• Journal of the Korean Ceramic Society
• /
• v.17 no.2
• /
• pp.96-100
• /
• 1980

The castable refractory, CaO.$2Al_2O_3$ is a useful alumina cement for iron, steel and cement for iron, steel and cement industries, however it is difficult to produce CaO.$2Al_2O_3$because of its high melting point(180$0^{\circ}C$) and narrow firing range. In this study, the coprecipitation method was used to produce CaO.$2Al_2O_3$ for lower temperature firing . This method involved the titration of mixed solution of calicum and aluminate which extracted from domestic kaolin with $NH4_OH$ solution under blowing $CO_2$ gas into the solution. The coprecipitate and its clacined products were analyzed by X-ray diffraction and DTA. The calcined products fired between 400 and 90$0^{\circ}C$ were amorphous, but at 100$0^{\circ}C$ the coprecipitate was converted into one compound, CaO$2Al_2O_3$. From those experimental results, it was found that we could synthesizze CaO.$2Al_2O_3$ at about 100$0^{\circ}C$ which is lower than conventional firing temperature by around 80$0^{\circ}C$. The refractoriness of this alumina cement was SK 34 and the compressive strength ( 1 day) was about 250kg/$\textrm{cm}^2$.

• Journal of the Korean Ceramic Society
• /
• v.35 no.3
• /
• pp.303-309
• /
• 1998

The fabrication of Al2O3/Al composite by pressureless infiltration was investigated by the change of Mg and Si content in Al alloy infiltration process and infiltration atmosphere. The effect of alloying elements infiltration atmosphere and interfacial reactants between Al alloy matrix and Al2O3 particles were in-vestigated in terms of bendingstrength and harness test,. The fabrication of Al2O3/Al composite by the vestigated in terms of bending strength and hardness test. The fabrication of Al2O3/Al composite by the pressureless infiltration was done in nitrogen atmosphere with Mg in Al alloy. It was successfully fabricated at $700^{\circ}C$ according to Mg contents in Al alloy and infiltration condition. Because Mg in the Al alloy and ni-trogen atmosphere of infiltratio condition produced Mg-N compound(Mg3N2) it decreased the wetting an-gle between molten Al alloy and Al2O3 particles by coating on surface of Al2O3 particles. The fracture strength of Al2O3/Al-Mg composite was 800MPa and Al2O3/Al-Si-Mg composite was 400MPa. Si in Al alloy decreased the interfacial strength between Al alloy matrix and Al2O3 particles.

• Transactions of the Korean hydrogen and new energy society
• /
• v.7 no.2
• /
• pp.147-155
• /
• 1996

The aim of this study is the development of technologies of methanol production from carbon dioxide by catalytic hydrogenation. Experiments about carbon dioxide hydrogenation by catalyst mixed with CuO, ZnO, $Cr_2O_3$ and $Al_2O_3$ were conducted to find optimum catalyst and reaction condition. Reactions were carried out at atmospheric and high pressures between 200 to $350^{\circ}C$. High yield of methanol was obtained with $Cu/ZnO/Cr_2O/Cr_2O_3/Al_2O_3$ catalyst at $250^{\circ}C$ and above 30 atmospheric pressure. There was not any increament of hydrogenation reactivity for the catalysts which was made by the addition of Pd to $Cu/ZnO/Cr_2O/Cr_2O_3/Al_2O_3$.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.50 no.10
• /
• pp.500-503
• /
• 2001

