• 한국세라믹학회지
• /
• 제28권8호
• /
• pp.593-602
• /
• 1991

Al2O3 and NiO-doped Al2O3 powders were prepared from the ethanol solution of Al (NO3)3$.$9H2O and Ni(NO3)2$.$6H2O by spray pylolysis method using two-fluid nozzle. As a result of spraying test with 0.3 mol/{{{{ iota }} concentration starting solution, mean droplet sizes varied with 8.99∼9.69$\mu\textrm{m}$ and those standard deviation were 4.57∼5.12. As-prepared powders which were synthesized at 1000$^{\circ}C$ have spherical shape, sizes of 0.1∼3.0$\mu\textrm{m}$ and specific surface area of 22.34∼24.20㎡/g. Most powders consisted of {{{{ gamma }}-Al2O3 phase and transforned into ${\alpha}$-A;2O3 phase by calcination at 1100$^{\circ}C$ for 1 hr. NiO-doped Al2O3 sintered bodies had better sinterability than those of pure Al2O3 and 0.3 wt% NiO-doped Al2O3 had near theoretical density and dense microstructure.

• 대한화학회지
• /
• 제25권5호
• /
• pp.318-324
• /
• 1981

일차입자의 크기와 응집상태가 다른 두 종류의 $Fe_2O_3$를 부분침전법과 ball-mill 혼합법으로 BaCO$_3$와 혼합한 $BaCO_3-Fe_2O_3$계의 고체반응에 있어 $Fe_2O_3$분체의 영향을 조사하였다. TG, XRD, SEM 등을 측정에 사용하였으며, X-선 회절분석결과 Ba-ferrite의 생성과정은 다음과 같은 연속적인 2단계로 이루어진다는 것을 알았다. $BaCO_3 + 6Fe_2O_3\;{\longrightarrow}\;BaFe_2O_3 + 5Fe_2O_3 + CO_2{\uparrow}\;BaFe_2O_4 + 5Fe_2O_3 \;{\longrightarrow}\;BaFe_{12}O_{19}$ 또 $Fe_2O_3$원료분체의 응집상태와 혼합방법은 고체반응에 현저한 영향을 미친다는 것을 확인했다.

• 자연과학논문집
• /
• 제8권2호
• /
• pp.111-118
• /
• 1996

$Na_2O$-CaO-$SiO_2$ 계 유리의 화학적 내구성을 향상시키면서 작업점도의 변화를 최소화 하기 위하여, 기본 조성 유리를 선정한 후, 이 조성에 $B_2O_3$, ZnO 성분의 첨가량을 변화시키고 $Na_2O$, $Al_2O_3$, $Li_2O$ 성분을 변화시켜가면서 각 성분이 물성에 미치는 영향을 조사하여 최적 조성비를 얻는 것을 목적으로 하였다. 본 실험결과 $Na_2O$-CaO-$SiO_2$계 유리에서 연화점 변화를 최소화하고 화학적내구성을 극대화 시키는 최적조성(wt%)은 다음과 같았다.$B_2O_3$:3.36%, ZnO:2.88%, $Na_2O$:9.93%, $Al_2O_3$, $Li_2O$:0.19%, $SiO_2$:70.56%, CaO:11.22%, $K_2O$:0.14%

• 한국결정성장학회지
• /
• 제2권2호
• /
• pp.71-76
• /
• 1992

$0.05Pb(Al_{2/3}W_{1/3})O_3-0.95Pb(Zr_{0.52}Ti0.48)O_3$를 기본 조성으로 $MnO_2,Fe_2O_3$를 첨가제로 하여 사진식각법(Photolithography)을 이용 세라믹 필터를 제작하였다. $MnO_2$의 첨가량이 증가함에 따라 전기 기계 결합 계수(Kp)가 낮아지며, $Fe_2O_3$의 경우 Kp값은 57% 정도로 우수하나 기계적 품질 계수(Qm)는 $MnO_2$첨가의 경우에 비해 상대적으로 낮은 값을 보여주고 있다. $MnO_2$0.3wt% 첨가의 경우 3dB 대역폭은 155kHz, $ Fe_2O_3$0.1wt%인 경우 260kHz로써 Qmr값이 크기에 반비례하였으며, 군지연시간 특성은 $MnO_2$의 경우 Gaussian 특성을,$Fe_2O_3$의 경우 Butterworth 특성을 나타내었다.

• 한국세라믹학회지
• /
• 제37권4호
• /
• pp.354-358
• /
• 2000

Tetragonal (t)-ZrO2/Al2O3 composites doped with Y2O3, Nb2O5, and Fe2O3 ((Y, Nb, Fe)-TZP/Al2O3) were prepared over the range containing Fe2O3 from 0.1 to 0.5 mol% with 0.1 mol% intervals to evaluate the effect of Fe2O3 addition on chromaticity, hydrothermal stability, and mechanical property of the composites. After autoclaving for 20 h at 18$0^{\circ}C$ under 3.5 MPa water vapor pressure, no tlongrightarrowm phase transformation was observed probably due to the preferential solid solubility of Fe2O3 in Al2O3, the presence of the rigid Al2O3 particles, and the inherent phase stability of (Y, Nb)-TZP. The optimized strength and the fracture toughness of the composite were 700 MPa and 8.5 MPa.m1/2, respectively, when 0.1 mol% Fe2O3 was added. The composites have shown a gradual color change from a slightly white ivory to a pale yellowish brown with increasing the Fe2O3 concentration.

