• Journal of Welding and Joining
• /
• v.29 no.4
• /
• pp.85-92
• /
• 2011

Microstructures and tensile properties in arc brazed joints of ferritic stainless steel, 429EM using Cu-8.6%Al insert metal was investigated as function of brazing current. The brazing speed was fixed at 800mm/min and brazing current varied in the range of 80A to 120A. The initial phase of filler metal was Cu single phase. However, the insert metal structures of brazed joints was composed of Cu matrix and intermetallic compound such as ${\gamma}_1(Al_4Cu_9)$, and flower-shape Fe-Cr. The fraction of ${\gamma}_1(Al_4Cu_9)$ phase was similar with 80A and 100A brazing currents while that of brazed with 120A was decreased. On the other hand, the fraction of Fe-Cr phase increased with increasing of the brazing current. A reaction layer at the base metal/insert metal interface was observed and this reaction layer was thickened with increasing of the brazing current. In the brazed joints with the current lower than 100A, crack was grew up along the interface which was perpendicular to the tensile stress, and then, passed through the insert metal in the final stage of fracture. As the brazing current increased to 120A, fracture occurred at the base metal.

• Journal of Powder Materials
• /
• v.13 no.1 s.54
• /
• pp.18-24
• /
• 2006

The brazing adhesion properties of Ag coated W-Ag electric contact on the Cu substrate have been investigated in therms of microstructure, phase equilibrium and adhesion strength. Precoating of Ag layer ($3{\mu}m$ in thickness) on the $W-40\%Ag$ contact material was done by electro-plating method. Subsequently the brazing treatment was conducted by inserting BCuP-5 filler metal (Ag-Cu-P alloy) layer between Ag coated W-Ag and Cu substrate and annealing at $710^{\circ}C$ in $H_2$ atmosphere. The optimum brazing temperature of $710^{\circ}C$ was semi-empirically calculated on the basis of the Cu atomic diffusion profile in Ag layer of commercial electric contact produced by the same brazing process. As a mechanical test of the electric contact after brazing treatment the adhesion strength between the electric contact and Cu substrate was measured using Instron. The microstructure and phase equilibrium study revealed that the sound interlayer structure was formed by relatively low brazing treatment at $710^{\circ}C$. Thin Ag electro-plated layer precoated on the electric contact ($3{\mu}m$ in thickness) is thought to be enough for high adhesion strength arid sound microstructure in interface layer.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.7 no.2
• /
• pp.113-119
• /
• 2006

Brazing is an important manufacturing process in the fabrication of Heavy Water Reactor fuel rods, in which bearing and spacer pads are joined to Zircaloy-4 cladding tubes. The physical vapor deposition(PVD) technique is currently used to deposit metallic Be on the surfaces of pads as a filler metal. Amorphous Zr-Be binary alloys which are manufactured by rapid solidification process are under developing to substitute the conventional PVD-Be coating. In the present study, brazed joint with PVD and amorphous alloys of $Zr_{1-x}Be_{x}(0.3{\le}x{\le}0.5)$ as filler metals are compared by mechanism, microstructure and hardness. The thickness of brazed joint with amorphous alloys became much smaller than that of PVD-Be. The erosion of base metal did not occur in the brazed joint with amorphous alloys. The brazing mechanism for PVD-Be seems to be Be diffusion into Zr-4 with capillary action resulting from eutectic reaction while that for amorphous alloys are associated with the liquid phase formation in the brazed joint. The brazed joint microstructure with PVD-Be consists of dendrite while that with amorphous alloys is globular. The $Zr_{0.7}Be_{0.3}$ alloy shows the smooth interface with little erosion in the base metal and is recommended a most suitable brazing filler metal for Zircaloy-4.

• Journal of Welding and Joining
• /
• v.17 no.4
• /
• pp.26-31
• /
• 1999

An attempt was made in this study to investigate the brazing characteristics of Zr-Be binary amorphous alloys for the development of a new brazing filler metal for joining Zircaloy-4 nuclear fuel cladding tubes. This study was also aimed at the feasibility study of rapidly solidified amorphous alloys to substitute the conventional physical vapor-deposited(PVD) metallic beryllium. The $Zr_{1-x}Be_{x}$($0.3\leq$x$\leq0.5$) binary amorphous alloys were produced in the ribbon form by the melt-spinning method. It was confirmed by x-ray diffraction that the ribbons were amorphous. The amorphous. the amorphous alloys were used to join bearing pads on Zircaloy-4 nuclear fuel cladding tubes. Using Zr-Be amorphous alloys as filler metals, it was found that the reduction in the tube wall thickness caused by erosion was prevented. Especially, in the case of using $Zr_{0.65}Be_{0.35}$ and $Zr_{0.7}Be_{0.3}$ amorphousalloys, the smooth and spherical primary $\alpha$-Zr particles appeared in the brazed layer, which was the most desirable microstructure from the corrosion-resistance standpoint.

