• 한국결정성장학회지
• /
• 제4권2호
• /
• pp.148-156
• /
• 1994

$YBa_2Cu_3O_X$상 부근의 3가지 조성을 skull melting 방법으로 4MHz에서 녹인 후 방향적 결정성장을 시켰다. 일반적인 무기재료 공정방법으로 처리된 분말을 skull에 넣은 후 $1200^{\circ}C$부근에서 용융시켰다. 사용한 성장속도는 4~0.25 cm/hr이었으며, 금속현미경, X-선 회절기, EDX 등을 이용해서 제조된 시편을 조사하여 사용한 분말의 조성에 따른 시편의 미세조직의 변화를 관찰하였다. $YBa_2Cu_7O_X$와 $YBa_5Cu_{11}O_X$ 시편의 대표적인 미세조직은 성장방향으로 자라난 침상형태의 $YBa_2Cu_3O_X$와 $Y_2BaCuO_5$ 상이 $CuO-BaCuO_2$의 공융 조직상 사이에 생성된 것으로 나타났다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1998년도 춘계학술대회 논문집
• /
• pp.351-354
• /
• 1998

The formation of the $YBa_2Cu_30_{7_\delta}$(Y123) thick films has been investigated by a surface diffusion Imcess between $3BaCu0_2$+2CuO composite coating powder and a $Y_2BaCuO_5$(Y211). This reaction has been studied in the temperature of $930^{\circ}C$ and $940^{\circ}C$ for 2h to 10h in an oxygen atmosphere. The Y211 substrates becomes covered by co-precipitation of Y123 grains and CuO inclusions. X-ray diflractotnctn. revealed that the lager consisted of an orthorhombic crystal structure. The maximum Jc of $400A/\textrm{cm}^2$ is abtained when the specimen was heat-treated at $930^{\circ}C$ for 6h on the Y211 substrate.

• 한국전기전자재료학회논문지
• /
• 제11권6호
• /
• pp.493-501
• /
• 1998

$YBa_2Cu_3O_X$ samples were fabricated by MPMG(Melt Powdered Melt Growth). Intitial composition of the mixed powders were prepared as follow ; $YBa_2Cu_3O_X$ : $Y_2BaCuO_5$ = 1:0, 1:0.2, 1:0.3, 1:0.4. After the first melt and cooling, 5wt% to 20wt% fo Ag power was added to the powder. Effects of the different initial $Y_2BaCuO_5$ and Ag addition amount on $J_c$ and magnetization of $YBa_2Cu_3O_X$ fabricated by MPMG method were investigated. The critical current density increased with the amount of $Y_2BaCuO_5$ and Ag. It was also observed that the difference between negative and positive magnetization in the magnetization hysteresis measurement at 77K was larger than the case where $Y_2BaCuO_5$and Ag were not added to the $YBa_2Cu_3O_X$ powders. It is concluded that $Y_2BaCuO_5$ sample with 40wt% amount of $Y_2BaCuO_5$ and 20wt% amount of Ag has not only the largest $J_c$ but also the improved pinning effect.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2008년도 제39회 하계학술대회
• /
• pp.1240-1241
• /
• 2008

Superconducting ceramics of YBaCuO was fabricated on SrTiO substrate by chemical fabrication method using fine powder of YBaCuO having diameter less than 1um. The pattern of the fabricated superconducting bulk was linear and the thickness of it can be controlled in the range of 50um. The structure of the surface of film by diffraction pattern and composition. The tape like YBaCuO bulk with width of 10mm was formed on substrate using similar method. Tape like film is expected to utilize as material of superconducting tape.

• 한국전기전자재료학회논문지
• /
• 제30권2호
• /
• pp.111-114
• /
• 2017

In this research, the development of fabrication technique of bulk YBaCuO superconductors for application was studied. In fluence of $BaZrO_3$ addition on magnetization characteristics of thermal pyrolysis textured YBaCuO superconductor was investigated. Fine $BaZrO_3$ particle were dispersed within the textured YBaCuO matrix by means of the thermal pyrolysis processing. Magnetic levitation force for YBaCuO superconductors were obtained using Nd-B-Fe permanent magnet, at 77 K and at the magnetic field from 0 to 5.3 K gauss. In the unadded superconductor and 5 wt% $BaZrO_3$ addition, anomalous magnetization behavior, which is characterized by the intermediate magnetic field, was observed at 77 K. Critical current density was about few hundreds $A/cm^2$ and the magnetic characteristics increased slightly by addition of $BaZrO_3$ powder. Maximum magnetic force was obtained in the YBaCuO superconducting bulk with 3 wt.% $BaZrO_3$ addition.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 1999년도 High Temperature Superconductivity Vol.IX
• /
• pp.271-274
• /
• 1999

