• Journal of the Korean Wood Science and Technology
• /
• 제20권1호
• /
• pp.15-22
• /
• 1992

This study was performed to investigate the corrosion of metal fasteners in waterborne preservative-treated wood. Of all the metal tested, steel exhibited the greatest amount of corrosion across all preservatives and exposure conditions whereas stainless steel was totally inert. Galvanized steel corroded at a much lower rate compared to steel and the corrosion of brass was negligible. Among the preservatives, CCA-Type B was the most corrosive system tested. The sequence for the average corrosivity across all metals was: CCA-type B>CCA-Type C${\geq}$ACC${\geq}$CCA-Type A. Across all metals and retentions the salt formulations were more corrosive than the oxide and the corrosion was increased with the increse in the amount of preservative loadings. The amount of corrosion was also increased with the increase in exposure relative humidity (RH) across all metals and presevatives However, at the 60% RH exposure condition, the corrosion of metals was very negligible. Consequently, it can be concluded that across all metals oxide-type preservatives should be used to prevent the corrosion problem of metal fasteners in contact with treated wood and the use of steel nail preservative-treated wood should be avoided without distinction of end-use location, i.e., exterior or interior, and the use of stainless steel or at least brass nail in damp exterior condition was strongly recommended.

• 자원리싸이클링
• /
• 제18권5호
• /
• pp.52-62
• /
• 2009

두부비지를 이용한 친환경적인 목재방부제를 조제하고, 두부비지 가수분해에 사용하는 산의 농도 및 염의 구성에 따른 방부능의 영향을 조사하는 실험을 수행하였다. 두부비지 방부제는 $25^{\circ}C$에서 1시간 동안 0, 1%, 그리고 2% 황산에 의해 가수분해된 두부비지와 염화구리 또는/그리고 붕산나트륨으로 조제되었고, 목재시편 내에 감가압법으로 주입하여 주입된 시편을 $70^{\circ}C$ 열수에서 72시간 동안의 용탈실험을 거친 후, 갈색부후균 Trametes palustris 및 백색부후균 Tyromyces versicolor에 대한 내후성을 조사하였다. 실험결과 두부비지를 가수분해한 산의 농도가 높아짐에 따라 방부제의 주입능과 내후성이 증가하였고, 용탈성은 감소하였다. 두부비지산 가수분해물/구리염 또는 두부비지 산 가수분해물/구리염/붕소염으로 처리된 목재시편은 T. palustris 및 T. versicolor에 대한 우수한 방부효능을 보였으나, 두부비지 산 가수분해물/붕소염 또는 두부비지가 포함되지 않은 방부제로 처리된 목재시편은 T. palustris에 의한 부후가 관찰되었다. 상기 결과를 토대로 1% 황산에 의해 가수분해한 두부비지, 염화구리 그리고 붕산나트륨으로 조제한 목재방부제가 두부비지를 이용한 목재방부제 조제의 최적 조건으로 평가되었다.

• Journal of the Korean Wood Science and Technology
• /
• 제33권3호통권131호
• /
• pp.64-71
• /
• 2005

본 실험에서는 초음파의 특성을 이용하여 목재를 방부처리하고 그 주입효과에 대해 검토하고자 하였다. 유용성 방부제인 NCU (나프텐산 구리)와 수용성 방부제 AAC (알킬암모늄 화합물)에 소나무 및 잣나무 시편을 침지한 후 40 kHz, 400 W 출력의 초음파를 발진시켰다. 초음파처리 이후 시편의 흡수율 및 침윤도는 시간 경과에 따라 지속적으로 증가하여 120시간 경과 후 AAC처리 잣나무, 소나무 모두에 대해 약 95%의 흡수율을 얻을 수 있었으며, 소나무 및 잣나무 각 시편 두께의 95, 83%에 해당하는 NCU의 침윤도를 얻을 수 있었다. 초음파 처리후의 시편을 SEM을 이용해 관찰하였으며, 초음파 발생에 의해 생성된 고온, 고압의 충격파가 목재 내 약액의 주입통로가 되는 벽공구를 파괴하고 초음파의 탈포작용과 목재내 추출물의 배출 등에 기인하여 약액의 주입성능이 향상된 것으로 판단된다. 초음파 처리에 의한 방부제의 주입은 가압방부처리의 적용이 어려운 소재, 단판 등에 적용이 가능할 것으로 판단된다.

