• Journal of Powder Materials
• /
• v.7 no.3
• /
• pp.161-167
• /
• 2000

Mechanically-alloyed NiAl powder and ball-milled (Ni+Al) powder mixture were sintered by spark-plasma sintering(SPS) process. Mechanical alloying was performed in a horizontal attritor for 20 h with rotation speed of 600 rpm. (Ni+Al) powder mixtures were prepared by ball milling for 1 and 10 h with 120 rpm. Both powders were sintered at $1150^{\circ}C$ for 5 min under $10^{-3}$ torr vacuum with 50 MPa die pressure in a SPS facility. Sintered densities of 97% and 99% were obtained from mechanically-alloyed NiAl powder and (Ni+Al) powder mixture, respectively. The sintered compact of (Ni+Al) powder mixture showed large grain size by a very rapid grain growth, while the grain size of mechanically-alloyed NiAl powder compact after sintering was extremely fine(80 nm). The difference in densification behavior of both powders were discussed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.04b
• /
• pp.64-67
• /
• 2000

Element distribution analysis and degradation characteristics of the ZnO varistors fabricated at the ambient sintering-process is investigated in this study. ZnO varistors made of Matsuoka's composition were fabricated by standard ceramic techniques. The ambient sintering-process is performed at the special electrical-furnace which is equipped with the vacuum system. The Gases of injection at sintering- process were oxygen, air, nitrogen and argon respectively. Element and quantitative analysis in the microstructure of ZnO varistors made use of EPMA equipment. Degradation characteristics were showed by DC degradation tests at $115{\pm}2\;^{\circ}C$ for period up to 13 h. From above analysis, it is found that at the DC degradation test the ZnO varistor sintered in oxygen atmosphere showed the excellent prop properties among them and these results could be explain by element and quantitative analysis in ZnO microstructure.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.35 no.5
• /
• pp.533-538
• /
• 2011

A plastic-compatible low-temperature metal deposition and patterning process is essential for the fabrication of flexible electronics because they are usually built on a heat-sensitive flexible substrate, for example plastic, fabric, paper, or metal foil. There is considerable interest in solution-processible metal nanoparticle ink deposition and patterning by selective laser sintering. It provides flexible electronics fabrication without the use of conventional photolithography or vacuum deposition techniques. We summarize our recent progress on the selective laser sintering of metals and metal oxide nanoparticles on a polymer substrate to realize flexible electronics such as flexible displays and flexible solar cells. Future research directions are also discussed.

• Journal of the Korean Ceramic Society
• /
• v.54 no.2
• /
• pp.121-127
• /
• 2017

Gadolinium tetraboride ($GdB_4$) was synthesized by reduction of $Gd_2O_3$ using boron carbide in presence of carbon. Effect of temperature on product quality was investigated. Pure $GdB_4$ powder was obtained in vacuum at $1500^{\circ}C$. Pressureless sintering experiments revealed that sintering takes place only above $1600^{\circ}C$. A maximum density of 77.1% of the theoretical value was obtained at $1800^{\circ}C$ by pressureless sintering. Hot pressing resulted in 95.5% of theoretical density at the lower temperature of $1700^{\circ}C$ under 35 MPa pressure. Hardness and fracture toughness of dense $GdB_4$ were measured and found to be 21.4 GPa and $2.3MPa{\cdot}m^{1/2}$, respectively. After exposure to air at $900^{\circ}C$, the formation of a porous and non-protective oxide layer was observed.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.6 no.6
• /
• pp.468-472
• /
• 2005

In order to prevent adhering of molten glass on a mold wall, the wall is swabbed with lubricant oil before forming. However, the swabbing process can be removed from the entire processes of the glass forming if the mold wall is made of a porous sintered material. The purpose of the present study is to manufacture a sintered material(having a sintered density of $85{\~}90\%$)which is the most appropriate into. plane material for a glass mold. For the research, SUS310L-based coarse powder (${\~}150{\mu}m$) and SUS420J2-based fine powder ($40{\~}50{\mu}m$) were used for the compact materials, and effects of compaction pressure and sintering condition(atmosphere, temperature) were investigated. The results obtained were as fellows. (1) By means of solid phase sintering, a desired sintering density could not be achieved in any case when using a 310L-based powder having a large particle size. (2) When sintering green compacts(compaction pressure of $2ton/cm^2$) in a commercial vacuum furnace(at $1300^{\circ}C$ for 2 hours), the sintered compacts had densities of $6.2g/cm^3(79\%)$ for 310L + 0.03$\%$B, $6.6g/cm^3 (86\%)$ for 420J2, $7.3g/cm^3(95\%)$ for 420J2+(0.03)$\%$B, and $7.6g/cm^3(99\%)$ for 420j2+(0.06)$\%$B, respectively. As a result, it is regarded that sintered compacts having a desired porosity may be achieved by vacuum sintering the 420J2-based powder (low pressure compaction) and the 310L+0.03$\%$B-based powder (high pressure compaction).

