• Journal of Korea Foundry Society
• /
• v.20 no.1
• /
• pp.29-37
• /
• 2000

The purpose of this study is to investigate the effect of misch metal addition on the microstructure and mechanical property of rapidly solidified AZ91 alloy by melt spinning process. As the contents of misch metal(rare earth element:Ce,La, Nd, Pr)was increased, the microstructure of RS ribbons and extrudates became finer than those of AZ91, and RE related phases($Al_{11}RE_3$, $Al_2RE$) were formed. At room temperature, the rapidly solidified AZ91+1 wt%Mm alloy showed the highest tensile strength, 430 MPa due to precipitation strengthening of${\beta}(Mg_{17}Al_{12})$ phase and Al11RE3 phase. At the elevated temperature, the mechanical property of AZ01+3 wt%Mm alloy was higher than those of other Mg alloys. The reasons were that $Al_{11}La_3$ phase was thermally stable and suppressed the grain growth. In contrast with $Al_{11}La_3$ phase, ${\beta}$ phase was thermally unstable and could not suppress the grain growth at the elevated temperature. Therefore, Al11RE3 phase contributed to improve the thermal stability of RS AZ91 Alloy.

• Journal of Korea Foundry Society
• /
• v.17 no.5
• /
• pp.494-501
• /
• 1997

In order to manufacture large rod preforms of 2014 Al alloy with a good mechanical property by spray forming method, it was spray-formed at a droplet temperature of $715^{\circ}C$, a droplet flight distance of 400mm, and a spraying angle of $35^{\circ}$. The rod preforms were extruded at $397^{\circ}C$ with the die temperature of $420^{\circ}C$ under the hot extrusion ratio 21:1 and T6 heat treatment was performed. The 2014 Al alloys cast by hot top process were also extruded and heat-treated at the same condition as a reference material. Microstructural observation and tensile test were carried out to investigate the effects of extrusion on microstructure and mechanical property of spray-formed Al alloy. Spray-formed Al alloys had many porosities due to inappropriate process conditions such as long droplet flight distance and low droplet temperature but have fine equiaxed grain. These porosities were reduced with decreasing in grain size by hot extrusion. Ultimate tensile strength and yield strength of spray formed-extruded 2014 Al alloy were inferior to those of the normal cast-extruded 2014 Al alloy, but elongations were superior. The control of porosity was important to get spray formed preform with a good mechanical property.

• Advances in materials Research
• /
• v.2 no.4
• /
• pp.221-235
• /
• 2013

To obtain bronze with good mechanical properties and high wear resistance, a new bronze (CADZ) is proposed on the basis of various fundamental information. The CADZ consists of the elements Al10.5, Fe4.2, Sn3.7 and Ni3.1, and its design is based on Cu-Al10.5 alloy. The Cu-10.5%Al is very hard and brittle. To obtain the high material ductility of the Cu-10.5%Al alloy, an attempt was made to add a few percent of Sn. Moreover, to make high strength of the Cu alloy, microstructure with small grains was created by the proper amount of Fe and Ni (Fe/Ni = 0.89). The mechanical properties of the CADZ sample have been examined experimentally, and those were compared with commercial bronzes. The tensile strength and wear resistance of CADZ are higher than those for commercial bronzes. Although the ductility of CADZ is the lower level, the strain to failure of CADZ is about 2.0~5.0% higher than that for the Cu-Al10.5 alloy. Details of the microstructural effects on the mechanical properties in the CADZ sample were further discussed using various experimental results.

• Transactions of Materials Processing
• /
• v.32 no.2
• /
• pp.67-73
• /
• 2023

To overcome a climate change, manufacturing complex-shaped electric mobility parts becomes one of the important issues for enhancing a performance of motor with reducing their weight. Therefore, development of laser-based additive manufacturing shed on light due to their flexible manufacturing capacity that can be suitable to solve the poor formability of Fe-Si alloys for electric mobility parts. Although there are several studies existed to optimize the performance of additively manufactured Fe-Si alloys, the post-annealing effect was not well investigated yet though this is important to control the texture and mechanical properties of additively manufactured parts. In the present work, annealing effect on the mechanical property and microstructure of additively manufactured Fe-4.5Si alloy was investigated. Because of the ordered phase initiation after annealing, the hardness of additively manufactured Fe-4.5Si alloy increased up to 1173 K while a hardness drop occurs at the 1273 K condition due to the micro-crack initiation. The response surface methodology result represents the 1173 K-5 h sample is an optimal condition to maximize the mechanical property of additively manufactured alloy without micro-cracks.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1023-1024
• /
• 2006

Al-8Fe-2Mo-2V-1Zr alloys were prepared by the gas atomization/hot extrusion and the melt spinning/hot extrusion. For the gas atomized and extruded alloy, equiaxed grains with the average size of 400 nm and finely distributed dispersoids with their particle sizes ranging from 50nm to 200nm were observed. For the melt spun and hot extrusion processed alloy, refined microstructural feature consisting of equiaxed grains with the average size of 200nm and fine dispersoids with their particle sizes under 50nm appeared to exhibit a difference in microstructure. Strength of the latter alloy was higher than that for the former alloy up to elevated temperatures.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.05a
• /
• pp.383-386
• /
• 2008

