• Textile Coloration and Finishing
• /
• v.24 no.2
• /
• pp.131-137
• /
• 2012

para-Aramid fibers were treated by low-temperature plasma to improve the adhesion. The surface of para-aramid fibers were treated with gaseous plasma of several discharge power and treatment time in oxygen gas at 1Torr pressure. The treated fibers at low-temperature plasma were taken oxygen-containing functional groups and micro-crator on the surface. The modified fibers were measured by dynamic contact angle analyzer and XPS(X-ray photoelectron spectroscopy). The Interfacial adhesion properties of aramid fabric and polyurethane resin were determined by T-peel test. The surface of aramid fibers were observed by FE-SEM photographs. It was found that surface modification and chemical component ratio of the aramid fibers were improved wettability and adhesion characterization.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.2
• /
• pp.79-82
• /
• 2005

This study investigated the effect of nitriding on the hardness and adhesion properties of $TiB_2$ coatings. Inductively coupled plasma (ICP) was used for both nitriding and deposition. By applying ICP, H13 steel was nitrided at a high rate of $50\;{\mu}m/hr$. After nitriding, a Fe4N compound layer or a diffusion layer was formed according to the hydrogen/nitrogen ratio. Both layers could improve the load-bearing capacity of the substrate by increasing the substrate hardness. The adhesion of the $TiB_2$ coatings increased to $\~30N$ after nitriding, but the hardness of the coating was lowered to 20-30 GPa. However, the adhesion of the $TiB_2$ coatings with a high hardness (>60 GPa) could not be improved substantially by nitriding due to the large difference in hardness between the coating and the substrate. The grain size of the $TiB_2$ coating was larger on the nitrided substrates, resulting in a decrease in the hardness of the coating.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.61-62
• /
• 2006

In this paper, it was demonstrated that organic thin- film transistors (OTFTs) were fabricated with the organic adhesion layer between an organic semiconductor and a gate insulator by vapor deposition polymerization (VDP) processing. In order to form polymeric film as an adhesion layer, VDP process was also introduced instead of spin-coating process, where polymeric film was co-deposited by high-vacuum thermal evaporation from 6FDA and ODA followed by curing. The saturated slop in the saturation region and the subthreshold nonlinearity in the triode region were c1early observed in the electrical output characteristics in our organic thin film transistors using the staggered-inverted top-contact structure. Field effect mobility, threshold voltage, and on-off current ratio in 15-nm-thick organic adhesion layer were about $0.5\;cm^2/Vs$, -1 V, and $10^6$, respectively. We also demonstrated that threshold voltage depends strongly on the delay time when a gate voltage has been applied to bias stress.

• Journal of Adhesion and Interface
• /
• v.8 no.4
• /
• pp.8-13
• /
• 2007

In this study, solvent-free waterborne polyurethanes (SWPU) were synthesized with teramethylxylene diisocyanate (TMXDI), poly(tetramethylene glycol) (PTMG) and polycarprolactone (PCL) and different mole ratio of dimethylol proponicacid (DMPA). The effect of ionic contents in the solvent-free waterborn polyurethane on thermal, mechanical properties and adhesion strength were studied. Glass transition temperature (Tg) were in range of $-70{\sim}-50^{\circ}C$ and increased as PCL contents increased in polyol. With more incorporation of PCL and DMPA contents in SWPU, tensile strength, adhesion strength and heat resistance of SWPU increased, while the elongation decreased.

• Journal of Adhesion and Interface
• /
• v.16 no.1
• /
• pp.22-28
• /
• 2015

In this study, Waterborne polyurethanes (WPU) using Epoxy group were synthesized with polyester polyol, epoxy resin, 4,4-dicyclohexylmethane diisocyanate ($H_{12}MDI$), dimethylol propionic acid (DMPA) to improve the hydrolysis resistance and adhesion. In addition, the properties of the synthesized waterborne polyurethane was evaluated through DSC, UTM, adhesion strength. Tg of the synthesized waterborne polyurethane is shown in the vicinity of $-50^{\circ}C$. Tg were increased with as epoxy resin contents increased. The tensile strength was increased as the content of epoxy resin increases, elongation was decreased. Optimum adhesion and hydrolysis-resistance strength were obtained when polyol : epoxy ratio was 99 : 1.

• Journal of Adhesion and Interface
• /
• v.23 no.4
• /
• pp.137-143
• /
• 2022

In this study, the polyurethane acrylates (PUA) resin with good adhesive and flexibility for adhesive for shoes and clothing were synthesized using that poly(tetramethylene adiphate glycol) (PTAd), poly(tetramethylene ether glycol) (PTMG) as polyester polyol and polyether polyol respectively, including 4,4'-methylene diphenyl diisocyanate (MDI), isophorone diisocyanate (IPDI), 1,4-butandiol (1,4-BD), 2-hydroxyethyl methacrylate (2-HEMA) and dibutyl amine (DBA). The effect of polyol blend in the polyurethane acrylate on thermal and mechanical properties, adhesion strength and flexural strength were studied. The glass transition temperature (T_g) of PUA was confirmed in range of -70~-40 ℃. In addition, the glass transition temperature (T_g), decomposition temperature (T_d), tensile strength adhesion strength and heat resistance were increased as increasing of PTAd amount while the elongation, water resistance and flexural properties were decreased. The synthesized polyurethane acrylate with 5:5 ratio of PTAd and PTMG indicated the highest adhesion strength and flexural properties.