• Journal of the Korean Society for Heat Treatment
• /
• v.29 no.1
• /
• pp.1-7
• /
• 2016

Titanium and its alloys can be usually joined with brazing method. And the alloys should be brazed at low temperature to keep their original microstructure. In this study, the mechanical strength and microstructure of the CP-Ti joint-brazed with $Zr_{54}Ti_{22}Ni_{16}Cu_8$ filler metal having melting temperature of $774{\sim}783^{\circ}C$ were investigated. The tensile strengths of the joint-brazed at $800^{\circ}C$ with $100^{\circ}C/min$ of cooling rate showed more than 400 MPa which was as high as base metal. The $Widmanst{\ddot{a}}tten$ structure consisting of Ti and $Ti_2Ni$ phase was observed in the joint area. However, the tensile strengths of the joint-brazed at $800^{\circ}C$ with $15^{\circ}C/min$ of cooling rate were decreased and the Ti, $(Ti,Zr)_2Ni$ and $Ti_2Ni$ phases were observed at the joint area. It is believed that the $(Ti,Zr)_2Ni$ laves phases could decrease the mechanical strength of the joint and the cooling rate should be controled to get high strength of the titanium joint.

• Journal of Welding and Joining
• /
• v.12 no.3
• /
• pp.48-55
• /
• 1994

In this experiment, to find optimum brazing conditions for Cu/Stainless Steel brazing using filler metals of Ag-Cu-Zn-Cd system, first of all spreading ratio was tested on 304 stainless Steel and low carbon steel. And then shear test of brazed joint was executed. As the result of that, the shear strengths of brazed joints were the range of 60-90 MPa. Through microstructure analysis for brazed interface layer, We found as follows. Firstly interface layer increased as time increased. Secondly continuous layer of Ag-Cd compound was observed along the side of stainless steel. Also by means of EDS analysis for fracture surface, ductile fracture was occurred and precipitates on the fracture surface were found to include Cr, Mn, Si in Ag-rich phase.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2006.05a
• /
• pp.23-27
• /
• 2006

Brazing Failure has been occurred in the process of thrust chamber assembly. The possible factors have been analyzed by sample tests. The actual causes of 'Overflow' phenomenon have been investigated horn Brazing Material and fabrication of Piece Parts. The rejection rate of process has been improved by appling this results to a real brazing process.

• Korean Journal of Materials Research
• /
• v.15 no.6
• /
• pp.399-407
• /
• 2005

The effect of IN738 additive powder on microstructure and mechanical properties of the wide-gap region brazed with BNi-3 filler metal powder was investigated. The wide-gap brazing was conducted in a vacuum of $2\times10^{-5}torr\;at\;1200^{\circ}C$ with various powder mixing ratios of additive to filler powders. The microstructures of the wide-gap brazed region were analyzed by SEM and AES. The region brazed with only BNi-3 filler metal powder had a microstructure consisted of proeutectic, binary eutectic and ternary eutectic structure, while that brazed with a mixture of IN738 additive powder and BNi-3 filler metal powder had a microstructure consisted of IN738 additive powder, binary eutectic of $Ni_3B-Ni$ solid solution and (Cr, W)B. The fracture strength of the wide-gap brazed region was about 680 MPa regardless of the additive powder mixing ratios. Cracks were initiated at the (Cr, W)B and binary eutectic of $Ni_3B-Ni$ solid solution, and propagated through them in the wide-gap brazed region, which lowered the fracture strength of the region.

• Journal of the Korean Ceramic Society
• /
• v.55 no.5
• /
• pp.492-497
• /
• 2018

This paper reports the efficacy of tape casting using an Ag-10 wt% CuO filler for the successful joining of a sintered $Ce_{0.9}Gd_{0.1}O_{2-{\delta}}-La_{0.7}Sr_{0.3}MnO_{3{\pm}{\delta}}$ (GDC-LSM) ceramic with a SUS 460 FC metal alloy by reactive air brazing. The as-prepared green tape was highly flexible without drying cracks, and the handling was easy when used as a filler material for reactive air brazing. Heat treatment for the GDC-LSM/SUS 460 FC joint was performed at $1050^{\circ}C$ for 30 min in air. Microstructural observations indicated a reliable and compact joining. The room temperature mechanical shear strength of the as-brazed joints was $60{\pm}8MPa$ with a cohesive failure. The flexural strength of joints was measured from room temperature up to $850^{\circ}C$, where the strength retention revealed to be almost 100% at $500^{\circ}C$. However, the joints showed a degradation in strengths at 800 and $850^{\circ}C$, exhibiting strength retentions of 57% and 37%, respectively.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2005.05a
• /
• pp.91-91
• /
• 2005