This study investigated the crystal growth, crystalline structure and the basic optical properties of $SnSe/BaF_2$ epilayers. The SnSe epilayer was grown on $BaF_2$(111) insulating substrates using a hot wall epitaxy(HWE) technique. It was found from the analysis of X-ray diffraction patterns that $SnSe/BaF_2$ epilayer was growing to single crystal with orthorhombic structure oriented [111] along the growth direction. Using Rutherford back scattering(RBS), the atomic ratios of the SnSe was found to be stoichiometric, almost 50 : 50. The best values for the full width at half maximum (FWHM) of the DCXRD was 163 arcsec for SnSe epilarer. The epilayer-thickness dependence of the FWHM of the DCXRD shows that the quality of the $SnSe/BaF_2$ is as expected. The dielectric function ${\varepsilon}$(E) of a semiconductor is closely related to its electronic energy band structure and such relation can be drawn from features around the critical points in the optical spectra. The real and imaginary parts(${\varepsilon}_1$ and ${\varepsilon}_2$) of the dielectric function ${\varepsilon}$ of SnSe were measured. These data are analyzed using a theoretical model known as the model dielectric function(MDF). The optical constants related to dielectric function such as the complex refractive index(n*-n+ik), absorption coefficient (${\alpha}$) and normal- incidence reflectivity (R) are also presented for $SnSe/BaF_2$.
This study investigated the crystal growth, crystalline structure and the basic optical properties of $PbSnSe/BaF_2$ epilayers. The PbSnSe epilayer was grown on $BaF_2$(111) insulating substrates using a hot wall epitaxy (HWE) technique. It was found from the analysis of X-ray diffraction patterns that $PbSnSe/BaF_2$ epilayer was grown single crystal with a rock-salt structure oriented along [111] the growth direction. Using Rutherford back scattering, the atomic ratios of the PbSnSe was found to be proper stoichiometric. The best values for the full width at half maximum (FWHM) of the DCXRD was 162 arcsec for PbSnSe epilayer. The epilayer-thickness dependence of the FWHM of the DCXRD shows that the quality of the $PbSnSe/BaF_2$ is as expected. The dielectric function ${\varepsilon}(E)$ of a semiconductor is closely related to its electronic energy band structure and such relation can be drawn from features around the critical points(CPs) in the optical spectra. The real and imaginary parts(${\varepsilon}1$ and ${\varepsilon}2$) of the dielectric function ${\varepsilon}$ of PbSe were measured, and the observed spectra reveal distinct structures at energies of the E1, E2 and E3 CPs. These data are analyzed using a theoretical model known as the model dielectric function (MDF). The optical constants related to dielectric function such as the complex refractive index ($n^*=n+ik$), absorption coefficient (${\alpha}$) and normal-incidence reflectivity (R) are also presented for $PbSnSe/BaF_2$.
Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
/
2008.06a
/
pp.477-477
/
2008
For more than three decades, the gate dielectrics in CMOS devices are $SiO_2$ because of its blocking properties of current in insulated gate FET channels. As the dimensions of feature size have been scaled down (width and the thickness is reduced down to 50 urn and 2 urn or less), gate leakage current is increased and reliability of $SiO_2$ is reduced. Many metal oxides such as $TiO_2$, $Ta_2O_4$, $SrTiO_3$, $Al_2O_3$, $HfO_2$ and $ZrO_2$ have been challenged for memory devices. These materials posses relatively high dielectric constant, but $HfO_2$ and $Al_2O_3$ did not provide sufficient advantages over $SiO_2$ or $Si_3N_4$ because of reaction with Si substrate. Recently, $HfO_2$ have been attracted attention because Hf forms the most stable oxide with the highest heat of formation. In addition, Hf can reduce the native oxide layer by creating $HfO_2$. However, new gate oxide candidates must satisfy a standard CMOS process. In order to fabricate high density memories with small feature size, the plasma etch process should be developed by well understanding and optimizing plasma behaviors. Therefore, it is necessary that the etch behavior of $HfO_2$ and plasma parameters are systematically investigated as functions of process parameters including gas mixing ratio, rf power, pressure and temperature to determine the mechanism of plasma induced damage. However, there is few studies on the the etch mechanism and the surface reactions in $BCl_3$ based plasma to etch $HfO_2$ thin films. In this work, the samples of $HfO_2$ were prepared on Si wafer with using atomic layer deposition. In our previous work, the maximum etch rate of $BCl_3$/Ar were obtained 20% $BCl_3$/ 80% Ar. Over 20% $BCl_3$ addition, the etch rate of $HfO_2$ decreased. The etching rate of $HfO_2$ and selectivity of $HfO_2$ to Si were investigated with using in inductively coupled plasma etching system (ICP) and $BCl_3/Cl_2$/Ar plasma. The change of volume densities of radical and atoms were monitored with using optical emission spectroscopy analysis (OES). The variations of components of etched surfaces for $HfO_2$ was investigated with using x-ray photo electron spectroscopy (XPS). In order to investigate the accumulation of etch by products during etch process, the exposed surface of $HfO_2$ in $BCl_3/Cl_2$/Ar plasma was compared with surface of as-doped $HfO_2$ and all the surfaces of samples were examined with field emission scanning electron microscopy and atomic force microscope (AFM).