• Journal of the Korean Wood Science and Technology
• /
• 제24권4호
• /
• pp.93-99
• /
• 1996

In order to investigate the extent of fixation of new water-borne preservatives in blocks of pinus densiflora sapwoods the streaming potential through the column with preservative treated wood was measured at various conditions. The rates of leachability of ingredients in the treated wood were estimated by the measurement of electric conductivity of the solution with the leached components. The solution was also analyzed by Atomic absorption spectrophotometer (AA). As a results, the experimental data indicated that the fixation of CCB, CCFZ and ACQ in wood were relatively unstable. The fixation rates of CCB, CCFZ were improved by increasing heat and drying time. The amounts of the leached ingredients were apparently higher in CCB and CCFZ than in CCA, while the rate of leaching of ACQ was not changed at various drying temperature.

• Journal of the Korean Wood Science and Technology
• /
• 제51권1호
• /
• pp.49-57
• /
• 2023

This research aimed to evaluate the durability of Samama (Anthocephalus macrophyllus) wood treated with boron preservatives, citric acid (CA), and heating against termites. Wood samples were impregnated firstly with 5% boron solutions, such as boric acid, borax and boric acid + borax combination at 1:1 (w/w). The second impregnation used 5% CA. The impregnations were conducted in a pressure tank at 7 kg/cm² for 4 hours. After impregnation, the samples were heat treated at 80℃ or 160℃. All the treated and control samples were exposed to decay fungi, drywood termites and subterranean termites based on SNI 7207:2014 standard. The results showed that boron preservatives reduced fungal attacks on Samama wood. The combination treatment of boric acid, CA and heat treatment at 160℃ was also effective to increase the resistance of Samama wood against white- and brown rot fungi, and drywood termites. Heat treatment consistently improved the resistance of Samama wood from decay fungi.

• 보존과학연구
• /
• 통권7호
• /
• pp.265-277
• /
• 1986

The degradation of wood is maimly caused by biological and thermal factor. In general, the field of wood preservation can be divided into two broadcategories; namely the deterioration, protection of wood, and the teatment of wood with preservatives. Wood in sea or brackish water incurs marine borer damage, consisting of attack by marine animal and also wood on land suffers severely from insect damage. But the largest wood degradation is caused by microorganism. Animals that attack wood in a marine environment are especially destructive in warm water-regions, little was achieved in their control recently. Therefore this manuscript only introduce the importance of wood deterioration caused by marine animal.

• Journal of the Korean Wood Science and Technology
• /
• 제38권4호
• /
• pp.341-348
• /
• 2010

목초액의 농약 또는 식품보존제로서의 이용 가능성을 검토하기 위하여 소나무 및 참나무류 기계식 목초액을 대상으로 항진균 및 항세균 활성을 검정하였다. 그 결과 항진균활성의 경우 미정제 목초액은 0.5% 이상의 농도 에서, 정제 목초액은 1.0% 이상의 농도에서 공시 식물병원균 및 목재부후균의 생장을 완전히 억제하여 미정제 목초액이 정제 목초액보다 항균활성이 높은 것으로 나타났다. 그리고 참나무류 목초액이 소나무 목초액보다 항 균활성이 높아 탄화 원료인 수종에 따라 항균활성의 차이가 있음을 알 수 있었다. 균종별로는 표고 해균인 주홍 꼬리버섯에 대한 항균효과가 다른 공시 균주에 비해 높은 것으로 나타나 균의 종류에 따라 목초액에 대한 감수성이 차이가 있는 것으로 밝혀졌다. 한편, 식품부패균 및 식중독균에 대한 항세균활성을 검정한 결과 소나무 및 참나무류 미정제 목초액의 경우 10% 농도에서 모든 공시 균주에 대해 생육저지환을 형성한 반면 정제 목초액 의 경우에는 저지환을 형성하지 않아 항세균활성도 미정제액이 정제액보다 높은 것으로 나타났다. 균종에 따른 감수성에도 차이가 있어 그람 양성균에 대한 항균활성이 그람 음성균에 비해 상대적으로 높았으나 탄화 원료에 의한 차이는 뚜렷하게 나타나지 않았다. 이상의 결과 목초액은 식물병원균, 목재부후균, 식품부패균 및 식중독 균에 대한 항균활성이 우수하여 유기합성 농약을 대체하거나 식품의 부패를 막기 위한 식품보존제로서 이용이 가능할 것으로 판단되었다.

