• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.10
• /
• pp.834-839
• /
• 2000

The structural properties that SEM photograph of ZnO varistors surface studied by fractal mathematics program were investigated to verify the relations of electrical characteristics. The SEM photograph of ZnO varistors surface were changed by binary code and the grain shape of that were analyzed by fractal dimension. The void of ZnO varistors surface was found by fractal program. The relation between grain density and electrical properties depend on fractal dimension. The grain size in ZnO varistors surface was decreased by increasing of Sb$_2$O$_3$ addition. The spinel structure was formed by Sb$_2$O$_3$addition and it was depressed the ZnO grain formation. The grain size of ZnO by Sb$_2$O$_3$addition were from 5 to 10[${\mu}{\textrm}{m}$]. Among of ZnO varistors, fractal dimension of ZnO4 was very high as a 1.764. The density of grain boundary in ZnO2 and ZnO3 varistors surface was 15[%] by formed spinal structure. The breakdown electric field of ZnO2 that fractal dimension has 1.752 was very high to be 8.5[kV/cm]. When the fractal dimensin was high, the grain shape of ZnO varistors was complex and the serial layers of ZnO grain was increased.

• Journal of the Korean Ceramic Society
• /
• v.39 no.3
• /
• pp.286-293
• /
• 2002

Microstructure and the electrical porperties of a ZnO-based multilayered chip-type varistor(abbreviated as MLV) with Ag/Pd(7:3) inner electrode have been studied as a function of firing of temperature. At 1100$^{\circ}$C, inner electrode layers began to show nonuniform thickness and small voids, which resulted in significant disappearance of the electrode pattern and delamination at 1100$^{\circ}$C. MLVs fired at 950$^{\circ}$C showed large degradation in leakage current, probably due to incomplete redistribution of liquid and transition metal elements in pyrochlore phase decomposition. Those fired at 1100$^{\circ}$C and above, on the other hand, revealed poor varistor characteristics and their reproductibility, which are though to stem from the deformation of inner electrode pattern, the reaction between electrode materials and ZnO-based ceramics, and the volatilization of $Bi_2O_3$. Throughout the firing temperature range of 950∼1100$^{\circ}$C, capacitance and leakage current increased while breakdown voltage and peak current decreased with the increase of firing temperature, but nonlinear coefficient and clamping ratio kept almost constant at ∼30 and 1.4, respectively. In particular, those fired between 1000$^{\circ}$C and 1050$^{\circ}$C showed stable varistor characteristics with high reproducibility. It seems that Ag/Pd(7:3) alloy is one of the electrode materials applicable to most ZnO-based MLVs incorporating with $Bi_2O_3$ when cofired up to 1050$^{\circ}$C.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.552-556
• /
• 2002

The microstructure and electrical characteristics of A~C's ZnO varistors fabricated according to variable sintering condition, which sintering temperature is $1130^{\circ}C$ and speeds of pusher are A: 2mm/min, B: 4mm/min, C: 6mm/min, respectively, were investigated. In the microstructure, A~C's ZnO varist-ors fabricated variable sintering condition was consisted of ZnO grain(ZnO), spinel phase$(Zn_{2.33}Sb_{0.67}O_4)$ Bi-rich $phase(Bi_{2}O_{3})$, wholly. Varistor voltage of A~C's ZnO varistors sintered at $1130^{\circ}C$ increased in order A < B < C's ZnO varistors. C's ZnO varistor exhibited good characteristics that nonlinear exponent is 31.70. Leakage current of A~C's ZnO varistors exhibited below 2mA at rated voltage. Lightning impulse residual voltage of A's ZnO varistor suited standard characteristics, which is 3.85kV at 2.5kA, 4.4kV at 5kA and 5.16kV at 10kA. After multi lightning impulse residual voltage test of A's ZnO varistor exhibited good discharge characteristics which ZnO varistor reveals no evidence of puncture, flashover, cracking in visual examination. After high current impulse test of A's ZnO varistor exhibited good discharge characteristics, which variation rate of residual voltage is 0.4% before and after test, and revealed no evidence.

