• Progress in Superconductivity
• /
• v.10 no.1
• /
• pp.12-16
• /
• 2008

In this work, nano size $BaCeO_3$, which is a possible flux pinning medium of melt processed $YBa_{2}Cu_{3}O_x$ superconductor, was synthesized by the conventional solid state reaction method using powders. $BaCeO_3$ and $CeO_2$ were mixed thoroughly using a ball milling for 24 hours and calcined at $1200^{\circ}C$ for 5 hours for the formation $BaCeO_3$ powder. The obtained $BaCeO_3$ powder was attrition milled at various milling times of 60 min, 120 min and 240 min. The $BaCeO_3$ powders of various milling times were mixed with $YBa_{2}Cu_{3}O_x$ powder. Seed melt processed $YBa_{2}Cu_{3}O_x$-$BaCeO_3$ (15wt.%) superconductors were prepared and the superconducting properties were investigated. It was found that $T_c$ of $Y_{1.5}Ba_{2}Cu_{3}O_x$ samples was not significantly affected by $BaCeO_3$ addition, but $J_c$ of samples was increased by $BaCeO_3$ addition. The $J_c$ improvement by fine $BaCeO_3$ powder (120 min attrition-milled) was effective at low magnetic fields less than 2 T.

• Korean Journal of Materials Research
• /
• v.8 no.10
• /
• pp.950-955
• /
• 1998

Ar 이온 식각법을 이용하여 (001) SrTiO3(STO) 단결정 기판 위에 200nm 높이의 계단형 모서리를 제작하였다. 계단식은 입사하는 Ar 이온 빔에 대한 Ar 이온 입사각과 마스크 회전각을 조절함으로써 38$^{\circ}$-70$^{\circ}$의 넓은 범위로 제어할 수 있었다. 초전도 YBa2Cu3O7-$\delta$박막은 계단이 있는 STO 기판 위에 펄스레이저 증착법을 이용하여 증착하였으며, 박막의 두께는 계단 높이에 대한 박막의 두께비가 0.5-1.2가 되도록 하였다. 계단형 모서리 조셉슨 접합의 임계전류밀도와 IcRn값은 77K에서 각각 104A/$\textrm{cm}^2$, 70-200$\mu$V이었다.

• Progress in Superconductivity
• /
• v.12 no.1
• /
• pp.6-11
• /
• 2010

The milling effects of a precursor $Y_2BaCuO_5$ (Y211) powder having 1 wt.% $CeO_2$ on the microstructure and critical current density ($J_c$) of liquid infiltration growth (LIG) processed $YBa_2Cu_3O_{7-y}$ (Y-123) bulk superconductors were investigated. The microstructure analysis revealed that the Y211 size in the final Y-123 products decreased with increasing the milling time and a relatively high density and uniform distribution of Y211 inclusions were observed in the sample prepared using 8 h milled powder. However, the unexpected Y211 particles coarsening was observed from the 4 h milled sample which was further increased for 10 h milled sample. Critical current density ($J_c$) of the LIG processed Y-123 bulk superconductors was found to be dependent on the milling time of the Y211 precursor powder. The $J_c$ increased with the increase of milling time and reached up to a maximum at 8 h in the self field while 10 h milled sample showed lower $J_c$ at the same field which might be due to the exaggerated growth and non-uniform distribution of Y211 particles.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.27 no.5
• /
• pp.724-728
• /
• 1990

The X-ray diffraction pattern, electrical resistance, density and critical temperature of a series of YBa2(Cu3-xNix)O7-\ulcornersamples (0\ulcorner\ulcorner.5) were investigated with the increase of the Ni content. The samples show a principal 1.2.3-like phase with well resolved orthorhombic peaks. The final pattern of the x=0.1 sample appears to be well reacted orthorhombic YBa2(Cu,Ni)3O7-\ulcornerwith minor impurities and an appreciable amorphous fraction. From the above results, we conclude that Ni does not play an important role for the superconductivity in the Y-Ba-Cu-O system.

