• Journal of Welding and Joining
• /
• v.18 no.6
• /
• pp.68-73
• /
• 2000

In case of overalyered wrapping roll, beadmark shape appear at wrapping roll surface due to irregular wear between weld bead. Irregular wear of this is caused by difference of hardness between weld bead. This study aims at investigating which matrix is good for removing of beadmark at wrapping roll surface. So, we make specimen with martensitic matrix and austenitic matrix. The overlayered alloys were deposited 4 times on a SS41 steel plate using self-shielding flux cored arc welding method. Difference of hardness between weld bead of specimen with matrix of martensite was higher than specimen with matrix of austenite both as-welded and after heat treatment. Therefore, austenitic matrix is between than martensitic matrix for removing of beadmark of wrapping roll surface.

• Journal of Power System Engineering
• /
• v.10 no.1
• /
• pp.77-82
• /
• 2006

In this study, dissimilar friction welding were produced using 15mm diameter solid bar in chrome molybedenum steel(SCM440) to carbon steel(S45C) to investigate their mechanical properties and the relationship between the weld parameters and the nondestructive coefficients, such as AE counts and ultrasonic attenuation coefficient. The main friction welding parameters were selected to endure good quality welds on the basis of visual examination, tensile tests, Vickers hardness surveys of the bond of area and heat affected zone. The specimens were tested as-welded and post weld heat treated(PWHT). The tensile strength of the friction welded steel bars was increased up to 100％ of the S45C base metal under the condition of all heating time. The ductility of PWHT specimens is higher than as-welded.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.12 no.3
• /
• pp.58-67
• /
• 2003

Welding characteristics of austienite 304 stainless and SM45C using a continuous wave Nd:YAG laser n experimentally investigated Laser beam welding is increasingly being used in welding of structural steels. The laser welding process is one of the most advanced manufacturing technologies owing to its high speed and deep penetration. The thermal cycles associated with laser welding are generally much Inter than those involved in conventional welding processes, leading to a rather small weld zone. Experiments are performed for 304 stainless steel plates changing several process parameter such as laser power, welding speed, shielding gas flow rate, presence of surface pollution, with fixed or variable gap and misalignment between the similar and dissimilar and plates, etc. The Nd:YAG laser welding process is one of the most advanced manufacturing technologies owing to its high speed and penetration. This paper describes the weld ability of SM45C carbon steel for machine structural use by Nd:YAG laser. The follow conclusions can be drawn that laser power and welding speed have a pronounced effect on size and shape of the fusion zone. Increase in welding speed resulted in an increase in weld depth/aspect ratio and hence a decrease in the fusion zone size. The penetration depth increased with the increase in laser power.

• Proceedings of the KSR Conference
• /
• 2008.06a
• /
• pp.980-985
• /
• 2008

Since its invention at TWI in 1991, Friction Stir Welding (FSW) has become a major joining process in the aerospace, railway and ship building industries especially in the fabrication of aluminium alloys. In an attempt to optimize the friction stir welding process of Al alloys for extrusion Aluminium carbody of HEMU-400X (Extrusion Aluminum 6xxx series), effects of joining parameters such as tool rotating speed, plunging depth and dwelling time on the weld joints properties were evaluated. Experimental tests were carried out for butt joined Al plates. A wide range of joining conditions could be applied to join Al alloys for Extrusion Aluminum 6xxx series without defects in the weld zone except for certain welding conditions with an insufficient heat input. The microstructures of welds have dynamic-recrystallized grain similar to stir zone in FSW weld. For sound joints without defects, at the rotation speed of 700 rpm with different welding speeds, the tensile strengths of the Stir Zone(SZ) were almost the same, 80% of those of the base metal. (JIS Z 2201)

• Journal of the Korean institute of surface engineering
• /
• v.48 no.6
• /
• pp.335-342
• /
• 2015

Recently, the production of oil and gas at the arctic ocean and offshore has been growing. Accordingly, S500 steel with the high tensile strength and excellent toughness has been used and flux cored wire that can be welded to the S500 has been required. In this study, we carried out observation of microstructures, mechanical properties and CTOD (crack tip openning displacement) in the weld zone that GMA (gas metal arc) welded with different component of $TiO_2$ flux core wire (the main components, rutile or Ti-slag) for S500 steel. Weld zone produced with Ti-slag flux cored wire has formed a enough acicular ferrite and shown excellent impact toughness at $-40^{\circ}C$, tensile strength at room temperature and CTOD at $-20^{\circ}C$. As a result, the developed flux cored wire was suitable for S500 steel.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.1154-1159
• /
• 2004

