• Tribology and Lubricants
• /
• 제12권4호
• /
• pp.18-27
• /
• 1996

An interlaboratory wear testing was performed in order to understand the friction behaviors and the wear mechanisms of the sintered composites. The specimens were the sintered bronze matrix composites having various contents of friction additives, friction control agents and reinforcements. The variation of the wear characteristics according to the constituents of the composites as well as the wear conditions was investigated by SEM, EPMA, OM, the hardness testing and the measurement of friction. The specimen having glass fiber as the matrix reinforcement showed a remarkable increase in wear resistance as increasing the content of glass fiber. Graphite particles in the composites exhibited the lubricating effect and also resulted in the lowering strength of the matrix. Addition of Mo powder to the composites led to the deterioration of wear properties at the room temperature, however, an enhanced wear properties were obtained in the containing Mo at an elevated temperature.

• Tribology and Lubricants
• /
• 제23권4호
• /
• pp.170-174
• /
• 2007

Wear and scuffing tests were conducted using friction and wear measurement of piston rings and cylinder blocks in low friction diesel engine. The frictional forces, wear amounts and cycles to scuffing in boundary lubricated sliding condition were measured using the reciprocating wear tester. The cylinder blocks were used as reciprocating specimens, and the piston rings with several coatings were used as fixed pin. Several coatings were used such as DLC, TiN, Cr-ceramic and TiAlN in order to improve the tribological characteristics. From the tests wear volume of piston ring surfaces applied various coatings were compared. During the tests coefficients of friction were monitored. Test results showed that DLC coatings showed good tribological properties. TiN and Cr-ceramic coated rings showed good wear resistance properties but produced high friction.

• 한국분말재료학회지
• /
• 제7권1호
• /
• pp.12-18
• /
• 2000

Effects of the microstrucrure of rapidy solidified Al-Pb-Cu-Mg alloys on the wear investigated. In order to overcome the miscility gap between Al and pb under equilibrium conditions, both in the solid and the liquid states, the alloy were rapidy solidifies to produce them in a segregation-free condition. Although the Pb particles showed relatively fine dispersion in the Al matrix in all the alloys by this process. the Al-16Pb alloy was found to have the most favorable microstructure with discretre with discrete Pb particles of abount 0.5 ${\mu}$m in size. With the addition of Cu and Cu-Mg to Al-16Pb, cellular structures were newly formed; not seen in the binary Al-Pb alloy. Wear properties of the Al-Pb binary alloys measured as a function of the sliding speen, sliding distance, and applied load showed that the Al-16Pb alloy has the best wear resistance, as expected from the fine microstructural features in this alloy. The were resistance of the alloy containing Cu-and Cu-Mg was higher than that of the Al-16Pvb alloy, due to matrix strengthening by precipitation hardeing. The wear mechanism was identified by examining the traces and wear debris.

• Tribology and Lubricants
• /
• 제39권1호
• /
• pp.13-20
• /
• 2023

Large drill bits may face high hardness ore and high working pressure when working. To optimize the use effect of large drill bits and prolong the use time, it is necessary to add a layer of pressure-resistant, wear-resistant, and low-friction coating on the surface of the drill bit. In this study, CoCrNiAlTi high-entropy alloy coatings and CoCrNiAlTi (70 wt%)-TiC (30 wt%) composite coatings are successfully prepared on Q235 steel by plasma spraying. The CoCrNiAlTi (70 wt%)-TiC (30 wt%) coating consists of FCC solid solution and a small amount of TiC phase. The effect of TiC on the composition phase, microhardness, and elastic modulus of HEA coating is studied by X-ray diffractometer (XRD) and microhardness tester. The effect of TiC on the friction and wear properties of HEA coatings is investigated using a wear tester. By improving the process parameters, the metallurgical bonding between the coating and the substrate is well combined, and a coating without pores and cracks is obtained. The experimental results confirm that the microhardness, elastic modulus, and wear resistance of CoCrNiAlTi-TiC composite coating are better, and the friction coefficient is lower.

• Journal of Advanced Marine Engineering and Technology
• /
• 제32권8호
• /
• pp.1178-1184
• /
• 2008

In this study, techniques of ion implantation were used in order to improve the characteristics of metal materials such as the oxidation and wear resistant. In particular it is necessary to develope their oxidation and wear resistant that could be used in severe environmental conditions. There are mainly two elementary technologies including ion implantation and/or thin film coating. Ion implantation method was performed for surface modification. As a result, it was found that some ion implantations methods such as Nb, high-temperature Nb ion implantation and Nb+C combined implantation are somewhat effective for improving the oxidation resistance of TiAl alloy. Furthermore, the fluorine PBII treatment is more effective for improving the oxidation resistance of the TiAl alloy with three-dimensional shapes. The implantation of boron ion into thin film of TiN was also effective for improving the properties of materials like high temperature wear resistance. TiCrN film was applied to the actual seal ring for steam turbines, and it was observed that its sliding property showed a successfully good performance.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2001년도 춘계학술발표대회 논문집
• /
• pp.29-33
• /
• 2001

