• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2011.11a
• /
• pp.115-116
• /
• 2011

TNowadays, the global warming is the most serious problem in the world and the cement industry is one of the factors which are responsible for it. Therefore, the development of new binders with enhanced environment and durability performance is needed. In this regard, the geopolymer technology is one of the breakthrough developments as an alternative to the portland cement. This paper shows some points of view on the development of geopolymers by reviewing previous researches including historical background, constituents of geopolymers, process of geopolymerization and several applications of geopolymer. Hence, the author proposes two research trends which are finding the best combination between the source materials and alkali liquid then, evaluating the corrosion for the metal bars.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.389-390
• /
• 2010

this study is preliminary experimental research for develop methods to utilize the natural Hwangtoh as replacement materials for the cement in concrete, via alkali activation at $60^{\circ}C$ using NaOH solution and liquefied $Na_2SiO_3$ in a manufacture process of Hwangtoh concrete binder.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.9 no.3
• /
• pp.120-128
• /
• 2005

In the construction industry, due to the cost rise of raw material for concrete, we have looked into recycling by-products which came from foundry. When using the Ground Granulated Blast-Furnace Slag(SG), it is good for enhancing the qualities of concrete such as reducing hydration heat, increasing fluidity, long-term strength and durability, but it has some problems : construction time is increased or the rotation rate of form is decreased due to low development of early strength. In this study, therefore, to enhance the early strength of SG mortar, we used some alkali activators(KOH, NaOH, $Na_2CO_3$, $Na_2SO_4$, water glass, $Ca(OH)_2$, alum. This paper deals with reacted products, setting time, heat evolution rate, flow and the strength development of SG cement mortar activated by alkali activators. From the results, if alkali activators were selected and added properly, SG is good for using as the materials of mortar and concrete.

• Journal of the Korean Ceramic Society
• /
• v.52 no.6
• /
• pp.483-488
• /
• 2015

Blast furnace slag(BFS) is well known for its hardening mechanism in ordinary Portland cement with alkali activation due to its latent hydraulic property. The possibility of using calcium compound as activator for BFS has been investigated in this study. The hydration properties of calcium compound activated BFS binders were explored using heat of hydration, powder X-ray diffraction and compressive strength testing. Heat of hydration results indicate that the hydration heat of BFS is lower than OPC paste by about 50%. And ettringite as hydration product was formed continuously as the calcium sulfate was decreased. The maximum compressive strength of hardened BFS mortar at 28 days is confirmed to be 83% as compared with hardened OPC mortar.

• Journal of the Korea Concrete Institute
• /
• v.24 no.3
• /
• pp.315-322
• /
• 2012

Alkali-activated slag (AAS) is the most obvious alternative materials that can replace OPC. But, AAS industrial usage as a structural material should be evaluated for its durability. Carbonation resistance is one of the most important factors in durability evaluation. Test results for 18 slag-based mortars activated by sodium silicate and 6 OPC mortars were obtained in this study to verify the carbonation property. Main variables considered in the study were flow, compressive strength before and after carbonation, and carbonation depth. Mineralogical and micro-structural analysis of OPC and AAS specimens prior to and after carbonation was conducted using XRD, TGA, FTIR FE-SEM. Test results showed that CHS was major hydration products of AAS and, unlike OPC, no other hydration products were found. After carbonation, CSH of hydration product in AAS turned into an amorphous silica gel, and alumina compounds was not detected. From the analysis of the results, it was estimated that the micro-structures of CSH in AAS easily collapsed during carbonation. Also, the results showed that this collapse of chemical chain of CSH lowered the compressive strength of concrete after carbonation. By increasing the dosage of activators, carbonation resistance and compressive strength were effectively improved.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2003.07a
• /
• pp.1009-1012
• /
• 2003

A novel powder processing technique for the preparation of copper activated zinc sulfide (ZnS:Cu,Al) phosphor by combustion process has been proposed. Exothermic reaction between dissolved copper nitrate and carbohydrazide give small-sized particles in presence of alkali metal halides at lower temperature than the traditional method of preparation. This new route takes less than five minutes and requires much less energy. The optical and luminescence characteristics of ZnS:Cu,Al phosphor thus prepared were found to be enhanced significantly. Carbohydrazide acted as fuel at $500^{\circ}C$ with rapid heating and then the phosphors obtained were heated at $900^{\circ}C$ in an inert atmosphere for 3hrs to get better luminescent properties.