Magnesium alloy sheets have been extending their field of applications to automotive and electronic industries taking advantage of their excellent light weight property. In addition to their excellent light property, magnesium alloys have several other advantages: high specific strength, good welding capability and corrosion resistance. Taking advantage of these benefits, magnesium alloys have also been substituting the polymeric materials in the electronic devices industries. In sheet metal forming application with magnesium alloys, the lower formability and high springback due to the lower elastic property (Young's modulus=45 GPa) at room temperature are major hurdles by which magnesium alloys have limited applications. In this study, commercial notebook case was adopted as the benchmark model, and then design parameters and process conditions are analyzed by the finite element simulation and physical try-outs.

• Journal of Korea Foundry Society
• /
• v.33 no.3
• /
• pp.103-112
• /
• 2013

Effect of Fe and Mn contents on the tensile properties of Al-4 wt%Mg-0.9 wt%Si alloy system has been studied. Common phases of Al-4 wt%Mg-0.9 wt%Si alloy system were ${\alpha}$-Al, $Mg_2Si$, ${\alpha}-Al_{12}(Fe,Mn)_3Si$ and ${\beta}-Al_5FeSi$. As Fe content of Al-4 wt%Mg-0.9 wt%Si alloy system increased from 0.15 wt% to above 0.3 wt%, ${\beta}-Al_5FeSi$ compound appeared. When Mn content of the alloy increased from 0.3 wt% to 0.5 wt%, morphology of plate shaped ${\beta}-Al_5FeSi$ compound changed to chinese script ${\alpha}-Al_{12}(Fe,Mn)_3Si$. As Fe content of Al-4 wt%Mg-0.9 wt%Si-0.3 wt%Mn alloy increased from 0.15 wt% to 0.4 wt%, tensile strength of the as-cast alloy decreased from 191 MPa to 183 MPa and, elongation of the alloy also decreased from 8.0% to 6.2%. Decrease of these properties can be explained as the formation of plate shape, ${\beta}-Al_5FeSi$ phase with low Mn/Fe ratio of the alloy. However, when Mn content of Al-4 wt%Mg-0.9 wt%Si-0.3 wt%Fe alloy increased from 0.3 wt% to 0.5 wt%, tensile strength of as-cast alloy increased from 181 MPa to 194 MPa and, elongation of the alloy increased from 6.8% to 7.0%. These improvements attribute to the morphology change from ${\beta}-Al_5FeSi$ phase to chinese script, ${\alpha}-Al_{15}(Fe,Mn)_3Si_2$ phase shape-modified from with high Mn/Fe ratio of the alloy.

• Journal of Korea Foundry Society
• /
• v.36 no.2
• /
• pp.60-66
• /
• 2016

In this study, comparison of corrosion properties of the Mg-1.5Ge-1Zn (GZ21) alloy and Mg-9Al-1Zn (AZ91) alloy were investigated. The studied alloys were fabricated by permanent mold casting method. And the potentiodynamic test, hydrogen evolution test, immersion test and A.C Impedance test were carried out in a 3.5% NaCl solution with pH7.2 at room temperature to measure the corrosion properties. The microstructure of GZ21 alloy was composed of ${\alpha}-Mg$ and $Mg_2Ge$ phases and AZ91 alloy was composed of ${\alpha}-Mg$ and $Mg_{17}Al_{12}$ phases. From the test results, the corrosion property was improved by adding Ge. It seemed that the corrosion mechanism was changed from galvanic corrosion (AZ91) to filiform corrosion (GZ21).

• Transactions of Materials Processing
• /
• v.14 no.4 s.76
• /
• pp.338-350
• /
• 2005

Recently, in the field of automobile industry, to solve the problem of reducing the weight of automobile for the improvement of fuel efficiency and the protection of environment, the aluminum alloy parts have been substituted for the steel parts. However, the aluminum alloy does not have as good mechanical property as the steel part. To improve the mechanical property, the semi-solid die casting process is performed to make automobile parts. In the fabrication of semisolid material the control of the liquid segregation is very important to improve the material properties of aluminum alloy. In the present paper we examine the influence of the liquid segregation by the injection conditions in the semi-solid die casting has been investigated.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.05a
• /
• pp.258-262
• /
• 2008

Micro forming is a suited technology to manufacture very small metallic parts(several $mm{\sim}{\mu}m$). In this study, the micro forming property was studied, using Al5083 superplastic alloy with micro grain, suitable for the micro forming process and Zr-BMG amorphous with pseudo-superplastic phenomena in the supercooled liquid state. Micro forming experiments under stastic load status showed that distortion by slip and spin of the grain system and slip inside the grain was observed in the Al5083 superplastic alloy. In case of Zr-BMG, because there is no grain, the distribution of the forming property was similar to the load distribution between punch and metal.