• Journal of the Korean Applied Science and Technology
• /
• v.29 no.2
• /
• pp.356-363
• /
• 2012

In this study we synthesis Hybrid resin(WPC) by milk casein and waterborne polyurethane(WPU). Then we experiment how casein effect to Hybrid resins in Full-Grain leather coatings. According to measured data for solvent resistance, WPU resin and Hybrid resins had good property. As test of tensile strength, WPU had most low strength(2.130 $kg_f/mm^2$) and WPC-3(WPU 91: casein resin 9) had most high strength(2.191 $kg_f/mm^2$). Also we knew that most good property of abrasion is WPC-3(50.090 mg.loss). In elongation case, WPU had most good result(637 %) in this experiment.

• Journal of Adhesion and Interface
• /
• v.9 no.4
• /
• pp.17-23
• /
• 2008

In this study, waterborne polyurethane (WPU)/nano ZnO was synthesized from various polyester polyols, 4,4-dicyclohexylmethane diisocyanate ($H_{12}MDI$), dimethylolpropionic acid (DMPA), triethylamine (TEA) and ethylenediamine (EDA), nano ZnO. The contents of metal oxide were varied from 0 to 1.0 wt% of total solid. The effects of nano ZnO contents and ionic contents in the WPU/nano ZnO on thermal, mechanical properties were studied. The glass transition temperature ($T_g$) of WPU/nano ZnO do not show a distinct tendency with incorporation of nano ZnO and the $T_g$ of WPU/nano ZnO a little increased with increase of DMPA contents. The tensile strength and 100% modulus increase and elongation at break decreases with increase of nano ZnO contents and DMPA contents.

• Applied Chemistry for Engineering
• /
• v.32 no.6
• /
• pp.607-612
• /
• 2021

Silicon (Si) is one of the promising active materials to replace the widely used graphite because of its low electrochemical potential and high theoretical capacity. However, Si anodes still face in problems with the huge volume expansion and continuous decomposition of the electrolyte during repeated charge and discharge processes. To address these issues, a cross-linkable waterborne polyurethane (CWPU) based on a bio-oil, castor oil, was prepared and reacted with Tris(2,3-epoxypropyl) isocyanurate (TGIC) linkers, resulting in the formation of a mechanically robust 3D network structure. Si anodes fabricated with the CWPU-TGIC exhibited stable cycling performances and excellent discharge capacities. The results revealed that the CWPU-TGIC binder efficiently accommodates the large volume change for Si anode during charge and discharge cycles. Overall, the eco-friendly binder shows great promise in improving the electrochemical performances of Si anodes.

• Journal of Adhesion and Interface
• /
• v.23 no.1
• /
• pp.8-16
• /
• 2022

In this study, self-healable waterborne polyurethane (SH-WPU) as shoes and coating materials with self-healable disulfide functionalities was synthesized by mixing polyether polyol to impart excellent durability and heat resistance and polycarbonate polyol to impart excellent mechanical properties. The synthesized SH-WPU was characterized by fourier transform-infrared spectroscopy (FT-IR), and physical and self-healing properties were confirmed through universal testing machine (UTM) and scanning electron microscope (SEM) measurements. Tensile strength and hardness were increased and elongation was decreased by using polycarbonate polyol. In addition, as a result of comparison of thermal properties, thermal stability has been increased as the content of polycarbonate polyol increased. The healing efficiency showed the highest efficiency when poly(tetramethylene ether)glycol : polycarbonate polyol = 0.75 : 0.25, and it was confirmed that the damaged part was healed through surface observation using a microscope and SEM.

