• 한국농공학회논문집
• /
• 제52권1호
• /
• pp.51-59
• /
• 2010

The cemented sand and gravel (CSG) method is a construction technique that adds cement and water to rock-like materials, such as rivered gravel or excavation muck which that can be obtained easily at areas adjacent to dam sites. This study was performed to evaluate the unconfined compressive strength properties and freezing and thawing resistance of CSG materials with unit cement content. The three types of CSG-80, CSG-100 and CSG-120 with cement content were designed to evaluate the optimum water content, dry density, strength, stress-strain, micro structure and durability factor. As the results, the optimum water content ratio with cement content showed almost similar tendency, and the unconfined compressive strength and dry density increased as cement content increases. The strength ratio of 7 days for 28 days were in the range of 55~61 % and the strain ratio in stress-strain curve were in the range of 0.8~1.6 % nearby maximum strength in 28 days. It is expected that this study will contribute to increasing application of CSG method as well as to increasing the utilizing of CSG materials as a environmentally friendly CSG method.

• 한국농공학회논문집
• /
• 제46권3호
• /
• pp.57-63
• /
• 2004

This study was performed to evaluate the engineering properties of cement mortar brick with loess and fly ash. The unit weight was in the range of $2,068{\sim}2,137\;kgf/m^{3}$ and $1,899{\sim}2,045\;kgf/m^{3}$ in water and dry curing, respectively It was decreased with increasing the loess content. The absorption ratio was in the range of $5.2{\sim}13.1%$ and $8.5{\sim}13.2%$ in water and dry curing, respectively. The compressive strength was decreased with increasing the loess content. The compressive strength of the 193 $kgf/m^{2}$ in water and 188 $kgf/m^{2}$ in dry curing at the curing age 28 days of the binder volume ratio 35% was exceeded in 163 $kgf/m^{2}$ of standard compressive strength about cement bricks. The carbonation depth was in the range of $0.9{\sim}1.4$ mm, $1.2{\sim}3.6$ mm, $1.4{\sim}6.7$ mm and $2.4{\sim}12.5$ mm in dry curing of curing age 14days, 28days, 90days and 360days, respectively.

• 한국건축시공학회지
• /
• 제6권3호
• /
• pp.107-114
• /
• 2006

In this study, the experiment was carried out to investigate and analyze the engineering properties of concrete using fine aggregate of PS bal slagl. The main experimental variables were water/cement ratio 30, 40, 50(%), water content $170kg/m^3$, replacement ratio of slag fine aggregate 0, 25, 50, 75(%) in experiment I and water/cement ratio 30, 40, 50(%), water content 165, 170, 175($kg/m^3$), replacement ratio of fine aggregate of PS ball 0, 50 in experiment II. According to the test results, the principle conclusions are summarized as follows (1) The workability of slag fine aggregate-mixed concrete tends to improve, as the replacement rate increases. (2) The air content of slag fine aggregate-mixed concrete tends to decrease, as the replacement rate increases. (3) The unit volume weight of slag fine aggregate-mixed concrete tends to significantly increase, as the replacement rate increases. (4) The compressive strength of slag fine aggregate-mixed concrete tends to show more increasing propensity, in case the curing period is relatively long, as the replacement rate increases.

• Elastomers and Composites
• /
• 제42권2호
• /
• pp.102-106
• /
• 2007

카본블랙, 커플링제가 없는 실리카, 그리고 커플링제를 함유한 실리카 등 다른 충전 시스템을 갖는 SBR 가황물의 수팽윤 거동에 대해 연구하였다. 증류수와 3.5% NaCl 용액을 팽윤 매질로 사용하였다. 증류수에서의 수팽윤비가 소금물에서의 그것보다 높았다. 카본블랙으로 보강된 가황물의 수팽윤비가 실리카로 보강된 것보다 낮았다. 실리카로 보강된 SBR 가황물의 경우, 커플링제가 없는 것이 커플링제를 함유한 것보다 더 큰 수팽윤비를 나타내었다. 1,2-유니트 함량이 다른 SBR 가황물의 수팽윤 거동에 대해서도 비교하였다. 수팽윤비는 1,2-유니트 함량이 증가함에 따라 감소하는 경향을 보였다.

