• 열처리공학회지
• /
• 제8권3호
• /
• pp.236-243
• /
• 1995

Since amorphous alloys have been known to have better mechanical and chemical properties than crystalline alloys of the same composition, a great number of studies on the formation of Al-based amorphous alloys have been carried out actively. However, little has been obtained about the effect of Rare-Earth metal and Transition metal addition on amorphous phase formed by melt spinning method. This study included fabrication of amorphous alloy $Al_{85}Ce_5Ni_{10}$ by melt spinning methods and DTA, XRD, TEM analysis to determine crystalization behavoir. Annealing treatments were carried out in Ar atmosphere under isothermal and nonisothermal conditions. The diffraction pattern of non-heated ribbons showed broad form characteristic of glass metallic alloy. The crystallization of amorphous $Al_{85}Ce_5Ni_{10}$ takes place eutedtoidly by homogeneous formation of Al and MS-1, followed by precipitation of the $Al_{11}Ce_3$ and later $MS-1{\rightarrow}Al_3Ni$ transformation.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2011년도 임시총회 및 하계학술연구발표회
• /
• pp.166-166
• /
• 2011

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2012년도 임시총회 및 하계학술연구발표회
• /
• pp.135-135
• /
• 2012

• Journal of Magnetics
• /
• 제19권4호
• /
• pp.327-332
• /
• 2014

The effect of minor element additions (Ca, Al) on microstructural change and magnetic properties of Fe-Nb-Cu-Si-B alloy has been investigated, in this paper. The Fe-Si-B-Nb-Cu(-Ca-Al) alloys were prepared by arc melting in argon gas atmosphere. The alloy ribbons were fabricated by melt-spinning, and heat-treated under a nitrogen atmosphere at $520-570^{\circ}C$ for 1 h. The soft magnetic properties of the ribbon core were analyzed using the AC B-H meter. A differential scanning calorimetry (DSC) was used to examine the crystallization behavior of the amorphous alloy ribbon. The microstructure was observed by X-ray diffraction (XRD), transmission electron microscope (TEM) and scanning electron microscope (SEM). The addition of Ca increased the electrical resistivity to reduce the eddy current loss. And the addition of Al decreased the intrinsic magnetocrystalline anisotropy $K_1$ resulting in the increased permeability. The reduction in the size of the ${\alpha}$-Fe precipitates was observed in the alloys containing of Ca and Al. Based on the results, it can be concluded that the additions of Ca and Al notably improved the soft magnetic properties such as permeability, coercivity and core loss in the Fe-Nb-Cu-Si-B base nanocrystalline alloys.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1990년도 하계학술대회 논문집
• /
• pp.236-238
• /
• 1990

For improving magnetic properties of the amorphous Fe-B-Si alloy, we annealed in a magnetic field oriented in the plane of the ribbon longitudinal to its long axis. By field annealing, coercive force and total core loss are reduced from 0.04 Oe to 0.02 Oe, and from 0.25 watt/kg to 0.15 watt/kg respectively comparing with non-field annealed specimen. These reductions were caused by the formation of $180^{\circ}$ domains parallel to the annealing field due to the induced anisotorpy.

• Journal of Magnetics
• /
• 제2권4호
• /
• pp.130-134
• /
• 1997

The amorphous Co-based alloy Co66Fe4Ni1B15Si14 (Metglas 2714A) is a suitable magnetic core material for high frequency operation. Appreciable reduction of the coercive force can be achieved by proper heat treatment. In this study, samples annealed at wide temperature range were analyzed using differential scanning calorimetry, high frequency B-H loop tester, X-ray diffractometer and resistivity meter. The results show that coercive force at 10 kHz decreases with in-creasing annealing temperature up to 773 K, but dramatically increases above this temperature. The squareness shows that the magnetic anisotropy on longitudinal direction of the as-cast state remains up to 773 K. Above this temperature, it decreases down to 0.5 that represents random distribution of magnetic domains. The crystallization abruptly occurs between 781 K and 783 K.