• Electrical & Electronic Materials
• /
• v.9 no.4
• /
• pp.404-409
• /
• 1996

The structural and electric properties of $Y_{1-x}$YbF$_{x}$Ba$_{2}$Cu$_{3}$O$_{7-y}$(x=0.0, 0.1, 0.2, 0.3, 0.4, 0.5 and 0.6) have been investigated by using XRD(X-ray diffraction), TMA(thennomechanical analysis), NMR(nuclear magnetic resonance) analysis and four probe method. $Y_{1-x}$YbF$_{x}$Ba$_{2}$Cu$_{3}$O$_{7-y}$ samples were prepared by conventional solid-state reaction method using $Y_{2}$O$_{3}$, BaCO$_{3}$, CuO and YbF$_{3}$ power. TMA and high temperature XRD results shows that orthorhombic to tetragonal phase transition occurs in the unfluorinated 1-2-3 sample while the phase change is not observed in the fluorinated 1-2-3 samples. Superconducting transition temperature(T$_{c}$) increases with increasing YbF$_{3}$ content ; T$_{c}$, of the sample reaching maximum of 102K for x=0.3, and then decreases with further increasing YbF$_{3}$ content. The structural analysis and T$_{c}$ results shows that the fluorine doping stabilize the orthorhombic phase, together with the increase in T$_{c}$.}$ c/.TEX> c/.

• Journal of Magnetics
• /
• v.1 no.1
• /
• pp.1-3
• /
• 1996

The $YBa_2Cu_3O_{7-x}$ structure has been fluorinated by a gas phase exchange technique. The ${^19}F$NMR (nuclear magnetic resonance) spin-lattice relaxation rate (1/T1) measurements on a fluorinated sample gave superconducting energy gap of $2\Delta=4.6kT_c$.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.6
• /
• pp.829-833
• /
• 1996

Superconducting YBaCuO thin films were deposited on MgO (100) single crystal substrate by rf reactive sputtering method. Sputtering target was prepared by mixing the original powders of $Y_2O_3$, $BaCO_3$, and CuO at $830^{\circ}C$, and its composition was $YBa_2Cu_{3.3}O_x$ adding the excess CuO to compensate for the loss of Cu in the deposition process. The sputtering conditions for a high quality of YBCO thin film were: substrate temperature of 13$0^{\circ}C$; gas pressure of 10 mTorr; gas mixture ($O_2$: Ar =10: 90); distance of 2.5 inch; and rf power density of 4.87 W /$\textrm{cm}^2$. The deposition rate was 2.4~2.6 nm/min. From the RBS results, it was found that Cu and Ba contents in thin films decreased with the increase of substrate temperature. The increase of gas pressure resulted in significant deficiency of Ba elements.

• 한국초전도학회:학술대회논문집
• /
• 2008.08a
• /
• pp.23-23
• /
• 2008

• Korean Journal of Materials Research
• /
• v.1 no.2
• /
• pp.71-76
• /
• 1991

The superconducting powders in $YBa_2Cu_3O_{7-x}$ and Bi-Pb-Sr-Ca-Cu-O system were easily prepared from water in oil type emulsion by loading each cation into the aqueous phase. In $YBa_2Cu_3O_{7-x}$ system, the superconducting orthorhombic phase was formed by calcining at $750^{\circ}C$ for 10h in $O_2$. The size of the superconducting phase powders was submicron. The density of the sintered specimen using this powders was about 95% of the theoretical density and the resistance sharply decreases at about 90K, In Bi-Pb-Sr-Ca-Cu-O system the low Tc phase($(Bi, Pb)_2Sr_2Ca_1Cu_2O_y$) was formed by calcining at $800^{\circ}C$ for 10h in a low oxygen partial pressure of 1/20 atm The shape of clacined powder is thin plate of which size is about $2\mu\textrm{m}$ and thickness is smaller than $\mu\textrm{m}$. It was observed that the high Tc phase ($(Bi, Pb)_2Sr_2Ca_2Cu_3O_y$) was formed by sintering at $850^{\circ}C$ for 30h in oxygen pressure of 1/20 atm without intermediary grinding. The above sintered sample exhibited superconductivity with a Tc(zero)=105K.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.242-246
• /
• 1999

For the fabrication of fault current limiting device using HTSC thick film, YBa$_2Cu_3O_x$ superconducting thick film was formed by surface diffusion process of the Y$_2BaCUO_5$ and the mixed compound of (3BaCuO$_2$+2CuO) expected to be liquid phase above the peritectic temperature of YBa$_2Cu_3O_x$. For the surface diffusion, the compounds of 3BaCuO$_2$+2CuO mixed with binder material was patterned on Y$_2BaCUO_5$ substrate by the screen printing method. After proper sintering, the characteristics of current limit on thick film fabricated was measured. The thick film was able to limit the current from 2.8213 mA$_{rms}$nu to 4.2034 mA$_{rms}$ with 500${\omega}$ load resistance, and from 4.1831 mA$_{rms}$ to 4.2150 mA$_{rms}$ with 10${\omega}$ load resistance.