• Fire Science and Engineering
• /
• v.12 no.4
• /
• pp.41-49
• /
• 1998

In this study, the thermal improvement of an isophthalic acid polyester resin by the incorporation of flame retardants has been investigated. Aluminium hydroxide, antimony oxide and alumina powder were used to formulate the flame retardant systems. The improvement of an isophthalic resin by incorporating aluminium hydroxide is dramatic(burning rate and smoke emission are reduced), although the mechanical property is decreased significantly. The addition of small amount(2.5 phr) of antimony oxide produces high char yield(31%) which acts as a protective layer on the surface of the resin.

• Journal of the Korean institute of surface engineering
• /
• v.20 no.3
• /
• pp.118-126
• /
• 1987

The Zn-Al composite electroplating was studied by using chloride zinc bath containing metal hydroxides $(Zn(OH)_2,\;Al(OH)_3))$ and aluminium powder. The size of Al powder codeposited in the beaker bath with Al powder of-400 mesh was under 10${\mu}m$. The Zn-Al composite was electro-deposited at 40$^{\circ}C$ in the ranges of current density of 5-50 A/$dm^2$ in the flowing electrolyte. The content of aluminium particles codeposited increased slightly with increasing flow rate of electrolyte from 0.5 m/sec to 1.0 m/sec, and decreased with increasing current density from 5 A/$dm^2$ to 50 A/$dm^2$. The content of aluminium particles codeposited by using the electrolyte containing zinc hydroxide(0.1M) was 2~4 wt%. The Al powder was codeposited mainly near the surface layer of the electrodeposits. The dissolution rate of aluminium particles in the electrolyte containing 0.1M $Zn(OH)_2$ and Boric acid was 0.41 g/l. day in comparison with 1.5 g/l. day dissolution rate in pure chloride bath.

• Geotechnical Engineering
• /
• v.2 no.3
• /
• pp.5-14
• /
• 1986

The results of stabilization process in silty.clays and sand-silts, which were, respectively, treated with Calcium hydroxide of the Calcium series and Aluminium Sulphate of the Aluminium series are follows. 1) In the former case used calcium hydrate and calcium cabonate for silty-clays, calcium aluminnium cabonate oxide hydrate and calcium carbonate for sandy-silts were produced 2) In the latter case used Aluminium Sulphate, by X-ray diffraction test, it was found that Aluminium Oxide was produced both in silty-clays and sandy-silts 3) As the results of stabilization process, in the former case, unconfined compression strength was increased greatly but in the latter case it was little increased.

• Journal of the Korea Furniture Society
• /
• v.27 no.4
• /
• pp.392-398
• /
• 2016

Wood-plastic composites (WPCs) composed of mainly wood flour and thermoplastics have attracted considerable attentions due to advantages of cost effectiveness, high durability, and microbial resistance. However, relatively poor fire resistance of WPCs from low thermal stability of wood and plastics prevents further uses. This study investigated the effect of expandable graphite (EG) and aluminium hydroxide (AH)/magnesium hydroxide (MH) on the properties of WPCs. The combined incorporation of both EG and metal hydroxide (i.e., AH or MH) into formulations leads to higher flexural modulus of filled composites compared to neat PP and WPC. In thermal properties, EG played an important role in improving thermal stability of filled composites by suppressing thermal decompositions of wood and PP. Moreover, EG showed better water absorption features. From this research, it can be said that EG and metal hydroxides have potentials as effective reinforcement, flame retardant, and moisture barrier.

• Elastomers and Composites
• /
• v.38 no.4
• /
• pp.316-325
• /
• 2003

The blends of waste-polyethylene (W-PE)/waste-ethylene vinyl acetate copolymer (W-EVA) with inorganic and phosphorous flame retardants (i.e., aluminium hydroxide, magnesium hydroxide, and so on) were prepared by melt mixing techniques at different compositions and foamed. The flame retardancy and foaming properties of the blends, limiting oxygen index (LOI), heat release rate (HRR), carbon monoxide yield (COY), total heat release (THR), effective heat of combustion (EHC), expandability and cell structure were investigated using cone calorimeter, SEM, LOI tester and polarizing microscope. When the composition ratios of the W-PE/W-EVA blends were 50/50 (w/w), and the ranges of the flame retardants contents were $175{\sim}220 phr$, we could obtain foams with the uniform and closed cell, high expandability (1900 % or more), high LOI, and low HRR values. These results depend on crosslinking and loaming conditions, a char formation and smoke suppressing effect. Aluminium hydroxide had more effect in the increase of LOI than magnesium hydroxide, while magnesium hydroxide considerably affected the decrease of HRR and COY.