The hexagonal $HoMn_{1-x}-Fe_xO_3$(x=0.00, 0.05) thin films were prepared using pulsed laser deposition(PLD) method on $Pt/Ti/SiO_2/Si$ substrate. The microstructure and magnetic properties have been studied by x-ray diffraction(XRD), atomic force microscopy (AFH), scanning electron microscope(SEM:), x-ray photoelectron spectroscopy(XPS), and conversion electron $M\"{o}ssbauer$ spectroscopy(CEMS). From the analysis of the x-ray diffraction patterns, the crystal structure for all films was found to be a hexagonal($P6_3cm$), which was preferentially grown along(110) direction. The lattice constant $c_0$ of the film with x=0.05 was close to that of single crystal, whereas lattice constant $a_0$ with respect to single crystal shows a slight decrease. This difference of lattice parameters between film and single crystal was caused by the lattice mismatch between the film and $Pt/Ti/SiO_2/Si$ substrate. Conversion electron $M\"{o}ssbauer$ spectrum of $HoMn_{0.95}Fe_{0.05}O_3$ thin film shows an asymmetry doublet absorption ratio at room temperature, which is due to the oriented direction of crystallographic domains. This is corresponding with analysis of x-ray diffraction. The quadrupole splitting(${\Delta}E_Q$) at room temperature is found to be $1.62{\pm}0.01mm/s$. This large ${\Delta}E_Q$ was caused by asymmetry environment surrounding Fe ion.
Proceedings of the Materials Research Society of Korea Conference
/
2009.11a
/
pp.24.2-24.2
/
2009
Indium Antimonide(InSb)는 $3{\sim}5\;{\mu}m$대 적외선 감지영역에서 기존 HgCdTe(MCT)를 대체할 물질로 각광받고 있다. 1970년대부터군사적 용도로 미국, 이스라엘 등 일부 선진국에서 연구되기 시작했으며,이온주입, MOCVD, MBE 등 다양한 공정을 통해 제작되어 왔다. InSb 적외선 감지소자는 $3{\sim}5{\mu}m$대에서 HgCdTe와 성능은 대등한데 반해, 기판의 대면적화와 저렴한 가격, 우주공간 및 야전에서 소자 동작의안정성 등으로 InSb적외선 감지기는 냉각형 고성능 적외선 감지영역에서 HgCdTe를 대체해 가고 있다. 하지만 InSb는 77 K에서 0.225eV의 작은 밴드갭을 갖고 있기 때문에 누설전류로 인한 성능저하가 고질적인문제로 대두되었고, 이를 해결하기 위한 고품질 절연막 연구가 InSb적외선 수광 소자 연구의 주요이슈 중 하나가 되어왔다. 그 동안 PECVD, photo-CVD, anodic oxidation 등의 공정을 이용하여 $SiO_2$, $Si_3N_4$, 양극산화막(anodic oxide) 등 다양한 절연막에 대한 연구가 진행되었고[1,2], 절연막과 반도체 사이 계면에서의 열확산을 억제하여 계면트랩밀도를 최소화하기 위한 공정개발이 이루어졌다[3]. 하지만 InSb 적외선 감지기술은 국방 및 우주개발의 핵심기술중 하나로 그 기술의 이전이 엄격히 통제되고 있으며, 현재도 미국과 이스라엘, 일본, 영국 등 일부 선진국 만이 기술을 확보하고 있고, 국내의 경우 연구가 매우 취약한 실정이다. 따라서 본 연구에서는 InSb 적외선 감지기의 암전류를 제어하기 위한 낮은 계면트랩밀도를 갖는 절연막 증착 공정을 찾고자 하였다. 본 연구에서는 n형 (100) InSb 기판 ($n=0.2{\sim}0.85{\times}10^{15}cm^{-3}$ @ 77K)에 PECVD를 이용하여 $SiO_2$, $Si_3N_4$ 등을 증착하고 절연막으로서 이들의 특성을 비교 분석하였다. $SiO_2$는 160, 200, $240^{\circ}C$에서 $Si_3N_4$는 200, $300^{\circ}C$에서 증착하였다. Atomic Force Microscopy(AFM) 사진으로 확인한 결과, 모든 샘플에서표면거칠기가 ~2 nm의 평탄한 박막을 얻을 수 있었다. Capacitance-Voltage 측정(77K)을 통해 절연막 특성을 평가하였다. $SiO_2$와 $Si_3N_4$ 모두에서 온도가 증가할수록 벌크트랩밀도가 감소하는 경향을 볼 수 있었는데, 이는 고온에서 증착할 수록 박막 내의 결함이 감소했음을 의미한다. 반면계면트랩밀도는 온도가 증가함에 따라, 1011 eV-1cm-2 대에서 $10^{12}eV^{-1}cm^{-2}$ 대로 증가하였는데, 이는 고온에서 증착할 수 록 InSb 표면에서의 결함은 증가하였음을의미한다. 암전류에 큰 영향을 주는 것은 계면트랩밀도 이므로, $SiO_2$와 $Si_3N_4$ 모두 $200^{\circ}C$이하의 저온에서 증착시켜야 함을 확인할 수 있었다.
