• Journal of Sensor Science and Technology
• /
• v.17 no.3
• /
• pp.203-209
• /
• 2008

Thick film formaldehyde (HCHO) gas sensors were fabricated by using $La_1_{-x}Sr_xMO_3$ (M= Fe, Co, Mn) ceramics. The powders of $La_1_{-x}Sr_xMO_3$ (M=Fe, Co, Mn) were synthesized by conventional solid-state reaction method. By using the $La_1_{-x}Sr_xMO_3$ (M=Fe, Co, Mn) paste, the thick-film formaldehyde sensors were prepared on the alumina substrate by silkscreen printing method. The experimental results revealed that $La_1_{-x}Sr_xMO_3$ (M= Fe, Co, Mn) ceramic powder has a perovskite structure and the thick-film sensor shows excellent gas-sensing characteristics to formaldehyde gas (sensitivity of $La_{0.8}Sr_{0.2}FeO_3$, S= 14.7 at operating temperature of $150^{\circ}C$ in 50 ppm HCHO ambient).

• Proceedings of the KIEE Conference
• /
• 2008.10a
• /
• pp.171-172
• /
• 2008

$(Ba_{0.57}Sr_{0.33}Ca_{0.10})TiO_3$ (BSCT) thick films doped with 0.1 mol% $MnCO_3$ and $Yb_2O_3$ ($0.1{\sim}0.7$ mol%) were fabricated by the screen printing method on the alumina substrate. And the structural and electrical properties as a function of $Yb_2O_3$ amount were investigated. The lattice constants of the BSCT thick film doped with 0.1 mol% is 0.3955 nm. The specimen doped with 0.7 mol% $Yb_2O_3$ showed dense and uniform grains with diameters of about 6.3 mm. The thickness of all BSCT thick films was approximately 60 mm. The Curie temperature of the BSCT specimen doped with 0.1 mol% $Yb_2O_3$ was $18^{\circ}C$, and the dielectric constantand dielectric loss at this temperature was 4637 and 4.2%, respectively. The BSCT specimen doped with 0.1 mol% $Yb_2O_3$ showed the maximum value of $349{\times}10^{-9}C/cm^2K$ at Curie temperature. The figure of merit $F_D$ for specific detectivity of the specimens doped with 0.1 mol% $Yb_2O_3$ showed the highest value of $10.9{\times}10^{-9}Ccm/J$.