• Journal of the Korea Concrete Institute
• /
• v.28 no.5
• /
• pp.593-600
• /
• 2016

The paper presented investigates the effects of kaolinite on strength properties of alkali-activated multi-component cement. The binders of this study was blended of ground granulated blast furnace slag (GGBFS), fly ash (FA), silica fume (SF) and kaolinite (KA). In this study, the specimens of combination of 20%~70% GGBFS, 10%~60% FA, 10% SF (constant ratio) and 10%~50% KA binder were used for strength properties tests. The water/binder ratio was 0.5. The binders (GGBFS + FA + SF + KA) was activated by sodium hydroxide (NaOH) and sodium silicate ($Na_2SiO_3$) was 10% by total binder weight (10% NaOH + 10% $Na_2SiO_3$). The research carried out is on the compressive strength, water absorption, ultrasonic pulse velocity (UPV) and X-ray diffraction (XRD). The compressive strength decreased as the contents of KA increase. One of the major reason for this is the low reactivity of KA compared with other raw materials used as precursors such as GGBFS or FA. The presence of remaining KA indicates that the initially used quantity has not fully reacted during hydration. Moreover, the results have indicated that increased of KA contents decreased UPV under all experimental conditions. The drying shrinkage and water absorption increased as the content of KA increase. Test result clearly showed that the strength development of multi-component blended cement were significantly dependent on the content of KA and GGBFS.

• Journal of the Korea Concrete Institute
• /
• v.29 no.4
• /
• pp.415-424
• /
• 2017

The purpose of this study is to investigate the effect of sulfate (${SO_4}^{2-}$) and magnesium ($Mg^{2+}$) ions on sulfate resistance of Alkali-activated materials using Fly ash and Ground granulated blast furnace slag (GGBFS). In this research, 30%, 50% and 100% of GGBFS was replaced by sodium silicate modules ($Ms(SiO_2/Na_2O)$, molar ratio, 1.0, 1.5 and 2.0). In order to investigate the effects of $Mg^{2+}$ and ${SO_4}^{2-}$, compression strength, weight change, lengh expansion of the samples were measured in 10% sodium sulfate ($Na_2SO_4$), 10%, 5% and 2.5% magnesium sulfate ($MgSO_4$), 10% magnesium nitrate ($Mg(NO_3)_2$), 10% [magnesium chloride ($MgCl_2$) + sodium sulfate ($Na_2SO_4$)] and 10% [magnesium nitrate $(Mg(NO_3)_2$ + sodium sulfate ($Na_2SO_4$)] solution, respectively and X-ray diffraction analysis was conducted after each experiment. As a result, when $Mg^{2+}$ and ${SO_4}^{2-}$ coexist, degradation of compressive strength and expansion of the sample were caused by sulfate erosion. It was found that the reaction of $Mg^{2+}$ with Calcium Silicate Hydrate (C-S-H) occurred and $Ca^{2+}$ was produced. Then the Gypsum ($CaSO_4{\cdot}2H_2O$) was formed due to reaction between $Ca^{2+}$ and ${SO_4}^{2-}$, and also Magnesium hydroxide ($Mg(OH)_2$, Brucite) was produced by the reaction between $Mg^{2+}$ and $OH^-$.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2005.05a
• /
• pp.131-135
• /
• 2005

• Journal of the Korean Society of Food Science and Nutrition
• /
• v.27 no.5
• /
• pp.993-999
• /
• 1998

Methanol extract of roots of Amblytropis pauciflora Kitagawa showed the antimicrobial activity to three test strains. Antimicrobial spectra of various extracts of Amblytropis pauciflora Kitagawa were tested against 24 strains of bacteria and fungi. The crude methanol extract inhibited the growth of 12 strains of bacteria and Asp. fumigatus with the exception of yeasts. The properties of the antimicrobial substance were very stable under heat(at 12$0^{\circ}C$), acid(pH 3.0) and alkali(pH 11.0) treatment. Only the root harvested in spring showed the antimicrobial activity. Among the components extracted by butanol, ginseng saponin Rg1 and various saponin-like materials were detected by TLC analysis using a plate of silica gel 60F254. The antimicrobial compound was purified by methanol extraction, activated charcoal column chromatography, Sep-pak(C18) pretreatment and reverse phase HPLC. The purified compound was detected at 13.520 min as a single peak(about 98% purity) through the HPLC analysis.