The mechanical and electrical properties of the hot-pressed and pressureless annealed SiC+39vol.%$TiB_2$electroconductive ceramic composites were investigated as a function of the liquid additives of $Al_2O_3+Y_2O_3$. The result of phase analysis for the SiC+39vol.%$TiB_2$composites by XRD revealed $\alpha$-SiC(6H), $TiB_2$, and $YAG(Al_5Y_3O_{12})4 crystal phase. The relative density of SiC+39vol.%$TiB_2$ composites was increased with increased $Al_2O_3+Y_2O_3$. contents. The fracture toughness showed the highest value of $7.8 MPa.m^{1/2}$ for composites added with 12 wt % $Al_2O_3+Y_2O_3$. additives at room temperature. The electrical resistivity and the resistance temperature coefficient showed the lowest value of $7.3\times10_{-4}\Omega.cm\; and\; 3.8\times10_{-3}/^{\circ}C$ for composite added with 12 wt% $Al_2O_3+Y_2O_3$. additives at room temperature. The electrical resistivity of the SiC+39vol.%$TiB_2$composites was all positive temperature coefficient resistance(PTCR) in the temperature ranges from $25^{\circ}C\; to\; 700^{\circ}C$.

• Journal of the Korean Magnetics Society
• /
• v.6 no.4
• /
• pp.204-210
• /
• 1996

M type hexa-ferrites were prepared by means of a solid state reaction using mill scale, $Fe_{2}O_{3}$, and the mixture of mill scale and $Fe_{2}O_{3}$. The mixture of powders were calcined at $1150^{\circ}C$ for 2 hrs. and sintered at $1250^{\circ}C$ for 2 hrs, with varing the mole ratio of $Fe_{2}O_{3}$/$BaCO_{3}$, by 5.2~6.0. And the magnetic properties and morphologies of Baferrites with impurities such as $SiO_{2},\;Al_{2}O_{3},\;MgO,\;CaO\;and\;Na_{2}O$ in the mill scale were investigated. The magnetic properties were worsened by the addition of $Na_{2}O because of non-reacted iron oxide and intermediate compound of $BaFe_{2}O_{4}$ but they were improved apparently by the addition of $Si_{2}$ and $Al_{2}O_{3}$ in the composition of $BaO.5.6Fe_{2}O_{3}$. Moreover, $M_{s}$ decreased but $_{B}H_{C}$ increased through the addition of $Al_{2}O_{3}$ in Ba-ferrite. ${(BH)}_{max}$ of sintered BM($BaCO_{3}$, mill scale mixture) and BFM($BaCO_{3}$, $Fe_{2}O_{3}$, and null scale mixture) were 0.86 and 1.04 MGOe, respectively, and the magnetic properties were changed around $440^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.37 no.3
• /
• pp.211-218
• /
• 2000

The attrition-milled powder mixtures of Al and Al2O3 were oxidized below 140$0^{\circ}C$ for 1 hr and post-sintered at 150$0^{\circ}C$ and 1$600^{\circ}C$ for 2 hr. During attrition milling, ZrO2 was added to the system by grinding effect of ZrO2 balls. The average particle size of the powder mixtures was decreased by the attrition milling as the aluminum content decrease. Above 120$0^{\circ}C$, sintering behaviro was observed on the fine Al2O3 particles resulted from the oxidation of Al. The specimens heat-treated at 140$0^{\circ}C$ for 1 hr showed the bending strength of 166 MPa and hardness of 220 MPa. The specimens post-sintered at 1$600^{\circ}C$ for 2hr had a linear shrinkage of 9~12% and a relative density of about 95%. After the post-sintering, the specimens having 55 vol% Al content revealed the bending strength of 513 MPa and hardness of 718 MPa. The Weibull modulus to the bending strength was about 16.

• Journal of the Korean Ceramic Society
• /
• v.26 no.3
• /
• pp.347-360
• /
• 1989

