• 통합자연과학논문집
• /
• 제2권4호
• /
• pp.233-236
• /
• 2009

This study was undertaken to measure the electrochemical corrosion of amorphous $Zr_{65}Al_8Ni_{15}Cu_{12}$ (at.%) alloy ribbon under various conditions, including 0.4 mM HCl solution, and for various values of the pH and the immersion time. The corrosion potentials($E_{corr}$) for the amorphous $Zr_{65}Al_8Ni_{15}Cu_{12}$ alloy in 0.4 mM HCl decreased with increasing temperature; the corrosion current density($I_{corr}$) increased with increasing temperature in general. The polarization resistance($R_p$) was inversely proportional to the corrosion rate. While pH=7, 9, 11 was not as sensitive as pH=3, 5, pH=3 was more sensitive for amorphous $Zr_{65}Al_8Ni_{15}Cu_{12}$ alloy than other pHs specially. The change of mass in the 70 mM $H_2SO_4$ solution with immersion time was the greatest in the first 100 h.

• 한국주조공학회지
• /
• 제36권1호
• /
• pp.18-23
• /
• 2016

Iron based amorphous ribbons with the nominal compositions of $(Fe_{79}C_{11}B_8Si_2)_{100-X}Cr_X$ (X = 0,2,4,6,8 at%) have been developed as reinforcements that can be applied to the concrete materials. Mechanical properties and glass forming ability of the ribbons can be enhanced by the optimum amounts of Cr additions that can also improve corrosion properties of the ribbons. Vein patterns typical of the fractured surface morphology of amorphous alloys have been observed on the surfaces of ribbons after tensile tests. It is inferred from the EDS analysis results of vein patterns that carbon segregations occur within the narrow shear band regions.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1994년도 춘계학술대회 논문집
• /
• pp.149-151
• /
• 1994

This thesis describes the effect of heat treatment on the magnetic properties of Co-bsaed Amorphous. A sample was chosen as basic composition with Co$\_$82//Si$\_$2//B$\_$16/ of zero magnetostriction. It was made by single roll method with quartz orifice 0.5[mmø], Ar gas pressure 0.6 [kg/cm$^2$] and roll speed 28 (m/sec) and atmosphere is ,Ar gas. We obtained the sample of width 2.4(mm), thickness 45[$\mu\textrm{m}$]. Made sample annealed for the improvement of magnetic propertics at at annealing temperature 325,350,375 and 400$^{\circ}C$ and annealing time 15, 30, 45, 60 and 120min respectiveily. Amorphous ribbon of co-based showed high permeab- ility ${\mu}$=8000∼14000, and became improvement of magnetic properties according to anneal ins temperature and time. Especially. Amorphous sample at 325$^{\circ}C$ ,45min appearanced high permeability ${\mu}$=13, 589 at frequency f= 100Hz. and loss factor was reduced at low frequency with rising anneal ins ti me and temperature more annealed sample than basic sample.

• 한국재료학회지
• /
• 제12권2호
• /
• pp.140-145
• /
• 2002

This study was conducted to investigate the brazing characteristics between Zircaloy-4 nuclear fuel cladding tubes and bearing pads with filler metals of amorphous $Zr_{1-x}Be_x$(0.3$\leq$x$\leq$0.5) binary alloy, in which they were produced in the ribbon form by the melt-spinning metod. The crystallization behavior, stability, hardness and micro-structure of brazed zone were examined by X-ray diffraction, differential scanning calorimetry, micro-Vickers hardness test, optical microscopy, and transmission electron microscopy. $Zr_{1-x}Be_x$(0.3$\leq$x$\leq$0.4) amorphous alloys were crystallized to $\alpha$-Zr with increasing the temperature, and the rest were transformed to ZrBe$_2$at higher temperatures. On the other hand, $Zr_{1-x}Be_x$(0.4$\leq$x$\leq$0.5) amorphous alloys were crystallized to $\alpha$-Zr and ZrBe$_2$, simultaneously. The thickness of the layer brazed with amorphous alloy was increased with increasing the beryllium content due to the higher diffusion of Be. The morphology of brazed layer with PVD Be filler metal showed dendrite while that brazed with amorphous alloys appeared globular. Micro-Vickers hardness of brazed zone increased as the beryllium content of filler metal was decreased.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1990년도 하계학술대회 논문집
• /
• pp.236-238
• /
• 1990

For improving magnetic properties of the amorphous Fe-B-Si alloy, we annealed in a magnetic field oriented in the plane of the ribbon longitudinal to its long axis. By field annealing, coercive force and total core loss are reduced from 0.04 Oe to 0.02 Oe, and from 0.25 watt/kg to 0.15 watt/kg respectively comparing with non-field annealed specimen. These reductions were caused by the formation of $180^{\circ}$ domains parallel to the annealing field due to the induced anisotorpy.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1994년도 하계학술대회 논문집 A
• /
• pp.57-59
• /
• 1994

The transformer core using amorphous Fe-B-Si ribbon were designed by magnetostatic software. The basic model of core is Butt-Lap-Step type, non-culled typo and stair type core joint. And the variables are the number of ribbons for on step, flux density and core shape.

• Journal of Magnetics
• /
• 제2권4호
• /
• pp.130-134
• /
• 1997

The amorphous Co-based alloy Co66Fe4Ni1B15Si14 (Metglas 2714A) is a suitable magnetic core material for high frequency operation. Appreciable reduction of the coercive force can be achieved by proper heat treatment. In this study, samples annealed at wide temperature range were analyzed using differential scanning calorimetry, high frequency B-H loop tester, X-ray diffractometer and resistivity meter. The results show that coercive force at 10 kHz decreases with in-creasing annealing temperature up to 773 K, but dramatically increases above this temperature. The squareness shows that the magnetic anisotropy on longitudinal direction of the as-cast state remains up to 773 K. Above this temperature, it decreases down to 0.5 that represents random distribution of magnetic domains. The crystallization abruptly occurs between 781 K and 783 K.

• Bulletin of the Korean Chemical Society
• /
• 제17권7호
• /
• pp.621-625
• /
• 1996

A variety of metal oxides were coated by sol-gel process from their metal alkoxides on the ribbons of Co-based and Fe-based amorphous alloys, and the effects of surface oxide coating on the magnetic properties of the alloy are investigated. The core loss is found to be reduced significantly by the oxide coating, the loss reduction becoming more prominent at higher frequencies. The shape of the hystersis loop is also dependent upon the kind of the coated metal oxide. The coatings of MgO, SiO2, MgO·SiO2 and MgO·Al2O3 induce tensile stress into the Fe-based ribbon whereas those of BaO, Al2O3, CaO·Al2O3, SrO·Al2O3 and BaO·Al2O3 induce compressive stress. These results may be explained by the modification of domain structures via magnetoelastic interactions with the shrinkage stress induced by the sol-gel coating.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2003년도 somma/kms meeting
• /
• pp.272-272
• /
• 2003

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2007년도 The 1st International Symposium on Advanced Magnetic Materials
• /
• pp.153.1-153.1
• /
• 2007