• Journal of the Korea Institute of Building Construction
• /
• v.18 no.6
• /
• pp.527-532
• /
• 2018

The objective of the present study is to evaluate a practical approach for enhancing the compressive strength and minimizing deforming of aerated concrete. Test results measured in the aerated concrete mixes that were produced using 40% ground granulated blast-furnace slag (GGBS) as a replacement of cement and cured under different conditions (i.e., high temperatures of $40^{\circ}C$ and $60^{\circ}C$ for 10 hrs or 15 hrs) were compared with those obtained from the specimens cured under room temperature. No deforming was observed in the mixes with 40% GGBS. The compressive strength of the prepared aerated concrete cured under high temperature was higher than that of the concrete cured at room temperature, even at the lower ranges of the apparent dry density. However, the curing time is needed to be controlled as not exceeding 10 hrs at the temperature of $60^{\circ}C$ to prevent the decrease in the compressive strength due to foam mergences.

• Journal of the Korea Concrete Institute
• /
• v.27 no.2
• /
• pp.177-184
• /
• 2015

In order to use the high-volume slag cement as a construction materials, a proper activator which can improve the latent hydraulic reactivity is required. The dissolved aluminum silicon ions from ground granulated blast furnace slag (GGBFS) react with sulfate ions to form ettringite. The proper formation of ettringite can increase the early-age strength of high-volume GGBFS (80%) cement. The aim of this study is to investigate the hydration properties with sulfate activators (sodium sulfate, anhydrite). In this paper, the effects of $Na_2SO_4$ and $CaSO_4$ on setting, compressive strength, hydration, micro-structure were investigated in high-volume GGBFS cement and compared with those of without activator. Test results indicate that equivalent $SO_3$ content of 3~5% improve the early-age hydration properties such as compressive strength, heat evolution rate, micro-pore structure in high-volume GGBFS cement.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.2
• /
• pp.103-111
• /
• 2011

This study examined rheological properties of blast furnace slag and ash paste that are widely used as cement concrete for mineral admixture in current. In that way rheological properties of the paste of mineral admixture only was examined. The result of this study were as follow: In order to analyze that the rheological properties of the mineral admixture only, fine particles were produced with grinding machine to 3 particle sizes. These powders in general from the result of comparison with and analysis of rheological properties and the coefficient n and De values. The result that ash powder was higher in plastic viscosity and yield stress than Slag powder, and with the same n value, ash powder showed higher plastic viscosity and yield stress than Slag powder. But Slag powder in particle size distribution showed a sensitive tendency on changing in rheological properties.

• Journal of the Korean Geotechnical Society
• /
• v.31 no.1
• /
• pp.37-46
• /
• 2015

In this study, a blast furnace slag with the alkaliphilic microorganism (Bacillus halodurans) alkaline activator was used to cement natural soils in the field. A low-cost and massive microbial solution for cementation of field soils was produced and compared with existing microbial culture in terms of efficiency. A field soil was prepared for three different cementation areas: a cemented ground with microbial alkaline activator (Microbially-treated soil), a cemented ground with ordinary Portland cement (Cement-treated soil), and untreated ground (Non-treated soil). The testing ground was prepared at a size of 2.6 m in width, 4 m in length, and 0.2 m in depth. After 28 days, a series of unconfined compression tests on the cement-treated and microbially-treated soils were carried out. On the other hand, a torvane test was carried out for non-treated soil. The strength of field soils treated with microorganism was 1/5 times lower than those of cement-treated soil but is 6 times higher than non-treated soil. The pH measured from microbially-treated soil was about 10, which is lower than that of cement-treated soil (pH = 11). Therefore, it is more eco-friendly than Portland cemented soils. The C-S-H hydrates were found in both cement- and microbially-treated soils through SEM-EDS analyses and cement hydrates were also found around soil particles through SEM analysis.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2013.05a
• /
• pp.37-38
• /
• 2013

The fine powder obtained from the manufacturing process of recycled coarse aggregate contains unhydareted cement particles on their surface. It is believed that the alkalinity of the powder (11.0-12.5) is enough to active the slag-based composites. In this paper, the obtained powder was sieved and divided into two sizes, i.e., 0.08 mm and 0.3 mm, and added to the slag-based mortar. Results showed that the fine powder had an effect on the slump and the compressive strength of slag-based composites. With the different pH values of the powder, it could be seen that the distance between the two level powders. And found the peak 28 days compressive strength as the replacement ratio of the recycled aggregate powder changed. The findings from this study provide an indication that with achieved compressive strength, the fine powder can be used in a light weight concrete.

