• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 가을 학술발표회 논문집
• /
• pp.769-774
• /
• 2002

In this study, methyl methacrylate (MMA)- modified polyester polymer concrete, in which the MMA was added to the unsaturated polyester resin, was developed for improving the early-age strength and the workability of the conventional polymer concrete, binder of which was the unsaturated polyester resin. Then the fundamental properties of the polymer concrete such as workability and strength were surveyed. The experimental results showed that the workability was remarkably improved as the MMA contents increased, and the filler-binder ratio was turned out to be important factor for the workability. Slump prediction equation was derived by the regression analysis based on MMA content and filler-binder ratio. Furthermore, early-age strength was greater when the MMA content were increased in the range of 20-40 % but the strength rather showed a tendency of decrease when the MMA content was 50 %.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2000년도 추계학술발표대회 논문집
• /
• pp.38-41
• /
• 2000

High temperature cure characteristics of polyester resin systems were investigated by isothermal and dynamic differential scanning calorimetries. During isothermal scanning, the experimental procedure was modified to reduce the initial Boss of heat. no kinetic equation from the isothermal experiment was compared with that from the dynamic experiment.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 추계 학술발표회 논문집
• /
• pp.741-744
• /
• 2006

The study focuses on the mixture of materials for the development of porous concrete with unsaturated polyester resin. The materials used in the mixture include the coarse aggregates unsaturated polyester resin as binder, calcium carbonate and sand as a filler. An experimental procedure has been carried out to select the best combination of the materials that satisfy both the required permeability and compressive strength.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 봄 학술발표회논문집(II)
• /
• pp.713-718
• /
• 1998

This paper deals with the consistency of fresh lightweight polyester mortars as high-performance or multifunctional building materials. Fresh lightweight polyester mortars using an unsaturated polyester resin, lightweight fillers and aggregate are mixed with various mix proportions, and tested for slump-flow and slump as a measure of consistency. At 10, 20 and 3$0^{\circ}C$, the influences of mix proportioning factors on the slump-flow and slump of the lightweight polyester mortars are examined, and the empirical equations for the slump predictions are successfully proposed.

• 콘크리트학회논문집
• /
• 제19권2호
• /
• pp.163-169
• /
• 2007

본 연구에서는 불포화 폴리에스터수지를 이용하여 적절한 투수성과 압축강도 및 내구성을 갖는 투수 콘크리트를 개발하고자 하였다. 투수 콘크리트 개발을 위해 사용된 재료로는 단입도 굵은골재와 결합재로서 불포화 폴리에스터수지 그리고 채움재로서 탄산칼슘을 이용하였다. 배합 방법은 굵은골재 최대치수, 결합재 비율, F/B 비율 등을 변화시키며 KS 규격에 준하여 각각의 배합에 따른 투수계수, 압축강도를 평가하였다. 그 결과, 투수계수는 약 $3.5{\times}10^{-1}cm/sec$, 공극률은 약 34%, 압축강도는 11 MPa로 나타나, 우수유출저감시설의 기준을 만족하는 것으로 나타났다.

• 콘크리트학회논문집
• /
• 제14권3호
• /
• pp.283-290
• /
• 2002

일반적으로 불포화 폴리에스테르 모르타르 및 콘크리트는 강도가 우수하고 내약품성이 좋지만, 취성적이어서, 내충격성이 요구되는 용도로는 사용하기 어렵다. 그러므로, 본 연구에서는 재생골재와 불포화 폴리에스테르 액상수지를 사용한 바닥마감재를 개발하기 위해 불포화 폴리에스테르 모르타르의 취성을 개선시켜보고자 하였다. 불포화 폴리에스테르 모르타르의 취성을 개선하기 위한 재료로 폴리우레탄 액상고무를 사용하였으며, 폴리올의 분자량과 폴리우레탄 액상고무의 치환율에 따른 모르타르의 특성을 검토했다. 실험결과, 폴리우레탄 액상고무의 사용에 따라 불포화 폴리에스테르 모르타르의 점도가 증가하였고, 경화수축은 감소하였다. 그리고, 모르타르내에 생성된 고무입자에 의해 압축강도 및 휨강도는 다소 저하하였지만, 내충격성이 향상되고, 휨파괴시험결과에서 파괴하중이후에도 급격한 파괴를 보이지 않는 결과를 얻을 수 있었다. 따라서, 본 연구의 결과는 폴리올의 분자량 2000, 3000인 폴리우레탄 액상고무를 불포화 폴리에스테르 모르타르에 사용하여 취성의 개선효과를 얻을 수 있다는 것을 제시하고 있다.

