• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.350-350
• /
• 2013

Sol-gel법을 이용하여 p-Si 기판위에 yttrium이 도핑된 ZnO (YZO)를 성장하였다. ZnO의 precursor로는 zinc acetate dihydrate를, yttrium의 source로는 yttrium acetate hydrate를 사용하였으며, 용매와 안정제로는 각각 2-methoxy ethanol과 monoethanolamine (MEA)를 사용하였다. yttrium의 doping 농도에 따른 영향을 알아보기 위하여 1~4 at.%로 제작된 YZO sol을 각각 p-type Si 기판에 성장하였으며, 이 후 furnace를 이용하여 500oC에서 1시간 동안 열처리하였다. 성장된 YZO 박막의 표면과 두께를 SEM을 통하여 확인하였으며, XRD를 통한 구조적인 특성을 분석한 결과 모든 박막에서 뚜렷한 c-축 배양성을 갖는 ZnO (0002)피크를 확인하였다. Hall effect를 통하여 YZO는 모두 n-type 특성을 나타낸다는 것을 확인하였으며, 광학적인 특성은 PL을 통해서 분석하였다. n-YZO/p-Si 이종접합의 전류-전압 특성을 분석한 결과 뚜렷한 정류특성을 나타내었다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.5
• /
• pp.457-460
• /
• 2006

Y doped zinc oxide (YZO) thin films were deposited on F doped $SnO_2$ (FTO) glass substrate by sol-gel method using the spin-coating system. A homogeneous and stable solution was prepared by dissolving acetate in the solution added diethanolamine as sol-gel stabilizer. YZO films were obtained after preheated on the hot-plate for 5minute before each coating; the number of coating was 3 times. After the coating of last step, annealing of YZO films performed at $450^{\circ}C$ for 30 minute. In order to confirming of a ultraviolet ray interruption and down-conversion effects, optical properties of YZO films, transmission spectrum and fluorescent spectrum were used. Also, for understanding the obtained results by experiment, the elestronic state of YZO was calculated using the density functional theory The results obtained by experiment were compared with calculated structure. The detail of electronic structure was obtained by the discrete variational Xa (DV-Xa) method, which is a sort of molecular orbital full potential method. The density of state and energy levels of dopant element were shown and discussed in association with optical properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.240-241
• /
• 2007

In general, high temperature superconducting coated conductors have intermediary buffers layer consisting of seed, diffusion barrier and cap layers. Simplification of the oxide materials buffer architecture in the fabrication of high temperature superconducting coated conductors is required because the deposition of multi-layers buffer architecture leads to a longer manufacturing time and a higher cost process of coated conductors. Thus, single buffer layer deposition seems to be important for practical coated conductor manufacturing process. In this study, a single gradient layered buffer deposition process of YZO for low cost coated conductors has been tried using DC reactive sputtering technique. About several thick YZO gradient single buffer layers deposited by DC co-sputtering process were found to act as a diffusion layer.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.200.2-200.2
• /
• 2013

Yttrium (Y)이 도핑 된 ZnO 나노 구조물을 수열합성법으로 제작하였다. 먼저 졸겔법으로 SiO2/Si 기판 위에 seed layer (Y-doped ZnO ; Y0.02Zn0.98O)를 제작하였으며 5번의 코팅을 진행하여 박막의 두께는 약 180 nm로 측정이 되었다. 그 후 진공 분위기에서 RTA를 이용하여 $500^{\circ}C$에서 3분간 열처리가 진행되었다. 이어서 수열합성법으로 mole 농도를 0.5~1.0 M 범위에서 변화시키며 YZO 시료를 제작하였다. X-ray diffraction (XRD)을 통해서 Y2O3 또는 결함과 관련된 피크는 관찰이 되지 않았으며, 모든 구조물에서 압축응력이 존재하는 알 수 있었으며, field emission scanning electron microscope (FESEM)에서 나노 구조물의 크기와 형태는 수열합성법의 mole 농도에 많은 영향을 받는 것으로 나타났다. Hall effect 측정을 통해서 모든 구조물은 n-type 전도 특성을 가지는 것으로 나타났다. 또한 광학적 특성인 photoluminescence (PL)에서는 수열합성법의 화학식을 고려할 때 Zn가 rich한 상태에서는 Zn interstitial로 존재하는 것으로 나타났고, mole 농도가 높아 질수록 free exciton에 의한 재결합인 UV emission이 우세하게 나타났다.