• International Journal of Precision Engineering and Manufacturing
• /
• v.4 no.4
• /
• pp.45-50
• /
• 2003

In order to investigate the effect of surface treatment (Anodizing) and rolling on AI 5083-H131 alloy, under hyper velocity impact, a ballistic testing was conducted. Ballistic resistance of these materials was measured by a protection ballistic limit ($V_{50}$)' a statistical velocity with 50% probability of penetration. Perforation behavior and ballistic tolerance, described by penetration modes, were respectfully observed, by $V_{50}$ test and Projectile Through Plates (PTP) test at velocities greater than $V_{50}$. PTP tests were conducted with 0$^{\circ}$ obliquity at room temperature using 5.56mm ball projectiles. $V_{50}$ tests with 0$^{\circ}$ obliquity were also done with projectiles that were able to achieve near or complete penetration during PTP tests. Resistance to penetration, and penetration modes of Al 5052-H34 alloy were compared to those of Al 5083-H 131 alloy.

• Tribology and Lubricants
• /
• v.15 no.2
• /
• pp.141-149
• /
• 1999

Fracture, fatigue and wear characteristics of Al-Si alloy used for compressor are experimentally studied. Plane strain fracture toughness test is carried out using three point bending specimen. Fatigue test is performed under constant loading condition and wear test is carried out as a function of sliding velocity and applied load. To obtain the crack propagation characteristics and wear mechanism of Al-Si alloy, fracture and worn surfaces are investigated using SEM. It is verified that fracture and fatigue strength of Al-Si alloy are improved by the fine microstructure of alloy. The wear behavior and specific wear amount of Al-Si alloy are not dependent on the microstructure but on a function of the silicon content. Anodizing on the surface of Al-Si alloy, surface hardness and wear characteristics are improved.

• Journal of the Korean institute of surface engineering
• /
• v.15 no.2
• /
• pp.69-76
• /
• 1982

With a view to manufacturing membranes for separation of gas mixtures, Al foils were anodized in a 2% oxalic-acid electrolyte at 40V and 80V. When anodizing was completed and Barrier layer existed at the extreme back site of the foil, the anodized foil was made to react with only electrolyte, with switching off the electric power. When the size and density of pores were changed through voltage change, the membr-anes did not show large difference in the permeability. Reacting with electrolyte, the existing Barrier layer turns into porous layer. During this process, several small pores grow from one relatively large pore, getting to the back site. The number and size of the small pores getting to the back surface increase as time passing. This change of Barrier layer into porous layer is thought to be directly related to the permeability change of the membranes. The selectivity of an anodized Al membrane was not related to the voltage change, and was high, being similar to the theoretical selctivity of metallic membranes, according to my observation.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.432-434
• /
• 2009

Metal nano-wire arrays on Cu-coated seed layers were fabricated by aqueous solution method using sulfate bath at room temperature. The seed layers were coated on Anodic aluminum oxide (AAO) bottom substrates by electrochemical deposition technique, length and diameter of metal nano-wires were dominated by controlling the deposition parameters, such as deposition potential and time, electrolyte temperature. Anodic aluminum oxide (AAO) was used as a template to prepare highly ordered Ni, Fe, Co and Cu multilayer magnetic nano-wire arrays. This template was fabricated with two-step anodizing method, using dissimilar solutions for Al anodizing. The pore of anodic aluminum oxide templates were perfectly hexagonal arranged pore domains. The ordered Ni, Fe, Co and Cu systems nano-wire arrays were characterized by Field Emission Scanning Electron Microscopy (FE-SEM) and Vibrating Sample Magnetometer (VSM). The ordered Ni, Fe, Co and Cu systems nano-wires had different preferred orientation. In addition, these nano-wires showed different magnetization properties under the electrodepositing conditions.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.6
• /
• pp.549-554
• /
• 2016

