Abstract
The hydrogen attack characteristics of 3Cr-1Mo-V steel as simulated weld heat affected state were studied in this paper. The hydrogen attack susceptibility was evaluated by the ratios of Charpy impact absorbed energy at 0℃($vE_{0HA}$/$vE_{0}$) and reduction of area by tensile test ($RA_{HA}$/RA) before and after exposure to hydrogen at 600℃ under 450kgf/㎠ for 300hr. The values of $vE_{0HA}$/$vE_{0}$ and $RA_{HA}$/RA were aggravated as the peak temperature of the simulated heat affected zone(HAZ) raised. These results were due to the increase of the possession of bubbles along the grain boundaries, which were resulted in the reduction of grain boundary area to be precipitated carbides due to grain coarsening and the carbon dissolved in the martensite-austenite constituent near by the prior austenite grain boundary. The possession ratio of methane bubbles formed along prior austenite grain boundaries were increased with raising the peak temperature. (Received February 22, 2000)