Laser beam welding is increasingly being used in welding of structural steels. The laser welding process is one of the most advanced manufacturing technologies owing to its high speed and deep penetration. The thermal cycles associated with laser welding are generally much faster than those involved in conventional arc welding processes, leading to a rather small weld zone. Experiments are performed for Inconel 600 plates changing several process parameter such as laser power, welding speed, shielding gas flow rate, presence of surface pollution, with fixed or variable gap and misalignment between plate and plate, etc. The follow conclusions can be drawn that laser power and welding speed have a pronounced effect on size and shape of the fusion zone. Increase in welding speed resulted in an increase in weld depth/ aspect ratio and hence a decrease in the fusion zone size. The penetration depth increased with the increase in laser power . Welding characteristics of austienite Inconel 600 using a continuous wave Nd:YAG laser are experimentally investigated. This paper describes the weld ability of inconel 600 for machine structural use by Nd:YAG laser.

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.232-232
• /
• 2000

The hydrogen attack characteristics of 3Cr-1Mo-V steel as simulated weld heat affected state were studied in this paper. The hydrogen attack susceptibility was evaluated by the ratios of Charpy impact absorbed energy at 0℃($vE_{0HA}$/$vE_{0}$) and reduction of area by tensile test ($RA_{HA}$/RA) before and after exposure to hydrogen at 600℃ under 450kgf/㎠ for 300hr. The values of $vE_{0HA}$/$vE_{0}$ and $RA_{HA}$/RA were aggravated as the peak temperature of the simulated heat affected zone(HAZ) raised. These results were due to the increase of the possession of bubbles along the grain boundaries, which were resulted in the reduction of grain boundary area to be precipitated carbides due to grain coarsening and the carbon dissolved in the martensite-austenite constituent near by the prior austenite grain boundary. The possession ratio of methane bubbles formed along prior austenite grain boundaries were increased with raising the peak temperature. (Received February 22, 2000)

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.105-111
• /
• 2000

The hydrogen attack characteristics of 3Cr-1Mo-V steel as simulated weld heat affected state were studied in this paper. The hydrogen attack susceptibility was evaluated by the ratios of Charpy impact absorbed energy at 0℃({TEX}$vE_{0} {HA}_/vE_{0}${/TEX}) and reduction of area by tensile test({TEX}$RA_{HA}/RA${/TEX}) before and after exposure to hydrogen at 600℃ under 450kgf/㎠ for 300hr. The values of {TEX}$vE_{0} {HA}_/vE_{0}${/TEX} and {TEX}$RA_{HA}/RA${/TEX} were aggravated as the peak temperature of the simulated heat affected zone(HAZ) raised. These results were due to the increase of the possession of bubbles along the grain boundaries, which were resulted in the reduction of grain boundary area to be precipitated carbides due to grain coarsening and the carbon dissolved in the martensite-austenite constituent near by the prior austenite grain boundary. The possession ratio of methane bubbles formed along prior austenite grain boundaries were increased with raising the peak temperature.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.11 no.2
• /
• pp.314-321
• /
• 1987

Post weld heat treatment (PWHT) of weldment of the low alloy Cr-Mo steel, in general, is carried out not only to remove residual stress and hydrogen existing in weldment but to improve fracture toughness of weld heat affected zone (HAZ). There occur some problems such as toughness decrement and stress relief cracking (SRC) in the coarse grained region of weld HAZ when PWHT is practiced. Especially, embrittlement of structure directly relates to the mode of fracture and is appeared as the difference of fracture surface such as grain boundary failure. Therefore, in this paper, the effect of heating rate on PWHT embrittlement under the various kinds of stresses simulated residual stress in weld HAZ was evaluated by COD fracture toughness test and observation of fracture surface. Fracture toughness of weld HAZ decreased with increment of heating rate under no stress, but it was improved to increment of heating rate under the stress. Grain boundary failure didn't almost appear at the heating rate of 600.deg.C/hr but it appeared from being the applied stress of 294 MPa at 220.deg.C/hr and 196 MPa at 60.deg.C/hr.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.6 no.4
• /
• pp.89-95
• /
• 1997

Welding technique is widely applied to general industry such as pressure vessel for chemical plant, pipe system, heavy industry, and automobile. There are some points which must be considered when robot system is used in welding automation process for productivity improvement. Welding quality is governed by heat input, and this quantity can be different according to shape, property, and thick of material . For desired heat input , weld input parameters such as welding voltage, current, and welding velocity must be determined with those consideration. Until now these parameters have been determined mainly by experience of operator. In this study, the size of welding zone was predicted by fuzzy rules were constructed from the relation between welding variables and weld pool size. Inverse model method which welding control input for welder is determined with optimum voltage and current by fuzzy controller is validatied by computer simulation.