• Advances in materials Research
• /
• v.4 no.3
• /
• pp.133-144
• /
• 2015

The aim of this investigation is to prepare geopolymer resin by alkali activation of ceramic waste (AACW) with different sodium hydroxide (NaOH) and liquid sodium silicate (LSS) concentrations. In order to prepare geopolymer cement, AACW was replaced by 10 and 30 % by weight (wt.,) of concrete waste (CoW) as well as 10 and 30 wt., % ground granulated blast-furnace slag (GGBFS). The results showed that, the compressive strength of AACW increases with the increase of activator content up to 15:15 wt., % NaOH: LSS. All AACW hardened specimens activated by 3:3 (MC6), 6:6 (MC12), 12:12 (MC24) and 15:15 wt., % (MC30) NaOH: LSS destroyed when cured in water for 24h. The MC18 mix showed higher resistivity to water curing. The results also showed that, the replacement of AACW containing 9:9 wt., % NaOH: LSS (MC18) by 10 (MCCo10) and 30 (MCCo30) wt., % CoWdecreased the compressive strength at all ages of curing. In contrast, the MCCo10 mix showed the lower chemically combined water content compared to MC18 mix. The MCCo30 mix showed the higher chemically combined water content compared to MC18 and MCCo10 mixes. The compressive strength and chemically combined water of all AACWmixes containing GGBFS (MCS10 and MCS30) were higher than those of AACWwith no GGBFS (MC18). As the amount of GGBFS content increases the chemically combined water increases. The x-ray diffraction (XRD) proved that as the amount of CoWcontent increases, the degree of crystallinity increases. Conversely, the replacement of AACW by GGBFS leads to increase the amorphiticity character. The infrared spectroscopy (FTIR) confirms the higher reactivity of GGBFS compared to CoW as a result of successive hydration products formation, enhancing the compaction of microstructure as observed in scanning electron microscopy (SEM).

• Advances in concrete construction
• /
• v.10 no.4
• /
• pp.311-317
• /
• 2020

Performance of Sustainable materials continues through using of recycled waste construction materials to minimize the utilization of the natural resources. The cement industry is a major source of CO₂ in the atmosphere which is the main cause of global warming. Replacement of OPC with other sustainable cementitious materials has been the most interesting area of researches. This investigation focuses on the properties of alkali-activated mortar with the different replacement ratios of ceramic tile powder (CTP) by fine soil powder (FSP) (0 to 100)% and different molarities of sodium hydroxide concentrations. The experimental program was conducted by examining the compressive strength, water absorption, and water sorptivity. The results showed that the compressive strength of the specimens at age of (28, 56, and 90 days) increases with an increase in the amount of fine soil powder content and decreases at the age of 120 days. Also, minimum water absorption at the age of 90 days was found in the mixes containing 100% fine soil powder. However, fine soil powder replacement had a negative effect on the sorptivity and water absorption values at the age of 120 days. On the other hand, the 12M sodium hydroxide concentration was considered the optimum concentration compared to other concentrations.

• Resources Recycling
• /
• v.28 no.6
• /
• pp.64-72
• /
• 2019

Fly ash has different chemical composition depending on the type and quality of flaming coal. Fly ash is classified according to carbon content and particle size. Waste glass powder is manufactured by crushing glass. Exterior Insulation Finish System (EIFS) is generally applied by using poly-styrene foam which is economical and has excellent thermal insulation performance. However, poly-styrene foam has excellent insulation performance, but it is vulnerable to fire, which is becoming a serious problem. In this study, using a fly ash and waste glass powder to produce a finishing mortar at high temperatures. Also, High temperature strength and flame retardant properties were tested according to the cover thickness. From the test result, finishing mortar prepared using fly ash and waste glass powder is due to the improved heat resistance by alkali-activated bonding. However, since the strength decreases at high temperatures, it is necessary to select an appropriate mixing proportion.