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2005.11a
• /
• pp.91-91
• /
• 2005

• Proceedings of the Korean Nuclear Society Conference
• /
• 2005.10a
• /
• pp.316-317
• /
• 2005

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.128-128
• /
• 2013

Fabrication of heterogeneous catalysts using Atomic Layer Deposition (ALD) has recently been attracting attention of surface chemists and physicists. In this talk, I will present recent results about structures and chemical activities of various catalysts prepared by ALD, particularly focusing on Ni-based catalysts. Ni has been considered as potential catalysts for $CO_2$ reforming of methane (CRM); however, Ni often undergoes rapid decrease in catalytic activity with time, and therefore, application of Ni as catalysts for CRM has been regarded as difficult so far. Deactivation of Ni catalysts during CRM reaction is from either coke formation on Ni surface or sintering of Ni particles during reaction. Two different strategies have been used for enhancing stability of Ni-based catalysts; $TiO_2$ nanoparticles were deposited on micrometer-size Ni particles by ALD, which turned out to reduce coke formation on Ni surfaces. Ni nanoparticles deposited by ALD on mesoporous silica showed high activity and long-term stability from CRM without coke deposition and sintering during CRM reaction. Ni-based catalysts have been also used for oxidation of toluene, which is one of the most notorious gases responsible for sick-building syndrome. It was shown that onset-temperature of Ni catalysts for toluene oxidation is as low as $120^{\circ}C$. At $250\circ}C$, total oxidation of toluene to $CO_2$ with a 100% conversion was found.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.255-255
• /
• 2013

WC-Co 초경합금은 실온경도, 고온경도, 강도, 내마모, 내충격 등 기계적 특성이 우수하여 공구재료, 절삭공구 및 고압용 부품 등 다양한 응용분야를 가지고 있으며 WC-Co 분말 코팅같은 경우 항공분야, 일반 공업 분야에 내마모 특성 및 내열특성 향상을 위한 코팅용 소재로서 활용되어 지고 있다. 활용분야가 넓은 WC-Co 초경합금의 제조방법은 WC, Co 분말을 혼합하여 약 900도에서 1차 예비소결 후 원하는 형상 가공 후 약 1,300~1,600도에서 2차 소결을 진행한다. 지금 현재 초경분말의 조성, 크기와 같은 변수들에 따른 초경합금의 기계적 특성 변화에 대한 연구가 계속적으로 진행되고 있다. 본 연구에서는 WC-Co 분말의 소결 특성을 향상시키고자 Planetary ball mill 장비를 활용하여 볼 밀링 공정을 진행하였고 Spark plasma sintering 장비를 활용하여 빠른 소결을 진행하였다. WC-Co 분말의 미세구조, 입도, 조성 및 분산의 변화를 관찰하기 위해 볼 밀링 전, 후 분말을 분석하였고 제조된 분말의 소결 특성을 확인하기 위해 상용화 된 WC-Co 분말의 소결 특성과 비교 평가하였다. 분석 결과 볼 밀링 공정 후 분말은 약 15 ${\mu}m$에서 4.4 ${\mu}m$로 미세해지는 것을 확인하였고 밀링 후 분말로 초경합금을 제작하였을 때 기존 상용화 초경합금제작 온도보다 약 100~400도 낮아지면서 경도 값은 약 20% 향상된 것을 확인할 수 있었다.

• Journal of Powder Materials
• /
• v.4 no.2
• /
• pp.113-121
• /
• 1997

The densification of the compacts of Co+32%Cr+20%W+l.5%C, Co+32%Cr+20%W+3.0%C and Co+32%Cr+20%W+4.5%C sintered under $H_2$ gas or vacuum was investigated. The effect of V and B addition on the densification was also investigated. The densification of these compacts were always incomplete regardless of sintering atmosphere, temperature and time. The amounts of oxygen and carbon in compacts sintered in $H_2$ for 3.6ks at 1523K were 0.105~0.160 mass% and 0.33~0.89 mass%, respectively. And those in vacuum were 0.028~0.032% and 0.957~4.08%, respectively. Relative density(Ds) of Co+29%Cr+17%W+3.0%C compact containing 6%V and Co+32%Cr+20%W+2.97%C compact containing 0.03%B were 99 and 100%, respectively, indicating complete densification by solid phase sintering. Victors hardness of sintered compacts containing 6%V or 0.03%B were 632 and 568, showing 50~60% increase in comparison to those without V or B. These results can be explained in terms of oxidation/reduction of oxides and equilibrium pressure of CO in isolated pore, instead of presence of liquid formation and grain boundary separation from pores due to large grain growth.