Low melting metals are difficult to weld because it is vaporized. But epoxy resin make bonding possible using low melting material and dismissal materials. This study is to improve the bonding strength of epoxy and substrate by mechanical and electrochemical methods. In case of mechanical work, bonding strength is 17.6MPa and in case of pre-work, bonding strength is 15.3MPa. When anodizing and mechanical work is applied, bonding strength is 25.3Mpa is increased 165%. When anodizing is applied, bonding strength is 27.6Mpa.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2008.11a
• /
• pp.105-106
• /
• 2008

Nanotube morphology change of Ti-Ta-Zr alloy as Zr content increase has been researched using various experimental methods. Ti-Ta-Zr(3, 7 and 15 wt%) alloys were prepared by arc melting and nano-structure controlled for 24 hr at $1000^{\circ}C$ in argon atmosphere. Formation of oxide nanotubes are conducted by anodizing a Ti-Ta-Zr alloy in $H_3PO_4$ electrolytes with small amounts of fluoride ions at room temperature. Electrochemical experiments were carried out with conventional three-electrode configuration with a platinum counter electrode and a saturated calomel reference electrode. The samples were embedded with epoxy resin, leaving a square surface area of $10mm^2$ exposed to the anodizing electrolyte, 1.0M $H_3PO_4$ containing 0.8wt% NaF.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.6
• /
• pp.427-431
• /
• 2017

Anodic aluminum oxide (AAO) film has recently attracted much attention as a key material for the fabrication of various nanostructures. A control of anodizing voltage (U) was employed to render different anodic aluminum oxide (AAO) nanostructures with pore diameter ($D_p$) and interpore distance ($D_{int}$) in oxalic acid. In this work, we study the effect of stepwise modulation of anodizing voltages on the shape and dimension of porous structures along the vertical direction and demonstrate the fabrication of hierarchical layers of systematically controlled three-dimensional (3D) pore profile.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2004.05a
• /
• pp.74-76
• /
• 2004

It is the new promising method of obtaining the information about the state of a surface of a solid body, thin and multilayer structures. An idea of the method consists in reading and analyzing the relations U(t), dU/dt(t), dU/dt(U) on an electrical cell when anodizing an investigated object. By these relation it is possible to control the presence of impurities in the metal on the path of the anodization front, a structure and characteristics of the object being oxidized as well as of an oxide which is being formed during anodizing, the change in composition of the oxide layer, the thickness and composition of metallic and dielectric layers being a part of the layers boundaries.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.545-546
• /
• 2006

This study was performed to investigate the surface properties of electrochemically oxidized pure titanium by anodic spark discharging method. Commercially pure titanium plates of $10{\times}20{\times}1[mm]$ in dimensions were polished sequentially emery paper. Anodizing was performed at current density of $76.2\;[mA/cm^2]$, application voltage of 290, 350, 400 [V] using a regulated DC power supply, which allowed automatic transition constant current when a preset maximum voltage has been reached. The Ti surface oxided films was characterized by scanning electron microscope(SEM). The precipitation of HA(Hydroxyapatite) crystals on anodized surface was greatly accelerated by hydrothermal treatment. The concentrations of DL-$\alpha$-Glycerolphosphate Magnesiurn(DL-$\alpha$-GP-Mg) salt and Ca acetate in an electrolyte was highly affected the precipitation of HA crystals converted by Ti Anodized oxide films by Shape of Impulse Voltage.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.05a
• /
• pp.482-484
• /
• 2008

Anodic aluminum oxide (AAO) which prepared with two-step anodizing method (with dissimilar solutions) was used as a template to fabricate highly ordered, free standing metal nano-rods. AAO nano-template technique can realize self-organized hexagonal pore structure with nanometer dimension size, it's easy to control pore diameter, length and density by varying anodizing conditions. Ni and Ni/Fe/Cu multi-metal layer nanorods were electrochemically deposited into AAO nano-template by AC voltage in simple sulfate solutions.. The properties of samples are tested by X-ray diffraction (XRD), field emission microscopy (FE-SEM).