• 한국건축시공학회지
• /
• 제9권2호
• /
• pp.85-91
• /
• 2009

W/C and unit volume, which significantly affect quality of concrete related to strength and durability, are regulated at below $185kg/m^3$ for regular concrete generally used in standard specification for constructions. The aim of this research is to develop chemical admixture and find out its potential use by identifying characteristics of admixtures added to soft concrete and hardening concrete, of which content ratio of component for each type of admixtures is subject to change in accordance with unit volume within KS' allowable range. Sodium gluconate, polyoxyethylene nonylphenyl ether, poly carboxylic copolymer in slump, which is characteristic of soft concrete, are deemed highly sensitive while there is no air entrainment except for $10\sim70%$ in WE, WR component content ratio and NP. In hardening concrete, strength in general showed higher action in compressive strength and tensile strength than in plain strength. Use of proper AE agent and AE water reducing agent at the same time is deemed to be used as chemical admixtures capable of manufacturing high-quality, high-quantity concrete.

• 아시안잔디학회지
• /
• 제3권1호
• /
• pp.24-33
• /
• 1989

This study was conducted to investigate the effect of paclobutrazol [(2 RS , 3 RS )1-(4- chlor-ophenyl )-4, 4- dimethyl -2- (1, 2, 4- triazol -1- yl )- pentan -3-01] on the tolerance of hi-gh temperature and drought stress as related to growth retardation , iranspiration rate , soil water content , nitrogen level and photosynthetic rate in perennial ryegrass ( Loliurn perenne L . ' Omega H , ). Plants were given a 30 ml soil drench of paclohutrazol at the concentrations of 0, 0.01, 0.1, 1.0, 10.. 0, mg / 6 .5cm- diameter pot . The rcsults were as follows : 1. Increasing concentrations of paclohutrazul reduced plant height , leaf area , fresh weight and dry weight , hut increased chlorophyll content per unit area . The number of tillers and leaf width were not affected hy the paclobutrazol concentrations . 2. The proper concentration of paclohatrazol on growth retardation in perennial ryegrass was about I mq /pot , hut leaf deformity and severe growth retardation were shown at high concentration of 10 mq / pot . 3. Perennial ryegrasses grown at 30˚C were shown significantly short plant height and low leaf nitrogen level compared with those grown at 20˚C. Increasing concentrations of paclohutrazol at 20˚C increased nitrogen level hut it could not increase nitrogen level at 30˚C . 4. During the drought stress , increasing temperatures significantly promoted transpiration rate and wilting time . It took about 5 days at 20˚C and 3 days at 30˚C to reach wilting time of leaves from water stress treatment . Soil water contents at wilting time of non-treated controls were averaged 6. 871% at 20˚C and 6. 17% at 30˚C 5. Paclohutrazol reduced transpiration rate at high temperature and drought stress . Wilting appeared at the lower water content of soil according to increasing concentrations of paclobutrazol at 30˚C hut there were no differences among concentrations of at 20˚C. 6.Paclohutrazol treatment at 1 rag /pot reduced injury rate of leaves from 67.1 % and 100 % in control plants to 15.7% and 80% at 20˚C and 3010, respectively. 7. Photosynthetic rate per unit area was significantly reduced at high temperature . Paclohutrazol stimulated photosynthetic rate with increase of concentrations at 20˚C but there was no increasing effect at 30˚C.

• 한국건설순환자원학회논문집
• /
• 제3권2호
• /
• pp.132-139
• /
• 2015

본 연구는 파쇄처리 순환골재를 사용한 콘크리트의 특성을 검토하기 위하여 순환골재의 흡수율별 단위시멘트량 및 물시멘트비를 변화시켜 콘크리트의 특성에 미치는 영향을 검토하였다. 실험결과 물시멘트비가 높은 저강도 배합에서는 파쇄처리 순환골재를 사용한 콘크리트와 쇄석 콘크리트의 압축강도가 동등한 수준으로 나타나 순환골재의 부착모르타르 영향이 작은 것으로 나타났다. 그러나, 물시멘트비가 낮은 고강도 배합에서는 파쇄처리 순환골재를 사용한 콘크리트가 부착모르타르의 영향으로 쇄석을 사용한 콘크리트보다 약 40%의 압축강도저하를 나타내었다. 한편, 흡수율 7%인 순환골재의 건조수축량은 재령 10주에서 흡수율 1%인 쇄석의 $-310{\times}10^{-6}$보다 2배 증가된 $-700{\times}10^{-6}$을 나타내어 콘크리트용 골재로의 재활용시 건조수축에 대한 검토가 선행되어야 할 것으로 사료된다. 또한 단위시멘트량 $450kg/m^3$인 부배합 콘크리트의 압축강도는 흡수율 3%인 순환골재 사용시 쇄석 사용 콘크리트와 동등하게 나타난 반면, 흡수율 7%인 순환골재를 사용한 경우에는 쇄석 사용 콘크리트에 비해 약 7%정도 낮게 나타났다. 그러나, 단위시멘트량 $350kg/m^3$인 일반배합 콘크리트의 압축강도는 쇄석 사용 콘크리트에 비해 압축강도 저하가 현저하게 나타났다.