In this paper, ZnO:Al thin films with c-axis preferred orientation were prepared on Soda lime glass substrates by RF magnetron sputtering technique. AZO thin film were prepared in order to clarify optimum conditions for growth of the thin film depending upon process, and then by changing a number of deposition conditions and substrate temperature conditions variously, structural and electrical characteristics were measured. For the manufacture of the AZO were vapor-deposited in the named order. It is well-known that post-annealing is an important method to improve crystal quality. For the annealing process, the dislocation nd other defects arise in the material and adsorption/decomposition occurs. The XRD patterns of the AZO films deposited with grey theory prediction design, annealed in a vacuum ambient($2.0{\times}10-3$Torr)at temperatures of 200, 300, 400 and $500^{\circ}C$ for a period of 30min. The diffraction patterns of all the films show the AZO films had a hexagonal wurtzite structure with a preferential orientation along the c-axis perpendicular to the substrate surface. As can be seen, the (002)peak intensities of the AZO films became more intense and sharper when the annealing temperature increased. On the other hand, When the annealing temperature was $500^{\circ}C$ the peak intensity decreased. The surface morphologies and surface toughness of films were examined by atomic force microscopy(AFM, XE-100, PSIA). Electrical resistivity, Gall mobility and carrier concentration were measured by Hall effect measuring system (HL5500PC, Accent optical Technology, USA). The optical absorption spectra of films in the ultraviolet-visibleinfrared( UV-Vis-IR) region were recorder by the UV spectrophotometer(U-3501, Hitachi, Japan). The resistivity, carrier concentration, and Hall mobility of ZnS deposited on glass substrate as a function of post-annealing.
[ $L1_0$ ]phase FePd nano-dot structures were successfully fabricated on self-organized Fe/Au bilayers. With atomic force microscopy, it is determined that surface morphologies of initially flat Fe/Au bilayer films were agglomerated and transformed their shape into nano-dots structures with increasing annealing temperature. With this bilayer as a template, FePd multilayers were deposited at various temperatures, i.e. $300^{\circ}C$, $350^{\circ}C$, $400^{\circ}C$, and $450^{\circ}C$. Surface morphologies of FePd superlattice had a near resemblance to self-organized bilayer. According to X-ray diffraction results, it is confirmed that $L1_0$ superlattice structures of FePd were obtained from samples which were annealed above $350^{\circ}C$. Results of X-ray photoelectron spectroscopy depth-profile analysis showed that chemical composition is identical to deposition sequence. As a result, without additional etching processes, fabrication of chemically ordered FePd superlattice nano-dots was achieved.
