• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2009년도 춘계학술대회 논문집
• /
• pp.270-273
• /
• 2009

A comb-like copolymer consisting of a poly(vinylidene fluoride-co-chlorotrifluoro-ethylene) backbone and poly(hydroxy ethyl acrylate) side chains, i.e. P(VDF-co-CTFE)-g-PHEA, was synthesized through atom transfer radical polymerization (ATRP) using CTFE units as a macroinitiator. Successful synthesis and a microphase-separated structure of the copolymer were confirmed by proton nuclear magnetic resonance (1H-NMR), FT-IR spectroscopy, and transmission electron microscopy (TEM). This comb-like polymer was crosslinked with 4,5-imidazole dicarboxylic acid (IDA) via the esterification of the -OH groups of PHEA and the -COOH groups of IDA. Upon doping with phosphoric acid ($H_3PO_4$) to form imidazole-$H_3PO_4$ complexes, the proton conductivity of the membranes continuously increased with increasing $H_3PO_4$ content. A maximum proton conductivity of 0.015 S/cm was achieved at $120^{\circ}C$ under anhydrous conditions. In addition, these P(VDF-co-CTFE)-g-PHEA/IDA/$H_3PO_4$ membranes exhibited good mechanical properties (765 MPa of Young's modulus), and high thermal stability up to $250^{\circ}C$, as determined by a universal testing machine (UTM) and thermal gravimetric analysis (TGA), respectively.

• 멤브레인
• /
• 제19권3호
• /
• pp.228-236
• /
• 2009

원자전달 라디칼 중합을 이용하여 poly(hydroxyl ethyl acrylate)-b-polystyrene-b-poIy(hydroxyl ethyl acrylate) (PHEA-b-PS-b-PHEA) 트리블록 공중합체를 합성하였다. 이렇게 합성된 PHEA-b-PS-b-PHEA블록 공중합체의 -OH 그룹과 이미다졸 디카르복실릭산(IDA)의 -COOH 그룹과의 에스테르 반응에 의하여 가교된 전해질막을 제조하였다. 인산(${H_3}{PO_4}$)을 도핑하여 이미다졸-인산 착체를 형성한 결과, 인산 함량이 증가함에 따라 고분자 전해질막의 수소 이온 전도도가 증가하였다. 특히 [HEA]:[IDA]:[${H_3}{PO_4}$]=3:4:4의 조성을 갖는 PHEA-b-PS-b-PHEA/IDA/${H_3}{PO_4}$ 고분자 전해질막은 $100^{\circ}C$의 비가습 조건에서 최대 0.01 S/cm의 수소이온 전도도를 나타내었다. 열분석 결과(TGA) 전해질막은 $350^{\circ}C$의 고온까지 열적으로 안정함을 확인하여 연료전지에 적용이 가능함을 보여주었다.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2009년도 춘계학술대회 논문집
• /
• pp.378-378
• /
• 2009

The ionic liquid-based sulfonated hydrocarbon composite membranes was prepared for use in anhydrous high temperature-polymer electrolyte fuel cells (HT-PEFCs). Ionic liquid behaves like water in the composite membranes under anhydrous condition. However the composite membranes show a low conductivity and high gas permeability as the content of ionic liquid increases due to its high viscosity and content of ionic liquid, respectively. Hence, in order to enhance the proton conductivity and to reduce the gas permeability of the composite membranes with low content of ionic liquids, the acid containing a common ion of ionic liquid was added to the composite membranes. The characterization of composite membranes was carried out using small-angle X-ray scattering (SAXS), thermogravimetric analyzer (TGA) and impedance spectroscopy. As a result, the composite membranes containing acid showed higher proton conductivity than those with no acid under the un-humidified condition due to a decrease in viscosity. In addition, the proton conductivity of composite membranes increased with increasing mole concentration of acid.

• 멤브레인
• /
• 제19권4호
• /
• pp.302-309
• /
• 2009

원자전달 라디칼 중합을 이용하여 polystyrene-b-poly (hydroxyethyl methacrylate) (PS-b-PHEMA) 블록 공중합체를 합성한 뒤, 블록 공중합체의 -OH 그룹과 이미다졸 디카르복실릭산 (IDA)의 -COOH 그룹과의 에스테르 반응에 의하여 가교된 전해질막을 제조하였다. 인산($H_3PO_4$)을 도핑하여 이미다졸-인산 착체를 형성한 결과, 인산 함량이 증가함에 따라 공중합체 전해질막의 수소 이온 전도도가 계속 증가하였다. 또한 인장강도와 인장률 모두 인산 함량에 따라 증가하였다. 특히 [HEMA]: [IDA]:[$H_3PO_4$] = 3:4:4의 조성을 갖는 PS-b-PHEMA/IDA/$H_3PO_4$ 블록 공중합체 전해질막은 $100^{\circ}C$의 비가습 조건에서 최대 0.01 S/cm의 수소이온 전도도를 나타내었다. 열분석(TGA) 실험을 통하여 전해질막은 $350^{\circ}C$의 고온까지 열적으로 안정함을 확인하였다.

• 멤브레인
• /
• 제19권2호
• /
• pp.89-95
• /
• 2009

Poly(vinyl chloride) (PVC) 주사슬과 poly(hydroxyethyl acrylate) (PHEA) 곁사슬로 구성된 빗살모양의 PVC-g-PHEA 공중합체를 원자전달라디칼 중합을 통해 합성하였다. 이렇게 합성된 PVC-g-PHEA의 OH 그룹과 이미다졸 디카르복실릭산 (IDA)의 COOH 그룹과의 에스테르 반응에 의하여 가교된 전해질막을 제조하였다. 인산(PA)을 도핑하여 이미다졸-인산 착체를 형성한 결과, PA함량이 증가함에 따라 고분자 전해질막의 수소 이온 전도도가 증가하였다. 특히 100도 비가습 조건에서 수소 이온 전도도는 최대 0.011 S/cm까지 증가하였다. 만능 재료 시험기(UTM) 측정결과, 제조된 PVC-g-PHEA/IDA/PA 전해질막은 575 MPa의 높은 Young 모듈러스 및 기계적 강도를 보여주었다. 열분석 결과(TGA) 전해질막은 $200^{\circ}C$까지 열적으로 안정함을 확인하였다.