• Journal of the Korea Concrete Institute
• /
• v.14 no.5
• /
• pp.742-749
• /
• 2002

This study was performed to clarify the formation procedure of continuous voids in cellular concrete, and to examine the effect of a foaming agent on the manufacture of cellular concrete with continuous voids. By the experiments, it was determined that cellular concrete to be formed with continuous voids is influenced by temperature, viscosity and flowability of cement paste, and stability of air voids, and is formed in accordance with cohesion of air voids. It was also found that separate voids are formed at an added amount of air voids corresponding to 2 ％ or less of the amount of cement, whereas an antifoaming phenomenon occurs when the added amount of air voids exceeds 9 ％ of the amount of cement. In products with respective cement fineness of 3,000, 6,000, and 8,000㎠/g, a higher compressive strength was exhibited at a higher cement fineness. The continuous void ratio depending on a variation in fineness was 38 ％, 52 ％, and 22 ％ in those products, respectively. That is, a highest continuous void ratio was exhibited at a cement fineness of 6,000㎠/g. When the water-cement ratio was reduced from 45％ to 25％, the compressive strength of the cellular concrete was increased from 15 kgf/㎠ to 20 kgf/㎠ Thus, the reduction in water-cement ratio was effective in achieving an increase in strength without any variation in the specific gravity of the cellular concrete.

• Journal of the Korea Concrete Institute
• /
• v.15 no.4
• /
• pp.566-573
• /
• 2003

This study was performed to manufacture a rigid sound absorbing material by increasing the continuous void ratio of cellular concrete, thereby achieving an increase in sound absorption ratio and an enhancement in strength of the cellular concrete. By the experiments, it was determined that an increase in sound absorption ratio is achieved by increasing the added amount of air voids, thereby increasing the continuous void ratio. When the material had a thickness of 5 cm, a satisfactory average sound absorption ratio of 70% was obtained at a continuous void ratio of 40% or more. An increase in the thickness of the sound absorbing material resulted in an increase in sound absorption ratio in a super bass range. The specific gravity of cellular concrete meeting an average sound absorption ratio of 70% was 0.4 at a material thickness of 5 cm, and 0.6 or less at a material thickness of 7 cm. The compressive strength of the cellular concrete having a specific gravity of 0.4 meeting an average sound absorption ratio of 70% or more was 1.37 Mpa at a cement fineness of 3,000. This compressive strength was increased to 3.34 MPa at a cement fineness of 8,000. Accordingly, it was determined that the compressive strength of cellular concrete having continuous voids increases with a higher cement fineness.

• KIEAE Journal
• /
• v.15 no.4
• /
• pp.45-52
• /
• 2015

Purpose: Foam concrete is the concrete that contains large amount of air voids inside. In general, the density of foam concrete depends on parameters like water/binder ratio, foam volume, aggregate and pozzolan content, etc. Method: In this study, the effect of foam volume and fly ash content on dry density is investigated intensively in order to find the relationship between each parameter and their abilities to counteract with each other. According to the above information, though there are quite a number of studies on the effect micro fiber on foam concrete at low volume fractions, there is still lack of information especially on the high fiber content side. The objective of the second study is to investigate further on the use of micro fiber at higher volume fraction and fill in the lacking information. Beside from this study, the investigation of the effect of micro-fiber (polypropylene) to enhance the properties of foam concrete is also carried out. Result: Of the two variables that are investigated in this study, the foam volume and the fly ash content, show significant effect on the properties of foam concrete. The foam volume tends to decrease the density and strength of foam concrete. In the second part of our study, a large fibre volume fraction is proved to be able to evidently increase the flexural strength of foam concrete up to about 40% due to the effect of fibre bridging over the crack and a significant number of fibres that intercepts the crack surfaces. However, the compressive strength is found to decrease severely due to the occurrence of large pores as the result of fibre being added into concrete mixture.