• 한국세라믹학회지
• /
• 제27권3호
• /
• pp.361-368
• /
• 1990

The properties of the powder of ZrO2＋3m/o Y2O3 system prepared by co-precipitation method at the pH values of 7, 9, 10 and 11 were investigated. ZrOCl2.8H2O and YCl3.6H2O were used as starting materials and NH4OH as a precipitation agent. Zirconium hydroxide near by Zr(OH)4 structure showed more excellent crystallinity and lower formation temperature of tetragonal ZrO2. In the range of this study, cubic ZrO2 was not formed and stability of tetragonal ZrO2 prepared in the conditiion of pH 7 was most excellent. Average particle sizes and specific surface areas of tetragonal ZrO2 powders, prepared as calcining amorphous zirconium hydroxides at $600^{\circ}C$ for 1h, were 0.6-0.8${\mu}{\textrm}{m}$ and 45-70$m^2$/g, respectively.

• 대한화학회지
• /
• 제38권4호
• /
• pp.309-318
• /
• 1994

La$_2O_3$-변형 BaTi$O_3$의 안정한 결함구조와 단일상 영역을 X-선 회절분석기와 주사전자현미경을 사용하여 연구하였다. La$_2O_3$-변형 BaTi$O_3$의 안정한 결함구조는 La$^{3+}$ 이온이 격자구조내의 Ba$^{3+}$ 이온을 치환하고 Ti빈자리가 전하 불균형을 보상하기 위한 결함으로 생성된 [($Ba^x_{Ba})_{1-2x}(La{\cdot}_{Ba})_{2x}][Ti^x_{Ti})_{1-x/2}(V""_{Ti})_{x/2}]O_3$이다. 안정한 결함구조가 형성되도록 BaTi$O_3$에 La$_2O_3{\cdot}3/2TiO_3$를 혼입할 때 단위격자는 약 3 mol%가 혼입될 때부터 정방정에서 입방정으로 변하였고, 고용한계는 약 14 mol%이었다. La2$O_3{\cdot}3/2TiO_2$를 고용한계 이상으로 혼입할 때는 이차상으로 La_4Ba_2Ti_5O){18}$가 생성되었다. La$_2O_3$-변형 BaTi$O_3$ 조성에서 BaO가 과량 존재하면 소결성이 나쁘지만, Ti$O_2$가 과량으로 존재하면 액상소결에 의하여 소결성이 좋아짐을 확인할 수 있다.

• 한국세라믹학회지
• /
• 제30권11호
• /
• pp.941-948
• /
• 1993

The powder mixture of Si3N4-AlN-Y2O3, Si3N4-AlN-CeO2 and Si3N4-AlN-Y2O3-CeO2 system was hot-pressed at 175$0^{\circ}C$ for 2h in N2 to prepare $\alpha$-Sialon ceramics. The mechanical property and oxidation behaviour of the prepared $\alpha$-Sialon ceramics were investigated. At 120$0^{\circ}C$, oxidation resistance was best for the Y2O3 added $\alpha$-Sialon ceramics and oxidation rate increased when the amount of CeO2 increased. But when the mixture of Y2O3 and CeO2 added $\alpha$-Sialon ceramics showed a good oxidation resistance. Fracture toughness of (Y2O3＋CeO2) added $\alpha$-Sialon ceramics was higher than Y2O3 added $\alpha$-Sialon ceramics.

• 한국세라믹학회지
• /
• 제15권2호
• /
• pp.66-71
• /
• 1978

The cobalt blue spinel stains (main composition; CoO:$Al_2O_3$=1 : 1) in CoO-NiO-$Al_2O_$3 and $CoO-Al_2O_3-Cr_2O_3$ system were prepared by the calcination of each component oxides to be adequate for the factory. The color development, the change of the lattice constnat of the spinel and its application to colored glazes were studied. The results were summarized as follows. 1) In CoO-Al_2O_3$ spinel, the excess addition of each component hardly made any variation in lattice constantand alumina-rich spinel specimens caused the brilliant blue color fade. 2) An increase of $Ni^{2+}$ in $CoO-NiO-Al_2O_3$ system, made the lattice constnat of the $CoO-Al_2O_3$ spinel smaller, and an increase of $Cr^{3+}$ in $CoO-Al_2O_3-Cr_2O_3$, larger. 3) Glazed stains under lead glaze were colored nearly same dark blue color fade.

• 한국재료학회지
• /
• 제10권4호
• /
• pp.270-275
• /
• 2000

Metal/ferroelectric/insulator/semiconductor(MFIS)-Field Effect Transistor을 위한 Pt/YMnO$_3$/Y$_2$O$_3$/Si 구조를 제조하여 MFIS 구조의 특성에 미치는 $Y_2$O$_3$박막의 영향을 고찰하였다. PLD법을 이용하여 p=type Si(111) 기판 위에 증착시킨 $Y_2$O$_3$박막은 증착온도와 관계없이 (111)방향으로의 우선배향성을 갖고 결정화 되었다. 실리콘 위에 바로 MOCVD법에 의해 강유전체 YMnO$_3$박막을 증착시킨 경우 실리콘과의 계면에서 Mn이 부족한 층이 형성되지만 $Y_2$O$_3$가 실리콘과 YMnO$_3$사이에 삽입된 경우는 $Y_2$O$_3$바로 위에서부터 화학양론비에 일치하는 양질의 YMnO$_3$박막을 얻을 수 있었다. 85$0^{\circ}C$, 100mtorr의 진공분위기에서 열처리한 YMnO$_3$박막은 $Y_2$O$_3$가 삽입된 경우 memory window 값이 $Y_2$O$_3$가 삽입되지 않은 경우보다 더 큰 값을 보였으며 5V에서 1.3V의 값을 보였다.