• Journal of Korean Society of Water and Wastewater
• /
• v.18 no.5
• /
• pp.573-579
• /
• 2004

Electroflotation, which is used as an alternative to sedimentation, is a separation treatment process that uses small bubbles to remove low-density particulates. Making allowances for recent collision efficiency diagram based on trajectory analysis, it is necessary to tailor zeta potential of bubbles that collide with negatively charged particles. In this paper, the study was performed to investigate the effects of magnesium and aluminium ions on zeta potential of bubbles. And, it was studied to find out factors which could affect the positively charged bubbles. Consequently, zeta potential of bubbles increased both with higher concentration of metal ions and in the acidic pH value. And, a probable principle that explained the procedure of charge reversal could be a combined mechanism with both specific adsorption of hydroxylated species and laying down of hydroxide precipitate. It also depended on the metal ion concentration in the solution to display its capacity to control the bubble surface.

• Journal of the Korean Ceramic Society
• /
• v.28 no.4
• /
• pp.338-346
• /
• 1991

The alumina-titania composite powders coated with Al2O3 were prepared by the method of hydrolysis-deposition of mixed aluminium salt solution of Al2(SO)4-Al(NO3)3-Urea. The effects of coating-process parameters on the characteristics of coated composite powders were also investigated. As the content of TiO2 dispersed in deionized water increased, the coated composite powders were found to be more uniform in size and unagglomerated. When TiO2 powders were coated for 30 min, the optimum TiO2 content in the coating process was 400 mg/ι. The size of TiO2 particle was increased approximately from 0.7${\mu}{\textrm}{m}$ to 1.0${\mu}{\textrm}{m}$ through coating of Al2O3. The IEP of coated composite powders was pH=8.3 identical to the value of aluminium hydroxides and the zeta-potential showed nearly similar values each other. When heat treating coated composite powders at 130$0^{\circ}C$, only two phases of TiO2(rutile) and Al2TiO5 were observed. These results showed that the suface of TiO2 could be uniformly coated with the aluminium hydroxide.

• Resources Recycling
• /
• v.15 no.5 s.73
• /
• pp.52-56
• /
• 2006

Waste aluminum dross was leached with hydrochloric acid to prepare PAC, poly aluminium chloride, used as water treatment chemicals. Metallic aluminum remained in the waste aluminum dross was dissolved into the hydrochloric acid solution. The solution could be used as PAC after adjusting the required alumina concentration and the basicity. Comparing to the conventional method far preparation of PAC using aluminum hydroxide, material cost could be saved in this method. Also, there is an additional merit in view of recycling of the waste aluminum dross by reducing the amount of waste dross to be landfilled.

• KSBB Journal
• /
• v.26 no.2
• /
• pp.143-150
• /
• 2011

The aim of the study was to optimize harvesting method for concentrating microalgae from microalgae mass culture. It is well known that the mass density of microalgae is usually very low and these are small size (5-20 ${\mu}m$) in the culture medium. It is essential that microalgae is harvested and concentrated economically for economical biodiesel production from microalgae. In this study, to determine optimized conditions for microalgae harvesting by chemical flocculation. Flocculation of three algae, Chlorella ellipsoidea, Dunaliella bardawil, and Dunaliella tertiolecta, was performed using various chemical flocculants, such as inorganic flocculants (aluminium sulfate, aluminium potassium sulfate, ferrous sulfate, ferric sulfate, ferric chloride, calcium hydroxide, sodium carbonate, sodium nitrite, and sodium aluminate), organic flocculant (polyacrylamide), and biopolymer flocculants (chitosan and starch). The results indicated that aluminium based inorganic flocculants is suitable for microalgae harvesting such as Chlorella ellipsoidea, Dunaliella bardawil, and Dunaliella tertiolecta. The results also recommended that flocculant doses, agitation speed, agitation time, sedimentation time for economical microalgae harvesting method using chemical flocculants.

• Journal of Korean Society for Atmospheric Environment
• /
• v.29 no.1
• /
• pp.56-63
• /
• 2013

This study was aimed at developing and evaluating a diffusive sampling method using a barium hydroxide solution as an absorbent for measuring carbon dioxide ($CO_2$) in ambient air. The collected $CO_2$ concentration was calculated by the change of conductivity resulted in the reaction of $CO_3{^{2-}}$ and $Ba^{2+}$ in aqueous solution. The sampling rate for the diffusive sampler was determined 0.218 mL/min, as obtained from the slope of the linear correlation between the $CO_2$ mass collected by the diffusive sampler and the time-weighted $CO_2$ concentration with the active sampling method. The unexposed blank sampler sealed in aluminium foil-polyethylene laminated packets has remained stable during at least one-month storage period. A good correlation was observed between the diffusive sampler and active sampler with a coefficient of determination of 0.956. This diffusive sampler would be suitable for the indoor $CO_2$ concentration monitoring.