• Journal of the Korean Society of Industry Convergence
• /
• v.10 no.4
• /
• pp.207-211
• /
• 2007

The durable lifetime of RC structures is shortened by various reasons, which are the generation of cracks in construction and service term, the exterior deterioration according to climatic condition, the surface damage due to chloride attack and the corrosion of reinforced bars. The durability of concrete structures is nevertheless able to be increased by the method and the material of reinforcement and repair. The epoxy resin is widely used for reinforment and repair of concrete because of the superiority in mechanical property, adhesive property, abrasion resistance, impact resistance and chemical resistance. The epoxy cement mortar with hardening agent has a lot of disadvantages that are troublesome mixing work, weakened weatherability and high cost for hardening agent. In this study, the mix proportion of mortar is presented just only with epoxy resin and some admixtures, and the test result of mortar without hardening agent shows the higher strength than the mortar with hardening agent. In the mix proportion, the weight of epoxy resin must be less than 15% of the unit weight of cement, and 10% of unit weight of cement is adequate for the weight of admixtures.

• Corrosion Science and Technology
• /
• v.16 no.3
• /
• pp.141-150
• /
• 2017

Impregnating with quality silicone water repellent on the concrete surface is an effective method of protecting concrete. Quality silicone water repellent has been widely used in the engineering profession because of its desirable properties such as hydrophobicity, keeping concrete breathable and preserving the original appearance of the concrete. The companies in China that produce silicone water repellent are listed. Test methods in the specifications or standards about silicone water repellent in China are summed. The test methods relative to durability of concrete impregnated with silicone water repellent (such as resistant to chloride ion penetration, resistant to alkali, resistance to freezing and thawing and weatherability etc.) and the constructive quality (such as water absorption rate, impregnating depth and the dry velocity coefficient etc.) are compared and analyzed. The results indicate that there are differences among test methods relative to different specifications with the same index and therefore, confusion has ensued when selecting test methods. All test methods with the exception of the method of water absorption rate by using a Karsten flask are not non-destructive methods or conducted in a laboratory. Finally, further research on silicone water repellent during application is proposed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.29-29
• /
• 2010

Engineering plastics have excellent electrical properties, mechanical strength and various characteristic which include chemical resistance, environmental resistance, weatherability at a wide temperature range. It has good characteristic(light weight, good productivity) as compare with epoxy or porcelain insulators. However, engineering plastics not suited to outdoor insulator because it isn't hydrophobic. Therefore, to over come these critical problems, we improve the surface insulation characteristics of engineering plastic by coating micro-, nano- size inorganic fillers added to RTV-SIR(Room temperature vulcanized-silicone rubber) at this plastic surface. The effect is analyzed through salt-fog test, tracking test. In conclusion, the engineering plastic coated RTV with micro-$Al_2O_3$20[phr], nano-Al(OH)3 1 ~ 3[phr] improved much better than the others.

• Applied Chemistry for Engineering
• /
• v.26 no.3
• /
• pp.326-330
• /
• 2015

Polymeric membranes have been used in various applications and generally applied to the systems prevented from exterior exposure. However, polymer membranes for outdoor usages such as, an air quality monitoring and membrane reservoirs for the selective recovery of useful metals from seawater, have been newly developed. Thus it is required to investigate the properties of the membrane for the outdoor use and also studies of the accelerated UV exposure onto the polymeric membranes are essential to estimate their weatherability. Herein, we report on the thermal and mechanical properties, morphology changes, and color differences of the polysulfone anisotropic membranes and non-woven type polypropylene membranes with the accelerated UV exposure. Results showed that the effect of UV exposure on the membrane depend not only on the polymer used but also on the form of the membrane. This work can provide some of key informations of the membrane for outdoor use.

• Polymer(Korea)
• /
• v.31 no.1
• /
• pp.8-13
• /
• 2007

To overcome drawbacks of the nylon 6/poly (acrylonitrile-co-butadiene-co-styrene) (ABS) blend, nylon 6 blend with poly (acrylonitrile - co-styrene - co-acrylic rubber) (ASA) which containing poly (butyl acrylate) as a rubber phase in substitute of poly (butadiene) in ABS, was examined. Poly (styrene-co-maleic anhydride) (SMA) containing 25 wt% of maleic anhydride (MA) or poly (styrene- co-acrylo-nitrile-co-maleic anhydride) (SANMA) containing less than 3 wt% MA was used as a compatibilizer to fabricate blends having high impact strength. Changes in the mechanical properties of nylon 6/ASA blend with compatibilizer content were similar with those of nylon 6/ABS blend. Blends haying high impact strength was produced when blends contained more than about 20 wt% rubber. Blends containing SAM or SANMA as a compatibilizer were stayed in a injection molding machine at the molding temperature and afterwards specimens for the examination of the impact strength was prepared. Impact strength of blends containing SMA was decreased with retention time, while that of blends containing SANMA was not changed with retention time.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.16 no.4
• /
• pp.30-37
• /
• 2002