We are investigating epitaxially grown YBa$_2Cu_3O_x$(123) on MgO single crystal by partial melting process for high power application. After fabricating of BaCuO$_2$(011), Y$_2BaCuO_5$(211) powder, we made YBa$_2Cu_3O_x$(123) Paste with just mixing of (211), (011) and CuO(001) powders. Screen printing method was used to coat YBa$_2Cu_3O_x$(123) paste on MgO single crystal. To reduce the reaction in low temperature, rapid heating was conducted at partial melting temperature. The film was analysed with the difference of cooling-rate, thickness, reaction temperature by XRD, SEM, in-plane alignment, out-of-plane alignment, temperature-resistivity characteristics.

• Bulletin of the Korean Chemical Society
• /
• 제15권1호
• /
• pp.20-22
• /
• 1994

The preparation of $YBa_2Cu_4O_8$ thick film on Ag substrate by electrophoretic deposition was directly studied. Electrophoretic deposition was carried out in solution, which was composed of presintered $YBa_2Cu_4O_8$ powder, sodium, and 2-propanol as a solvent. The deposited thick films were heat-treated in $O_2$ at 815$^{\circ}$C for 12 hours and at 450$^{\circ}$C for 12 hours. We succeeded in obtaining superconducting $YBa_2Cu_4O_8$ films on Ag substrate. Even though the chemical reactions at the $YBa_2Cu_4O_8$/Ag interface occurred in the range of 10 ${\mu}$m, superconductivity was not depressed. The thickness of the films was in the range of 60-80 ${\mu}$ m. The characteristics of the films were examined by electric resistance measurements, X-ray diffraction, and SEM observations.

• 한국분말재료학회지
• /
• 제8권2호
• /
• pp.117-123
• /
• 2001

Formation of pores in melt-processed $YBa_2Cu_3O_{7-x}$ (123) oxides and its effect on the microstructure were studied. Spherical pores with a size of a few tens of microns were formed due to the evolution of oxygen gas during melting of a 123 oxide. Some of pores were converted into liquid pockets by liquid filling, but others remained unfilled. The liquid pockets were converted into spherical 123 regions with a lower $Y_2BaCuO_5$ (211)density through the peritectic reaction during subsequent cooling, while the pores were entrapped into the periteictically grown 123 grains. The spherical 123 regions often consists of a residual melt due to the unbalanced peritectically reaction.

• Transactions on Electrical and Electronic Materials
• /
• 제10권1호
• /
• pp.31-34
• /
• 2009

The improvement of preparation process of ${YBa_2}{Cu_3}{O_x}$ superconductor and its conducting properties is important for practical applications. In this study, the additives such as $Ag_{2}O$ and PbO were used to improve the preparation conditions of ${YBa_2}{Cu_3}{O_x}$ superconducting bulk samples and the properties of ${YBa_2}{Cu_3}{O_x}$ superconductors prepared with powders using sol-gel method and solid state reaction method were studied. The effects of the different powders and the additives to the density, grain alignment, and porosity of samples, that affect the critical current density of superconductor, also have been investigated. It is found that the properties of ${YBa_2}{Cu_3}{O_x}$ prepared with sol-gel synthesized powder and the additives showed better superconductivities than those of conventionally prepared superconductors.

• Bulletin of the Korean Chemical Society
• /
• 제9권5호
• /
• pp.280-282
• /
• 1988

The structural, electrical and magnetic properties were investigated for the high-Tc superconductor $YBa_2Cu_3O_{7-x}$, where x was 0.13. The results of temperature dependence of the resistivity and the magnetization in $YBa_2Cu_3O_{6.87}$ whose structure and phase are confirmed by arialysis of X-ray powder diffraction pattern have been reported. A very sharp superconductivity transition appears at 92K in the specimen whose chemical composition is determined from redox titration, strongly suggesting that this specimen consists of a single-phase superconductor. From the results of X-ray diffraction analysis, magnetization curves, levitation and resistance measurements, it is suggested that the observed superconductivity is bulk property in nature and that the $YBa_2Cu_3O_{6.87}$ phase is responsible for the superconductivity of the present reproducible specimen.