• Carbon letters
• /
• v.5 no.2
• /
• pp.51-54
• /
• 2004

Isotropic pitch-based carbon fiber was isothermally activated in $CO_2$ atmosphere. Structural parameters of the isotropic carbon fibers and activated carbon fibers (ACFs) were evaluated by X-ray diffraction (XRD). The $d_{002}$ and La of the carbon fibers were measured to be 4.04 ${\AA}$ and 23.6 ${\AA}$ and those of ACFs were 4.29 ${\AA}$ and 22.7 ${\AA}$, respectively, representing less ordered through activation process. The pores in the ACFs were characterized by BET, and they showed super-high specific surface area of maximum value 3,495 $m^2/g$ from average pore size of 8.3 ${\AA}$ at 59% burn-off. It was recognized that 8-9 ${\AA}$ was optimum range of pore size for efficient creation of high specific surface area. The average size of the pores formed at higher temperature ($1100^{\circ}C$) was larger than that of the pores formed at lower temperature ($900^{\circ}C$).

• Journal of Korean Society for Atmospheric Environment
• /
• v.25 no.2
• /
• pp.122-132
• /
• 2009

Adsorption of toluene by activated carbon fiber (ACF) coated with dielectric heating element and desorption by applying microwave were investigated. In order to prepare adsorbent so that VOC can be desorbed by microwave heating, fine dielectric heating element with nano size was coated on the surface of the ACF using hybrid binder. Eight adsorbents (ACF-DHE, Activated Carbon Fiber coated with Dielectric Heating Element) were prepared with different amount of dielectric heating element, kinds of hybrid binder, and solvent. In order to investigate adsorption characteristics, BET surface area, pore volume, and average pore size were measured for each adsorbent including ACF. Breakthrough experiments with toluene concentration, flow rate, bed length using fixed bed reactor were performed to investigate adsorbality of adsorbent, and results were compared with that of the ACF. Desorption reactor was constructed with modified microwave oven to investigate heating effect on ACF-DHE by applying microwave power. Each adsorbent saturated with toluene were put into desorption reactor. Composition of desorbed gas generated by applying controlled microwave power to reactor was measured. Up to now, hot air desorption method has been used. Experimental results showed that desorption method with new adsorbent prepared by coating dielectric heating element on ACF can be used for industrial application.

• Analytical Science and Technology
• /
• v.13 no.2
• /
• pp.131-135
• /
• 2000

We studied adsorption isotherm, surface properties and antibacterial activity of Cu treated activated carbon fiber (ACF). The BET surface area of Cu treated ACF are distributed to $688.2-887.8m^2/g$. The adsorption results show that BET surface areas move gradually to lower value with increasing treated Cu mole concentration. Using t-method, the specific micropore volumes and average pore size were obtained. From the SEM study, it is also observed that many of micropores in activated carbon fiber are blocked surface after the treatment. And we also observed that the activity of E. coli in kind of colon bacillus increases gradually to larger range with increasing Cu mole ratio. From these results, we suggest the antibacterial mechanism for metal treated ACF.

• Journal of the Korean Vacuum Society
• /
• v.2 no.4
• /
• pp.491-500
• /
• 1993

The adsorption of nitrogen (77K) and carbon dioxide(273K) was performed on a series of activated carbon fiber. Theadsorption iotherm of nitrogen was typical type 1 and that of carbon dioxide was convex. As the specific surface area increases, there are linear increases in BET constant C mean pore diameter, the width of pore size distribution, wide micropore volume, total micropore volume, total pore volume and external surface area, however, narrow micropore volume was nealy constant . The total micorpore volume fraction in total pore volume is above 97%.

• Proceedings of the Korean Fiber Society Conference
• /
• 1996.10a
• /
• pp.117-123
• /
• 1996

Cabon fiber of general purpose was prepared from coal tar pitch modified with 10% benzoquinine(BQ) at 380C for 3 hours. Such a modified pitch raised the softening of the pitch from 85C to 271C at the yield of 40%. The modified pitch was spun smoothly at a rate of 480m/min into a fiber of 20um diameter. The fiber was stabilized stepwise at 236C (5C/min) and 312C (1C/min) for 3 hours each. Both carbonized and graphitized fibers exhibited tensile strength of 570MPa which appears large enough as a precursor for active carbon fiber. The activated carbon fiber prepared exhibited relatively high surface area of 2062m2/g at 76% burn-off and rather narrow distribution pore size of 20A.

