• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 추계학술대회 논문집
• /
• pp.214-214
• /
• 2009

While critical properties of BSCCO wires rely considerably on grid direction upon BSCCO and have very complicated mechanism of generating a superconducting phase, making it difficult to improve properties of wires, YBCO thin-film wires which can be formed in a superconducting phase upon metal board through vapor deposition processing can get excellent direction and reduce manufacturing costs with more flexibility in improving critical properties; thus, they will be suitable for instrument application in the future. Contrary to BSCCO wires for which thick silver alloy covering materials should inevitably be used, moreover, YBCO thin-film wires have an advantage of making thickness and quality of covering materials different by usage. Such a property can be an important element to widen application of wires by presenting possibility of using thin-film wires as superconducting material for fault current limiter as well as for high power current application. In this study we intend to prepare YBCO thin-film wires with different stabilizer layers to analyze current application and current restriction properties by stabilizer layers on the basis of detailed researches on changes in current classification properties below critical value.

• 한국초전도저온공학회:학술대회논문집
• /
• 한국초전도저온공학회 2003년도 학술대회 논문집
• /
• pp.109-112
• /
• 2003

The high temperature superconducting YBCO films were deposited on the SrTiO$_3$(100) single crystals to find out the proper deposition conditions of YBCO on biaxially-textured metal substrates. Different sets of the substrate temperature, oxygen partial pressure and laser fluence were used to investigate the effect of deposition conditions on the superconducting properties. The new apparatuses for measuring critical temperature (Tc) and critical current (Ic) were designed and manufactured, which were used to obtain Tc's and Ic's of the deposited films. The accuracy of the new apparatus was confirmed by comparing the results with those from SQUID magnetometer. The results on the YBCO films deposited on single crystal substrates which will be used to get the optimum deposition conditions of YBCO films in the coated conductor, are summarized in this report.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.65-68
• /
• 2004

A lot of R&D efforts are being concentrated on the development of high performance HTS coated conductors(CC). Unlike the HTS Bi-2223 tape, a variety of processes have been tried to fabricate CC tapes. PLD and MOD are believed to be very effective methods, and high critical currents of long length CC tape have been reported. In this study, we prepared two kinds of YBCO CCs to evaluate electromagnetic property. One is YBCO tape deposited on IBAD template by PLD and the other is AMSC's MOD CC tape Critical current (Ic) in magnetic fields, its angular dependency, and n-value were measured and analyzed. Magnetic field property of Ic was appeared to be different due the fabrication process. MOD tape showed higher in-field property, n-value of both PLD and MOD tapes exponentially decreased with magnetic field. MOD tape showed higher n-value in whole magnetic fields.

• Progress in Superconductivity
• /
• 제9권2호
• /
• pp.167-172
• /
• 2008

We fabricated $YBa_2Cu_3O_{7-x}$(YBCO) films on (00l) $LaAlO_3$ substrates prepared by metal organic deposition(MOD) method using trifluoroacetate(TFA) solution. The films with various thicknesses were prepared by repeating the dip-coating and calcining processes. The effects of film thickness on phase formation, microstructures, and critical properties were evaluated by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. The microstructure and resultant critical current($I_C$) and critical current density($J_C$) varied remarkably with film thickness: The ($I_C$) value increased from 39 to 160 A/cm-width as the number of coatings increased from one to four, while the corresponding $J_C$ was measured to be in the range of $0.84-1.21\;MA/cm^2$. Both the $I_C$ and $J_C$ decreased when an additional coating was applied due to microstructural degradation, indicating that the optimum thickness is in the range of $1.1-1.8\;{\mu}m$. The possible cause for the decrease in the $I_C$ and $J_C$ value for film thicker than $1.8\;{\mu}m$ include non-uniform thickness, increased surface roughness, and the poor formability of the YBCO phase and texture arising from the insufficient heat treatment time with respect to the increased thickness.

• 한국전기전자재료학회논문지
• /
• 제19권5호
• /
• pp.467-476
• /
• 2006

We fabricated the YBCO films on LAO substrate using the TFA-MOD method and evaluated the effects of heat treatment temperature and film thickness on the microstructure, degree of texture, and critical properties. The calcining and firing were peformed at the temperature range of $370^{\circ}C-460^{\circ}C\;and\;750^{\circ}C-800^{\circ}C$, respectively. For the films fired at $775^{\circ}C$ after calcining at $400^{\circ}C-430^{\circ}C$showed highest critical temperature (Tc-onset) of 89.5 K and critical current (Ic) of 40A/cm-width which corresponds to critical current density (Jc) of $1.8MA/cm^2$. The highest critical properties are probably attributed to the formation of purer YBCO phase, stronger biaxial texture, and higher oxygen content, according to the XRD, pole-figure, SEM, Raman analysis. From the multi-coated films, the Ic increased from 39 to 169 A/cm-width as the coating repeated to four times, while the corresponding Jc was measured from once to be in the range of $0.8-1.2MA/cm^2$. Both Ic and Jc degraded as the coating repeated further, indicating that the optimum thickness is in the range of $1.0{\mu}m-1.7{\mu}m$.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2009년도 제40회 하계학술대회
• /
• pp.834_835
• /
• 2009

현재 전력 계통에서 발생하는 고장 전류에 대한 해결책으로 초전도전력기기인 고온초전도 한류기가 실용화를 눈앞에 두고 있다. 그러나, 실제 계통에 적용하기에는 몇 가지의 과제들이 아직 남아있다. 그 중에서도 한류소자의 회복속도는 고장전류 발생 후 계통의 재폐로와 연계되기 위한 중요한 성능 요소라고 할 수 있다. 본 논문에서는 초전도 한류 소자로 쓰일 수 있는 다양한 YBCO CC(Coated Conductor)들의 회복 시간에 대하여 실험을 통하여 연구하였다. 10 mA의 전류를 초전도선재에 지속적으로 인가하여, 고장전류 인가 후 발생하는 저항에 의한 전압의 추이를 관찰하여 회복 시간을 예측하였다. 그 후, 예측된 회복 시간 후 전류를 재투입하여 선재의 회복을 확인하였고, 실제 회복 시간과 비교하고 분석하였다

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2003년도 High Temperature Superconductivity Vol.XIII
• /
• pp.73-73
• /
• 2003

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2009년도 Korea Superconductivity Society Meeting 2009
• /
• pp.126-126
• /
• 2009

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2009년도 Korea Superconductivity Society Meeting 2009
• /
• pp.116-116
• /
• 2009

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2009년도 Korea Superconductivity Society Meeting 2009
• /
• pp.117-117
• /
• 2009