• Journal of the Korean Wood Science and Technology
• /
• v.46 no.6
• /
• pp.726-734
• /
• 2018

In this study, for using effectively domestic (temperate) small and medium diameter logs as a wooden floorboard, cross-laminated wood panels were manufactured using domestic larch and tulip woods as a base material for teak and merbau wood flooring, and static bending strength performances were measured to investigate the applicability as the base materials of wooden flooring in place of plywood. Static bending MOE was much influenced by the strength performances of the top layer lamina than that of the laminae for base materials. Bending MOR showed the higher values in tulip wood that was hardwoods than in larch wood that was softwoods regardless of the strength performances of the top layer laminae, and it was found that the values were much influenced by the strength performances of the base materials used in the core and bottom layers. However these values were 1.4-2.5 times higher values than the bending strength of the wooden floorboards specified in KS, it was found that it can be sufficiently applied to the base materials of wooden floorboards in place of plywood.

• Earthquakes and Structures
• /
• v.11 no.6
• /
• pp.943-966
• /
• 2016

Recently, magnetorheological elastomer (MRE) material and its devices have been developed and attracted a good deal of attention for their potentials in vibration control. Among them, a highly adaptive base isolator based on MRE was designed, fabricated and tested for real-time adaptive control of base isolated structures against a suite of earthquakes. To perfectly take advantage of this new device, an accurate and robust model should be built to characterize its nonlinearity and hysteresis for its application in structural control. This paper first proposes a novel hysteresis model, in which a nonlinear hyperbolic sine function spring is used to portray the strain stiffening phenomenon and a Voigt component is incorporated in parallel to describe the solid-material behaviours. Then the fruit fly optimization algorithm (FFOA) is employed for model parameter identification using testing data of shear force, displacement and velocity obtained from different loading conditions. The relationships between model parameters and applied current are also explored to obtain a current-dependent generalized model for the control application. Based on the proposed model of MRE base isolator, a second-order sliding mode controller is designed and applied to the device to provide a real-time feedback control of smart structures. The performance of the proposed technique is evaluated in simulation through utilizing a three-storey benchmark building model under four benchmark earthquake excitations. The results verify the effectiveness of the proposed current-dependent model and corresponding controller for semi-active control of MRE base isolator incorporated smart structures.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.7
• /
• pp.513-516
• /
• 2010

In this work, a study is presented of the static characteristics of 4H-SiC DMOSFETs obtained by adjustment of the p-base region. The structure of this MOSFET was designed by the use of a device simulator (ATLAS, Silvaco.). The static characteristics of SiC DMOSFETs such as the blocking voltages, threshold voltages, on-resistances, and figures of merit were obtained as a function of variations in p-base doping concentration from $1\;{\times}\;10^{17}\;cm^{-3}$ to $5\;{\times}\;10^{17}\;cm^{-3}$ and doping depth from $0.5\;{\mu}m$ to $1.0\;{\mu}m$. It was found that the doping concentration and the depth of P-base region have a close relation with the blocking and threshold voltages. For that reason, silicon carbide DMOSFET structures with highly intensified blocking voltages with good figures of merit can be achieved by adjustment of the p-base depth and doping concentration.

• Smart Structures and Systems
• /
• v.25 no.3
• /
• pp.323-335
• /
• 2020

Magnetorheological elastomer (MRE), a smart material, is an innovative material for base isolation system. It has magnetorheological (MR) effect that can control the stiffness in real-time. In this paper, a new hybrid base isolation system combining two electromagnetic closed circuits and the roller bearing is proposed. In the proposed system, the roller part can support the vertical load. Thus, the MRE part is free from the vertical load and can exhibit the maximum MR effect. The MRE magnetic loop is constructed in the free space of the roller bearing and forms a strong magnetic field. To demonstrate the performance of the proposed hybrid base isolation system, dynamic characteristic tests and performance evaluation were carried out. Dynamic characteristic tests were performed under the extensive range of strain of the MRE and the change of the applied current. Performance evaluation was carried out using the hybrid simulation under five earthquakes (i.e., El Centro, Kobe, Hachinohe, Northridge, and Loma Prieta). Especially, semi-active fuzzy control algorithm was applied and compared with passive type. From the performance evaluation, the comparison shows that the new hybrid base isolation system using fuzzy control algorithm is superior to passive type in reducing the acceleration and displacement responses of a target structure.

• Journal of Welding and Joining
• /
• v.24 no.3
• /
• pp.49-54
• /
• 2006

The Plasma Transferred Arc (PTA) overlaying method is lately introduced as one of the most useful surface modification method of the engine component. In this paper, the characteristics of the Co-base and Ni-base super alloy overlay layers by PTA method were investigated through the metallurgical, abrasive and cavitation erosion test. Experimental results showed that the abrasive wear resistance of the Co-base Stellite 6 overlayer was the most superior and followed in order of Nimonic 80A, Inconel 625 and Inconel 718. However, the cavitation erosion characteristic of the Stellite 6 overlayer was the most inferior and it was better in order of Inconel 625, Inconel 718 and Nimonic 80A.

