalyst were effective of the formation of MgAl2O spinel. An activation energy 49.7kcal/mol. was calculated to form a MaAl2O4 spinel from unreacted materials.

• Bulletin of the Korean Chemical Society
• /
• 제35권7호
• /
• pp.2013-2018
• /
• 2014

The adsorption and decomposition of trimethylene oxide ($C_3H_6O$) molecule on the Al(111) surface were investigated by the generalized gradient approximation (GGA) of density functional theory (DFT). The calculations employed a supercell ($6{\times}6{\times}3$) slab model and three-dimensional periodic boundary conditions. The strong attractive forces between $C_3H_6O$ molecule and Al atoms induce the C-O bond breaking of the ring $C_3H_6O$ molecule. Subsequently, the dissociated radical fragments of $C_3H_6O$ molecule oxidize the Al surface. The largest adsorption energy is about -260.0 kJ/mol in V3, V4 and P2, resulting a ring break at the C-O bond. We also investigated the decomposition mechanism of $C_3H_6O$ molecules on the Al(111) surface. The activation energies ($E_a$) for the dissociations V3, V4 and P2 are 133.3, 166.8 and 174.0 kJ/mol, respectively. The hcp site is the most reactive position for $C_3H_6O$ decomposing.

• 대한화학회지
• /
• 제37권10호
• /
• pp.867-873
• /
• 1993

결정화 시간 및 반응 혼합물내의 $H_2O/Al_2O_3$의 비가 AlPO$_4$-5 분자체의 합성에 미치는 영향을 X-선 회절(XRD), 질소흡착실험, 전자현미경(SEM) 그리고 고체상 $^{27}$Al nuclear magnetic resonance(NMR)를 사용하여 조사하였다. 반응온도가 150$^{\circ}$C일 때 AlPO$_4$-5의 결정화 시간에 따른 결정성은 S자형 곡선을 보였으며, 유도기간(induction period)은 1시간 이내인 것으로 나타났다. 반응물에서 생성물, AlPO$_4$-5로의 전환을 명확히 관측할 수 있었으며 약 2시간의 결정화 전후 측정된 모든 물성은 큰 변화를 보였다. 반응물내의 $H_2O/Al_2O_3$의 비가 증가함에 따라 다결정의 AlPO$_4$-5는 육각기둥 모양의 단결정으로 변화하였으며 얻어진 결정의 길이/너비의 비는 증가하였다.

• 한국세라믹학회지
• /
• 제52권2호
• /
• pp.114-118
• /
• 2015

$V_2O_5-P_2O_5-ZnO-Sb_2O_3$ glasses modified with BaO and $Al_2O_3$ are synthesized as a sealing material for large-scale dye-sensitized solar cells (DSSCs). A compositional study is performed in order to determine the glass that can be sintered below $500^{\circ}C$ with a high chemical stability against the electrolyte. The flow size of the glasses after the heat treatment and the glass stability are increased with the addition of $Al_2O_3$ and BaO, while the glass transition temperature is decreased. After the reaction with the electrolyte at $60^{\circ}C$ for 72 h, the addition of 5 mol% of BaO and 2 mol% of $Al_2O_3$ considerably enhances the chemical stability of the glass. X-ray diffraction (XRD) and scanning electron microscope (SEM) are used to examine the reaction between the electrolyte and glasses. The structural contribution of the additives is also investigated and discussed.

• 한국생산제조학회지
• /
• 제4권4호
• /
• pp.61-68
• /
• 1995

TiC-Al2O3 composite ceramics has high hardness, high strength, high wear and corrosion resistance. Therefore, composite ceramics have been concerned significantly with some excellent properties and many functions as new industrial materials to the industry at large. In present research, experiments are carried out to obtain the machinability and machining properties by EDM. As a result, the most suitable machining conditions of TiC-Al2O3 composite ceramics was that the pulse duration is 10-60$mutextrm{s}$, the peak current is 10-16A. The machining speed and the wear of the tool electrode increased with the increase in peak current.

• 한국세라믹학회지
• /
• 제29권6호
• /
• pp.451-458
• /
• 1992

Dense glass-ceramics for low firing temperature substrate were prepared by addition of CeO2 flux to the glass of MgO-Al2O3-SiO2 system. Glass powders were fabricated by melting at 150$0^{\circ}C$ and ball milling. Glass powder compacts were sintered at 800~100$0^{\circ}C$ for 3h. The crystallization and the shrinkage behaviors of glass powder compacts were analyzed by XRD, DTA and TMA. The shrinkage of glass powder compact increased with increasing the amount of CeO2. Because the softening temperature decreased and the crystallization temperature increased with increasing the amount of CeO2. Apparently, addition of CeO2 prevented formation of $\mu$-cordierite phase from the glass-ceramics and improved formation of $\alpha$-cordierite phase. Therefore crystallization properties were enhanced.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1991년도 추계학술대회 논문집
• /
• pp.37-39
• /
• 1991

This paper is studies the effects of additives on the magnetic properties of Sr-ferrite. The specimens have been composed of SrO and Fe$_2$O$_3$with ratio of 1:5.9. As 1st additives, it is mixed to 0.2wt%, 0.7wt% and 1wt% of CaCo$_3$with 0.3wt% SiO$_2$. As 2nd addition, it is mixed to 0.5wt%, 1wt% of Na$_2$SiO$_3$, 0.5wt%, 1wt% of Cr$_2$O$_3$and 0.5wt%, 1wt% of Al$_2$O$_3$and sintering conditions was carried out at 1210$^{\circ}C$, 1230$^{\circ}C$ and 1250$^{\circ}C$. From experiments on the magnetic properties of specimen, the results were shown follows; (1) In case of additive SiO$_2$and CaO, it is stable magnetoplumbite structure for liquid phase grown, enhances mignetic propertics. (2) In case of basic compositions + 0.5wt% Al$_2$O$_3$, it is confirmed better properties by increasing of the coercivity than 0.5wt% Cr$_2$O$_3$additives. (3) In case of mixed additives of Cr$_2$O$_3$and Al$_2$O$_3$, magnetic propeties decrease with sintering density.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1987년도 전기.전자공학 학술대회 논문집(I)
• /
• pp.461-464
• /
• 1987

With the fabrication of Al-$Al_2O_3$-n(p) type Si devices, the analysis and measurement of various characteristics, this study presented the electric physical property theory for the charge distribution of MAS device $Al_2O_3$ films, and inquired out the devices available. In order to study them, Al-(450A)$Al_2O_3$-n(p) type Si was the main objects in the study. They were examined through carrier injection, C-V curves of devices on time, ${\Delta}V_{FB}$-t curves, I-V curves and $Al_2O_3$ film's breakdown characteristics.