• 한국주조공학회지
• /
• 제28권1호
• /
• pp.31-36
• /
• 2008

Ti-Ni-Cu alloys are very attractive shape memory alloys for applications as actuators because of a large transformation elongation and a small transformation hysteresis. Rapidly solidified Ti-Ni alloy ribbons have been known to have the shape memory effect and superelasticity superior to the alloy ingots fabricated by conventional casting. In this study, solidification structures and shape memory characteristics of $Ti-Ni_{30}-Cu_{20}$ alloy ribbons prepared by melt spinning were investigated by means of DSC and XRD. Operating parameters to fabricate the amorphous ribbons were the wheel velocity of 55 m/s and the melt spinning temperature of $1500^{\circ}C$. The crystallization temperature was measured to be $440^{\circ}C$. The crystallized ribbons exhibited very fine microstructure after annealing at $440^{\circ}C$ for 10 minutes and $460^{\circ}C$ for 5 minutes and was deformed up to about 6.8% and 6.23% in ductile manner, respectively. Stress-strain curve of the ribbon exhibited a flat stress-plateau at 64 MPa and this is associated with the stress-induced a B2-B19 martensitic transformation. During cycle deformation with the applied stress of 220 MPa, transformation hysteresis and elongation associated with the B2-B19 transformation were observed to be $4.3^{\circ}C$ and 3.6%.

• Journal of Magnetics
• /
• 제1권1호
• /
• pp.24-30
• /
• 1996

The relationship between effective permeability and the remanence ratio of an Fe-based amorphous alloy (Metglas 2605S3A) is investigated over a wide frequency range, in an effort to understand magnetization behavior of the alloy. In the frequency range from 1 to 200 kHz, the permeability is maximum at the remanence ratio of 0.4-0.5 and, at frequencies over 500 kHz, the correlation with negative coefficients emerges indicating that the permeability decreases with the remanent ratio, except for the ribbon coated with an insulating layer of MgO which exhibits both high values of the effective permeability and remanence ratio. It is considered from the correlation results that the boundary at which the dominant magnetization mechanism changes from domain wall motion to spin rotation is near 500 kHz. The core loss is also investigated as a function of annealing time when the samples are annealed at a fixed temperature of $435^{\circ}C$. The core loss in most cases decreases with the annealing time, the degree of the loss may consist of the hysteresis loss and anomalous eddy current loss. The two loss components are considered to be of similar magnitudes at low frequencies while, at high frequencies, the dominant contribution to the total loss is the anomalous loss.

• Bulletin of the Korean Chemical Society
• /
• 제17권7호
• /
• pp.621-625
• /
• 1996

A variety of metal oxides were coated by sol-gel process from their metal alkoxides on the ribbons of Co-based and Fe-based amorphous alloys, and the effects of surface oxide coating on the magnetic properties of the alloy are investigated. The core loss is found to be reduced significantly by the oxide coating, the loss reduction becoming more prominent at higher frequencies. The shape of the hystersis loop is also dependent upon the kind of the coated metal oxide. The coatings of MgO, SiO2, MgO·SiO2 and MgO·Al2O3 induce tensile stress into the Fe-based ribbon whereas those of BaO, Al2O3, CaO·Al2O3, SrO·Al2O3 and BaO·Al2O3 induce compressive stress. These results may be explained by the modification of domain structures via magnetoelastic interactions with the shrinkage stress induced by the sol-gel coating.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.478-482
• /
• 1995

The iron-based Metglas 2605S3A amorphous alloy ribbons are annealed at $435^{\circ}C$ for various periods from 5 to 210 min, and the effect of annealing is investigated on the dc magnetic properties of the ribbon. Typical square-type hysteresis loops are observed for the ribbons annealed fo 5 min, indicative of the nearly complete removal of residual stresses which are produced during melt-quenching. As the annealing time increases, the coercivity increases and the shape of hysteresis loops transforms to round type and finally to sheared one at the longest annealing time of 210 min. These results may be explained by the formation of clusters with chemical shortorder and very fine crystallites (at the annealing time of 210 min), and the diffusion-induced stresses during the formation of the clusters. For the samples annealed for 5 min, very good dc properties of the squareness ratio, coercivity and maximum permeability are observed, but, rather unexpectedly, the initial permeability is found to be very low. These results are considered to be due to a simple domain structure consisting of very small number of $^{\circ}$ domains.