• Journal of the Korean Wood Science and Technology
• /
• 제41권6호
• /
• pp.576-582
• /
• 2013

구리계 보존제 처리에 대한 기초 자료를 얻기 위하여 Douglas fir 변재와 ACQ-2 보존제를 사용하여 목재 내 침투 및 부후 특성을 조사하였다. 약제의 주입이 어려운 Douglas fir 수종에 대하여 약제의 주입이 잘된 곳과 안된 곳의 시료를 채취하여 약제 이동을 방해하는 인자를 구명하고자 방사조직 높이, 방사조직 밀도, 가도관의 길이를 실체현미경, 광학현미경, 그리고 전자현미경으로 측정 및 관찰하였다. 그 결과 방사조직의 높이와 밀도 그리고 가도관길이는 약제의 주입이 용이했던 부분과 주입이 안된 부분에서 차이를 보이지 않았지만, 목재 구성 세포들의 벽공에서는 차이가 나타났음을 전자현미경을 통해 관찰할 수 있었다. 약제의 주입이 안된 곳에서는 폐색된 벽공이 많이 관찰되었다. 그리고 여러 농도의 ACQ로 처리한 목재 시편을 갈색부후균으로 부후시킨 후 광학 현미경으로 부후 특성을 관찰하였다. 그 결과 무처리 시편의 가도관, 방사조직, 수지구 등의 조직이 부후되어 파괴된 것을 볼 수 있었으며, 약제 처리 농도가 낮으면 부후가 진행되므로 일정 농도 이상으로 처리해야함을 알 수 있었다.

• Journal of the Korean Wood Science and Technology
• /
• 제37권5호
• /
• pp.421-425
• /
• 2009

This research investigates the effect of copper retention on copper leaching in wood treated with copper-based preservatives. Radiata pine (Pinus radiata D. Don) sapwood samples were ground in a Wiley mill equipped with a 20-mesh screen. The ground wood was vacuum-treated with various concentrations of alkaline copper quat (ACQ), bis-(N-cyclohexyl-diazeniumdioxy)-copper (CB-HDO), and copper azole (CUAZ). The treated samples were conditioned at $70^{\circ}C$ and 100% RH for 72 hours. The samples were leached by using the distilled water for four weeks, and the copper contents in each sample were measured by X-ray spectroscopy. As expected, the copper leaching was increased with increasing of copper retention. The copper leaching from the ACQ and CB-HDO treated samples were gradually decreased with increasing copper retention: however, the copper losses from the CUAZ treated samples appeared to be proportionally increased with the increase in copper retention in all retention levels tested. The results indicate that at the conditions of the same copper retention ACQ and CB-HDO treated wood have a better leaching resistance compared to CUAZ treated wood.

• Journal of the Korean Wood Science and Technology
• /
• 제44권5호
• /
• pp.743-749
• /
• 2016

균일한 품질의 방부처리 목재 생산을 위해서는 방부약액의 농도관리가 필요하다. 아직까지 목재방부처리 현장에서 농도관리를 위하여 간편하게 방부약액의 농도를 측정할 수 있는 방법은 개발되어 있지 않다. 본 연구에서는 ACQ 목재방부제를 대상으로 비교적 손쉽게 측정할 수 있는 탁도를 이용하여 농도를 예측할 수 있는 방법을 검토하였다. 탁도가 현저하게 작은 알칼리성의 ACQ 약액에 20%의 인산 용액을 첨가하면 백색의 현탁 물질이 생성되며 탁도가 증가한다. 인산 용액의 최적 첨가량은 약액의 탁도가 최고치에 도달하는 pH 7 수준이며, 첨가량이 많아지면 약액의 산성화와 함께 탁도가 급격하게 떨어지고 약액은 투명해진다. ACQ 약액의 농도와 탁도 간에는 정(正)의 상관을 가지며 고도의 유의성이 인정되었다. 농도와 탁도로부터 유도된 회귀방정식을 사용하여 산출한 현장 채취 약액의 예측 농도 값과 적정법으로 측정한 실측 농도 값 간의 농도 차이에는 t 검정 결과, 유의성이 인정되지 않았다. 따라서 탁도와 회귀방정식을 이용하여 ACQ 현장 약액의 농도 관리가 가능할 것으로 예상된다.