• Proceedings of the Korean Fiber Society Conference
• /
• 2001.10a
• /
• pp.21-24
• /
• 2001

Polyurethane are used for a wide range of commercial applications such as adhesives or coatings for various substrates including textile fabric, plastic, wood, glass fiber, and metals. The types of polyurethane ionomers have been reported according to the ionic charges on the polymer main chain, i.e. anionomer, cationomer, and zwitterconomers. (omitted)

• Fibers and Polymers
• /
• v.7 no.2
• /
• pp.95-104
• /
• 2006

In order to improve the water swelling, thermal/mechanical and adhesion properties of waterborne polyurethane (WBPU), a series of the crosslinkable WBPUs containing hydrophilic ionic component, dimethylol propionic acid (20 mole%), were prepared by in-situ polymerization using a cross-linker hexakis (methoxymethyl) melamine (HMMM). Effects of the HMMM content (2, 4, and 6 wt%) and curing temperature on these properties of the crosslinked WBPUs samples were investigated. All properties were found to increase with increasing HMMM content. It was found that the optimum curing temperature of the WBPU films and adhesives was near $120^{\circ}C$, which was not dependent on the HMMM content.

• Journal of the Korean Applied Science and Technology
• /
• v.34 no.4
• /
• pp.778-786
• /
• 2017

In this study, analyzed the changes occurred after adding casein emulsions to water - dispersed polyurethane using polypropylene glycol (PPG). For this purpose, anionic water - dispersed polyurethane containing PPG, IPDI and DMPA and casein emulsion prepared by dissolving casein in distilled water using ammonia water were prepared. As a result of measuring the alkali resistance by using the prepared resin, there was no change in the physical properties. The tensile strength of the sample having a high casein content was measured to be $2.227kgf/mm^2$. Elongation was measured at 474% for samples containing less casein and The abrasion resistance was measured as 46.090 mg.loss of sample containing much casein as a result of the surface roughness measurement.

• Proceedings of the Korean Environmental Sciences Society Conference
• /
• 2008.11a
• /
• pp.533-537
• /
• 2008

• Macromolecular Research
• /
• v.12 no.3
• /
• pp.303-310
• /
• 2004

We have prepared an aqueous dispersion of poly(aniline-dodecyl benzene sulfonic acid complex) (PANI-DC) that has an intrinsic viscosity (〔η〕) near 1.3 dL/g using aniline as a monomer, dodecyl benzene sulfonic acid(DBSA) as a dopant/emulsifier, and ammonium peroxodisulfate(APS) as an oxidant. We found that the electrical conductivity of a PANI-DC pellet was 0.7 S/cm. A waterborne-polyurethane (WBPU) dispersion, obtained from isophorone diisocyanate/polytetramethylene oxide glycol/dimethylol propionic acid/ethylene diamine/triethylene amine, was used as a matrix polymer. We prepared blend films of WBPU/PANI-DC with variable weight ratios (from 99/1 to 66/34) by solution blending/casting and investigated the effects that the PANI-DC content has on the mechanical and dynamic mechanical properties, hardness, electrical conductivity, and antistaticity of these films. The tensile strength, percentage of elongation, and hardness of WBPU/PANI-DC blend films all decreased markedly upon increasing the PANI-DC content. The antistatic half-life time ($\tau$$\sub$$\frac{1}{2}$/) of pure WBPU film was about 110 s, but we found that those of WBPU/ultrasound-treated PANI-DC blend films decreased exponentially from 1.2 s to 0.1 s to almost 0 s upon increasing the PANI-DC content from 1 wt% to 15 wt% to > 15 wt%, respectively.

• Journal of Adhesion and Interface
• /
• v.7 no.4
• /
• pp.53-59
• /
• 2006

The paper highlights technical advances and introduces recent innovations such as smart curing laminating adhesives for flexible packaging with low migration rates of aromatic isocyanates and amines. Latent reactive one-part systems on the basis of surface deactivated solid isocyanates open up new dimensions for heat setting adhesives and waterborne PU dispersions. The new generation of Purmelt Micro Emission adhesives contains less than 0.1% of MDI monomer, thereby drastically reducing the emission of hazardous isocyanate vapors during processing and setting a significantly improved technical standard in occupational safety. Once again, polyurethane adhesives have demonstrated their unique ability to adapt to new process, product, safety and environmental requirements.