Spinel, mullite, forsterite and cordierite composition powders were synthesized from Mg(NO3)2.6H2O, Al(NO3)3.9H2O and SiCl4-ethanol solution by spray pyrolysis method and the sinterability of these powders were investigated. The bulk density of spinel and mullite specimens sintered at 1,$700^{\circ}C$ for 1hr was 3.56g/㎤(99.5% relative density) and 3.16g/㎤(99.7% relative density), respectively. (Green compacts were made from powders prepared at 1,00$0^{\circ}C$). The bulk density of forsterite and cordierite specimens sintered at 1,480 and 1,40$0^{\circ}C$ for 2hrs were 3.217 and 2.155g/㎤, respectively. (Green compacts were made from powders prepared at 1,00$0^{\circ}C$). The constituent compositions of spinel and mullite specimens sintered at 1,$700^{\circ}C$ for 1hr were 27.5wt% MgO and 70.5wt% Al2O3, respectively. Vickers microhardness and fracture toughness of spinel sintered at the above condition were 13.7GPa and 2.6MN.m3/2, respectively, and room temperature bending strength, 425MPa, was nearly maintained even at the elevated temperature. In the case ofmullite specimens, those values were 13.5GPa, 2.2MN/m3/2 and 430MPa, respectively.

• Journal of the Korean Ceramic Society
• /
• v.37 no.2
• /
• pp.122-127
• /
• 2000

The thermal expansion, thermal stability, mechanical strength and infrared radiative property of Al2TiO5-clay composites, prepared from synthesized Al2TiO5 and clay, were investigated to develop a material for far infrared radiators. The emittance of composites containing 10~50 wt% clay, heated at 1,20$0^{\circ}C$ for 3 h, increased with increasing clay content and emittance was about 0.3 and 0.92 in the ranges of 3,400~2,500 cm-1 and 2,500~400cm-1, respectively. The bulk density and bending strength of the Al2TiO5-clay composites increased with increasing clay content. 50 wt% Al2TiO5-50 wt% clay composite, heat-treated at 1,20$0^{\circ}C$, had an adequate strength for infrared radiators; 80 MPa. The degree of thermal expansion hysteresis decreased with increasing clay content and the mean thermal expansion coefficient increased with increasing clay content. The thermal expansion coefficient of 50 wt% Al2TiO5-50 wt% clay composite heated at 1,20$0^{\circ}C$ was 5.78$\times$10-6/$^{\circ}C$.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.50 no.11
• /
• pp.550-554
• /
• 2001

$(Ba_{0.6}Sr_{0.4}Ca_x)TiO_3 + yAl_2O_3$ wt% (x=0.10, 0.15, 0.20, y=0~3.0) ceramics were fabricated by the mixed-oxide method, and their structural and dielectric properties were investigated with variation of composition ratio and $Al_2O_3$ doping content. As results of the X-ray diffraction and microstructure analysis, all BSCT specimens showed dense and homogeneous structure without presence of the second phase. The sintered density was decreased with an increase of $Al_2O_3$ doping content. The Curie temperature and relative dielectric constant at room temperature were decreased with increasing $Al_2O_3$doping content. The dielectric loss is minimum at BSCT doped with 1.5wt% $Al_2O_3$content. The tunability was decreased with increasing an Ca content and the BSCT(50/40/10) specimen doped with 2.0wt% $Al_2O_3$content showed the maximum value of 4.2%.

• Korean Journal of Materials Research
• /
• v.25 no.5
• /
• pp.233-237
• /
• 2015

Silicon oxynitride that can be deposited two times faster than general SiNx:H layer was applied to fabricate the passivation protection layer of atomic layer deposition (ALD) $Al_2O_3$. The protection layer is deposited by plasma-enhanced chemical vapor deposition to protect $Al_2O_3$ passivation layer from a high temperature metallization process for contact firing in screen-printed silicon solar cell. In this study, we studied passivation performance of ALD $Al_2O_3$ film as functions of process temperature and RF plasma effect in plasma-enhanced chemical vapor deposition system. $Al_2O_3$/SiON stacks coated at $400^{\circ}C$ showed higher lifetime values in the as-stacked state. In contrast, a high quality $Al_2O_3$/SiON stack was obtained with a plasma power of 400 W and a capping-deposition temperature of $200^{\circ}C$ after the firing process. The best lifetime was achieved with stack films fired at $850^{\circ}C$. These results demonstrated the potential of the $Al_2O_3/SiON$ passivated layer for crystalline silicon solar cells.