• Journal of the Korean Ceramic Society
• /
• v.40 no.10
• /
• pp.943-948
• /
• 2003

The microstructure and electrical characteristics of Zn-Pr-Co-Cr-Dy oxides-based varistors were investigated with Dy$_2$ $O_3$ content in the range of 0.0∼2.0 ㏖%. As Dy$_2$ $O_3$ content is increased, the average grain size was decreased in the range of 18.2∼4.6 $\mu\textrm{m}$ and the ceramic density was decreased in the range of 5.49∼4.64 g/㎤. The incorporation of Dy$_2$ $O_3$ markedly enhanced the nonlinear properties of varistors more than 9 times in nonlinear exponent, compared with the varistor without Dy$_2$ $O_3$ The varistor with 0.5∼1.0 ㏖% Dy$_2$ $O_3$ exhibited the high nonlinearity, in which the nonlinear exponent is above 55 and the leakage current is below 1.0 ${\mu}\textrm{A}$. The donor concentration and the density of interface states were decreased in the range of (4.66∼0.25)${\times}$10$\^$18//㎤ and (5.70∼1.39)${\times}$10$\^$12//$\textrm{cm}^2$, respectively, with increasing Dy$_2$ $O_3$ content. The minimum dielectric dissipation factor of 0.0023 was obtained for 0.5 ㏖% Dy$_2$ $O_3$, but further addition of Dy$_2$ $O_3$ increased it.

• Korean Journal of Materials Research
• /
• v.2 no.1
• /
• pp.12-18
• /
• 1992

The trap levels of ZnO-based varistor are obtained by Isothermal Capacitance Transient Spectroscopy method. Here ICTS measuring system consists of YHP 4192A Impedance Analyzer and a personal computer for the data acquisition. Between $-40^{\circ}C$ and $60^{\circ}C$, the grain boundary trap levels of 0.48 and 0.94eV were detected for $ZnO-Bi_2O_3-MnO$ system. The hole omission spectra are observed in the case of the addition of CoO into the $ZnO-Bi_2O_3$ system, while the electron emission spectra are detected in the case of the addition of MnO. The nonlinear resistance coefficient $\alpha$ increases with the decrease of the dormer concentration. Finally, the trap level density of $ZnO-Bi_2O_3-MnO$ system is found to decrease with the amount of CoO, while $\alpha$ is found to increase with the amount of CoO.

• Electrical & Electronic Materials
• /
• v.9 no.7
• /
• pp.708-718
• /
• 1996

The microstructure and electrical properties of the nonlinear ZnO varistor with A1$_{2}$ $O_{3}$ additions is investigated. The variation of nonlinear behavior with A1$_{2}$ $O_{3}$ additions is indicated from J-E and C-V measurement to be a result of the change of the interface defects density $N_{t}$ at the grain boundaries and the donor concentration $N_{d}$ in the ZnO grains. The optimum composition which has the nonlinear coefficients of -57 was observed in the sample with 0.005wt% A1$_{2}$ $O_{3}$ additions. The conduction mechanism at the pre-breakdown region is consistent with a Schottky thermal emission process obeying a relation given by $J^{\var}$exp[-(.psi.-.betha. $E^{1}$2/)kT] and the conduction process at the breakdown region follows a Fowler-Nordheim tunneling mechanism of the form $J^{\var}$exp(-.gamma./E).

