• 한국반도체및디스플레이장비학회:학술대회논문집
• /
• 한국반도체및디스플레이장비학회 2006년도 춘계학술대회
• /
• pp.190-193
• /
• 2006

Gadolinium-substituted bismuth titanate, $Bi_{3.3}Gd_{0.7}Ti_{3}O_{12}$, thin films were successfully fabricated on Pt(111)/Ti/$SiO_2$/Si(100) substrates by a MOCVD process. Fabricated BGT thin films were found to be random oriental ions, which were confirmed by X-ray diffraction and scanning electron microscope analysis. The remanent polarization value ($2P_r$) of the BGT thin film annealed at $720^{\circ}C$ was $45.13{\mu}C/cm^2$, at an applied voltage of 5 V. The BGT thin film exhibits a good fatigue resistance up to $1{\times}10^{11}$ switching cycles at a frequency of 1 MHz with applied voltage of 5 V. These results indicate that the randomly oriented BGT thin film is a promising candidate among ferroelectric materials useful in lead-free nonvolatile ferroelectric random access memory applications.

• 한국표면공학회지
• /
• 제25권2호
• /
• pp.82-89
• /
• 1992

The effect of interlayer coating of Ni and Ti on corrosion behavior was studied in TiN ion plated steel plate. Interlayer coating was carried out in a single and bi-layer to a various thickness combination prior to final TiN coating of $2\mu\textrm{m}$. Corrosion behavior was evaluated by anodic polarization test in 1N H2SO4 as well as salt spray test. Porosity of each coating was also tested by using SO2 test. Corrosion resistance was improved with increasing the thickness of Ni interlayer coating and Ni-Ti interlayer coating markedly enhanced the corrosion resistance. Ni/Ti interlayer coating of $2\mu\textrm{m}$/2$\mu\textrm{m}$ prior to $2\mu\textrm{m}$ TiN coating decreased the corrosion current density of active range by an order of 4 and that of passive range by an order of 1. This improvement was associated with the retardation of corrosive agent penetration with increasing coating thickness and inherent corrosion resistance of Ni and Ti interlayers, Ni/Ti interlayers coating were also very effective in improvement of corrosion resistance under salt atmosphere.

• 한국표면공학회지
• /
• 제26권2호
• /
• pp.55-62
• /
• 1993

The effect of interlayer coating thickness of Ni and Ti on corrosion behavior was studied for TiN ion plat-ed steel plate. Interlayer coating was carried out in a single and bi-layer to a various thickness combination prior to final TiN coating. Corrosion behavior was evaluated by anodic polarization test in 1N H2SO4 as well as salt spray test. Ni interlayer coating was effectived in reducing corrosion current density of active region and Ti interlayer coating over Ni coating reduced the anodic corrosion current density by an order of 4 with increasing the thickness of Ti up to$ 3\mu\textrm{m}$. The improvement of corrosion resistance by Ni/Ti interlayer coating was attributed to the effective prevention of penetration of active corrosion agent resulting from the inherent corrosion resistance of Ni and Ti. Putting corrosion behavior was observed from salt spray test result for all specimens and corrosion resistance at salt atmosphere was enhanced with increasing Ni and Ti thickness, Cor-lay TiN coating was spalled out by the generation of corrosion products.

• 한국전기전자재료학회논문지
• /
• 제14권9호
• /
• pp.731-735
• /
• 2001

S $r_{0.89}$B $i_{2.4}$T $a_2$ $O_{9}$ (SBT) thin films are deposited on Pt-coated electrode(Pt/Ti $O_2$/ $SiO_2$/Si) using RF magnetron sputtering method. In the XRD pattern, the SBT thin films had (105) orientation. As annealing temperature was increased from $600^{\circ}C$ to 85$0^{\circ}C$, the intensities of peak were increased. In the SEM images, Bi-layered perovskite phase was crystallized above $650^{\circ}C$ and rod-like grains grew above 75$0^{\circ}C$. The maximum remanent polarization and the coercive electric field at annealing temperature of 75$0^{\circ}C$ are 11.60$\mu$C/$\textrm{cm}^2$ and 48kV/cm respectively. The dielectric constant and leakage current density at annealing temperature of 75$0^{\circ}C$ are 213 and 1.01x10$^{-8}$ A/$\textrm{cm}^2$, respectively. The fatigue characteristics of SBT thin filmsdid not change up to 10$^{10}$ switching cycles.s.s.