• 한국지반공학회논문집
• /
• 제32권2호
• /
• pp.53-62
• /
• 2016

흙의 다짐 특성에 영향을 주는 주요인자 중 하나인 온도는 지역과 계절에 따라 다양하게 변화하는 특성을 가진다. 최근 동토지방에서 많은 토목공사가 시행되고 있지만, 온도와 관련된 흙의 다짐기준 및 지침을 정량화할 수 있는 문헌은 미비한 실정이다. 따라서 본 연구는 온도에 따른 흙의 다짐특성을 시험을 통해 평가하고자 하였다. 시험을 위해 러시아 시베리아, 캐나다 앨버타 주 오일 샌드 지역 등에서 자주 쓰이는 성토재료인 모래의 온도별 다짐특성을 나타낼 수 있는 주문진 모래를 사용하였으며, 표준다짐시험을 흙의 다양한 온도조건($-10^{\circ}C$에서 $17^{\circ}C$)에서 수행하였다. 시험 결과 영상 온도에서는 다짐 시 벌킹 효과로 인해 흙 공시체의 부피 팽창이 발생하였으며, 그 범위는 0%~6%이였다. $0^{\circ}C$에서 $17^{\circ}C$까지 온도가 증가하면서 최대 부피(최소 건조단위중량)에 해당하는 함수비는 감소하였고, 최소 부피(최대 건조단위중량)에 해당하는 함수비는 온도가 증가함에 따라 약간 증가하였다. 영하 온도의 경우 함수비가 추가됨에 따라 건조단위중량은 지속적으로 감소하였다. 영하 온도에서는 벌킹이 발생하지 않았으며 물의 단위부피보다 얼음의 단위부피가 더 크기 때문에 흙 공시체의 부피가 증가하였다.

• Steel and Composite Structures
• /
• 재36권6호
• /
• pp.657-669
• /
• 2020

This study investigates the fire resistance characteristics of reactive powder concrete according to changes in the cement content per unit area, mixing ratio of metakaolin (MK), and content of polypropylene fiber. A fire test was conducted, and the resulting residual strength characteristics were investigated through flexural and compressive strength measurements, as well as condition rating classification based on visual evaluation. MK effectively reduced the initial high content of calcium hydroxide, thereby reducing the water vapor pressure generated during pyrolysis and slowing spalling. Furthermore, the pore structure and loose tissue were effective for relieving the water vapor pressure in the event of a fire.

• KCI Concrete Journal
• /
• 제11권3호
• /
• pp.19-28
• /
• 1999

This study treated self-compacting high Performance concrete as two Phase materials of Paste and aggregates and examined the effect of powder and aggregates on self-compacting high performance, since fluidity and segregation resistance of fresh concrete are changed mainly by paste. To improve the fluidity and self-compactibility of concrete, optimum powder ratio of self-compacting high performance concrete using fly ash and blast-furnace slag as powders were calculated. This study was also designed to provide basic materials for suitable design of mix proportion by evaluating fluidity and compactibility by various volume ratios of fine aggregates, paste, and aggregates. As a result, the more fly ash was replaced, the more confined water ratio was reduced because of higher fluidity. The smallest confined water ratio was determined when 15% blast-furnace slag was replaced. The lowest confined water ratio was acquired when 20% fly ash and 15% blast-furnace slag were replaced together. The optimum fine aggregates ratio with the best compactibility was the fine aggregate ratio with the lowest percentage of void in mixing coarse aggregate and fine aggregate In mixing the high performance concrete. Self-compacting high performance concrete with desirable compactibility required more than minimum of unit volume weight. If the unit volume weight used was less than the minimum, concrete had seriously reduced compactibility.