• Journal of the Korea Concrete Institute
• /
• v.16 no.5 s.83
• /
• pp.621-626
• /
• 2004

The use of blast-furnace slag (BFS) in making not only normal concrete but also high-performance concrete has several advantages with respect to workability, long-term strength and durability. However, slag concrete tends to show more shrinkage than normal concrete, especially autogenous shrinkage. High autogenous shrinkage would result in severe cracking if they are not controlled properly. Therefore, in order to minimize the shrinkage stress and to ensure the service life of concrete structures, the autogenous shrinkage behavior of concrete containing BFS should be understood. In this study, small prisms made of concrete with water-binder (cement+BFS) ratio (W/B) ranging from 0.27 to 0.42 and BFS replacement level of $0\%$, $30\%$, and $50\%$, were prepared to measure the autogenous shrinkage. Based on the test results, thereafter, material constants in autogenous shrinkage prediction model were determined. In particular, an effective autogenous shrinkage defined as the shrinkage that contributes to the stress development was introduced. Moreover, an estimation formula of the 28-day effective autogenous shrinkage was proposed by considering various W/B's. Test results showed that autogenous shrinkage increased with replacement level of BFS at the same W/B. Interestingly, the increase of autogenous shrinkage is dependent on the W/B at the same content of BFS; the lower W/B, the smaller increasing rate. In concluding, it is necessary to use the combination of other mineral admixtures such as shrinkage reducing admixture or to perform sufficient moisture curing on the construction site in order to reduce the autogenous shrinkage of BFS concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.6
• /
• pp.74-82
• /
• 2017

This research presents the results of the strength and drying shrinkage properties to study the effect of ground granulated blast furnace slag(GGBFS), fly ash(FA) and calcium sulfoaluminate(CSA) for activated ternary blended slag cement. The activated ternary blended cement(ATBC) mortar were prepared having a constant water-cementitious materials ratios of 0.4. The GGBFS contents ratios of 100%, 80%, 70% and 60%, FA replacement ratios of 10%, 20%, 30% and 40%, CSA ratios of 0%, 10%, 20% and 30% were designed. The superplasticizer of polycarboxylate type were used. The activator was used of 10% sodium hydroxide(NaOH) + 10% sodium silicate($Na_2SiO_3$) by weight of binder. Test were conducted for mini slump, setting time, V-funnel, water absorption, compressive strength and drying shrinkage. According to the experimental results, the contents of superplasticizer, V-funnel and compressive strength increases with an increase in CSA contents for all mixtures. Moreover, the setting time, water absorption ratios and drying shrinkage ratio decrease with and increase in CSA. One of the major reason for the increase of strength and decrease of drying shrinkage is the accelerated reactivity of GGBFS with alkali activator and CSA. The CSA contents is the main parameter to explain the strength development and decreased drying shrinkage in the ATBC.

• International Journal of Concrete Structures and Materials
• /
• v.8 no.1
• /
• pp.69-81
• /
• 2014

In this study, portland cement (PC) has been partially replaced with a Class F fly ash (FA) at level of 70 % to produce high-volume FA (HVFA) concrete (F70). F70 was modified by replacing FA at levels of 10 and 20 % with silica fume (SF) and ground granulated blast-furnace slag (GGBS) and their equally combinations. All HVFA concrete types were compared to PC concrete. After curing for 7, 28, 90 and 180 days the specimens were tested in compression and abrasion. The various decomposition phases formed were identified using X-ray diffraction. The morphology of the formed hydrates was studied using scanning electron microscopy. The results indicated higher abrasion resistance of HVFA concrete blended with either SF or equally combinations of SF and GGBS, whilst lower abrasion resistance was noted in HVFA blended with GGBS.

• Computers and Concrete
• /
• v.13 no.5
• /
• pp.621-632
• /
• 2014

This paper is aimed at adapting Artificial Neural Networks (ANN) to predict the compressive strength of High Performance Concrete (HPC) containing binary and quaternary blends. The investigations were done on 23 HPC mixes, and specimens were cast and tested after 7, 28 and 56 days curing. The obtained experimental datas of 7, 28 and 56 days are trained using ANN which consists of eight input parameters like cement, metakaolin, blast furnace slag and fly ash, fine aggregate, coarse aggregate, superplasticizer and water binder ratio. The corresponding output parameters are 7, 28 and 56 days compressive strengths. The predicted values obtained using ANN show a good correlation between the Experimental data. The performance of the 8-9-3-3 architecture was better than other architectures. It concluded that ANN tool is convenient and time saving for predicting compressive strength at different ages.

• Journal of the Korea Concrete Institute
• /
• v.25 no.3
• /
• pp.305-312
• /
• 2013

This paper reports the results of an investigation into the effects of silica fume on strength properties of alkali-activated slag cement (AASC) with water-binder (W/B) ratio and replacement ratio of silica fume content. The W/B ratio varied between 0.50 and 0.60 at a constant increment of 0.05. The silica fume content varied from 0% to 50% by weight of slag. The activators was used sodium hydroxide (NaOH) and the dosage of activator was 3M. The strength development with W/B ratio has been studied at different ages of 1, 3, 7 and 28 days. For mixes of AASC mortars with varying silica fume content, the flow values were lower than the control mixes (without silica fume). The flow value was decrease as the content of silica fume increase. This is because the higher surface areas of silica fume particles increase the water requirement. The analysis of these results indicates that, increasing the silica fume content in AASC mortar also increased the compressive strength. Moreover, the strength decreases with the W/B ratios increases. This is because the particle sizes of silica fume are smaller than slag. The high compressive strength of blended slag-silica fume mortars was due to both the filler effect and the activated reaction of silica fume evidently giving the mortar matrix a denser microstructure, thereby resulting in a significant gain in strength.