• Journal of Adhesion and Interface
• /
• v.2 no.3
• /
• pp.16-24
• /
• 2001

The curing behavior of a phenolic resin (F/p: 1.3, 1.9, 2.5 for resol resin, F/P: 0.5, 0.7, 0.9 for novolac resin) has been studied by FT-IR spectroscopy. In this study is to synthesis of resol and novolac type phenolic resin with different F/P molar ratios and to compare the level of cure at different curing temperature conditions ($130^{\circ}C$, $160^{\circ}C$, $180^{\circ}C$ for resol resin, $160^{\circ}C$, $170^{\circ}C$, $180^{\circ}C$ for novolac resin) for 3, 5, 7, 10, 20, and 60 (min.), respectively. The conversion (${\alpha}$) was determined by the ratio of the peak area with time to the peak area of non-baked phenolic QH ($3300cm^{-1}$) at spectra. It is concluded that the initial curing rate of resol and novolac resin was increased as the molar ratio of formaldehyde/phenol increased and as the curing temperature of resin increased. According to the analysis was by the homogenous first-order model, the initial curing rate of resol and novolac resin was increased as the molar ratio of formaIdehyde/phenol increased at specific curing temperature.

• Journal of Korean Ophthalmic Optics Society
• /
• v.16 no.1
• /
• pp.97-106
• /
• 2011

Purpose: This review article was written to theoretically compare the depressing force (pressure, adhesion) to the cornea between when the spherical lenses were being tightly and flat fitted. Methods: Mathematical equations and their numerical solution programs (model) were formulated to calculate the depressing (adhesion) force to the cornea by both the tightly and flat fitted contact lenses. Based on this proposed model the effects of parameters characterizing a contact lens such as BCs, diameters, edge shape and corneal shape (ratio of long and short corneal axis, p) on the depressing force to the cornea were predicted/analyzed in both tightly and flat fitting regimes. Results: Corneal adhesion increased as the corneal p-value increased. Adhesion increase caused by the increased p-value was much larger in flat fitted case than in tight fitted one. Corneal adhesion reduced abruptly as the BC increased in flat fitting regimes while the adhesion rise was insignificant in tight fitting ones. Reduction in corneal adhesion due to lens-size increase was predicted to be insignificant in both tight and flat fitting regimes. Both the lens edge shape (edge angle) and thickness were relevant only in tight fitting regime. Corneal adhesion increased as the increased with tight-fitted lenses. As the thickness of tight fitted lenses increased, corneal adhesion inversely decreased. Conclusions: The two most significantly affecting the depressing force to cornea were found to be the degree of corneal bending toward the periphery and the BCs of lenses.

• Journal of Adhesion and Interface
• /
• v.2 no.4
• /
• pp.1-9
• /
• 2001

Silicone sealants are composed of polymer, plasticizer, crosslinker, catalyst and filler. Types and compositions of components are effected on sealant performances. In recent, use of alkoxy type silicone sealant increased due to environmental advantage. In this study, we investigated effects of component types and ratios on one-part room temperature curable alkoxy type silicone sealant preparation and adhesion properties. Alkoxy type silicone sealants were prepared with various PDMS (polydimethylsiloxane) viscosities. In addition, the effect of plasticizer, crosslinkers, and catalyst on sealant obtained from by mixture of PDMS viscosities of 20000 and 80000 was investigated. Reaction temperature on change of mixing time was observed, and then proper crosslinking systems were found. Adhesion (properties) of silicone sealants were measured. In the sealants preparation, stable reaction was achieved by adjusting composition variance ratio in the sealant mixture temperature below $40^{\circ}C$. The adhesion properties of sealant differ from substrate composition. The order of adhesion strength was glass/glass > glass/aluminum > aluminum/aluminum system. The elongation of sealant was increased as polymer viscosity and plasticizer content increased. The strength was increased as crosslinker and plasticizer decreased, while catalyst increased.

• Parasites, Hosts and Diseases
• /
• v.55 no.2
• /
• pp.213-218
• /
• 2017

Most men infected with Trichomonas vaginalis are asymptomatic and can remain undiagnosed and untreated. This has been hypothesized to result in chronic persistent prostatic infection. Adhesion of the protozoan organisms to mucosal cells is considered a first and prerequisite step for T. vaginalis infection. Adhesion of T. vaginalis to prostate epithelial cells has not yet been observed; however, there are several reports about inflammation of prostate epithelial cells induced by T. vaginalis. The aim of this study was to investigate whether adhesion and cytotoxicity of T. vaginalis are involved in inflammation of prostate epithelial cells. When RWPE-1 cells were infected with T. vaginalis (1:0.4 or 1:4), adhesion of T. vaginalis continuously increased for 24 hr or 3 hr, respectively. The cytotoxicity of prostate epithelial cells infected with T. vaginalis (RWPE-1: T. vaginalis=1:0.4) increased at 9 hr; at an infection ratio of 1:4, cytotoxicity increased after 3 hr. When the RWPE-1 to T. vaginalis ratio was 1:0.4 or 1:4, production of IL-$1{\beta}$, IL-6, CCL2, and CXCL8 also increased. Epithelial-mesenchymal transition (EMT) was verified by measuring decreased E-cadherin and increased vimentin expression at 24 hr and 48 hr. Taken together, the results indicate that T. vaginalis adhered to prostate epithelial cells, causing cytotoxicity, pro-inflammatory cytokine production, and EMT. Our findings suggest for the first time that T. vaginalis may induce inflammation via adhesion to normal prostate epithelial cells.