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.6
• /
• pp.258-263
• /
• 2021

ZnO varistor is a semiconductor device which can serve to protect the circuit from surge voltage because its non-linear I-V characteristics by controlling the microstructure of grain and grain boundaries. In order to obtain desired electrical properties, it is important to control microstructure evolution during the sintering process. In this research, we defined a dataset composed of process conditions of sintering and relative permittivity of sintered body, and collected experimental dataset with DOE. Meta-models can predict permittivity were developed by learning the collected experimental dataset on various machine learning algorithms. By utilizing the meta-model, we can derive optimized sintering conditions that could show the maximum permittivity from the numerical-based HMA (Hybrid Metaheuristic Algorithm) optimization algorithm. It is possible to search the optimal process conditions with minimum number of experiments if meta-model-based optimization is applied to ceramic processing.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.1106-1110
• /
• 2003

The electrical characteristics of $A{\sim}C's$ ZnO varistors fabricated according to variable sintering condition, which sintering temperature is $l130^{\circ}C$ and speeds of pusher are A: 2mm/min, B: 4mm/min, C: 6 mm/min, respectively, were investigated. The varistor voltage of $A{\sim}C's$ ZnO varistors sintered at $1130^{\circ}C$ increased in order A < B $A{\sim}C's$ ZnO varistors exhibited below 2mA at rated voltage. Lightning impulse residual voltage of A's ZnO varistor suited standard characteristics, which is 3.85kV at 2.5kA, 4.4kV at 5kA and 5.16kV at 10kA. After multi lightning impulse residual voltage test of A's ZnO varistor exhibited good discharge characteristics which ZnO varistor reveals no evidence of puncture, flashover, cracking in visual examination. After high current impulse test of A's ZnO varistor exhibited good discharge characteristics, which variation rate of residual voltage is 0.4% before and after test, and revealed no evidence.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.5
• /
• pp.402-410
• /
• 2000

The electrical properties and stability of Pr$_{6}$/O$_{11}$-based ZnO wvaristors consisting of ZnO-Pr$_{6}$/O$_{11}$-CoO-Dy$_{2}$/O$_{3}$ based ceramics were investigated in the Dy$_{2}$/O$_{3}$ additive content range o 0.0 to 2.0 mol%. The density was nearly constant 5.62 g/cm$^3$corresponding to 97% of theoretical density as Dy$_{2}$/O$_{3}$ additive content increases up to 0.5 mol%. However the density decreased as Dy$_{2}$/O sub 3/ additive content is further additive content. Pr$_{6}$/O$_{11}$-based ZnO varistors doped with 0.5mol% Dy$_{2}$/O$_{3}$ exhibited a good nonlinearity, which is 37.76 in the nonlinear exponent and 5.36 $mutextrm{A}$ in the leakage current. And they exhibited very stress (0.80 V$_{1mA}$/9$0^{\circ}C$/12h)+(0.85 V$_{1mA}$/115$^{\circ}C$/12h)+(0.95 V$_{1mA}$/1$25^{\circ}C$/12h). Consequently it was estimated that ZnO-0.5 mol% Pr$_{6}$/O$_{11}$-1.0 mol% CoO-0.5 mol% Dy$_{2}$/O$_{3}$ based ceramics will be sufficiently used as a basic composition to develop the advanced Pr$_{6}$/O$_{11}$-based ZnO varistors in the future.he future.uture.he future.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.308-311
• /
• 1999

The varistor characteristics of $ZnO-Pr_6O_11-CoO-Er_2O_3$-based ceramics were investigated. $ZnO-Pr_6O_11-CoO-Er_2O_3$-based ceramics were sintered at $1300^{\circ}C$ and $1350^{\circ}C$in the addition range 0.0~2.0mol% $Er_2O_3$, respectively. $ZnO-Pr_6O_11-CoO-Er_2O_3$-based ceramics, which are added with 0.5mol% $Er_2O_3$ at $1300^{\circ}C$ and l.Omol% $Er_2O_3$ at $1350^{\circ}C$ sintering temperature, exhibited the bestexcellent varistor characteristics, namely, the nonlinear exponent was better 52.78 at $1300^{\circ}C$ thanat 13$1350^{\circ}C$ and the leakage current was better 6.57$\mu\textrm$A at $1350^{\circ}C$ than at $1300^{\circ}C$. Consequently, it is estimated that $ZnO-Pr_6O_11-CoO-Er_2O_3$-based ceramics, which $Er_2O_3$ is added in the range 0.5~l.Omol% will begin to be used as a predominant basic composition of $PR_6O_11$-based ZnO varistors.