In the present study, AZ91Mg/$\textrm{Al}_2\textrm{O}_3$ short fiber+SiC particulates hybrid metal matrix composites(MMCs) were fabricated by squeeze casting method. Different particulate sizes of 45, 29 and $9\mu\textrm{m}$ were hybridized with 5% volume fraction to investigate the effect of SiC particulates size on microstructure, mechanical and thermal properties such as hardness, flexural strength, wear resistance and thermal expansion. Results show that the microstructure of the hybrid composites were quite satisfactory, namely revealing relatively uniform distribution of reinforcements. Some aggregation of SiC particulates caused by particle pushing was observed especially in the hybrid composites containing in fine particulates($9\mu\textrm{m}$). The hardness and flexural strength were improved by decreasing particulates size, whereas wear resistance improved by increasing particulates size because of large particulates restricting matrix wear from contacted stress. Regardless of particulates size, thermal expansion of composites was the same. This may be because the content of particulates was in all cases 5 volume fraction.1

• 한국생산제조학회지
• /
• 제8권6호
• /
• pp.71-77
• /
• 1999

Monitoring of Cutting tool wear is a critical issue in automated machining system and has been extensively studied for many years. An austempered ductile iron(ADI) exhibits the excellent mechanical properties and the wear resistance. ADI has generally the poor machinability due to the characteristic. This paper presents the in-process detection of flank wear of cutting tools using the acoustic emission sensor and the digital oscilloscope. The amplitude level of AE signal(AErms) is mainly affected by cutting speed and it is proportional to cutting speed. There have been the relationship of direct proportion between the amplitude level of AE signals and the flank wear width of cutting tool. The flank wear with corresponding to the tool life is successfully detected with the monitor-ing system used in this study.

• 한국결정성장학회:학술대회논문집
• /
• 한국결정성장학회 1997년도 Proceedings of the 13th KACG Technical Meeting `97 Industrial Crystallization Symposium(ICS)-Doosan Resort, Chunchon, October 30-31, 1997
• /
• pp.187-187
• /
• 1997

Silicon nitride is the most excellent materials among structural ceramics. It has been reported that fracture toughness was improved with adding second phase particles, whisker, fiber etc. However, containing of second phase particles enhanced fracture toughness, however flexural strength was degraded. As adding nanosize SiC particles into silicon nitride, the physical properties of fluxural strength, fracture toughness, the modulus of elasticity. In this study, 2wt% $Al_2$O$_3$ and 4 wt% $Y_2$O$_3$ were added into UBE E-10 and 0, 10, 20, 30, 40, 50 vol% nano-SiC powder (Sumitomo T1 powder) were added, respectively. It is hot pressed at 185$0^{\circ}C$ for 1 hour. Most of structural ceramics for engineering application are wear resistance. In this study, wear behaviors (in water) of silicon nitride with varying the amount of nano-size silicon carbide were investigated, and was compared to physical properties. Simultaneously wear mechanism will be found out.

• Composites Research
• /
• 제33권5호
• /
• pp.241-246
• /
• 2020

본 연구에서는 교반주조 공정을 통해 B₄C 입자가 균일하게 분산된 알루미늄 금속복합재료를 제조하고 후 공정으로 열간압연을 수행하였다. 제조된 복합재료의 미세조직, 기계적 특성 및 내마모 특성에 대해 분석하였다. 40 ㎛ 크기의 B₄C 입자가 균일하게 분산된 복합재료는 강화재의 체적율이 증가함에 따라 인장강도는 증가하였으며, 마모 성능도 개선되었다. 20 vol.% 복합재료의 경우 인장강도 값은 292 MPa로 기지재인 Al6061 대비 155% 증가하였다. 내마모시험 결과 20 vol.% 복합재료의 경우 마모 너비와 깊이가 각각 856 ㎛, 36 ㎛이며, 마찰계수는 0.382로 Al6061 대비 상당히 우수한 내마모 특성을 나타내었다.

• Tribology and Lubricants
• /
• 제31권2호
• /
• pp.56-61
• /
• 2015

In this study, we investigated the effectiveness of an ultrasonic nanocrystal surface modification (UNSM) technique on the mechanical and wear properties of tungsten carbide (WC). The UNSM technique is a newly developed surface modification technique that increases the mechanical properties of materials by severe plastic deformation. The objective of this study was to improve the wear resistance of press die made of WC by applying the UNSM technique. We observed the microstructures of the untreated and UNSM-treated specimens using a scanning electron microscope (SEM), and energy-dispersive X-ray spectroscopy (EDX) was used to investigate the chemical composition. The SEM observations showed the pore size and the number of pores decreased after the UNSM treatment. We assessed the wear behavior of both the untreated and UNSM-treated specimens using a scratch test. The test results showed that the wear resistance of the UNSM-treated specimens increased by about 46% compared with the untreated specimens. This may be attributed to increased hardness, reduced surface roughness, induced compressive residual stress, and refined grain size following the application of the UNSM technique. In addition, we found that the UNSM treatment increased the carbon concentration to 63% from 33%. We expect that implementing the findings of this study will lead to an increase in the life of press dies.