This paper reports on the results of weathering test, tracking test and salt-fog test of various kinds of cycloaliphatic epoxy systems. UV irradiation dramatically induced the loss of surface hydrophobicity due to the chain scission attack at the surface under UV irradiation. It could be seen that samples containing an UV absorbent/antioxidant and a silicone oil additive have a good performance in weathering test, while ATH(alumina tri-hydrate) filled ones have high resistance against tracking failure than others. Under salt fog chamber test, specimens mixed with silicone oil are able to suppress leakage current development. It was thought that silicone oil mixed into cycloaliphatic epoxy system could lead to lower the surface energy and to retain hydrophobic properties for a long time, which are desirable for outdoor use.

• Applied Chemistry for Engineering
• /
• v.5 no.2
• /
• pp.215-222
• /
• 1994

As a toughness modifier for plastics chlorosulfonated polyethylene(CSM) can be used. CSM has a good resistance to oxygen and ozone. CSM has a crosslinkable functional group(sulfonyl chorid) with sulfur and metal oxide. Polyvinylchloride(PVC) is widely used industrial plastics because of its balanced properties and low cost. But it has some disadvantages such as low impact strength, light, ozone and oxygen degradation. In order to improve these properties of PVC, CSM was blended with PVC. The toughening effect appeared at about 10wt% and there is no additional effect above 30wt% of CSM. The weatherability, ozone resistance and mechanical properties of PVC were improved by blending with CSM. The toughening mechanism is studied by SEM.

• Polymer(Korea)
• /
• v.26 no.5
• /
• pp.607-614
• /
• 2002

Polyorganosiloxane(HBPS) modified polyurethane (UMPS) was synthesized to improve weatherability in the polyurethane (ITPU) sealant and its rheological propoerty was investigated. It was found that the viscosity increased with increasing HBPS content in polyurethane and maximum viscosity was observed in UMPS having 70/30 ITPU/HBPS ratio. This was understood that the segregation of HBPS segment in UMPS chain has been developed. Further increasing of the content of HBPS resulted in the lowering of viscosity because of the flexibility of HBPS block segment in UMPS chain. It was also found that UMPS has more sensitive environmental dependency of viscosity than ITPU such as shear rate, humidity and temperature. In additions, UMPS having Si(O$CH_3$)$_3$ end group (TUMPS) by adding coupling agent up to 0.3 wt% resulted in the increase of viscosity by the acceleration of curing. But introducing more than 0.5wt% curing agent to TUMPS caused the lowering of viscosity because of less NCO group in TUMPS for the curing.

• Journal of Adhesion and Interface
• /
• v.4 no.1
• /
• pp.9-17
• /
• 2003

The UV hard coating materials are attracting more and more attention to modern industry, in terms of the development of low or non solvent coating materials which will contribute to economizing both materials and energy and to reducing pollution. This study was performed in order to invent UV curable coating materials containing colloidal silica which have actual industrial applications. As results of experiments, the oligomers type and the concentration of colloidal silica acrylate oligomer (SAOC) have an influence on various especially, The properties of UV hardening cooling, such as chemical, abrasion resistance and weatherability, were greatly enhanced, the impact properties of coated polycarbonate substrate were improved compared with the noncoated that. The UV cured films containing 30 wt% SAOC obtained showed the best properties.

• Journal of Conservation Science
• /
• v.26 no.1
• /
• pp.61-67
• /
• 2010

After selecting five types of adhesive epoxy resin for metallic cultural assets such as $Araldite^{(R)}$ rapid type, $Devcon^{(R)}$, $Araldite^{(R)}$ SV427+HV427, $CDK^{(R)}$520, $Araldite^{(R)}$ AW106+HV953 which had already been studied, this paper approached more closely the problem of yellowing and the signal of aging with time passing by connecting the problems with the safety of metallic cultural assets. The change of physical properties according to the change of state of epoxy adhesives was investigated through the change of flexural strength and the change of surface hardness by artificially providing the possible environmental change factors such as ultra-violet ray, and acid base, and how the epoxy chemically changes in its ingredients by the environment was analyzed through FT-IR. As a result of the experiment, for the most part of adhesives brought about the physical change of flexural strength, the change of surface hardness, and the chemical change of chemical ingredients as the product of alcohol, which were respectively different according to the time of ultraviolet irradiation, and acid base change. Under most of the conditions, SV427+HV427 and $CDK^{(R)}$520 were fairly stabilized under each condition of weatherability, but it seems that they should be refrained from being applied in case that the area to restore is thin and wide because the degree of flexural strength of themselves is low. Also, it is found that the preservation environment is very important not only for artifacts but also for the preservation of resins sused for preservation treatment.