• 한국전기전자재료학회논문지
• /
• 제28권10호
• /
• pp.615-619
• /
• 2015

In this study, in order to develop the composition ceramics with the excellent electrocaloric properties, 8/65/35 PLZT ceramics were fabricated by the conventional solid-state method with the addition of $Bi_2O_3$, CuO, $Li_2CO_3$ and the variation of sintering temperature from $930^{\circ}C$ to $990^{\circ}C$. The XRD pattern of all specimens indicated general perovskite structure and the rhombohedral phase were observed. Curie temperature ($T_c$) of all specimens was observed in the vicinity of about $190^{\circ}C$. Density, coercive field and remnant polarization of the specimen sintered at $950^{\circ}C$ was $7.55g/cm^3$, 8.895 kV/cm, $11.22{\mu}C/cm^2$, respectively. EC effect of PLZT ceramics was measured by indirect method and the temperature change ${\Delta}T$ due to the electrocaloric effect was calculated by Maxwell's relations. ${\Delta}T$ of ceramic sintered at $950^{\circ}C$ was $0.21^{\circ}C$ under application of 40 kV/cm at $190^{\circ}C$.

• 한국진공학회지
• /
• 제8권3A호
• /
• pp.238-244
• /
• 1999

Pt/SBT/Pt capacitors were fabricated using the MOD-derived $SrBi_{2x}Ta_2O_9$ (SBT) films and their ferroelectic and leakage current characteristics were investigated with post annealing at 400~$800^{\circ}C$. Although the MOD-derived SBT film exhibited the hysteresis loop typical for the leaky film, the well-saturated ferroelectric hysteresis loop could be obtained by post annealing the Pt/SBT/Pt capacitors at $550^{\circ}C$~$800^{\circ}C$. The remanent polarization $2P_r$ of the SBT film exhibited a maximum value of 9.72$\mu\textrm{cm}^2$ with post annealing at $600^{\circ}C$, and then decreased with increasing the post annealing temperature above $600^{\circ}C$. The MOD-derived SBT films exhibited the high leakage current density of ~$10^{-3} \textrm{A/cm}^2$ at 75kV/cm. With post annealing the Pt/SBT/Pt capacitor at 600~$800^{\circ}C$, however, the leakage current density decreased remarkably to less than $10^{-6}\textrm{A/cm}^2$ at 75kV/cm.

• Corrosion Science and Technology
• /
• 제20권5호
• /
• pp.315-323
• /
• 2021

In this study, we examined corrosion behaviors of two types of Pb alloys for a lead acid battery comparatively. One containing 6.6 wt% Sn, 36 mg/kg Bi, and 612.4 mg/kg Ca was prepared by twin-roll continuous casting. The other containing 5.2 wt% Sn, 30.5 mg/kg Ag, and 557 mg/kg Ca was made by twin-belt continuous casting. Potentiodynamic polarization tests were performed to evaluate corrosion resistance. Cyclic voltammetry was done to examine oxidation and reduction reactions occurring on the surface of each alloy in 4.8 M H₂SO₄ solution. Electrochemical test results implied that the Pb alloy prepared with the twin-belt casting method was less stable than that cast with the twin-roll method. Such results might be due to precipitations formed during the casting process. Rolling did not appear to affect the corrosion behavior of the twin-roll samples with Ag < 10 mg/kg, while it reduced the anodic reaction of Ag on the surface of the twin-belt sample with 30.5 mg/kg Ag.

• 한국전기전자재료학회논문지
• /
• 제17권1호
• /
• pp.7-15
• /
• 2004

The ferroelectric SBT thin films as a material of capacitors for non-volatile FRAMs have some problems that its remanent polarization value is relatively low and the crystallization temperature is quite high abovc 80$0^{\circ}C$. Therefore, in this paper, SBTN solution with S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$N $b_{0.2}$$O_{9}$ composition was synthesized by sol-gel method. Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$and Nb(O $C_2$ $H_{5}$)$_{5}$ were used as precursors, which were dissolved in 2-methoxyethanol. SBTN thin films with 200 nm thickness were deposited on Pt/Ti $O_2$/ $SiO_2$/Si substrates by spin-coating. UV-irradiation in a power of 200 W for 10 min and rapid thermal annealing in a 5-Torr-oxygen ambient at 76$0^{\circ}C$ for 60 sec were used to promote crystallization. The films were well crystallized and fine-grained after annealing at $650^{\circ}C$ in oxygen ambient. The electrical characteristics of 2Pr=11.94 $\mu$C/$\textrm{cm}^2$, Ps＋/Pr＋=0.54 at the applied voltage of 5 V were obtained for a 200-nm-thick SBTN films. This results show that 2Pr values of the UV irradiated and rapid thermal annealed SBTN thin films at the applied voltage of 5 V were about 57% higher than those of no additional processed SBTN thin films. thin films.lms.s.s.