Proceedings of the Korean Vacuum Society Conference
/
1999.07a
/
pp.117-117
/
1999
최근 광소자와 더불어 발전과 더불어 고효율의 새로운 광소자에 대한 수요가 증가되고 있다. ZnO는 이러한 특성을 가진 재료중에 한가지로서 최근 들어 그 가능성에 대한 연구가 활발히 이루어지고 있다. 특히 상온에서 exciton binding energy가 다른 재료보다 큰 60meV로 고효율의 blue, UV 발광이 가능한 재료로 알려져 있다. 본 연구에서도 광소자로서 ZnO를 활용하기 위해서 RF magnetron sputtering법을 이용하기 위하여 광특성의 향상에 목적을 두고 연구하였다. ZnO 박막은 RF magnetron sputtering법을 이용하여 sapphire (0001) 기판위에 성장시켰다. RF power는 60W에서 120W까지 변화시켰고 박막의 성장온도는 55$0^{\circ}C$와 $600^{\circ}C$로 변화시켰으며, 박막의 성장시간은 60분, ZnO target과 기판과의 거리는 4.5cm로 하여 성장시켰다. 성장된 ZnO 박막은 XRD $\theta$-rocking scan 측정을 통해서 박막의 C-축 배향성과 RBS channeling를 이용하여 ZnO 박막의 epitaxial 성장 정도를 측정하였다. 박막의 상온 발광 특성은 He-Cd laser를 사용한 photoluminescence spectra로 측정하였다. 또한 표면의 morphology는 atomic force microscope(AFM)를 이용하여 관찰하였으며 transmission electron microscopy(TEM)을 사용하여 ZnO박막의 단면적을 관찰함으로서 grain의 성장과 광특성 및 결정성과의 영향에 대해서 연구하였다. ZnO 박막의 성장온도 55$0^{\circ}C$에서 RF power를 60W에서 120W까지 변화시킬 경우 XRD $\theta$-rocking peak의 반치폭이 0.157$^{\circ}$에서 0.436$^{\circ}$까지 변화하였고 80W에서 최소값을 가졌으며 in-plain에 대한 XRD 측정 결과 ZnO 박막의 성장은 sapphire 기판에 대해서 30$^{\circ}$회전되어 성장된 것으로 알 수 있었으며 이는 ZnO [100]∥ Al2O3[110]의 관계를 갖는다는 것을 나타낸다. 광특성의 측정 결과인 PL peak의 반치폭은 133.67meV에서 89.5meV까지 변화함을 알 수 있었고 80W에서 최대값을 가졌으며 이는 RF power의 변화에 따른 결정성의 변화와는 반대되는 현상임을 알 수 있었다. 그러나 성장온도 $600^{\circ}C$일때에는 XRD $\theta$-rocking peak의 반치폭이 0.129$^{\circ}$로 결정성이 우수한 박막임을 확인할 수 있었고 PL peak의 반치폭 또한 Ar과 O2의 비율에 따라 76.32meV에서 98.77meV로 광특성도 우수한 것으로 나타났다. RBS channeling 결과 55$0^{\circ}C$에서는 $\chi$min값이 50~60%였으나 $600^{\circ}C$일 때에는 $\chi$min값이 4~5%로 박막이 epitaxial 성장을 하였다는 것을 알 수 있었다. 결정성과 광특성과의 연관성을 알아보기 위해 TEM을 이용한 박막의 cross section image를 관찰한 결과 광특성이 우수한 시편일수록 grain의 크기가 큰 것으로 나타났고 결정성이 우수한 시편의 경우에서는 XRD분석 결과에서처럼 C-축배향성이 우수한 것을 확인할 수 있었다. 이상의 결과로부터 RF magnetron sputtering 법으로 광특성이 우수한 양질의 ZnO박막 성장이 가능하였다는 것을 알 수 있었으며 광소자로써의 가능성을 확인 할 수 있었다.
Journal of the Korea Academia-Industrial cooperation Society
/
v.18
no.10
/
pp.771-776
/
2017
The cover glass of mobile displays and photovoltaic cells needs a functional coating, such as an anti-reflection and self-cleaning coating. Numerous studies have been conducted on the engineering application of biomimetic functional surfaces, such as moth eye and lotus leaf Anti-reflection coantings of silica nanoparticles could enhance the light transmittance. $TiO_2$ photocatalyst coatings have been applied to self-cleaning functional films. In this study, transparent hydrophobic anti-reflective coatings consisting of thin layers of $SiO_2/TiO_2$ nanoparticles were fabricated on a slide glass substrate by the sol-gel process and dip-coating process. The dependence of the surface morphology of the functional coatings was investigated by the atomic force microscopy (AFM), contact angle measurement, and UV-visible spectroscopy. It was found that the coating of $TiO_2$ nanoparticles exhibited a high average transmittance comparable to that of the bare slide glass substrate in the visible light range. The bi-layered functional coating of 7 nm $SiO_2$/7nm $TiO_2$ nanoparticles exhibits a transparent hydrophobic surface with a contact angle of $110^{\circ}$ and an improvement of the average transmittance of 2.3% compared to the bare slide glass substrate in the visible light range.
Lanthanum modified lead zirconate titanate ($Pb_{1.1}La_{0.08}Zr_{0.65}Ti_{0.35}O_3$) thin films were fabricated on indium doped tin oxide (ITO)-coated glass substrate by R.F magnetron sputtering method. The thin films were deposited at $500^{\circ}C$ and post-annealed with various temperature ($550-750^{\circ}C$) by rapid thermal annealing technique. The structure and morphology of the films were characterized with X-ray diffraction (XRD) and atomic force microscopy (AFM) respectively. The hysteresis loops and fatigue properties of thin films were measured by precision material analyzer. As the annealing temperature was increased, the remnant polarization value was increased from $10.6{\mu}C/cm^2$ to $31.4{\mu}C/cm^2$, and coercive field was reduced from 79.9 kV/cm to 60.9 kV/cm. As a result of polarization endurance analysis, the remnant polarization of PLZT thin films annealed at $700^{\circ}C$ was decreased 15% after $10^9$ switching cycles using 1MHz square wave form at ${\pm}5V$.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.