• 한국안전학회지
• /
• 제30권1호
• /
• pp.34-39
• /
• 2015

The feasibility of recycling wasted printed circuit board (PCB) is investigated by preparing PCB added flame retardant composites filled with either unsaturated polyester or polyurethane. In order to improve electroconductive properties, copper powder was added into the composites, which results also in improving their antistatic properties. The prepared composite samples showed a binding between the polymer fillers observed by a scanning microscope. The sample group using unsaturated polyester is elastomeric that led to appreciable elongation and elasticity. In case of polyurethane, the tensile strength increased proportionally as increase of the amount of PCB powder. The composite materials can be utilized as antistatic composite materials, since the surface resistivity result showed increase of the electroconductive properties by adding Cu. The flammability of the samples is not satisfactory according to UL-94 vertical test. However, the flame retardant properties were improved by adding PCB power. This study, therefore, showed that it is feasible to fabricate polymer composite materials and improve the material characteristics by adding PCB powder, which can replace existing additives used for the preparation of polymer composite materials and can reduce the environment contamination by recycling the wasted PCB.

• 한국농공학회논문집
• /
• 제58권1호
• /
• pp.19-26
• /
• 2016

This study was performed to evaluate the strength and durability properties of modified epoxy composites with waste tire chip, recycled coarse aggregate, filler and modified epoxy to improve elongation and elasticity of epoxy. Additionally, for comparing to modified epoxy and unsaturated polyester resin as a binder, unsaturated polyester resin composites were developed in the same condition. The mix proportions were determined to satisfy the requirement for the workability and slump according to aggregate size and binder content. Tests for the compressive and flexural strength, freezing and thawing and durability for 20 % sulfuric solution were performed. The compressive and flexural strength of modified epoxy composites were in the range of 34.9~61.6 MPa and 10.2~18.3 MPa at the curing 7 days, respectively. Also, the compressive and flexural strength of unsaturated polyester resin composites were in the range of 44.2~77.8 MPa and 11.3~20.8 MPa at the curing 7 days, respectively. After 300 cycles of freezing and thawing, weight decrease ratio and durability factor of modified epoxy composites were in the range of 0.8~1.9 % and 95~98, respectively. Accordingly, modified epoxy composites will greatly improve the durability of concrete.

• 폴리머
• /
• 제25권3호
• /
• pp.375-384
• /
• 2001

불포화 폴리에스테르(unsaturated polyester: UP)의 희석제로 많이 사용되는 스티렌 단량체 (SM)대신에 단일 중합체의 유리전이온도가 낮은 비닐 아세테이트(VAc), 메틸 아크릴레이트(MA)를 SM과 혼합하여 사용하였을 때 혼합초성에 따른 UP의 기계적 물성 변화를 조사하였다. SM/MA 혼합계는 MA함량 증가에 따라 전체적으로 강인성의 향상이 나타난 반면, SM/VAc 혼합계의 경우에는 VAc 단량체치 함량 증가에 마른 강인성의 향상을 기대하기가 힘든 것으로 나타났다. 이러한 현상은 전체 계의 유리전이온도의 저하 효과와 상분리에 의한 응력 완화 효과에 미치는 각 단량체의 영향이 서로 다르기 때문인 것으로 해석되었다.

• 폴리머
• /
• 제24권5호
• /
• pp.599-609
• /
• 2000

본 연구에서는 불포화 폴리에스테르 수지의 기계적 물성을 증진시키기 위하여 프로필렌글리콜(PG)과 네오펜틸글리콜(NPG)의 몰비를 달리한 불포화 폴리에스테르 수지를 제조하여 경화거동 및 기계적 물성을 조사하였다. 경화거동은 microgel reaction mechanism을 이용하여 설명하였고, NPG 몰비의 증가는 최종 전화율을 증가시키나 경화속도가 늦어짐을 알 수 있었다. 그리고 글리콜 몰비중에서 NPG 몰비의 증가는 굴곡강도, 인장탄성율, 흡수율, 함침성이 증가하였고, 반면에 인장강도, 신율, 굴곡탄성율이 감소하는 경향으로 나타났다. 따라서 중합한 불포화 폴리에스테르 수지에서 PG/NPG 몰비가 0.5/0.5, 0.25/0.75의 영역일 때 섬유강화 플라스틱 복합재료의 물성이 우수한 것으로 관찰되었다.