• 한국전기전자재료학회논문지
• /
• 제35권1호
• /
• pp.24-31
• /
• 2022

This study investigated microstructures, crystal structures, polarization, dielectric and electromechanical properties of 0.76Bi_1/2Na_1/2TiO₃-0.24SrTiO₃ (BNT-24ST)-based piezoceramcs by adding Li₂CO₃ and B₂O₃ (LB) as sintering aids for low-temperature sintering. All samples were successfully synthesized using conventional solid-state reaction method and sintered at 950, 1,000, 1,050, 1,100 and 1,175℃ for 2 hours. Without LB, specimens required sintering temperatures over 1,175℃ for sufficient densification, while the addition of 0.10-mol LB decreased the sintering temperatures down to 950℃. The average grain size and dielectric properties of BNT-24ST-10LB ceramics were enhanced with increasing sintering temperature. We found that the low-temperature sintered BNT-24ST piezoceramics by adding LB showed the d₃₃*value of 402 pm/V at 4 kV/mm after sintering at 1,050℃, which was better than that of high-temperature fired specimens sintered at 1,175℃ without LB (242 pm/V). We believe that the results of this study promise a candidate for low-cost multilayer ceramic actuator applications.

• 한국전자파학회논문지
• /
• 제17권5호
• /
• pp.461-475
• /
• 2006

본 논문은 Ka/K 통신 대역 및 Ku 방송 대역에서 동작하는 무궁화 3호 정지 궤도 위성을 이용하여 화상 전화, 인터넷과 같은 위성 멀티미디어 및 방송 서비스를 제공하는 이동체 탑재형 안테나 시스템 설계에 관한 것이다. 앙각 방향으로 팬 빔 특성을 갖는 안테나 시스템의 방사부는 준-오프셋 이중 성형 반사판과 삼중 대역 급전기로 구성된다. 또한, 삼중 대역 급전기는 돌출 유전체 막대를 이용한 Ka/K 이중 대역 급전기 및 원형 편파기, 직교 모드 변환기 그리고 Ku 대역 원형 편파 급전 배열로 구성된다. 특히, Ka/K 이중 대역 원형 편파기는 제작이 용이한 comb 구조를 사용하여 구현되었다. Ku 대역 급전 배열은 이동시 위성을 고속으로 추적하기 위하여 전자 빔을 형성할 수 있는 $2{\times}2$ 능동 위상 배열 구조를 갖는다. 그리고, 급전 배열에서 $90^{\circ}$ 하이브리드 결합기를 이용하여 원형 편파를 생성하는 4개의 방사 소자들을 $90^{\circ}$씩 회전하여 배열함으로써 원형 편파 특성을 개선하였다. Ku 대역 전자 빔을 생성하는 4개의 빔 성형 채널은 출력에서 주 빔 채널 및 추적 빔 채널로 구분되며, 각 채널의 내부 구성 유니트들의 잡음 온도 기여도를 바탕으로 채널 잡음 온도 특성을 분석하였다. 제작된 안테나 시스템으로부터 측정된 Ka 송신 채널의 $P_{1dBc}$ 출력은 34.1 dBm 이상, K/Ku 수신 채널의 잡음 지수는 각각 2.4 dB 및 1.5 dB 이하의 전기적인 성능들을 보여주었다. 안테나 시스템은 근접 전계 측정 방법을 사용하여 삼중 대역에서의 주 편파 및 교차 편파 방사 패턴들을 측정하였다. 특히, Ku 대역의 방사 패턴 측정은 급전 배열들의 독립 여기에 의한 부분 방사 패턴들을 측정하여 각 능동 채널들의 초기 위상들을 보정한 후 이루어졌다. 안테나 시스템의 Ka/K/Ku 대역에서 측정된 안테나 이득은 각각 39.6 dBi, 37.5 dBi, 29.6 dBi 이상이었으며, 그리고 Ka 대역 송신 EIRP는 43.7 dBW 이상, K/Ku 대역 수신 감도 G/T는 각각 13.2 dB/K와 7.12 dB/K 이상의 우수한 시스템 성능들을 보여주었다.