• 대한금속재료학회지
• /
• 제46권10호
• /
• pp.672-682
• /
• 2008

The resistance spot welding of TRIP590 steels was investigated to enhance understanding of weld fracture during tensile-shear strength (TSS) test. The main failure modes for spot welds of TRIP590 steels were nugget pullout and interfacial fracture. The peak load to cause a weld interfacial failure was found to be related to fracture toughness of the weld and the weld diameter. Although interfacial fracture occurred in the samples, the load carrying capacity of the weld was high and not significantly affected by the fracture mode. Substantial part of the weld exhibits the characteristic dimple (or elongated dimple) fractures on interfacial fractured surface, in spite of the high hardness values associated with the martensite microstructures. The high load-bearing ability of the weld is directly associated with the area of ductile fracture occurred in weld. Therefore, the judgment of the quality of resistance spot welds in TRIP590 steels, the load carrying capacity of the weld should be considered as an important factor than fracture mode.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2012년도 추계학술대회 논문집
• /
• pp.67-68
• /
• 2012

• 한국해양공학회지
• /
• 제13권4호통권35호
• /
• pp.98-104
• /
• 1999

The crank shafts need anti-corrosion materials. So STS 304 is the essential material to manufacture this shaft. However, it costs more to manufacture the shafts by using only STS 304 than welding of STS 304 to other carbon steels. And it has been difficult to weld this sort of dissimilar materials. They could be unstable in the quality by the conventional arc welding. And also they have a lot of technical problems in manufacturing. But by the friction welding technique, it will be able to be made without such problems. Then, this study aimed not only to develop the optimization of dissimilar friction welding of crank shafts steels of STS 304, SM35C, but also to develop the application technique of the acoustic emission to accomplish in-process real-time quality(such as tensile) evaluation during friction welding of the shafts by the AE technique.

• 소성∙가공
• /
• 제9권5호
• /
• pp.512-525
• /
• 2000

Designers are frequently faced with multiple quality issues in injection molded parts. These issues are usually In conflict with each other, and thus tradeoff needs to be made to reach a final compromised solutions. The objective of this study is to develop an automated injection molding design methodology, whereby part defects such as warpage and weld line are optimized. The features of the proposed methodology are as follows: first, Utility Function approach is applied to transform the original multiple objective problem into single objective problem. Second is an implementation of a direct search-based Injection molding optimization procedure with automated consideration of process variation. The Space Reduction Method based on Taguchi's DOE(Design Of Experiment) is used as a general optimization tool in this study. The computational experimental verification of the methodology was partially carried out for a can model of Cavallero Plastics Incorporation, U. S. A. Applied to production, this study will be of immense value to companies in reducing the product development time and enhancing the product quality.

• 한국레이저가공학회지
• /
• 제2권1호
• /
• pp.30-37
• /
• 1999

Laser-welded Tailored Blank is the hottest thing in many automobile companies. But they demand on weld quality, reproducibility, and formability. So it is the great problem of automation of laser welding process. Therefore, it is requested to construct on-line process monitoring system on high accuracy. The light which is emitted from plasma and spatter in laser welding was detected by photo-diodes. It was found that the light intensity depends on welding speed. laser power, and flow rate of assist gas. The relationship between the plasma and spatter and the weld quality can be used for on-line laser weld monitoring systems.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2003년도 춘계학술발표대회 개요집
• /
• pp.102-104
• /
• 2003

Laser weldability of aluminized steels of 0.8mm thick has been investigated. Test materials were cut from the commercial steels that were produced at the Coating Mill of POCOS. Test coupons for welding were prepared by using a conventional shearing machine and no additional edge treatment was peformed. Nd:YAG laser welding system was mainly applied to make weld specimens. Test results revealed that almost no spattering was observed even though the welding was peformed with no overlap joint clearance. Bead quality of aluminized steel laser weld was smooth and stable. According to x-ray inspection results, it was proved that the laser welds of aluminized steels were metallurgically defect free.

