• Journal of the Korea institute for structural maintenance and inspection
• /
• v.17 no.5
• /
• pp.94-104
• /
• 2013

Experiments were divided into two parts; one part is to understand the basic properties of high flowable VA/VeoVa-modified cement mortar with different polymer cement ratio (P/C) and the weight ratio of fine aggregate to cement (C:F) and the other part is to investigate the effect of surface water spread on the concrete substrate on adhesion in tension. To understand the basic performance, the specimens were prepared with proportionally mixing VA/VeoVa redispersible powder, ordinary portland cement, silica sand, superplasticizer and viscosity enhancing agent. Here, P/C were 10, 20, 30, 50 and 75% and C:F were 1:1 and 1:3. As the change of P/C and C:F unit weight, flow test, crack resistance and adhesion in tension were measured. Three specimens with good adhesion properties were selected among specimens with different P/C and C:F. The effect of surface water evenly sprayed on concrete substrate on adhesive strength is investigated. The results show that surface water on concrete substrate increases the adhesion in tension of high flowable VA/VeoVa-modified cement mortar and additionally improves the flowability compared to the non-sprayed case.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.727-730
• /
• 2004

The purpose of this study is to evaluate the fundamental properties of fine type cement grouts with redispersible polymer powders. Cement grouts with redispersible polymer powders are prepared with various polymer-cement ratios, and tested. for flow, water absorption, drying shrinkage, flexural and compressive strengths. From the test results, flow of the cement grouts with EVA and Va/VeoVa polymer powers decreased with increasing elapsed time. Regardless of polymer type, the flexural strength of the cement grouts tends to increase with increase in polymer-cement ratio. The maximum compressive strengths of the cement grouts are obtained at a polymer-cement ratio of $5\%$.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.261-266
• /
• 2003

This study is to investigate the heating value and noxious gases generation such as CO, NO and $SO_2$ known as dangerous gas for human from specimen made of cement and lightweight aggregate. The most quanity of CO gas is generated in EPS(Expanded Poly Styrene), core of commercial sandwich panel. Although specimens mainly composed of cement discharged the relatively less CO gas than organic core such as EPS, specimens which SBR was added discharged the very much amount of CO gas similar to EPS and especially, specimens including foaming agent, gas foaming agent or redipersible powder of VA/VeoVa showed the good properties in the generation of CO gas. From the standpoint of the generation of NO and $SO_2$ gas, both the core of commercial sandwich panel such as EPS, Glass wool and specimens made with polymer dispersion such as St/BA and SBR discharge the very much amount of NO and $SO_2$ gas in comparison of the other specimens. From this study, it was confirmed that organic materials such as core of commercial sandwich panel dischared much more noxious gas than specimens composed of cement and inorganic lightweight aggregate.