• Journal of Korean Society of Environmental Engineers
• /
• v.35 no.1
• /
• pp.31-37
• /
• 2013

To acquire enhanced adsorption capacity for especially targeted VOCs, activated carbon fiber of which surface area was $1,100m^2/g$ was selected and active metals were loaded. After screening study, Cr and Cu were selected as a base metal for improving adsorption capacity of activated carbon fiber. For acquiring better performance, metal loading, loading temperature, loading hours and kinds of loaded metals were changed as preparing variables. Properties measurement and adsorption capacity evaluation were performed. We found that the best conditions for metal loading were 5 hours loading at $100^{\circ}C$ and the adsorption capacity was enhanced almost double. Also we confirmed that more than 0.5 seconds contact time is needed for best adsorbate diffusion and adsorption over activated carbon fiber.

• Carbon letters
• /
• v.10 no.4
• /
• pp.339-344
• /
• 2009

Henequen fiber was air-stabilized, carbonized, and steam-activated to obtain high surface area activated henequen fiber (AHF). Thermal behavior of henequen fibers has been studied by TGA. The structural morphology and characteristics were observed by SEM and BET surface area measurement. The yield of AHF from natural henequen was in the range of 20~25 wt%. Mesopores (2~2.5 nm) were developed on the AHF as the activation temperature was raised up to $700^{\circ}C$, and the band of mesopore size distribution moved to 15~30 nm when the activation were carried out at $900^{\circ}C$ for 30 min. The specific surface area and the total pore volume were about $1394\;m^2/g$ and $1.30\;cm^3/g$, respectively at this activation conditions.

• Particle and aerosol research
• /
• v.6 no.4
• /
• pp.185-192
• /
• 2010

This paper reports that the installation of a carbon fiber ionizer in front of an activated carbon fiber(ACF) filter enhanced the antibacterial efficiency. In addition, the effect of the ionizer on the filtration of bioaerosols is reported. Negative air ions from the ionizer were used as antibacterial agent. The test bacteria(Escherichia coli) were aerosolized using an atomizer and were deposited on the ACF filter media for 10 minutes. E. coli deposited on the filter were exposed to negative air ions for 0, 1, 5 and 10 minutes. Then they were separated from the ACF filter by shaking incubation with nutrient broth for 4 hours. The separated E. coli were spread on nutrient agar plates and incubated at $37^{\circ}C$ for 1~3 days. The antibacterial efficiency of E. coli was measured using a colony counting method. The antibacterial efficiencies of E. coli exposed to negative air ions for 1, 5 and 10 minutes were 14%, 48% and 71%, respectively. The filtration efficiency was evaluated by measuring the number concentration of bioaerosols at the upstream and downstream of the filter media. The increase of filtration efficiency by air ions was 14%, that is similar to the 17% filtration efficiency by none air ions. The ozone concentration was below the detection limit (under 0.01ppm) when the carbon fiber ionizers were on.

• Journal of environmental and Sanitary engineering
• /
• v.12 no.2
• /
• pp.65-74
• /
• 1997

The purpose of this study was to investigate the removal effect and variation of contaminated water by various water treatment processes using sediment filter, activated carbon, photocatalysis, reverse osmosis, ultra violet sterilizer and ultra filtration. The removal effect of chloride and trace metal was low by activated carbon and ultra filter but high in reverse osmosis. The removal effect of bacteria and E. coli was low by activated carbon and membrane filter system using activated carbon but high in impregnated activated carbon. The removal effect of TCE was low in sand and ultra filter system as compared with activated carbon. Ultra filtration process was effective for purify agricultural water without E.coli. Reverse osmosis was effective to remove heavy metal and activated carbon was effective to remove halogenated organic chemical compound. The flux and the removal effect of COD in spiral wound ultrafilter were higher than the hollow fiber ultrafilter.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.04a
• /
• pp.309-310
• /
• 2003

활성탄소 (activated carbons, ACs)는 넓은 비표면적을 가지고 있어 흡착용량이 크며, 발달된 미세공을 가지고 있기 때문에 오염물질의 제거능력이 높을 뿐만 아니라 경제적, 환경 친화적인 측면에서도 유리하다. 특히 섬유화된 할성탄소섬유 (activated carbon fibers, ACFs)는 균일한 세공이 표면에 노출되어 있어 흡착속도가 빠르며, 안정성과 재생성이 좋고 섬유상이기 때문에 가공이 용이하며 직포, 부직포, 시트 등의 형태로 만들어져 용매회수, 공업제품의 정제, 오폐수의 처리시설, 소각시설의 유해 배기가스의 흡착등에 널리 사용되고 있다.[1,2] (중략)