• Journal of Welding and Joining
• /
• 제15권6호
• /
• pp.49-56
• /
• 1997

Effect of process parameters on the quality of condenser discharge weld for coated sheet steels was discussed. The welding specimens were coated with pure Zn of 20/20 g/m2 in the production line. Direct measurements of welding parameters such as the discharge current, the pressures and the voltage drop across the electrodes were carried out with welding process monitoring system. High speed camera was also utilized to analyze the weld formation process. Test results indicated that the relation between weld strength and applied energy was stabilized at the acceptable welding heat input range. It was thought that the acceptable welding heat input should be redefined based on the monitored data because the calculated value of the welding heat input could hardly be utilized if the discharge condition was changed. Mechanical test results and high speed photographs showed that expulsion deteriorated the weld quality and the strength at the same time especially when the size of the spatter was large enough to carry the molten metal, which should form the nugget, out of the welding spot. Results also demonstrated that the discharge current should be applied at the appropriate time during the process because sufficient nugget was not produced if the time was deviated from the optimum range.

• 한국기계가공학회지
• /
• 제19권4호
• /
• pp.52-57
• /
• 2020

The frequency of the manufacturing and modification of automotive press dies via overlay welding has recently increased, but the welding quality depends on the operator skills and the working conditions. Therefore, this study presents a way to improve the overlay welding quality regardless of the operator skills. Three welding conditions with different pre- and post-heating treatments were tested on some specimens; the weld surface quality was analyzed by examining the cutting face. The results demonstrated the best quality of the weld surface that was heated before and after the welding.

• Journal of Welding and Joining
• /
• 제20권3호
• /
• pp.122-128
• /
• 2002

The laser welding in the automotive industries has been used widely for the butt joint of blank sheets rather than the lap joint of automotive body panels. But as a substitute far the spot welding of automotive body panels, the so called three dimensional laser welding will be important far the body panel engineers. Specially the laser welding of body panels with a smooth weld line is applied increasingly, for example, to the side panels. So far, some criteria of the laser weld quality was suggested by in-house regulations or national standards from experiences and/or rule of thumbs. In the manufacturing places, a go or no-go criterion is adopted because of the simplicity or a lack of rational criteria. It is true specially for the selection of the process parameters, which gives the basic causes for the good quality of laser welds. In this study, the effects of joint combination, gap and welding speed on the lap joint $CO_2$ laser welding of two mild steel sheets with different thicknesses are obtained through a $2{\times}3{\times}7$ factorial experiment. The results of the weld quality are statistically analysed using analysis of variance (ANOVA) and compared between two characteristic zones, which are separated by the type of sectional shapes and the level of input energy per volume. The thickness combinations are 0.8mm/1.2mm, 1.2mm/0.8mm of mild steel sheets. The welding speed covers from the deep penetration to the partial penetration. The gap size has three levels of no-gap, 0.16m, and 0.26mm. The bead width, penetration depth and input energy per volume are measured and used as the weld quality criteria.

• 한국해양공학회지
• /
• 제22권6호
• /
• pp.27-34
• /
• 2008

The temperature distribution in the weldment is not uniform because a weldment is locally heated. Thermal plastic deformation results from the local expansion and shrinkage by the heating and cooling of metal. Therefore, residual stresses and distortion occur in the weldment. In this study, we had conducted on the weld thermal cycle simulation that is supposed as the HAZ on SS400 steel and STS304 steel. The residual stresses that were obtained from the drawing and the weld thermal cycle simulation were estimated by X-ray diffraction. We also carried out ultrasonic test for the weld thermal cycle simulated specimens, and then conducted on nondestructive evaluation by the ultrasonic parameters obtained ultrasonic test. From the results, residual stresses of weld thermal cycle simulated specimens after the residual stress removal heat treatment are lower than that of the drawing.