• The Journal of Korean Academy of Prosthodontics
• /
• v.41 no.5
• /
• pp.626-639
• /
• 2003

Statement of problem : Recently, in attempts to reinforce the acrylic resin and to reduce the polymerization shrinkage, it has been reported that adding vinyloligo-silsesquioxane (vinyl-POSS) to PMMA significantly compensates for polymerization shrinkage and somewhat increases the fracture resistance. Purpose : There haven't been any studies on abrasion that can affect the adaptation of the denture in long-term use. In this study abrasion resistance was compared between acrylic resin with vinyl-POSS and commercialized acrylic resin for denture base. In addition, the difference in abrasion resistance according to molding methods was compared. Material and method : Using PaladentR 20 including vinyl-POSS. PaladentR 20, Lucitone 199R, SR IvocapR, denture bases were fabricated using compression molding technique and continuous-pressure injection technique. Surface hardness and abrasion were measured for each group, and the worn surfaces were observed under a scanning electron microscope. Results : 1. When surface hardness was measured for each material and molding technique, there was no statistically significant difference among the materials. (p<0.05) 2. When same denture base material and molding technique were used, the abrasion due to toothpaste solution was 5 times as severe as the abrasion due to soap solution. 3, When toothpaste solution was used, the abrasion decreased in the order of PaladentR20, PaladentR 20 including vinyl-POSS, SR IvocapR, and Lucitone 199R. However statistically significant difference was seen only among PaladentR 20, SR IvocapR, and Lucitone 199R. (p<0.05). 4. When soap solution was used, the abrasion was more severe in PaladentR 20 and including vinyl-POSS PaladentR 20 groups than in SR IvocapR and Lucitone 199R groups. (p<0.05). Conclusion : Addition of vinyl-POSS doesn't improve the abrasion resistance, and the abrasion resistance was similar to those of existing materials. Additional studies under different conditions are needed. For clinical application of vinyl-POSS, further investigations with different requirements and conditions are necessary.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.15 no.1
• /
• pp.63-69
• /
• 2006

This study deals with the friction welding of A2024- T6 to A6061- T6; The friction time was variable conditions under the conditions of spindle revolution of 2000rpm, friction pressure of 50MPa, upset pressure of 100MPa, and upset time of 5.0seconds. Under these conditions, the microstructure of weld interface, tensile fracture surface and mechanical tests were studied, of friction weld, and so the results were as follows. 1. When the friction time was 1.5seconds under the conditions, the maximum tensile strength of the friction weld happened to be 292MPa, which is $94.2\%$ of the base material's tensile strength(310MPa). At the same condition, the maximum shear strength was 2l2MPa, which is equivalent to $103\%$ of the base material's shear strength (205MPa). 2. At the same condition, the maximum vickers hardness was Hv 146 at A2024- T6 nearby weld interface, which is higher Hv3 than condition of the friction time 0.5seconds, and the maximum vickers hardness was Hvl20 from weld interface of A6061-T6, which is higher Hv28 then base material's. 3. The results of microstructure analysis show that the structures of two base materials have fractionized and rearranged along a column due to heating and axial force during friction, which has affected in raising hardness and tensile strength.

• Korean Journal of Materials Research
• /
• v.27 no.5
• /
• pp.276-280
• /
• 2017

This study was carried out to evaluate the developed microstructures and mechanical properties of friction welded A6063 alloy. For this work, specimens were prepared at a size of 12 mm ${\O}{\times}80mm$, and friction welding was carried out at a rotation speed of 2,000 RPM, friction pressure of $12kgf/cm^2$ and upset pressure of $25kgf/cm^2$. To perform an analysis of the grain boundary characteristic distributions, such as the grain size, orientation and misorientation angle distributions, the electron back-scattering diffraction method was used. In addition, in order to identify the dispersed intermetallic compounds of the base and welded materials, transmission electron microscopy was used. The experimental results found that the application of friction welding on A6063 led to significant grain refinement of the welded zone relative to that of the base material. Besides this, intermetallic compounds such as AlMnSi and $Al_2Cu$ were found to be dispersed with more refined size relative to that of the base material. This formation retains the mechanical properties of the welds, which results in the fracture aspect at the base material zone. Therefore, based on the developed microstructures and mechanical properties, the application of friction welding on A6063 could be used to obtain a sound weld zone.

• Journal of the military operations research society of Korea
• /
• v.35 no.2
• /
• pp.1-14
• /
• 2009

During wartime, the Air Force have to plan where, and how much, and what need to be distributed to surrounding local area from a chosen central bases. Each base, which has surplus more than needed amount of a certain material collected from near area of the base, is expected to distribute such surplus to other bases in shortage of it. By sending such surplus to other bases in shortage of the material, every base may get sufficient amount of all kinds of materials needed for each base during wartime. Because number of items of materials needed in each military bases during wartime are usually quite large and the frequencies of delivery from a place to other place are also pretty large if each item is delivered from a surplus place to other places in shortage, the Head Quarter of Air Force or the Logistics Command will face to difficulty to decide a reasonable delivery plan between bases for efficient and fast allocation of all materials needed to all bases during wartime. Therefore, this study suggests a solving algorithm with an established TC (transfer center: collecting and distributing center for all materials) to solve such a distribution and transportation problem.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.48 no.2
• /
• pp.168-175
• /
• 2021

This study compared the microleakages and compressive strengths of various base materials. To evaluate microleakages, 50 extracted permanent premolars were prepared. The teeth divided into 5 groups of 10 each according to the base materials. Cavities with a 5.0 mm width, 3.0 mm length, and 3.0 mm depth were formed on the buccal surfaces of the teeth. After filling the cavities with different base materials, a composite resin was used for final restoration. Each specimen was immersed in 2% methylene blue solution and then observed under a stereoscopic microscope (× 30). To evaluate the compressive strength, 5 cylindrical specimens were prepared for each base material. A universal testing machine was used to measure the compressive strength. The microleakage was highest in the Riva light cure^TM group and lowest in the Biodentine^TM and Well-Root^TM PT groups. For the compressive strengths, in all groups, acceptable strength values for base materials were found. The highest compressive strength was observed in the Fuji II LC^TM group and the lowest strength in the Well-Root^TM PT group.